Friday, June 03, 2011, 09:16 |
John Wong | Ta#37 | LP-SIS | ITW | TM1 | 38634-5 | 36833-7 | Spent | Target is done |
Fri Jun 3 12:40:30 2011
Ta#37-LP-SIS (w.o#38634-5)
Filled with 400 Ta foils (25/pk), 4.0 cm in length. Total mass + Ta wire = 42.32g. The heat shield was assembled and tested, and the standard salts were added. Target was installed in the test stand on Jun 1, 2011.
Fri Jun 17 09:19:46 2011: The following salts have been added: Li, Na, Rb @ 10uL, K @ 5uL, Cs @ 15uL, and Be @ 10uL.
Wednesday, July 06, 2011, 14:08: TM1 is still under repairing. It was tested at the test-stand. Target is on the shelve and ready to be used.
Tuesday, July 26, 2011, 15:58: Salt added before going into the hotcell: Li,Na,Rb,K,Cs. Target is ready to be used for TM1 test.
Wednesday, July 27, 2011, 10:48: It was found that the extraction electrode had some arc marking on it (see attachment: EE). Investigating...
Wednesday, July 27, 2011, 12:51: After further investigation on the extraction electrode, we found some black and blue(or green) deposit on the outside surface and inside of the EE. This deposit is most likely copper oxide, which formed during the HV test. The EE was removed, and wiped clean with methanol. (see attachment: EE_CuO). This target will be used in TM1.
Friday, August 26, 2011, 09:48: As per Friday Aug 26 TIS meeting, bNMR is very satisfied with the beam; the count rate is very stable.
|
| Attachment 1: EE.JPG
|
|
| Attachment 2: EE-CuO.jpg
|
|
|
|
9
|
Friday, June 17, 2011, 11:58 |
John Wong | UCx (flakes) | LP-SIS | | | | | Problems/Solutions | Making UC2 flakes (stock# 2011_A & _B) |
Fri Jun 17 10:28:47 2011
First batch of UO2/C mixture of carbonization (Stock# 2011_A):
UO2 used = 50.120g (left overs + container = 411.23g)
C(grv) used = 10.653g (or 21.25% w/w)
Mass of organics = 4.842g (or 9.66% w/w)
Mass of dried cast = 47.420g
Waste collected in jar = 18.195g (including UO2, C and Org)
Waste accountable for UO2 = 12.57g
The carbonization process started from May 26 to June 4 (9 days).
See attachment #1 and #2 for the striptools during the UO2/C carbonization
Total Mass UC2 flakes = 35.310g
Fri Jun 17 11:56:15 2011
Attempted to make the second batch of UO2/C mixture of carbonization on June 13, but it failed. The milling jar gasket seal partially came out during the high speed milling. As a result, the UO2/C mixture squirted out and contaminated the planetary mill (See attachment #3 & #4). RPG and all other groups were informed. The planetary mill and the lab were properly cleaned up (see attachment #5), no activities were found after the cleaning. Attachments #6, #7, #8 are some of the discussion about the UO2 spill.
All the UO2 taken out from the container (50.23g) is accountable for waste.
June 28, 2011 - Re-making 2nd batch of UO2/C mixture was successful.
Stock#2011_B:
UO2 used = 50.29g
C(grv) used = 10.0g
Mass of Organics = 4.84g
Mass of Dried green = 71.96g (the cast was let dry over night <24hrs due to time restriction. It might not be completely dried as a result of such heavy mass remained. However, the UO2 waste was very minimum, <5.0g)
Total Mass UC2 flakes = 56.853g
|
| Attachment 1: UO2_C_IG1_CG2_2011_A.jpg
|
|
| Attachment 2: UO2_C_TGHT_IG1_2011_A.jpg
|
|
| Attachment 3: UO2_mill_spill_01.png
|
|
| Attachment 4: UO2_mill_spill_02.png
|
|
| Attachment 5: UO2_spill_cleanup.png
|
|
| Attachment 6: UO2_spill_discussion_01.png
|
|
| Attachment 7: UO2_spill_discussion_02.png
|
|
| Attachment 8: UO2_spill_discussion_03.png
|
|
|
|
12
|
Wednesday, July 06, 2011, 14:32 |
John Wong | Ta#36 | LP-SIS | ITE | TM4 | 38634-2 | 38307-10 | Spent | Target ready, will go online on July 27 |
Ta-LP-SIS (w.o#38634-2)
Target consists of 400 Ta foils, 4.4 cm in length. Total mass + Ta wire = 40.87g.
Thursday, July 07, 2011, 15:43: Begin target assembly.
Friday, July 08, 2011, 14:24: assembly completed. Std stds added for test-stand: Li, Na, Rb, K, Cs.
Friday, July 15, 2011, 09:09: Target currently in test-stand. Will come out on Monday next week. Need to add std salts + Be.
Monday, July 18, 2011, 10:58: Target removed from test-stand. Std salts added (Li, Na, Rb, K, Cs) & Be (as requested by Jens). Maico D.V will do a final inspection on the target before it goes into the hotcell
|
|
|
13
|
Tuesday, August 09, 2011, 14:31 |
John Wong | UCx#2 | LP-SIS | ITW | TM1 | 38634-8 | 38633-5 | Spent | UCx#2 run is finished. |
UCx#2 Spec:
Target wrapped with 3 Ta-heat shields
Target length = 11.2cm
Total UC2/C foils = 245 discs
Total U/cm2 = 15.27g
Standard salts = 10uL Na, 10uL Li
Tuesday, August 09, 2011, 14:27:
Target came out from the glovebox and transported to the cold lab for assembly. During the assembly, one of the screw-heads for the heat-shield broke (see attachment#1: broken_screwhead).
The target was leak checked and fine.
Target is going back to the glovebox to be kept under Ar until RH is ready (see attachment #2: UCx#2).
Tuesday, October 04, 2011, 10:21
UCx#2 run was finished last week.
Target was moved from ITW to south hot cell, and stored in a bucket under argon feed.
|
| Attachment 1: broke_screwhead.jpg
|
|
| Attachment 2: UCx#2.jpg
|
|
|
|
14
|
Tuesday, September 06, 2011, 13:19 |
John Wong | TaC#1 | LP-SIS | ITE | TM1 | 38634-6 | | Spent | Target is done |
Tuesday, September 06, 2011, 13:14:
Average mass = 0.206g
Average Thickness = 0.0189 cm
Area of D-shaped disc = 2.21 cm2
D-shape discs diameter = 18.5mm (14.5mm cut-out length)
Oven ID, L= 18.22mm, R = 18.20mm
Density = 4.9266 g/cm3
% Yield Density = 47.20%
Attachment#1 - TaC density measurements.
Loaded target with 125 discs --> 9.6g Ta/cm2
Total discs mass = 30.41g
Total length = 4.5 cm
Thursday, September 15, 2011, 10:45
Na & Li were added.
Re foil inserted.
No Ta-heat shields required.
Friday, September 30, 2011, 14:10
After the test-stand, 10uL of Na and Li were added yesterday.
Target is now ready, and will be moved into the hotcell next week.
Wednesday, November 16, 2011, 15:51
After the target was finished and transferred into the hotcell, it was found that the target broke apart from the center block. This might have happened during the end of the target cooldown. See link for more details:
http://documents.triumf.ca/docushare/dsweb/View/Collection-7438
|
| Attachment 1: TaC_density_measurements.xls
|
|
|
16
|
Tuesday, September 27, 2011, 10:36 |
Anders Mjos | TaC#1 | LP-SIS | ITE | TM1 | 38634-6 | 36833-6 | Problems/Solutions | Material deposited on Extraction Electrode after Test Stand |
| John Wong wrote: |
|
Tuesday, September 06, 2011, 13:14:
Average mass = 0.206g
Average Thickness = 0.0189 cm
Area of D-shaped disc = 2.21 cm2
D-shape discs diameter = 18.5mm (14.5mm cut-out length)
Oven ID, L= 18.22mm, R = 18.20mm
Density = 4.9266 g/cm3
% Yield Density = 47.20%
Attachment#1 - TaC density measurements.
Loaded target with 125 discs --> 9.6g Ta/cm2
Total discs mass = 30.41g
Total length = 4.5 cm
Thursday, September 15, 2011, 10:45
Na & Li were added.
Re foil inserted.
No Ta-heat shields required.
|
Tuesday, September 27, 2011, 10:29
After the test stand, deposited material was found on the Extraction Electrode. A sample of the material was taken for later analysis. The electrode was cleaned with methanol. See attachment for photos. |
| Attachment 1: Deposited_material.pdf
|
|
|
|
18
|
Wednesday, November 16, 2011, 14:08 |
John Wong | UCx#3 | LP-SIS | ITW | TM1 | 38634-10 | 36833-3 | Spent | UCx#3 ready to go online |
Wednesday, November 16, 2011, 13:51
UCx#3 descriptions:
Target oven wrapped with 3-Ta heat shields, including the back block (see attachment#1)
Total UCx/C discs = 365
Total disc length = 12.9cm
UC2/C (365 foils) = 44.76 g
UC2/C (365 foils) - organics = 39.24g
U (365 foils) = 34.05g
U (365 foils) thickness = 16.03 g
Salts added: Na, Li, K, Rb, & Ce. |
| Attachment 1: UCx#3_assembly.jpg
|
|
|
|
19
|
Monday, February 13, 2012, 16:00 |
John Wong | Nb#6 | LP-SIS | ITW | TM1 | 38634-4 | 36833-1 | Spent | Nb#5 ready in the Conditioning Station |
Monday, February 13, 2012, 16:00
Nb#5 target description:
Total Nb foils = 400
Total Mass (400 foils + Ta wire) = 24.52g
Total Length = 4.0cm
Target thickness = 11.57 g/cm2
Target Density = 8.57g/cm3
Inserted Rh foil (1cmx1cm)
Added standard salts before test-stand:
15ml Cs
10ml Li, Na, Rb
5ml K
Monday, April 23, 2012, 08:58
Target was tested in the test stand, see https://elog.triumf.ca/TIS/Test-Stand/77 for more details.
No salts were added after the test. The target is now in the conditioning station.
|
|
|
22
|
Friday, June 01, 2012, 11:43 |
John Wong | Ta#38 | LP-SIS | ITW | TM1 | 39165-2 | 38633-2 | Spent | Ta#38 target description |
Ta#38 LP-SIS target description:
Total Ta foils = 400
Foil thickness = 0.025mm
Target density = 16.69 g/cm3
Target area = 2.12cm2
Target length = 4.3cm
Total Mass (400 foils + Ta wire) = 42.8013g
See the link for more details: http://documents.triumf.ca/docushare/dsweb/View/Collection-8541
Friday, June 01, 2012, 11:36
The target is now in the test-stand, and by next week Tuesday, it should go in the Hotcell.
Monday, June 04, 2012, 16:56
The target was tested in the Test-stand. The EE was inspected and a small amount of deposit was discovered after the test (the same stuff was found on Ta#36), see attachment #1. The samples were collected and will be analyzed through SEM/EDX/XRD.
The EE and the common plate were cleaned with methanol and were assembled back.
The target is ready to go in the Hotcell tomorrow, June 05.
Monday, November 05, 2012, 16:42
The deposits on the EE and CC were analyzed using XRD
On the EE, it was mainly copper hydroxide nitrate, Cu2(OH)3(NO3). (see attachment #2)
On the CE, it was mainly tantalum, Ta. (see attachment #3)
|
| Attachment 1: Ta_38_EE_deposit.JPG
|
|
| Attachment 2: Ta#38_EE.PNG
|
|
| Attachment 3: Ta#38_CE.PNG
|
|
|
|
23
|
Monday, June 11, 2012, 13:46 |
John Wong | Nb#6 | LP-SIS | ITW | TM1 | 38634-4 | 36833-1 | Spent | Nb#5 run finished |
| John Wong wrote: |
|
Monday, February 13, 2012, 16:00
Nb#5 target description:
Total Nb foils = 400
Total Mass (400 foils + Ta wire) = 24.52g
Total Length = 4.0cm
Target thickness = 11.57 g/cm2
Target Density = 8.57g/cm3
Inserted Rh foil (1cmx1cm)
Added standard salts before test-stand:
15ml Cs
10ml Li, Na, Rb
5ml K
Monday, April 23, 2012, 08:58
Target was tested in the test stand, see https://elog.triumf.ca/TIS/Test-Stand/77 for more details.
No salts were added after the test. The target is now in the conditioning station.
|
Monday, June 11, 2012, 13:42
The Nb#5 run was good. The target is now in the storage.
see https://elog.triumf.ca/TIS/RH-ISAC/124
|
|
|
25
|
Friday, July 20, 2012, 11:39 |
John Wong | UCx#4 | LP-SIS | ITW | TM1 | 38634-9 | 36833-4 | Spent | UCx#4 target description |
Friday, July 20, 2012, 11:35
UCx#4 target description, see attachment#1
The target is assembled and stored in the Ar-glove box. It will be transported to the South Hotcell on July 31, 2012.
|
| Attachment 1: UCx#4_specfications.PNG
|
|
|
|
27
|
Wednesday, August 29, 2012, 14:52 |
John Wong | UCx#5 | LP-SIS | ITW | TM4 | 39165-5 | | Failed | UCx#5 target description |
Wednesday, August 29, 2012, 14:50
UCx#5 target description, see attachment#1
The target is currently undergoing the final conditioning in the Evaporator #1.
Wednesday, December 05, 2012, 15:46
This target was broken right before the end of the final run. The target was inspected today inside the Hotcell and the pictures can be found here: http://documents.triumf.ca/docushare/dsweb/View/Collection-9357
Looks like the protective layer (TaC coating) was worn out over the course of the run time.
We need to improve the target coating so this can be prevented in the future.
More info about this later...
|
| Attachment 1: UCx#5_specifications.PNG
|
|
|
|
28
|
Wednesday, September 12, 2012, 01:53 |
John Wong | Nb#7 | LP-SIS | | | 39165-6 | | Spent | Nb#7 target description |
Wednesday, September 12, 2012, 02:10
Nb#7 target description:
Total Nb foils = 400 discs
Total Nb mass (Nb foils + Ta wires) = 26.529g
Total length (after filled) = 4.6cm
(see attachment #1) |
| Attachment 1: Nb#7_target_description.jpg
|
|
|
|
31
|
Tuesday, March 19, 2013, 13:32 |
John Wong | SiC#28-RFQ | LP-SIS | | TM4 | LP-RFQ (NEW) | | Spent | SiC#28-RFQ target description |
Tuesday, March 19, 2013, 12:28
SiC#28 - RFQ target description:
Total SiC foils = 325 discs
Total SiC + C-grv foils = 38.48 g
Total length = 10.9cm
Average mass of SiC/disc (without graphite foil) = 0.083 g
Average thickness of SiC (without graphite foil) = 0.18 mm
No Rh foil added
See attachment #1: SiC#28 RFQ density measurements
See link for more details: https://documents.triumf.ca/docushare/dsweb/View/Collection-9771
|
| Attachment 1: SiC#28_RFQ_density_measurements.xlsx
|
|
|
32
|
Thursday, April 11, 2013, 14:30 |
John Wong | Ta#39 | LP-SIS | ITW | TM1 | 39165-7 | | Spent | Ta#39 target description |
Ta#38 LP-SIS target description:
Total Ta foils = 400
Foil Thickness = 0.025mm
Target density = 16.69 g/cm3
Target length = 4.1cm
Total Mass (400 foils + Ta wire) = 43.15g
Disc area = 2.12 cm2
Ta thickness = 20.354g/cm2
See link for more details:
http://documents.triumf.ca/docushare/dsweb/View/Collection-9934
|
|
|
33
|
Thursday, May 30, 2013, 16:58 |
John Wong | UCx#6 | LP-SIS | | TM1 | 39165-6 | 39230-8 | Spent | UCx#6 - target description |
Thursday, May 30, 2013, 16:57
UCx#6 target specification, see attachment #1.
The target is currently undergoing the final conditioning in the Evaporator#1.
Wednesday, June 12, 2013, 17:10
Target is assembled and stored in the Ar glove box.
It's ready to go into the Hotcell.
|
| Attachment 1: UCx#6_specifications.PNG
|
|
|
|
35
|
Friday, August 30, 2013, 12:08 |
John Wong | UCx#7 | LP-SIS | ITW | TM1 | 38634-7 | 39230-4 | Spent | UCx#7 - target description |
Friday, August 30, 2013, 12:06
UCx#7 target specification, see attachment #1.
The target is assembled and going online soon.
|
| Attachment 1: UCx#7_specifications.PNG
|
|
|
|
39
|
Monday, March 17, 2014, 16:15 |
John Wong | Ta#42 | LP-SIS | ITW | TM4 | 40282-1 | 39956-1 | Spent | Ta#42 Target description |
Monday, March 17, 2014, 16:14
Ta#42 LP-SIS target description:
Total Ta foils = 400
Foil Thickness = 0.025mm
Target density = 16.69 g/cm3
Target length = 4.2cm
Total Mass (400 foils + Ta wire) = 45.899g
|
|
|
42
|
Friday, June 06, 2014, 14:09 |
John Wong | UCx#9 | LP-SIS | | | 39165-9 | | Ready | UCx#9 - Target description |
Friday, June 06, 2014, 14:08
See attachment for the target description
|
| Attachment 1: UCx#9_target_description_1.JPG
|
|
|
|
43
|
Tuesday, July 15, 2014, 10:54 |
Laura Lambert | Ta # 43 | LP-SIS | ITW | TM1 | 40282-2 | | Ready | Ta # 43 Target Description |
Tuesday, July 15, 2014, 9:45
Ta#42 LP-SIS target description:
Total Ta foils = 400
Foil Thickness = 0.025mm
Target density = 16.69 g/cm3
Target length = 4.9cm
Total Mass (400 foils + Ta wire) = 45.920g
|
|
|
44
|
Tuesday, July 15, 2014, 11:01 |
Laura Lambert | UCx # 10 | LP-SIS | ITE | TM4 | 39165-10 | | Ready | UCx#10 Target Description |
Tuesday, July 15, 2014, 10:58
See attachment for target description |
| Attachment 1: UCx_10_target_description.PNG
|
|
|
|
45
|
Monday, July 28, 2014, 15:57 |
John Wong | ZrC#6 | LP-SIS | ITW | TM1 | 40282-3 | | Spent | ZrC target description |
Monday, July 28, 2014, 15:52
See attachment#1 for ZrC target description.
Target is currently undergoing the sintering process
|
| Attachment 1: ZrC#6.JPG
|
|
|
|
46
|
Monday, August 18, 2014, 14:39 |
Laura Lambert | ThO2 #1 | LP-SIS | | | | | | ThO2 #1 Target Description |
Monday, August 18, 2014, 14:53
See attachment for target description
|
| Attachment 1: ThO2#1_target_description.JPG
|
|
|
|
48
|
Thursday, November 06, 2014, 13:35 |
Laura Lambert | UCx # 11 | LP-SIS | ITE | TM4 | 40282-5 | | Ready | UCx#11 Target Description |
Thursday, November 06, 2014, 13:29
See attachment for target description
|
| Attachment 1: UCx_11_target_description.PNG
|
|
|
|
50
|
Friday, April 17, 2015, 16:00 |
Laura Lambert | UCx # 12 | LP-SIS | ITW | TM1 | 41177-2 | | Ready | UCx#12 Target Description |
Thursday, April 16, 2015, 14:07
See attachment for target description |
| Attachment 1: UCx_12_target_description.PNG
|
|
|
|
52
|
Wednesday, June 03, 2015, 10:55 |
Laura Lambert | ZrC#7 | LP-SIS | ITW | TM2 | 41177-1 | | Ready | ZrC#7 target description |
Wednesday, June 03, 2015, 10:53
Total length packed = 12.3cm
See attachment for target description.
|
| Attachment 1: target_production_elog_ZrC#7.JPG
|
|
| Attachment 2: ZrC#7_final_density.xlsx
|
|
|
53
|
Monday, July 06, 2015, 12:18 |
John Wong | ZrC#7 | LP-SIS | ITW | TM2 | 41177-1 | | Failed | ZrC#7 target description |
| Laura Lambert wrote: |
|
Wednesday, June 03, 2015, 10:53
Total length packed = 12.3cm
See attachment for target description.
|
Monday, July 06, 2015, 12:10
This target did not pass the test-stand and will not be used for online (unless if it gets approved). The target container is deformed. An increase of voltage was observed during the test; perhaps it's a sign of the container being cracked?! See Test-stand e-log#450 for more details.
Another target is already prepared and being tested. (Target Oven WO# 41177-2).
|
|
|
54
|
Tuesday, July 07, 2015, 13:00 |
John Wong | ZrC#7 | LP-SIS | ITW | TM2 | 41177-2 | | Ready | ZrC#7 (backup1) target description |
Tuesday, July 07, 2015, 12:36
Total no. discs = 422
Total packed length = 13.2 cm (measured after the sintering process)
Note: The theoretical length (ZrC + graphite foils) is 10.52cm After the sintering process, the stack of discs expanded in length. To avoid crushing the materials while inserting the endcaps, the discs are gentally packed to 13.2cm.
(see attachments for more details)
|
| Attachment 1: ZrC#7_backup.PNG
|
|
| Attachment 2: ZrC_specification_(backup#1_WO#41177-2).xlsx
|
|
|
59
|
Monday, October 26, 2015, 16:33 |
Laura Lambert | UCx#14 | LP-SIS | | | 41077-5 | | Ready | UCx#14 Target Description |
Monday, October 26, 2015, 16:23
Attached please find the UCx#14 target description.
Note: This is the first UCx target using the new LP-SIS small center block design.
|
| Attachment 1: Capture.JPG
|
|
|
|
60
|
Friday, March 04, 2016, 14:57 |
Laura Lambert | UCx#15 | LP-SIS | ITW | | 41077-1 | | Ready | UCx#15 Target Description |
Friday, March 04, 2016, 14:56
Attached please find the UCx#15 target description.
Note: This is the second UCx target using the new LP-SIS small center block design.
|
| Attachment 1: UCx_15_description.jpg
|
|
|
|
65
|
Tuesday, August 02, 2016, 15:28 |
Laura Lambert | UCx#17 | LP-SIS | | | 41790-3 | | Ready | UCx#17 Target Description |
Tuesday, August 02, 2016, 15:27
Attached please find the UCx#17 target description.
|
| Attachment 1: UCx#17_description.jpg
|
|
|
|
69
|
Tuesday, October 18, 2016, 12:06 |
Laura Lambert | Ta#50 | LP-SIS | | | 41790-5 | | Ready | Ta#50 target description |
Tuesday, October 18, 2016, 10:12
Ta#50 LP-SIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.025mm
Target density = 14.03 g/cm3
Target length = 3.4cm
Total Mass = 47.6889g [Incl foils + Ta wire on 6 packs] |
|
|
70
|
Friday, October 21, 2016, 13:47 |
Laura Lambert | UCx#18 | LP-SIS | | | 41790-6 | | Ready | UCx#18 Target Description |
Friday, October 21, 2016, 13:46
Attached please find the UCx#18 target description.
|
| Attachment 1: UCx#18_description.jpg
|
|
|
|
71
|
Tuesday, March 07, 2017, 10:00 |
Laura Lambert | UCx#19 | LP-SIS | | TM4 | 42218-12 | | Ready | UCx#19 Target Description |
Tuesday, March 07, 2017, 09:54
Attached please find the UCx#19 target description.
|
| Attachment 1: UCx#19_description.jpg
|
|
|
|
72
|
Wednesday, March 08, 2017, 15:42 |
Laura Lambert | Ta#51 | LP-SIS | | TM2 | 41790-4 | | In progress | Ta#51 target description |
Wednesday, March 08, 2017, 15:40
Ta#51 LP-SIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.025mm
Target density = 14.64 g/cm3
Target length = 3.4cm
Total Mass = 49.7916g [Incl foils + Ta wire on 6 packs]
|
|
|
75
|
Wednesday, May 31, 2017, 09:53 |
Laura Lambert | Ta# 52 | LP-SIS | | TM4 | 42218-14 | | In progress | Ta#52 target description |
Wednesday, May 31, 2017, 09:51
Ta#52 LP-SIS target description:
Total Ta foils = 400 [4x20 packs + 320 single discs]
Foil Thickness = 0.025mm
Target density = 14.77 g/cm3
Target length = 2.9cm
Total Mass = 42.8228g [Incl foils + Ta wire on 4 packs]
|
|
|
77
|
Thursday, July 06, 2017, 15:36 |
Anders Mjos | Ta#55 | LP-SIS | | | 42218-11 | | Ready | Ta#55 target description |
Target loaded by Matt yesterday
320 foils = 33.7832 g
4 x 20 packs = 9.1170 g
Total Weight = 42.9002 g
Length of foils is 2.88 cm
Target conditioned at ISAC Test Stand (580 A) without Ta heat shields |
|
|
78
|
Monday, August 21, 2017, 11:13 |
Laura Lambert | UCx#21 | LP-SIS | | | 42218-15 | | Ready | UCx#21 Target Description |
Monday, August 21, 2017, 11:09
Attached please find the UCx#21 target description.
|
| Attachment 1: target_description.JPG
|
|
|
|
81
|
Monday, April 16, 2018, 09:55 |
Laura Lambert | UCx#22 | LP-SIS | | | 42218-13 | | Ready | UCx#22 Target Description |
Monday, April 16, 2018, 09:53
Attached please find the UCx#22 target description.
|
| Attachment 1: target_description.JPG
|
|
|
|
84
|
Monday, August 27, 2018, 17:11 |
John Wong | UCx#24 | LP-SIS | | | | | Ready | UCx#24 Target Description |
Monday, August 27, 2018, 17:09
See attachment for UCx#24 target description
|
| Attachment 1: Capture.JPG
|
|
|
|
85
|
Monday, September 17, 2018, 11:39 |
John Wong | np-SiC#1 | LP-SIS | | | 43044-1 | | Ready | nano-SiC#1 Target description |
Monday, September 17, 2018, 11:32
See attachment for the target description.
Some notes about the target conditioning in Evap#2 (see elog ID#414):
TGHT at 500A, 8.4V, temp at 1600 C (4.2 kW)
TGHT at 475/7.84V, temp at 1550 C (3.72 kW - Max operating target heating power)
TGHT at 450/7.31V, temp at 1500 C (3.28 kW)
|
| Attachment 1: target_description.JPG
|
|
|
|
86
|
Friday, October 12, 2018, 17:14 |
John Wong | UCx#25 | LP-SIS | | | | | In progress | UCx#25 Target Description |
Friday, October 12, 2018, 17:11
See attachment for UCx#25 target description.
|
| Attachment 1: UCx#25_target_description.JPG
|
|
|
|
89
|
Friday, May 31, 2019, 16:11 |
Aaron Schmidt | Ta#58 | LP-SIS | ITE | TM2 | 43044-4 | 42972-7 | Ready | Ta#58 Target desription |
Ta#58 LP-SIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.025mm
Target density = 14.16 g/cm3
Target length = 3.4 cm
Total Mass = 48.138 g [Incl foils + Ta wire on 6 packs]
Total mass w/ Target oven= 464 g
Discs in target are arranged as follows: 1pack / 75singles / 1pack / 100singles / 2packs / 100singles / 1pack / 75singles / 1pack
End caps installed (not yet expanded). No Ta heat shield added. |
| Attachment 1: Ta#58_Loading_data.pdf
|
|
|
|
90
|
Monday, July 22, 2019, 16:33 |
Marla Cervantes | UCx#27 | LP-SIS | | | 49044-9 | | Ready | UCx#27 Target Description |
Monday, July 22, 2019, 16:31
Attached please find the UCx#27 target description.
|
| Attachment 1: UCx#27.JPG
|
|
|
|
91
|
Tuesday, July 30, 2019, 15:52 |
Darwin Ortiz Rosales | ZrC#8 | LP-SIS | ITE | TM2 | 43044-5 | | Ready | Target description |
Tuesday, July 30, 2019, 15:50
See attachment for details
Thursday, August 01, 2019, 07:41
See attachment#2 for SEM - JW
|
| Attachment 1: ZrC8.png
|
|
| Attachment 2: ZrC_8_SEM.pdf
|
|
|
|
92
|
Tuesday, September 17, 2019, 08:47 |
Aaron Schmidt | Ta#59 | LP-SIS | | TM2 | 44062-5 | | In progress | Ta#59 Target description |
Tuesday, September 17, 2019, 08:44:
Ta#59 LP-SIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.025mm
Target density = 13.74 g/cm3
Target length = 3.4 cm
Total Mass = 46.7314 g [Incl foils + Ta wire on 6 packs]
Total mass w/ Target oven= 436 g (440 g w/ end caps)
Discs in target are arranged as follows: 1pack / 75singles / 1pack / 100singles / 2packs / 100singles / 1pack / 75singles / 1pack
End caps installed (not yet expanded). No Ta heat shield added. |
| Attachment 1: Ta#59_Loading_Data.pdf
|
|
|
|
93
|
Wednesday, October 02, 2019, 11:18 |
Marla Cervantes | UCx#28 | LP-SIS | | | 44062-4 | | Ready | UCx #28 Target description |
Wednesday, October 02, 2019, 11:17
Attached please find the UCx#28 target description. |
| Attachment 1: UCx28-target_description.JPG
|
|
|
|
95
|
Monday, October 21, 2019, 12:38 |
Darwin Ortiz Rosales | UCx#29 | LP-SIS | | | 44062-6 | | Ready | UCx29-target_description |
|
| Attachment 1: UCx#29.PNG
|
|
|
|
96
|
Tuesday, November 19, 2019, 12:20 |
Darwin Ortiz Rosales | UCx#30 | LP-SIS | | | 44062-3 | | Ready | UCx30-target_description |
|
| Attachment 1: UCx#30.PNG
|
|
| Attachment 2: UCx30-taret_description_revised.png
|
|
|
|
98
|
Thursday, February 20, 2020, 08:11 |
Aaron Schmidt | Ta#60 | LP-SIS | | | 44139-13 | | Ready | Ta#60 Target Description |
Thursday, February 20, 2020, 08:07:
Ta#60 LP-SIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.025mm
Target density = 14.081 g/cm3
Target length = 3.33 cm
Total Mass = 46.891 g [Incl foils + Ta wire on 6 packs]
Total mass w/ Target oven= 445g w/ end caps)
Discs in target are arranged as follows: 1pack / 75singles / 1pack / 100singles / 2packs / 100singles / 1pack / 75singles / 1pack
End caps installed (Expanded). No Ta heat shield added. |
| Attachment 1: Ta#60_Loading_Data.pdf
|
|
|
|
100
|
Thursday, June 04, 2020, 15:00 |
Marla Cervantes | C#1 | LP-SIS | | | 43044-8 | | In progress | Target C#1 Description |
Thursday, June 04, 2020, 15:00
See attached picture for description |
| Attachment 1: C1-Description.PNG
|
|
|
|
101
|
Tuesday, September 29, 2020, 11:50 |
Marla Cervantes | C#2 | LP-SIS | ITW | TM2 | 44139-9 | | In progress | Target C#2 Description |
Tuesday, September 29, 2020, 11:49
See attached picture for description |
| Attachment 1: C2-Description.JPG
|
|
|
|
102
|
Tuesday, October 06, 2020, 14:25 |
Aaron Schmidt | Ta#61 | LP-SIS | ITE | TM4 | 44508-1 | | In progress | Ta#61 Target Description |
Ta#61 LP-SIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.025mm
Target density = 12.76 g/cm3
Target length = 3.4 cm
Total Mass = 43.388 g [Incl foils + Ta wire on 6 packs]
Total mass w/ Target oven= 464 g (w/ end caps)
Discs in target are arranged as follows: 1pack / 100 singles / 1pack / 75 singles / 2packs / 75 singles / 1pack / 100 singles / 1pack
End caps installed (not yet expanded). No Ta foil heat shield added |
|
|
103
|
Tuesday, October 27, 2020, 12:53 |
Aaron Schmidt | Nb#9 | LP-SIS | ITE | TM4 | 44508-2 | | Ready | Nb#9 LP-SIS target description |
Nb#9 LP-SIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.025mm
Target density = 7.24 g/cm3
Target length = 3.5 cm
Total Mass = 25.343 g [Incl foils + Ta wire on 6 packs]
Total mass w/ Target oven= 425 g (w/ end caps)
Discs in target are arranged as follows: 1pack / 75 singles / 1pack / 100 singles / 2packs / 100 singles / 1pack / 75 singles / 1pack |
| Attachment 1: Nb#9_Target_Loading_data.pdf
|
|
|
|
106
|
Thursday, April 08, 2021, 09:54 |
Aaron Schmidt | Ta#62 | LP-SIS | | | 44139-10 | | Ready | Ta#62 target description |
Ta#62 LP-SIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.025mm
Target density = 13.96 g/cm3
Target length = 3.4 cm
Total Mass = 47.461 g [Incl foils + Ta wire on 6 packs]
Total mass w/ Target oven= 445 g (w/ end caps)
Discs in target are arranged as follows: 1pack / 75 singles / 1pack / 100 singles / 2packs / 100 singles / 1pack / 75 singles / 1pack
End caps installed (expanded). No Ta foil heat shield added |
|
|
107
|
Wednesday, June 09, 2021, 11:45 |
Darwin Ortiz Rosales | UCx#33 | LP-SIS | | | 44139-12 | | Ready | UCx#33-Target_description |
Cartridge with discs was further heated in EVAP1 (eLog 271 Evaporator 1). |
| Attachment 1: UCx33-target_description.png
|
|
|
|
108
|
Wednesday, June 23, 2021, 18:13 |
Aaron Schmidt | Ta#62 | LP-SIS | ITE | TM4 | 44691-4 | | In progress | Ta#62 Target Description (2) |
Ta#62 LP-SIS target description: (REPLACEMENT FOR 44139-10)
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.025mm
Target density = 14.29 g/cm3
Target length = 3.4 cm
Total Mass = 48.602 g [Incl foils + Ta wire on 6 packs]
Total mass w/ Target oven= 456 g (w/ end caps)
Discs in target are arranged as follows: 1pack / 75 singles / 1pack / 100 singles / 2packs / 100 singles / 1pack / 75 singles / 1pack
End caps installed (Not expanded). No Ta foil heat shield added |
|
|
109
|
Monday, August 16, 2021, 11:02 |
John Wong | UCx#34 | LP-SIS | ITW | TM2 | 44691-5 | 44378-1 | Ready | Target description |
Monday, August 16, 2021, 11:01
See attachments for the target description and SEM images
|
| Attachment 1: UCx#34_target_description.PNG
|
|
| Attachment 2: UCx_34_SEM_Density_Measurements.pdf
|
|
|
|
111
|
Tuesday, September 21, 2021, 21:08 |
Darwin Ortiz Rosales | C#3 | LP-SIS | | | 44691-7 | | Ready | Target C #3 Description |
Tuesday, September 21, 2021, 21:09
See attached file for target description. |
| Attachment 1: C#3_Target_description.png
|
|
|
|
113
|
Monday, November 08, 2021, 11:30 |
Darwin Ortiz Rosales | UCx#36 | LP-SIS | | | 44691-1 | | Ready | UCx#36_Target_Description |
|
| Attachment 1: UCx#36_properties.png
|
|
|
|
114
|
Wednesday, November 10, 2021, 18:09 |
Aaron Schmidt | Ta#63 | LP-SIS | ITE | TM4 | 44691-11 | | In progress | Ta#63 |
Ta#63 LP-SIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.025mm
Target density = 15.38 g/cm3
Target length = 3.4 cm
Total Mass = 52.296 g [Incl foils + Ta wire on 6 packs]
Total mass w/ Target oven= 457 g (w/ end caps)
Discs in target are arranged as follows: 1pack / 75 singles / 1pack / 100 singles / 2packs / 100 singles / 1pack / 75 singles / 1pack
End caps installed (Not expanded). No Ta foil heat shield added |
| Attachment 1: Ta#63_Target_Loading_Data.pdf
|
|
|
|
116
|
Thursday, June 02, 2022, 16:55 |
Aaron Schmidt | Ta#64 | LP-SIS | ITE | TM4 | 44691-12 | | In progress | Ta#64 Target Description |
Thursday, June 02, 2022, 16:54:
Ta#64 LP-SIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.0254mm (0.0010") Measured.
Target density = 12.005 g/cm3
Target length = 3.35 cm
Total Mass = 40.2166 g [Incl foils + Ta wire on 6 packs]
Total mass w/ Target oven= 446 g (w/ end caps)
Discs in target are arranged as follows: 1pack / 75 singles / 1pack / 100 singles / 2packs / 100 singles / 1pack / 75 singles / 1pack
End caps installed (Not expanded). No Ta foil heat shield added
|
| Attachment 1: Ta#64_Target_Loading_Data.pdf
|
|
|
|
119
|
Friday, July 15, 2022, 10:47 |
Darwin Ortiz Rosales | UCx#38 | LP-SIS | | | 44508-3 | | Ready | UCx#38_Target_Description |
The bulk density was corrected. Use attachment number 2.
Darwin |
| Attachment 1: UCx#38.png
|
|
| Attachment 2: UCx#38.png
|
|
|
|
122
|
Thursday, September 22, 2022, 13:18 |
Darwin Ortiz Rosales | C#4 | LP-SIS | | | 44691-3 | | Ready | Target C#4 Description |
Thursday, September 22, 2022, 13:17 |
| Attachment 1: C#4_Target_Description.png
|
|
|
|
123
|
Tuesday, October 25, 2022, 13:10 |
Darwin Ortiz Rosales | UCx#40 | LP-SIS | | | 45550-2 | | Ready | UCx#40 Target Description |
Tuesday, October 25, 2022, 13:10
Target in Glovebox |
| Attachment 1: UCx#40_Description.png
|
|
|
|
124
|
Tuesday, November 15, 2022, 08:41 |
Darwin Ortiz Rosales | UCx#41 | LP-SIS | | | 45220-13 | | Ready | |
|
| Attachment 1: UCx#41_Description.png
|
|
|
|
127
|
Monday, March 06, 2023, 13:38 |
Aaron Schmidt | Ta#65 | LP-SIS | | | 45220-7 | | Ready | Ta#65 Target Description. |
Monday, March 06, 2023, 13:38:
Ta#65 LP-SIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.033mm (0.0013") avg Measured.
Target material batch: Ta 2023-1 Mt'l PO# TR-2022-03028
Target density = 18.2685 g/cm3
Target length = 3.40 cm
Total Mass = 62.113 g [Incl foils + Ta wire on 6 packs]
Total mass w/ Target oven= 460.8 g (w/ end caps)
Discs in target are arranged as follows: 1pack / 75 singles / 1pack / 100 singles / 2packs / 100 singles / 1pack / 75 singles / 1pack
Dimpling direction on foils/ Packs. --> Center <--
End caps installed (Not expanded). No Ta foil heat shield added
Tuesday, May 16, 2023, 10:44: End cap removed post conditioning to remove rhenium foil. End cap replaced, & weight updated. Length remains the same. |
|
|
133
|
Wednesday, July 26, 2023, 09:42 |
Darwin Ortiz Rosales | UCx#42 | LP-SIS | | | 45220-1 | | Ready | UCx#42_Description |
|
| Attachment 1: UCx#42_Description.png
|
|
|
|
134
|
Wednesday, July 26, 2023, 12:03 |
Darwin Ortiz Rosales | UCx#43 | LP-SIS | | | 45447-11 | | Ready | UCx#43_Description |
|
| Attachment 1: UCx#43_Description.png
|
|
|
|
136
|
Wednesday, September 20, 2023, 14:25 |
Aaron Schmidt | Ta#66 | LP-SIS | ITW | TM2 | 45220-5 | | In progress | Ta#66 Target description. |
Ta#66 LP-SIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.033mm (0.0013") avg Measured.
Target material batch: Ta 2023-1 Mt'l PO# TR-2022-03028
Target density = 12.446 g/cm3
Target length = 5.0 cm
Total Mass = 62.230 g [Incl foils + Ta wire on 6 packs]
Total mass w/ Target oven= g (w/ end caps)
Discs in target are arranged as follows: 1pack / 75 singles / 1pack / 100 singles / 2packs / 100 singles / 1pack / 75 singles / 1pack
Dimpling direction on foils/ Packs. --> Center <--
End caps installed (Not expanded). No Ta foil heat shield added |
| Attachment 1: Ta#66_Target_Loading_Data.pdf
|
|
|
|
137
|
Thursday, October 05, 2023, 12:48 |
Aaron Schmidt | | LP-SIS | | | 45220-3 | | | Ta#( ) Target description. (Spare) |
Ta# LP-SIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.033mm (0.0013") avg Measured.
Target material batch: Ta 2023-1 Mt'l PO# TR-2022-03028
Target density = 12.515 g/cm3
Target length = 4.97 cm
Total Mass = 62.202 g [Incl foils + Ta wire on 6 packs]
Total mass w/ Target oven = 461g (w/ end caps)
Discs in target are arranged as follows: 1pack / 75 singles / 1pack / 100 singles / 2packs / 100 singles / 1pack / 75 singles / 1pack
Dimpling direction on foils/ Packs. --> Center <--
End caps installed (Not expanded). No Ta foil heat shield added |
| Attachment 1: Ta#68_Target_Loading_Data.pdf
|
|
|
|
139
|
Tuesday, March 05, 2024, 10:15 |
Aaron Schmidt | Ta | LP-SIS | | | 45447-15 | | Ready | Ta# (March stock) Target Description. |
Tuesday, March 05, 2024, 10:12: Ta# (Stock - Loaded today) LP-SIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.033mm (0.0013") avg Measured.
Target material batch: Ta 2023-1 Mt'l PO# TR-2022-03028
Target density = 18.2 g/cm3
Target length = 3.4 cm
Total Mass = 61.9 g [Incl foils + Ta wire on 6 packs]
Total mass w/ Target oven = 459.6 g (w/ end caps)
Discs in target are arranged as follows: 1pack / 75 singles / 1pack / 100 singles / 2packs / 100 singles / 1pack / 75 singles / 1pack
Dimpling direction on foils/ Packs. --> Center <--
End caps installed (Not expanded). No Ta foil heat shield added. |
|
|
140
|
Wednesday, May 22, 2024, 22:32 |
Darwin Ortiz Rosales | UCx#45 | LP-SIS | | | 45220-9 | | Ready | UCx#45_Description |
|
| Attachment 1: UCx#45_Description.png
|
|
|
|
143
|
Tuesday, August 13, 2024, 10:08 |
Aaron Schmidt | Ta#67 Thin Foil Target | LP-SIS | ITE | TM2 | 45447-14 | 45235-10 | Ready | Ta#67 Thin Foil Target description & Notes |
Ta#67 Thin foil LP-SIS target description:
Total Ta foils = 470 loaded into 2 packs of 235 foils each.
Foil Thickness = 0.010mm (0.0004") avg Measured.
Target material batch: See attached*
Target density = 4.498 g/cm3
Target length = 3.7465 cm
Total Mass = 16.8509 g [Incl foils + Ta wire on 2 packs]
Total mass w/ Target oven = 415g (No end caps)
Discs in target are arranged as follows: 2packs
Dimpling direction on foils/ Packs. --> Center <--
No Ta foil heat shield added
The original HS 45253-23 Had to be replaced due to a leak being discovered during a leak check. Reassembled in 45235-10
However post-TS https://elog.triumf.ca/TIS/Test-Stand/1014 & https://elog.triumf.ca/TIS/Test-Stand/1015, it was discovered there was electrical shorts, components stuck together, including the retainer to the ovens tube. This had to be repaired & rebuilt.
Repairs included opening ITD0542 inner diameter to 11/16"
increasing the slot gap on the HS for the target leg to bottom insulator clearance
Source Cup inner ID opened 0.030" as the short was found to be the tube touching the Cu wall.
Top & bottom insulators were also replaced pre-TS. Checked post TS. They held 540 OL & 1049 OL respectively afterwards.
Run in TS: https://elog.triumf.ca/TIS/Test-Stand/1018
Link to Checklist & Docushare details below.
https://documents.triumf.ca/docushare/dsweb/View/Collection-39715 |
| Attachment 1: Certificate_of_Analysis_-_Ta_0.01mm.pdf
|
|
|
|
146
|
Friday, September 20, 2024, 14:26 |
Aaron Schmidt | Ta# | LP-SIS | ITE | TM2 | 45447-18 | 45235-13 | Ready | Ta# Target Description |
Spare for Ta#68 Ta# LP-SIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.0254mm (0.0010") avg Measured.
Target material batch: PO# TR-2023-06149
Target density = 14.17 g/cm3
Target length = 3.505 cm
Total Mass = 47.6553 g [Incl foils + Ta wire on 6 packs]
Total mass w/ Target oven = 454g (w/ end caps)
Discs in target are arranged as follows: 1pack / 75 singles / 1pack / 100 singles / 2packs / 100 singles / 1pack / 75 singles / 1pack
Dimpling direction on foils/ Packs. --> Center <--
End caps installed (Expanded). No Ta foil heat shield added |
|
|
149
|
Thursday, January 02, 2025, 12:54 |
Darwin Ortiz Rosales | UCx#47 | LP-SIS | | | 45447-12 | | Ready | UCx#47_Description |
|
| Attachment 1: UCx#47_Description.png
|
|
|
|
38
|
Wednesday, November 27, 2013, 17:56 |
John Wong | UCx#8 | LP-IG-LIS | ITE | TM4 | 39814-IV | | Spent | UCx#8 target description |
Wednesday, November 27, 2013, 17:49
UCx#8 target description - see attachment#1
|
| Attachment 1: UCx_8_specification.PNG
|
|
|
|
55
|
Friday, July 10, 2015, 11:23 |
John Wong | UCx#13 | LP-IG-LIS | ITE | TM4 | 40860-1 | | Ready | UCx#13 Target description |
Friday, July 10, 2015, 11:15
Attached please find the UCx#13 target description.
Note: Target container was coated/sintered with TaC twice. Would like to see if this will improve the life-span of the target.
|
| Attachment 1: UCx_13_target_description.PNG
|
|
|
|
63
|
Wednesday, June 08, 2016, 15:55 |
Laura Lambert | UCx#16 | LP-IG-LIS | | | 40860-2 | | Ready | UCx#16 Target Description |
Wednesday, June 08, 2016, 15:52
Attached please find the UCx#16 target description.
|
| Attachment 1: Target_Description.JPG
|
|
|
|
67
|
Friday, September 02, 2016, 14:45 |
John Wong | SiC#34 | LP-IG-LIS | | | 39814-V2-1 | | Ready | SiC#34 Target Description |
Friday, September 02, 2016, 14:43
See attachment for target description
|
| Attachment 1: SiC34_target_description.JPG
|
|
|
|
73
|
Tuesday, May 16, 2017, 13:18 |
Laura Lambert | UCx#20 | LP-IG-LIS | ITE | TM4 | 42218-1 | | Ready | UCx#20 Target Description |
Tuesday, May 16, 2017, 13:13
Attached please find the UCx#20 target description.
|
| Attachment 1: target_description.JPG
|
|
|
|
88
|
Thursday, November 29, 2018, 14:23 |
Marla Cervantes | UCx#26 | LP-IG-LIS | | | 42281-3 | | Ready | UCx#26 Target description |
Thursday, November 29, 2018, 14:20
Attached please find the UCx#26 target description.
|
| Attachment 1: UCx_26-description.JPG
|
|
|
|
112
|
Wednesday, September 29, 2021, 10:37 |
Darwin Ortiz Rosales | UCx#35 | LP-IG-LIS | | | 42218-5 | | Ready | UCx#35-Target_description |
| Target ID |
UCx#35 |
| General |
Total No. Discs |
179 |
|
| Disc area |
0.95 |
cm2 |
| Ave graphite foil thickness/disc |
0.013 |
cm |
| Ave. graphite foil mass/disc |
0.015 |
g |
| |
Total mass of discs |
14.97 |
g |
| Green Target |
Total Green mass of discs |
13.89 |
g |
| Ave. mass/disc |
0.084 |
g |
| Ave. mass/disc (no C-foil & org) |
0.078 |
g |
| Ave. thickness/disc (no C-foil) |
0.037 |
cm |
| Theoretical length (with C-foil) |
9.0 |
cm |
| Total packed length (with C-foil) |
10.0 |
cm |
| Final Target |
UC2 in Target |
11.05 |
g |
| Free C in Target |
0.83 |
g |
| Total massUC2+free C |
11.88 |
g |
| U mass |
10.04 |
g |
| U thickness |
10.56 |
g/cm2 |
| UC2 bulk density (measured) |
2.88 |
g/cm3 |
| Theoretical Density |
8.24 |
g/cm3 |
| % Yield Density |
34.91 |
% |
| Theoretical Porosity |
0.651 |
|
|
| Attachment 1: UCx#35_Target_Description_.png
|
|
|
|
120
|
Tuesday, August 09, 2022, 11:02 |
Darwin Ortiz Rosales | UCx#39 | LP-IG-LIS | | | 42218-4 | | Ready | UCx#39_Target_Description |
|
| Attachment 1: UCx#39_Description.png
|
|
|
|
132
|
Friday, June 23, 2023, 09:02 |
Aaron Schmidt | Nb#10 | LP-IG-LIS | ITW | TM2 | 45447-7 | | | Nb#10 target description. |
Nb#10 LP-IG-LIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.025mm (0.001")
Target density = 7.36 g/cm3
Target length = 3.5 cm
Total Mass = 25.7576 g [Incl foils + Ta wire on 6 packs]
Total mass w/ Target oven= 438 g (w/ end caps)
Discs in target are arranged as follows: 1pack / 75 singles / 1pack / 100 singles / 2packs / 100 singles / 1pack / 75 singles / 1pack
Dimpling direction on foils/ Packs. --> Center <--
End caps installed (Not expanded). No Ta foil heat shield added |
|
|
135
|
Thursday, August 24, 2023, 14:16 |
Aaron Schmidt | Nb#11 | LP-IG-LIS | ITW | TM2 | 45447-9 | | In progress | Nb#11 Target description |
Nb#11 LP-IG-LIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.025mm (0.001")
Target density = 7.13 g/cm3
Target length = 3.53 cm
Total Mass = 25.165 g [Incl foils + Ta wire on 6 packs]
Total mass w/ Target oven= 434 g (w/ end caps)
Discs in target are arranged as follows: 1pack / 75 singles / 1pack / 100 singles / 2packs / 100 singles / 1pack / 75 singles / 1pack
Dimpling direction on foils/ Packs. --> Center <--
End caps installed (Not expanded). No Ta foil heat shield added
Replacement for Nb#10 |
| Attachment 1: Nb#11_Target_Loading_Data.pdf
|
|
|
|
148
|
Tuesday, November 12, 2024, 12:49 |
Darwin Ortiz Rosales | UCx#46 | LP-IG-LIS | | | 42218-2 | | Ready | UCx#46_Description |
|
| Attachment 1: UCx#46_Description.png
|
|
|
|
83
|
Friday, July 13, 2018, 14:41 |
John Wong | UCx#23 | LP-FEBIAD-CTL | | | | | Ready | UCx#23 target description |
Friday, July 13, 2018, 14:40
Target is ready for installation.
See attachment for description
|
| Attachment 1: UCx_23-target_description.JPG
|
|
|
|
20
|
Monday, February 20, 2012, 16:39 |
John Wong | UO2/Nb #1 | LP-FEBIAD | ITE | TM4 | 38481-9 | | Spent | target ready for assembly |
Monday, February 20, 2012, 16:25
Mass of empty target oven used = 461.55g
Target oven filled with 402 discs of UO2/Nb, 5.0cm in length, and tot mass (before sintered) was 61.49g (UO2+Nb+org).
Target finished the sintering process on Feb 20, 2011.
U(402 foils) mass = 35.689g
U(402 foils) thickness = 16.834 g/cm2
Target is stored in the Hotlab and ready for assembly.
|
|
|
24
|
Wednesday, July 04, 2012, 11:32 |
Anders Mjos | UO2/Nb #1 | LP-FEBIAD | ITE | TM4 | 38481-9 | 39069-3 | Spent | target assembled |
| John Wong wrote: |
|
Monday, February 20, 2012, 16:25
Mass of empty target oven used = 461.55g
Target oven filled with 402 discs of UO2/Nb, 5.0cm in length, and tot mass (before sintered) was 61.49g (UO2+Nb+org).
Target finished the sintering process on Feb 20, 2011.
U(402 foils) mass = 35.689g
U(402 foils) thickness = 16.834 g/cm2
Target is stored in the Hotlab and ready for assembly.
|
Target assembled with new anode end cap.
See attachment for gap size and DocuShare for further information. |
| Attachment 1: UO2#3_Anode_End_Cap.xlsx
|
|
|
26
|
Wednesday, August 01, 2012, 09:37 |
Pierre Bricault | ITE-TM4-UO#3 | LP-FEBIAD | ITE | TM4 | | | Problems/Solutions | Short has developed while lowering the cathode heater |
On tuesday July we lower the cathode heater to swap the anode-cathode bias. While lowering the cathode heater a short on the anode developed.
The polarity swap was not possible because the target/tube assembly has also a short to common.
We return the configuration has it was and we added two 100 Ohms: 5 W resistor between the common and the heaters to prevent current to flow back to the common.
The anode short disappear during the cathode and target heating. |
|
|
129
|
Monday, May 01, 2023, 14:59 |
Darwin Ortiz Rosales | TiC #5 | LP-FEBIAD | | | 44692-5 | | Ready | Target TiC #5 Description |
|
| Attachment 1: TiC#5.png
|
|
|
|
138
|
Tuesday, October 24, 2023, 11:30 |
Darwin Ortiz Rosales | UCx#44 | LP-FEBIAD | | | 41790-7 | | Ready | UCx#44_Description |
Three Ta heatshields left installed on container. |
| Attachment 1: UCx#44_Description.png
|
|
|
|
3
|
Tuesday, March 29, 2011, 14:14 |
John Wong | Ta#35 | HP-SIS | ITE | TM4 | 38481-3 | 38303-4 | Spent | ITE-TM4-Ta#35-Hp-SIS |
ITE-TM4-Ta#35-Hp-SIS
Thu Apr 7 15:32:32 2011:
Target oven - w.o#38481-3.
Packs of Ta foils were previously prepared by Vicky H.
Marik loaded the target: 400 of 0.025mm foils (25 foils/pk) in 3.5cm length. (Recommended length 4.0-4.5cm; If too closely packed, wires get squeezed and snapped)
Average mass per discs = 0.105g
Total mass (Ta+wire) = 45.06g
Disc area = 2.12cm2
Ta thickness = 21.25g/cm2
Thu Apr 28 :
Target heat Shield (w.o 38303-4) cleaned
Target is now assembled by John and Rick
Megger Test Performed:
TA-->HS = 540V, OL
TA-->EE = 540V, OL
HS--> EE = 1049V, OL
Leak Check OK
*SIS restraint used in this target ion source
Mon May 9 10:32:40 2011: Standard salts added: Li, Na, Rb @ 10uL, K @ 5uL (but added 10uL), Cs @ 15uL. Target will be going to the test stand.
Fri May 20 16:57:22 2011:
Target was tested on the Test Stand but problems with the software (see Test stand elog).
Standard salts added: Li, Na, Rb @ 10uL, K @ 5uL (but added 10uL), Cs @ 15uL, and Be @ 10uL.
Monday, July 18, 2011, 11:15: Target ended on July 16. The target was used online for an extra 2 weeks and performed very well.
|
| Attachment 1: Ta-HPSIS.jpg
|
|
|
|
4
|
Thursday, March 31, 2011, 15:38 |
John Wong | SiC#25 | HP-SIS | ITE | TM4 | 38481-1 | 38307-? | Spent | ITE-TM4-SiC#25-Hp-SIS |
Thu Mar 31 15:19:51 2011: SiC#25 was made sometime in December of 2010. It is now in the target module and ready to be conditioned.
Mon Apr 18 18:17:05 2011: It was found later that no salt was added to this target after it came out from the test stand. However, there were enough 40Ca and 39K for tuning (See attachment#1 for the big mass scan). Once the P+ is back, the yields will be measured.
Fri Apr 29 15:30:26 2011: Low 27Al was ionized from the surface for some reason. However, after the green laser was shone into the extraction tube, more 27Al was produced. Then, the laser was turned off, the target continued to surface ionizing 27Al. There could be a blockage from the rhenium (Re) ionizer foil. Jens L. will investigate this further and do a test with the lasers and the rhenium foil.
|
| Attachment 1: big_mass_scan.jpg
|
|
|
|
8
|
Thursday, June 16, 2011, 17:26 |
John Wong | Nb | HP-SIS | | | 38817-1 | | Spent | Target is ready and stored in cabinet |
Thu Jun 16 17:21:10 2011
Two targets of Nb-HP-SIS are complete and ready to be installed in the heat shields:
-----------------------------------------------------------------------------------
Target oven w.o# 38817-1:
inner diameter: left = 18.27mm, right = 18.25mm.
Filled with 400 foils Nb (16pk, 5 foils/pk).
Discs spec: 18.65mm/14.65mm, thickness = 0.022mm
Total mass + Ta-wire = 22.74g
Total length = 4.5cm
Rn foil inserted for ionization. (0.1mm, 0.004", 1cm x 1cm)
------------------------------------------------------------------------------------
Wednesday, July 06, 2011, 14:35: Salts were added and tested in test-stand last 2 weeks.
|
|
|
10
|
Wednesday, July 06, 2011, 14:13 |
John Wong | Ta#40 | HP-SIS | | | 38295-4 | | Spent | Target description |
Details about Ta Hp surface, w.o#38295-4 (spare):
This target was built as a spare.
Note: Left side target arm replaced, Nov 18, 2010. Weld prep on centre block misaligned. (Marik has more details about this).
Packs of Ta foils were prepared by JW.
Target was filled with 400 of 0.025mm foils (25 foils/pk) in 4.0cm length.
Total Mass of 16 packs of Ta foils + Ta wires = 42.70g.
See attachment#1 for the measurement.
Friday, April 19, 2013, 09:44
Target was tested at the Teststand. Result Good.
Ready for use.
|
|
|
11
|
Wednesday, July 06, 2011, 14:29 |
John Wong | Nb/Spare | HP-SIS | | | 38817-2 | | In progress | Target ready for Assembly |
Target oven w.o# 38817-2:
inner diameter: left = 18.29mm, right = 18.16mm.
Filled with 400 foils Nb (16pk, 5 foils/pk).
Discs spec: 18.65mm/14.65mm, thickness = 0.022mm
Total mass + Ta-wire = 22.66g
total length = 4.5cm
Rn foil inserted for ionization. (0.1mm, 0.004", 1cm x 1cm)
|
|
|
21
|
Thursday, May 24, 2012, 11:04 |
John Wong | SiC#27 | HP-SIS | ITE | TM4 | 38817-3 | 39069-2 | Spent | HP-SIS SiC27 target description |
Thursday, May 24, 2012, 10:34
SiC#27- HPSIS target description:
Total SiC foils = 240 discs
Total SiC+ C-grv = 27.79g
Total length = 8.3cm
Average mass of SiC/disc (without C-grv) = 0.085g
Average thickness of SiC (without C-grv) = 0.24mm
No Rh foil added
Salt added = 10uL Li, 10uL Na
see attachment#1: SiC#27_density measurements
see link for more details: http://documents.triumf.ca/docushare/dsweb/View/Collection-8530
|
| Attachment 1: SiC#27_specification.png
|
|
|
|
37
|
Friday, October 25, 2013, 17:35 |
John Wong | Ta#41 | HP-SIS | ITW | TM4 | 38817-10 | | Spent | Ta#41 target description |
Friday, October 25, 2013, 17:35
Ta#41 HP-SIS target description:
Total Ta foils = 400
Foil Thickness = 0.025mm
Target density = 16.69g/cm3
Target length = 4.0cm
Total Mass (400 foils + Ta wire) = 42.19g
|
|
|
40
|
Monday, March 31, 2014, 15:02 |
John Wong | TiC#4 | HP-SIS | | | 38817-8 | 39956-10 | Spent | Target Description |
Monday, March 31, 2014, 15:00
Target consists of 360 discs of TiC + graphite foils.
Total length = 11.7cm
Total green mass = 40.945g
(see attachment for more details)
|
| Attachment 1: TiC#4_description.JPG
|
|
|
|
47
|
Thursday, September 25, 2014, 16:01 |
Laura Lambert | Ta#44 | HP-SIS | ITE | TM4 | 38817-9 | 40316-11 | Ready | Ta#44 target description |
Thursday, September 25, 2014, 15:59
Ta#44 HP-SIS target description:
Total Ta foils = 400
Foil Thickness = 0.025mm
Target density = 16.69 g/cm3
Target length = 4.5cm
Total Mass (400 foils + Ta wire) = 47.49g
|
|
|
49
|
Wednesday, April 01, 2015, 11:27 |
Laura Lambert | Ta # 45 | HP-SIS | | | 38817-5 | | In Use | Ta#45 target description |
Wednesday, April 01, 2015, 11:25
Ta#45 HP-SIS target description:
Total Ta foils = 400
Foil Thickness = 0.025mm
Target density = 13.48 g/cm3
Target length = 3.4cm
Total Mass (400 foils + Ta wire) = 45.8181g
|
|
|
51
|
Wednesday, April 29, 2015, 15:39 |
Laura Lambert | SiC#31 | HP-SIS | | | 38817-7 | | Ready | SiC#31 Target description |
Wednesday, April 29, 2015, 15:30
SiC#31 HP-SIS target description:
Total SiC foils = 520 discs
Total mass SiC + C_grv foils = 60.2441 g (before sintering, expecting ~13% loss of organic mass after burnt off)
Average mass SiC/disc (without C_grv) = 0.0853g
Average thickness SiC (without C_grv) = 0.2093mm
Total packed length = 17cm
See attachment #1 for the density measurement.
|
| Attachment 1: final_density_measurements.JPG
|
|
| Attachment 2: density_measurements.xlsx
|
| Attachment 3: SiC_density_Jan_10_'14_cast_-_Copy.xlsx
|
| Attachment 4: SiC_density_Oct_31_'14_cast.xlsx
|
|
|
56
|
Thursday, September 10, 2015, 13:33 |
Laura Lambert | Ta # 46 | HP-SIS | | | 41369-3 | | Ready | Ta#46 target description |
Thursday, September 10, 2015, 13:31
Ta#46 HP-SIS target description:
Total Ta foils = 505
Foil Thickness = 0.025mm
Target density = 15.85 g/cm3
Target length = 3.4cm
Total Mass = 75.2772g
|
|
|
58
|
Wednesday, September 30, 2015, 17:08 |
John Wong | Ta # 46 | HP-SIS | | | 41369-3 | | Ready | Ta#46 target description |
| Laura Lambert wrote: |
|
Thursday, September 10, 2015, 13:31
Ta#46 HP-SIS target description:
Total Ta foils = 505
Foil Thickness = 0.025mm
Target density = 16.69 g/cm3
Target length = 3.4cm
Total Mass = 75.2772g
|
Wednesday, September 30, 2015, 17:01
The average mass per disc = 0.105g
Total mass (505 discs + some Ta wire for packing) = 53.876g ( Not 75.277g as mentioned above. See Target Logbook 2015 Dropbox for more details)
|
|
|
62
|
Tuesday, April 19, 2016, 11:33 |
Laura Lambert | Ta # 48 | HP-SIS | | | 41369-5 | | Ready | Ta # 48 target description |
Tuesday, April 19, 2016, 11:24
Ta#48 HP-SIS target description:
Total Ta foils = 505
Foil Thickness = 0.025mm
Target density = 15.86 g/cm3
Target length = 3.4cm
Total Mass = 53.9381g [Incl foils + Ta wire on 6 packs]
|
|
|
64
|
Wednesday, June 29, 2016, 11:49 |
Laura Lambert | SiC # 33 | HP-SIS | | | 41369-4 | | Ready | SiC#33 target description |
Wednesday, June 29, 2016, 11:47
See attachment for target description.
|
| Attachment 1: elog_target_description.JPG
|
|
|
|
66
|
Tuesday, August 02, 2016, 15:42 |
Laura Lambert | Ta # 49 | HP-SIS | | | 41369-6 | | Ready | Ta#49 target description |
Tuesday, August 02, 2016, 15:30
Ta#49 HP-SIS target description:
Total Ta foils = 500 [6x20 packs + 380 single discs]
Foil Thickness = 0.025mm
Target density = 14.87 g/cm3
Target length = 3.4cm
Total Mass = 50.6142g [Incl foils + Ta wire on 6 packs]
|
|
|
76
|
Monday, June 26, 2017, 13:36 |
Laura Lambert | Ta #53 | HP-SIS | | TM2 | 42218-6 | | Ready | Ta#53 target description |
Monday, June 26, 2017, 13:32
Ta#53 HP-SIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.025mm
Target density = 14.80 g/cm3
Target length = 3.4cm
Total Mass = 50.3105g [Incl foils + Ta wire on 6 packs]
|
|
|
79
|
Tuesday, September 26, 2017, 12:07 |
Laura Lambert | Ta#54 | HP-SIS | ITW | TM2 | 42218-10 | | Ready | Ta#54 target description |
Tuesday, September 26, 2017, 09:31
Ta#54 HP-SIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.025mm
Target density = 14.72 g/cm3
Target length = 3.4cm
Total Mass = 50.0372g [Incl foils + Ta wire on 6 packs]
|
|
|
82
|
Thursday, June 21, 2018, 11:34 |
Aaron Schmidt | Ta#56 | HP-SIS | | | 42218-9 | | Ready | Ta#56 target description |
Thursday, June 21, 2018, 11:33:
Ta#56 HP-SIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.025mm
Target density = 14.01 g/cm3
Target length = 3.4 cm
Total Mass = 47.374 g [Incl foils + Ta wire on 6 packs]
Total mass w/ Target oven= 1469 g
No endcaps inserted, no Rh foil inserted.
Tuesday, July 03, 2018, 08:30: Endcaps inserted & expanded. Rh foil inserted. |
| Attachment 1: Ta#56_Loading_Data.pdf
|
|
|
|
99
|
Wednesday, April 15, 2020, 08:10 |
Darwin Ortiz Rosales | SiC#40 | HP-SIS | | | 42218-8 | | Ready | Target SiC#40 Description |
Wednesday, April 15, 2020, 07:51
See attached picture for description |
| Attachment 1: Annotation_2020-04-15_080836.png
|
|
|
|
104
|
Thursday, November 12, 2020, 11:32 |
Darwin Ortiz Rosales | UCx#31 | HP-SIS | ITE | TM4 | 44160 | 43822 | Ready | UCx#31-Target_description |
Target full name ITE-TM4-UC#31-P2N-SIS
|
| Attachment 1: UCx31-target_description.png
|
|
|
|
105
|
Tuesday, March 16, 2021, 17:05 |
Luca Egoriti | ITE-TM4-UC#32-P2N-SIS | HP-SIS | ITE | TM4 | - | - | In progress | UO2 discs cutting |
This afternoon, Darwin prepared in the hot lab fume hood the two UO2 slurries to be cut into P2N target discs. Later, I took over cutting both slurries. A total of 49 annular discs were cut and loaded into the P2N graphite container.
The discs thickness was measured by stacking 5 discs on each other, and measuring their thickness in two points.
#discs = 49
Average disc thickness = 0.453mm
Empty cartridge weight = 9.42 g
Full cartridge weight = 39.86 g
UO2+C weight = 30.44 g
The unused material plus the cutting scrap were left in a zip lock bag on a shelf in the right hand side of the fume hood. The center scraps and the loaded target were placed in a plastic tray on the top shelf. The used tools and scales were left on the right of the working area, the napkins on the bottom were put into the garbage bag (inside the fume hood) and replaced, while the only napkin left is the one with the target information (recorded in attached picture). |
| Attachment 1: UC32-P2N_material_info.jpg
|
|
| Attachment 2: Fume_hood.jpg
|
|
|
|
110
|
Monday, September 13, 2021, 14:53 |
Darwin Ortiz Rosales | SiC#41 | HP-SIS | | | 42218-7 | | Ready | Target SiC#41 Description |
Monday, September 13, 2021, 14:52
|
| Attachment 1: Screenshot_2021-09-13_144830.png
|
|
|
|
130
|
Friday, May 26, 2023, 11:35 |
Darwin Ortiz Rosales | TiC#6 | HP-SIS | | | 44692-10 | | Ready | Target TiC #6 Description |
|
| Attachment 1: TiC_#6.png
|
|
|
|
131
|
Friday, May 26, 2023, 11:53 |
Darwin Ortiz Rosales | SiC#45 | HP-SIS | | | 44692-3 | | Ready | |
|
| Attachment 1: SiC#45.png
|
|
|
|
141
|
Friday, June 14, 2024, 14:12 |
Darwin Ortiz Rosales | SiC#46 | HP-SIS | | | 44692-2 | 45235-6 | Ready | SiC#46_description |
|
| Attachment 1: SiC#46.png
|
|
|
|
145
|
Tuesday, September 10, 2024, 09:53 |
Darwin Ortiz Rosales | TiC#9 | HP-SIS | | | 45447-29 | 45235-19 | Ready | TiC#9_Description |
|
| Attachment 1: TiC#9.png
|
|
|
|
147
|
Monday, October 07, 2024, 13:16 |
Aaron Schmidt | Ta#68 | HP-SIS | ITE | TM2 | 45447-26 | 45235-16 | Ready | Ta#68 Target Description |
Ta#68 HP-SIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.0254mm (0.0010") avg Measured.
Target material batch: PO# TR-2023-06149
Target density = 14.204 g/cm3
Target length = 3.50 cm
Total Mass = 49.7146 g [Incl foils + Ta wire on 6 packs]
Total mass w/ Target oven = 1483g (w/ end caps)
Discs in target are arranged as follows: 1pack / 75 singles / 1pack / 100 singles / 2packs / 100 singles / 1pack / 75 singles / 1pack
Dimpling direction on foils/ Packs. --> Center <--
End caps installed (Expanded). No Ta foil heat shield added |
| Attachment 1: ITE-TM2-Ta#68-HP-SIS_Target_Loading_Data.pdf
|
|
|
|
34
|
Wednesday, July 10, 2013, 18:41 |
John Wong | SiC#29 | HP-FEBIAD-CTL | ITE | TM4 | 38481-6 | 39956-4 | Spent | SiC#29 - Target description |
Wednesday, July 10, 2013, 18:32
SiC#29 HP-FEBIAD-CTL target description:
Total SiC foils = 510 discs
Total mass SiC + C_grv foils = 62 g (before sintering, expecting ~13% loss of organic mass after burnt off)
Average mass SiC/disc (without C_grv) = 0.0892 g
Average thickness SiC (without C_grv) = 0.21mm
No Rh foil and salt added for this run.
See attachment #1 for the density measurement.
Wednesday, July 10, 2013, 18:40
Target is currently in the Test-Stand. Once it's tested; it is ready to go online.
Happy Beaming! 
|
| Attachment 1: SiC#29_density_measurements_final.xlsx
|
|
|
74
|
Tuesday, May 30, 2017, 15:15 |
Laura Lambert | SiC#36 | HP-FEBIAD-CTL | | TM2 | 41369-10 | | Ready | SiC#36 target description |
Tuesday, May 30, 2017, 15:12
See attachment for target description.
|
| Attachment 1: SiC#36_Target_Description.JPG
|
|
|
|
15
|
Friday, September 23, 2011, 17:03 |
Anders Mjos | SiC#26 | HP-FEBIAD | ITE | TM4 | 38295-9 | 38307-8 | Spent | Run finished |
Friday, September 23, 2011, 16:54:
- Cu-gaskets used for leak checking target had a leak rate of about 10-8 10-9 atm cc/sec. Replaced with silver plated SS gaskets and no leak detected above 10-11 atm cc/sec.
- The target can not hold high voltage when it is sitting on the jig. The insulator on the jig have reduced resistance over time (less than 1 G Ohm). All high voltage tests passed when target is tested not sitting on the jig.
- Target is now in the test stand and pumping down.
|
|
|
17
|
Monday, October 17, 2011, 14:45 |
John Wong | SiC#26 | HP-FEBIAD | ITE | TM4 | 38295-9 | 38307-8 | Spent | Run finished |
| Anders Mjos wrote: |
|
Friday, September 23, 2011, 16:54:
- Cu-gaskets used for leak checking target had a leak rate of about 10-8 10-9 atm cc/sec. Replaced with silver plated SS gaskets and no leak detected above 10-11 atm cc/sec.
- The target can not hold high voltage when it is sitting on the jig. The insulator on the jig have reduced resistance over time (less than 1 G Ohm). All high voltage tests passed when target is tested not sitting on the jig.
- Target is now in the test stand and pumping down.
|
Monday, October 17, 2011, 14:41
After the test-stand, the extraction electrode showed some electric arcing mark, but no solid deposits were found. (see attachment#1: EE_after_teststand.jpg)
See attachment for the target specification. |
| Attachment 1: EE_after_teststand.jpg
|
|
| Attachment 2: SiC#26_specification.png
|
|
|
|
29
|
Thursday, October 11, 2012, 11:41 |
John Wong | NiO#1 | HP-FEBIAD | ITE | TM4 | 38481-7 | 39069-1/10(lid) | Spent | NiO target description |
(Should have posted this before my long vacation... Anyway, it's for documentation)
Thursday, October 11, 2012, 11:38
| NiO/Ni #1 |
Average |
| NiO + Ni (g) |
0.109 |
| NiO - Ni foil (g) |
0.06 |
| NiO + Ni thickness (mm) |
0.116 |
| NiO - Ni Thickness (mm) |
0.091 |
| Area (cm2) |
2.212 |
| NiO + Ni - organics 8.95% (g) |
0.099 |
| NiO - Ni - Organics (g) |
0.055 |
| NiO Density (g/cm3) |
2.145 (32%) |
Target contains 500 NiO/Ni discs and is measured at 9.0 in length. |
|
|
30
|
Tuesday, December 11, 2012, 15:44 |
Anders Mjos | SiC | HP-FEBIAD | ITW | TM4 | na | na (old style fittings) | Ready | Test target for the Conditioning Station |
The target has been used for operator training previously at the ISAC Test Stand.
- 9-pin connector was completed and grounded
- RH gripper arms added to the heat shield
Further documentation on DocuShare |
|
|
36
|
Friday, August 30, 2013, 14:45 |
John Wong | NiO#2 | HP-FEBIAD | | | 39530-6 | 39069-4 | Spent | NiO target description |
Friday, August 30, 2013, 14:38
NiO/Ni#2 Average
NiO+ Ni (g) 0.114
NiO - Ni foil (g) 0.066
NiO + Ni thickness (mm) 0.116
NiO - Ni thickness (mm) 0.104
Area (cm2) 2.212
NiO + Ni - organics (8.95%) (g) 0.104
NiO - Ni - organics (8.95%) (g) 0.060
NiO Density (g/cm3) 2.110
% Yield density 32%
# discs in target 530
Total target length (cm) 9.0
|
|
|
41
|
Wednesday, April 30, 2014, 16:36 |
John Wong | SiC#30 | HP-FEBIAD | ITE | TM3 | 38481-8 | | Spent | SiC#30 Target description |
Wednesday, April 30, 2014, 15:16
Note:
This target was built in 2011. The endcaps were replaced after they got vaporized in Evap#1 during the sintering process, and the target was re-conditioned.
See elogs for more details:
https://elog.triumf.ca/TIS/Evaporator_1/20
The target was inspected and was good for online use.
Total SiC foils = 555 discs
Total length (packed) = 17.5cm
Total SiC mass (plus graphite foils) = 52.902g
See attachment for density measurements
|
| Attachment 1: SiC#30_density_measurements.xlsx
|
|
|
57
|
Thursday, September 24, 2015, 13:42 |
Laura Lambert | SiC#32 | HP-FEBIAD | | | 39530-5 | | Ready | SiC#32 target description |
Thursday, September 24, 2015, 11:46
See attachment for target description.
|
| Attachment 1: elog_snapshot.JPG
|
|
|
|
68
|
Friday, October 07, 2016, 16:27 |
John Wong | SiC#35 | HP-FEBIAD | | | 39530-9 | | Ready | SiC35 Target description |
Friday, October 07, 2016, 16:28
See attachment for the target description
|
| Attachment 1: SiC35_target_description.JPG
|
|
|
|
80
|
Wednesday, September 27, 2017, 09:14 |
Laura Lambert | SiC#37 | HP-FEBIAD | ITE | TM4 | 39530-10 | | Ready | SiC#37 target description |
Wednesday, September 27, 2017, 09:13
See attachment for target description.
|
| Attachment 1: Target_Description.JPG
|
|
|
|
94
|
Friday, October 11, 2019, 09:26 |
Darwin Ortiz Rosales | SiC#38 | HP-FEBIAD | | TM2 | 42464-4 | | Ready | Target SiC#38 Description |
Friday, October 11, 2019, 09:25
See attached picture for description.
|
| Attachment 1: SiC#38.PNG
|
|
|
|
97
|
Friday, November 29, 2019, 10:53 |
Darwin Ortiz Rosales | SiC#39 | HP-FEBIAD | | TM2 | 42464-3 | | Ready | Target SiC#39 Description |
Friday, December 06, 2019, 15:34
Added SEM images (see attachment#2) - JW
|
| Attachment 1: SiC#39_description.PNG
|
|
| Attachment 2: SiC39_SEM.pdf
|
|
|
|
115
|
Wednesday, May 25, 2022, 10:15 |
Darwin Ortiz Rosales | SiC#42 | HP-FEBIAD | | | 44692-9 | | Ready | Target SiC#42 Description |
Wednesday, May 25, 2022, 10:15
|
| Attachment 1: Description-SiC#42.png
|
|
|
|
117
|
Monday, June 20, 2022, 10:35 |
Darwin Ortiz Rosales | SiC#43 | HP-FEBIAD | | | 42464-1 | | Ready | Target SiC#43 Description |
Monday, June 20, 2022, 10:33
|
|
|
121
|
Tuesday, August 16, 2022, 09:48 |
Darwin Ortiz Rosales | SiC#44 | HP-FEBIAD | | | 37978-1 | | Ready | Target SiC#44 Description |
Tuesday, August 16, 2022, 09:47
|
|
|
142
|
Friday, June 14, 2024, 14:16 |
Darwin Ortiz Rosales | TiC#7 | HP-FEBIAD | | | 45447-5 | 45235-15 | Ready | TiC#7_Description |
Please note that this target comes in a Graphite cartridge. |
| Attachment 1: TiC#7.png
|
|
|
|
144
|
Tuesday, September 03, 2024, 16:11 |
Darwin Ortiz Rosales | TiC#8 | HP-FEBIAD | | | 45447-2 | | Ready | TiC#8_Description |
This was back-up target |
| Attachment 1: TiC#8_(2).png
|
.png.png "TiC#8_(2).png")
|
|
|
61
|
Friday, March 11, 2016, 10:18 |
Laura Lambert | Ta # 47 | | ITE | TM4 | | | Spent | Ta # 47 target desscription |
Friday, March 11, 2016, 10:13
Ta#47 LP-SIS [new small center block] target description:
Total Ta foils = 470
Foil Thickness = 0.025mm
Target density = 15.05 g/cm3
Target length = 3.4cm [exactly 7.8cm space on both sides]
Total Mass = 51.1533g [Incl foils + Ta wire on 6 packs]
Note: Target consists of 350 single discs and 6x20 packs of Ta discs
|
|
|
87
|
Monday, October 15, 2018, 07:36 |
Aaron Schmidt | Ta#57 | | ITE | TM4 | 41177-3 | | | Ta#57 Target Description. |
(Laura Lambert: Evap 2 Elog ID: 404) Tuesday, April 17, 2018, 10:20
Target consists of 470 discs.
Total packed length 3.4cm [exactly 7.8cm space on both sides]
Total mass g [Incl foils + Ta wire on 6 packs]
Target consists of 350 single discs and 6x20 packs of Ta discs
Discs in target are arranged as follows: 1pack / 75singles / 1pack / 100singles / 2packs / 100singles / 1pack / 75singles / 1pack
Weight not included. Should be identical to Ta#54 (Below)
Comparable as the foils are all 0.001" & the quantities are the same.
(Laura Lambert: Target Production Elog ID: 79)
Ta#54 HP-SIS target description:
Total Ta foils = 470 [6x20 packs + 350 single discs]
Foil Thickness = 0.025mm
Target density = 14.72 g/cm3
Target length = 3.4cm
Total Mass = 50.0372g [Incl foils + Ta wire on 6 packs] |
|
|
118
|
Tuesday, June 21, 2022, 15:34 |
Matthew Gareau | SiC#42, SiC#43 | | | TM2 | | | Problems/Solutions | Multipin guide pin issues |
While removing the SiC#42 it became apparent that the multipin guide pin had become loose again and was not allowing the target to dismount from the module.
The multipin shoulder bolts were removed and then the multipin was able to be pried off.
However the NHC manipulator were not able to reach the guide pin to remove it, which would be required before the SiC#43 could be installed.
The target module was then moved to the SHC where the guide pin could be removed and the installation of SiC#43 took place, along with the transfer of the parasitic attachment onto the SiC#43.
This problem seems to suggest that the multipin could use some redesign to ensure smoother target exchanges. |
|
|
125
|
Wednesday, December 14, 2022, 10:28 |
Darwin Ortiz Rosales | C#5 | | | | 44691-13 | | Ready | Target C#5 Description |
Graphite target |
| Attachment 1: C#5_Description.png
|
|
|
|
126
|
Monday, February 06, 2023, 10:02 |
Darwin Ortiz Rosales | C#6 | | | | 45220-6 | | Ready | Target C#6 Description |
|
| Attachment 1: C#6_Description.png
|
|
|
|
128
|
Friday, March 10, 2023, 07:21 |
Aaron Schmidt | | | | | | | Ready | Target Material Batch - Ta |
Tantalum - Standard foils.
MTR PO: TR-2022-03028
Average foil thickness: 0.0013" |
| Attachment 1: Ta_2023_-_01.pdf
|
|