Marla Cervantes wrote:

Tuesday, February 13, 2018, 11:39 35 circles of 14 mm diameter were packed into a graphite sample container. 35 x UO2/C circles = 5.74 g Graphite container = 5.20 g Graphite tube is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3 used Ta foils for heat shielding and the boat was installed in Evap1. Chamber currently pumping down.  Tuesday, February 13, 2018, 15:30 Initial IGP1 = 2.73x10e-6 Torr Tapped up entire process manually to 520 A in 30 min TGHT = 520 A, 5.41 V Vacuum coming down nicely indicating carbonization process complete. Current trip off after 5 min of being at 520 A.  Wednesday, February 14, 2018, 15:32 EVAP1 vented with Argon and the target was removed. Target was transferred to glove box. Ta boat and graphite container look unbroken.

 Friday, March 02, 2018, 16:31

A test was performed in EVAP1 (see log ID 194):

- A Ta boat without Ta shielding was submitted to 520 A and it remained at that current point overnight.

-No trip off

 Wednesday, February 28, 2018, 15:19

Last two rounds of materials in evap1 have tripped off the TGHT in epics within minutes of the target reaching 520A.

Loaded an empty target boat, no heat shields.

Will ramp up with same speed as last two samples to see how TGHT reacts and whether a trip is induced or not.

Currently pumping down now.

 Thursday, March 01, 2018, 13:53

IGP1 = 9.6e-7 Torr

Tapped up to 100A @ 1.0A/s, waited ~6min

IGP1 = 1.77e-6 Torr

Tapped up 40A/min to 140A, waited ~2min

Tapped up 40A/min to 180A, waited ~2min

Tapped up @ a rate of 1.0A/s for 40sec, then wait 20sec. Used this rate consistently up to 520A.

TGHT = 520A, 5.75V

Friday, March 02, 2018, 10:09 

TGHT = 520A, 5.81V this morning.

TGHT still on! 

No trip induced.

IGP1 = 1.7e-6 Torr.

Initiating auto-cool at 2.0A/min

 Thursday, March 05, 2018, 14:07

Container removed, test complete.

 Tuesday, February 13, 2018, 11:39

35 circles of 14 mm diameter were packed into a graphite sample container.

35 x UO2/C circles = 5.74 g

Graphite container = 5.20 g

Graphite tube is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3 used Ta foils for heat shielding and the boat was installed in Evap1.

Chamber currently pumping down.

 Tuesday, February 13, 2018, 15:30

Initial IGP1 = 2.73x10e-6 Torr

Tapped up entire process manually to 520 A in 30 min

TGHT = 520 A, 5.41 V

Vacuum coming down nicely indicating carbonization process complete.

Current trip off after 5 min of being at 520 A.

 Wednesday, February 14, 2018, 15:32

EVAP1 vented with Argon and the target was removed.

Target was transferred to glove box.

Ta boat and graphite container look unbroken.

Marla Cervantes wrote:

Marla Cervantes wrote:  Thursday, February 08, 2018, 14:50 35 circles from cast#2 of 14 mm diameter were packed into a graphite sample container. 35 x UO2/C circles = 4.76 g Graphite container = 5.3 g Graphite tube is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3 new Ta foils for heat shielding and the boat was installed in Evap1. Chamber currently pumping down.  Friday, February 09, 2018, 10:40 Initial IGP1 = 4.54e-7 Torr Tapped up entire process manually to 520A in 25 min TGHT = 520 A, 5.49 V Vacuum coming down indicating carbonization process complete.   Current suddenly tripped off from 520 A to 0 A. There was not a power outage. There was good vacuum. Water cooling did not trip off     Friday, February 09, 2018, 16:49 The power supply was tested and its working normally. Apparently a glitch on EPICS caused the tripped off.

 Friday, February 09, 2018, 17:00

Target remained in EVAP1 for 2 hours at 0 A to ensure cooling.

EVAP1 was vented with Ar and the target was removed from EVAP1.

Graphite container seems unbroken.

Ta boat looks unbroken.

Marla Cervantes wrote:

Thursday, February 08, 2018, 14:50 35 circles from cast#2 of 14 mm diameter were packed into a graphite sample container. 35 x UO2/C circles = 4.76 g Graphite container = 5.3 g Graphite tube is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3 new Ta foils for heat shielding and the boat was installed in Evap1. Chamber currently pumping down.  Friday, February 09, 2018, 10:40 Initial IGP1 = 4.54e-7 Torr Tapped up entire process manually to 520A in 25 min TGHT = 520 A, 5.49 V Vacuum coming down indicating carbonization process complete.   Current suddenly tripped off from 520 A to 0 A. There was not a power outage. There was good vacuum. Water cooling did not trip off

 Friday, February 09, 2018, 16:49

The power supply was tested and its working normally.

Apparently a glitch on EPICS caused the tripped off.

 Thursday, February 08, 2018, 14:50

35 circles from cast#2 of 14 mm diameter were packed into a graphite sample container.

35 x UO2/C circles = 4.76 g

Graphite container = 5.3 g

Graphite tube is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3 new Ta foils for heat shielding and the boat was installed in Evap1.

Chamber currently pumping down.

 Friday, February 09, 2018, 10:40

Initial IGP1 = 4.54e-7 Torr

Tapped up entire process manually to 520A in 25 min

TGHT = 520 A, 5.49 V

Vacuum coming down indicating carbonization process complete.  

Current suddenly tripped off from 520 A to 0 A.

There was not a power outage.

There was good vacuum.

Water cooling did not trip off 

Monday, February 05, 2018, 17:24

35 circles from cast#2 of 14 mm diameter were packed into a graphite sample container.

35 x UO2/C circles = 4.59 g

Graphite container = 5.3 g

Graphite tube is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3 new Ta foils for heat shielding and the boat was installed in Evap1.

Chamber currently pumping down.

 Tuesday, February 06, 2018, 10:59

Initial IGP1 = 4.79e-7 Torr

Tapped up entire process manually to 520A in 30 min

TGHT = 520 A, 5.32 V

Vacuum coming down indicating carbonization process complete.  

Will remain at max setpoint for 4 hrs to ensure full carbonization before cooling down.

 Tuesday, February 06, 2018, 14:44

Initiating auto-cool at 2.0 A/min 

 Thursday, February 08, 2018, 10:43

Vented with Ar and removed from EVAP1

 Thursday, February 01, 2018, 12:59

35 circles of 14 mm diameter were packed into a graphite sample container.

28 discs corresponded to cats#1 and 7 discs to cast#2

35 x UO2/C circles = 3.42 g

Graphite container = 6.96 g

Graphite tube is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3 new Ta foils for heat shielding and the boat was installed in Evap1.

Chamber currently pumping down.

 Friday, February 02, 2018, 13:18

Initial IGP1 = 4.82x10e-7 Torr

Tapped up entire process manually to 520A in 30 min

TGHT = 520 A, 5.63 V

Vacuum coming down nicely indicating carbonization process complete 

Will remain at max setpoint for 4 hrs to ensure full carbonization before cooling down.

 Friday, February 02, 2018, 16:57

Initiating auto-cool at 2.0 A/min 

Monday, February 05, 2018, 17:23 

Marla Cervantes wrote:

Marla Cervantes wrote: Marla Cervantes wrote:  Monday, January 29, 2018, 09:26 35 circles of 14 mm diameter were packed into a graphite sample container. 35 x UO2/C circles = 4.94 g Graphite container = 5.03 g Graphite tube is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3 new Ta foils for heat shielding and the boat was installed in Evap1. Chamber currently pumping down.    Monday, January 29, 2018, 11:06 A power outage around 10 am tripped off EVAP1.  Monday, January 29, 2018, 14:22 Water flow turned on. Chamber set to pumping down.

 Tuesday, January 30, 2018, 16:06

Initial IGP1 = 9.4x10e-7 Torr

Tapped up entire process manually to 520A in 32 min

TGHT = 520 A, 5.45 V

Vacuum coming down indicating carbonization process complete 

Will remain at max setpoint for 4 hrs to ensure full carbonization before cooling down.

 Tuesday, January 30, 2018, 18:40

 Initiating auto-cool at 2.0 A/min 

 Wednesday, January 31, 2018, 14:00

Marla Cervantes wrote:

Marla Cervantes wrote:  Monday, January 29, 2018, 09:26 35 circles of 14 mm diameter were packed into a graphite sample container. 35 x UO2/C circles = 4.94 g Graphite container = 5.03 g Graphite tube is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3 new Ta foils for heat shielding and the boat was installed in Evap1. Chamber currently pumping down.    Monday, January 29, 2018, 11:06 A power outage around 10 am tripped off EVAP1.

 Monday, January 29, 2018, 14:22

Water flow turned on.

Chamber set to pumping down. 

Marla Cervantes wrote:

Monday, January 29, 2018, 09:26 35 circles of 14 mm diameter were packed into a graphite sample container. 35 x UO2/C circles = 4.94 g Graphite container = 5.03 g Graphite tube is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3 new Ta foils for heat shielding and the boat was installed in Evap1. Chamber currently pumping down.

 Monday, January 29, 2018, 11:06

A power outage around 10 am tripped off EVAP1.

 Monday, January 29, 2018, 09:26

35 circles of 14 mm diameter were packed into a graphite sample container.

35 x UO2/C circles = 4.94 g

Graphite container = 5.03 g

Graphite tube is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3 new Ta foils for heat shielding and the boat was installed in Evap1.

Chamber currently pumping down.

Marla Cervantes wrote:

Marla Cervantes wrote: Marla Cervantes wrote:  Friday, January 19, 2018, 12:29 Circles from cast 1 were used, the same as the last round of 1stepUCx [see elog i.d. 164] A 14mm punch was used to punch out circles from the cast. 35 circles were packed into a graphite sample container. 35 x UO2/C circles = 5.69 g Graphite container = 6.84 g Graphite container is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3-layers of heat shield and installed in Evap1. Chamber currently pumping down.    Monday, January 22, 2018, 9:00 A power outage on Sunday tripped off EVAP1.  Monday, January 22, 2018, 10:00 Chamber pumping down. Water flow turned on. Monday, January 22, 2018, 13:30 IGP1 = 8e-6 Torr Tapped up entire process manually to 520A in 45 min TGHT = 520 A, 6.08 V  Vacuum coming down indicating carbonization process complete Will remain at max setpoint overnight.

 Tuesday, January 23, 2018, 9:30

Initiating auto-cool at 2 A/min

 Tuesday, January 23, 2018, 16:00

 EVAP1 was not vented, Ar tank has low level, Ar tank will be replaced.

Wednesday, January 24, 2018, 11:37

 EVAP1 was vented very carefully using the Ar remaining in the Ar tank.

Ar tank remaining gas: ~8 psi.

Wednesday, January 24, 2018, 15:42 

UCx was transferred to glove box.

Final mass 4.501 g

Marla Cervantes wrote:

Marla Cervantes wrote:  Friday, January 19, 2018, 12:29 Circles from cast 1 were used, the same as the last round of 1stepUCx [see elog i.d. 164] A 14mm punch was used to punch out circles from the cast. 35 circles were packed into a graphite sample container. 35 x UO2/C circles = 5.69 g Graphite container = 6.84 g Graphite container is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3-layers of heat shield and installed in Evap1. Chamber currently pumping down.    Monday, January 22, 2018, 9:00 A power outage on Sunday tripped off EVAP1.

 Monday, January 22, 2018, 10:00

Chamber pumping down.

Water flow turned on.

Monday, January 22, 2018, 13:30

IGP1 = 8e-6 Torr

Tapped up entire process manually to 520A in 45 min

TGHT = 520 A, 6.08 V 

Vacuum coming down indicating carbonization process complete

Will remain at max setpoint overnight.

Marla Cervantes wrote:

Friday, January 19, 2018, 12:29 Circles from cast 1 were used, the same as the last round of 1stepUCx [see elog i.d. 164] A 14mm punch was used to punch out circles from the cast. 35 circles were packed into a graphite sample container. 35 x UO2/C circles = 5.69 g Graphite container = 6.84 g Graphite container is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3-layers of heat shield and installed in Evap1. Chamber currently pumping down.

 Monday, January 22, 2018, 15:48

A power outage on Sunday tripped off EVAP1.

 Friday, January 19, 2018, 12:29

Circles from cast 1 were used, the same as the last round of 1stepUCx [see elog i.d. 164]

A 14mm punch was used to punch out circles from the cast.

35 circles were packed into a graphite sample container.

35 x UO2/C circles = 5.69 g

Graphite container = 6.84 g

Graphite container is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3-layers of heat shield and installed in Evap1.

Chamber currently pumping down.

Laura Lambert wrote:

Marla Cervantes wrote:  Wednesday, January 10, 2018, 14:44 Circles from cast 1 were used, the same as the last round of 1stepUCx [see elog i.d. 164] A 14mm punch was used to punch out circles from the cast. 35 circles were packed into a graphite sample container. 35 x UO2/C circles = 5.75 g Graphite container = 5.38 g Graphite container is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3-layers of heat shield and installed in Evap1. Chamber currently pumping down.  Friday, January 12, 2018, 07:43 IGP1 = 0.0266 Torr TGHT = 520A, 5.92V Voltage has been climbing consistently since it has reached it's max setpoint, gone up ~0.8V in ~18hrs Carbonization complete. Initiating auto-cool at 2.0A/min Will update later with more information on this process.  Friday, January 12, 2018, 09:47 Turned the turbo pump back on, to ensure safe cooling.

 Monday, January 15, 2018, 10:00

Vented with Argon and removed from evap1

NB: The initial mass of the UO2/C discs was 5.9 g

       The final mass of the UCx discs was 4.614 g

 Monday, January 15, 2018, 13:37

35 circles of 14 mm diameter were packed into a graphite sample container.

35 x UO2/C circles = 5.58 g

Graphite container = 5.22 g

Graphite tube is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3 new Ta foils for heat shielding and the boat was installed in Evap1.

Chamber currently pumping down.

Tuesday, January 16, 2018, 13:41 

Initial IGP1 = 9x10e-7 Torr

Tapped up entire process manually to 520A in 1.5 hrs

TGHT = 525 A, 5.64 V

Vacuum coming down nicely indicating carbonization process complete 

Will remain at max setpoint overnight to ensure full carbonization before cooling down.

Wednesday, January 17, 2018, 10:30

Initiating auto-cool at 2.0A/min 

Wednesday, January 17, 2018, 4:30

Marla Cervantes wrote:

Wednesday, January 10, 2018, 14:44 Circles from cast 1 were used, the same as the last round of 1stepUCx [see elog i.d. 164] A 14mm punch was used to punch out circles from the cast. 35 circles were packed into a graphite sample container. 35 x UO2/C circles = 5.75 g Graphite container = 5.38 g Graphite container is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3-layers of heat shield and installed in Evap1. Chamber currently pumping down.

 Friday, January 12, 2018, 07:43

IGP1 = 0.0266 Torr

TGHT = 520A, 5.92V

Voltage has been climbing consistently since it has reached it's max setpoint, gone up ~0.8V in ~18hrs

Carbonization complete.

Initiating auto-cool at 2.0A/min

Will update later with more information on this process.

 Friday, January 12, 2018, 09:47

Turned the turbo pump back on, to ensure safe cooling.

 Wednesday, January 10, 2018, 14:44

Circles from cast 1 were used, the same as the last round of 1stepUCx [see elog i.d. 164]

A 14mm punch was used to punch out circles from the cast.

35 circles were packed into a graphite sample container.

35 x UO2/C circles = 5.75 g

Graphite container = 5.38 g

Graphite container is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3-layers of heat shield and installed in Evap1.

Chamber currently pumping down.