Tuesday, May 08, 2018, 15:02

22 np-SiC fibrous discs loaded in the tube container (coated and sintered with TaC)

Heat treatment is similar to previous process, see elog #408. 

TGHT should be set at 330A/5.2V to reach temp 1575C (+/- 25).

Omega slope set at 1.05 (for carbide)

Chamber is currently being pumped down

 Tuesday, May 08, 2018, 22:46

Pressure at 2.2e-6 Torr.

Initiated autoramping at 0.2A/min to reach 330A

 Friday, May 11, 2018, 11:11

TGHT reached to 330A/5.1V but temp was measured at 1400A; It was held at that current for about 10 hours.

Increased TGHT to 335A/5.2V - temp is holding at 1420C (Will check the window if there is any coating that might have caused the discrepancy)

 Sunday, May 13, 2018, 00:25

In fact, the window is slightly coated.  The temperature should already be at optimum, 1600C.  Will keep heating for another day.

 Sunday, May 13, 2018, 14:10

Temp holding up well.. Pressure at 1.8e-7 torr. 

cooling down at 2A/min.

 Monday, May 14, 2018, 09:33

Target has been cooled for over 18 hours.  Pressure at 1.1e-7 Torr.

Venting chamber.

mass loss = (8.65 - 4.32)g = 4.33 g (50%) [slightly higher than expected, likely due to increase of 5A on TGHT]

Tuesday, July 03, 2018, 17:02

49 discs/ 15.42g np-SiC fibrous discs loaded into the tube container

Heat treatment is similar to previous process, see elog#408/409.

TGHt should be set at 330A/5.2V to reach temp 1575C (+/- 25C)

Omega slope set at 1.05 (for carbide)

Chamber is currently being pumped down

 Wednesday, July 04, 2018, 10:38

Pressure at 1.5 e-6 Torr.

Initiated auto-ramping at 0.2A/min to reach 330A/5.2V.

 Monday, July 09, 2018, 14:44

TGHT has been stabilized at 330A/5.2V for 24 hours.  Pressure at 3.7e-7 Torr.

Temp was measured at 1400C - light coating on window likely affected the measurements.

Measured with one-color pyrometer on Ta body inside the target container = 1550 C (with the correction of 250C for Ta). 

Adjusted OMEGA slope to 1.18, temp currently at 1580 C.

 Monday, July 09, 2018, 16:42

Pressure stabilized at 3.5e-7 Torr. 

Initiated auto-cooling at 1A/min.

 Tuesday, July 10, 2018, 11:11

Target is at room temperature. 

Process completed; see attachment for the data retrieval and dropbox (np-SiC production folder) for screen capture.

mass loss = (15.42 - 8.09) g = 7..33 g (47.5%) [in agreement - good!]

Monday, August 20, 2018, 17:58

14.9 g of np-SiC fibrous target discs are loaded into the container (previously coated with TaC and sintered, see elog ID 414).

Total loaded length 9.5 cm. 

A 1.5" width graphite sheet is used as under layer to prevent TaC diffused to the discs; this was observed during the heat treatment, (see dropbox SEM images).

Both end caps are in.  With ionizer pointing out, right cap is expended BUT NOT left cap - will need to expend this after the conditioning.

No Ta heat-shield is used.

Final conditioning temperature:  1500 C (As per e-log 414, TGHT = 450A/7.31V, 3.28kW) 

Keeping TBHT at 0A for now - will ramp up after TGHT reach to the desired temperature. 

OMEGA slope set at 0.99

Good vac = 3.0e-5 Torr,

Bad vac = 5.0e-5 Torr.

 Tuesday, August 21, 2018, 10:24

Pressure at 1.2e-6 Torr. 

Initiated autoramping at 2A/min for TGHT to reach 400A - monitoring temp and vacuum.

TBHT set at 10A. 

 Tuesday, August 21, 2018, 15:13

Temp reached to 1350C. TGHT at 400A/6.7V. Pressure at 1.9e-6 Torr after holding at the temp for 100 min.

 Tuesday, August 21, 2018, 15:28

Tapped up TGHT to 450A/7.8V (3.5kW).  Temp measured at 1465 +/- 5 C.  Pressure coming down from 3.5 e-6 Torr.

 Tuesday, August 21, 2018, 15:32

Tapping up TBHT to 230A

 Tuesday, August 21, 2018, 16:25

TBHT at 230A/4.33V.  Pressure started to increase from 150A, and reached to 3.3e-6 Torr after TGHT reached to the setting.

Temperature measured at 1475 C +/- 5C.  Holding at this temperature until vacuum comes to stabilization (est.2-3 hours)

 Tuesday, August 21, 2018, 16:45

Checked with Mikron (slope set at 0.99); temp on left end-cap measured at 1490 +/- 20C (that's close enough).  Temp on ionizer tube about 1900C

 Tuesday, August 21, 2018, 22:12

Pressure at 1.7e-6 Torr.  Temp holding at 1480C, TGHT at 450/7.7V, TBHT 230A/4.27V.

Cooling down at 2A/min for TGHT and 1A/min for TBHT

Monday, September 28, 2020, 11:49

6 discs of np-SiC were loaded to the target boat wrapped with 3 layers of heat shields.

Desired temperature at 1500 C, (As per e-log 414/416, TGHT = 450A/7.31V, 3.28kW) 

Omega slope set at 1.05 (for carbide)

Good vac = 3.0e-5 Torr,

Bad vac = 5.0e-5 Torr.

Pumping down in progress

 Monday, September 28, 2020, 21:44

Pressure at 1e-6 Torr.  Initiated autoramping at 0.2A/min to reach 300 A.  Monitor temp.

 Wednesday, September 30, 2020, 11:39

TGHT reached to 300 A/ 4.5V, temp at 1130 C.  No coating on windows.

Continue to ramp up 330A.  Monitor temp.

 Wednesday, September 30, 2020, 16:38

TGHT reached 330 A / 5.04 V, temp at 1190 C. 

Ramp up to 400 A. Current pressure at 9.8 e-7 Torr.

Thursday, October 01, 2020, 10:28

TGHT reached 400 A/ 6.3V, temp at 1320 C.  Continue to ramp up to 450 A.

 Thursday, October 01, 2020, 16:44

TGHT reached to 450 A/ 7.4 V.  TEmp at 1500 C. 

Pressure at 1.35 e-6 Torr and coming down.   Continue to hold TGHT at 1500 C for at least 24 hr.

 Sunday, October 04, 2020, 16:49

TGHT has been holding at 450 A/ 7.3 V for nearly 3 days; temp has gone up and stabilized at 1554 C; pressure at 2.13 e -7 Torr.

Initiated cooling down at -2A/min.

 Monday, October 05, 2020, 10:02

Chamber vented.

 Friday, May 29, 2015, 11:21

Total number of foils: 425 discs

Total mass of materials [incl graphite foils]: 44.41g

Total length packed: 12.3cm

Container has no heat shields.

No endcaps inserted to allow outgassing.

Currently being pumped down.

 Friday, May 29, 2015, 14:13

HS water valves opened, no leaks detected.

IGP1 = 5.4e-6 Torr.

Tapping up manually.

Friday, May 29, 2015, 16:48

Tapped up manually to 20A.

IGP1 = 5.9e-6 Torr.

Initiating auto-ramp at 0.2A/min for the TGHT and 0.1A/min for the TBHT.

Max setpoints set to 580A and 230A for the TGHT and TBHT respectively.

Good Vacuum = 3.0e-5 Torr. Bad Vacuum = 4.0e-5 Torr.

 Monday, June 01, 2015, 09:17

IGP1 = 3.8e-6 Torr.

TGHT = 478A.

TBHT reached max setpoint of 230A.

Increasing ramping rate to 0.5A/min.

 Monday, June 01, 2015, 13:15

Checked window for temperature readings, good visibility, no coating on window. 

IGP1 = 9.1e-6 Torr.

TGHT reached max setpoint of 580A 30min ago.

Stepping up manually to a target temperature of 2000C...

 Monday, June 01, 2015, 16:25

IGP1 = 6.5e-6 Torr.

TGHT = 870A, 17.90V

OMEGA = 1948C

Laura Lambert wrote:

Friday, May 29, 2015, 11:21 Total number of foils: 425 discs Total mass of materials [incl graphite foils]: 44.41g Total length packed: 12.3cm Container has no heat shields. No endcaps inserted to allow outgassing. Currently being pumped down.  Friday, May 29, 2015, 14:13 HS water valves opened, no leaks detected. IGP1 = 5.4e-6 Torr. Tapping up manually. Friday, May 29, 2015, 16:48 Tapped up manually to 20A. IGP1 = 5.9e-6 Torr. Initiating auto-ramp at 0.2A/min for the TGHT and 0.1A/min for the TBHT. Max setpoints set to 580A and 230A for the TGHT and TBHT respectively. Good Vacuum = 3.0e-5 Torr. Bad Vacuum = 4.0e-5 Torr.  Monday, June 01, 2015, 09:17 IGP1 = 3.8e-6 Torr. TGHT = 478A. TBHT reached max setpoint of 230A. Increasing ramping rate to 0.5A/min.  Monday, June 01, 2015, 13:15 Checked window for temperature readings, good visibility, no coating on window.  IGP1 = 9.1e-6 Torr. TGHT reached max setpoint of 580A 30min ago. Stepping up manually to a target temperature of 2000C...  Monday, June 01, 2015, 16:25 IGP1 = 6.5e-6 Torr. TGHT = 870A, 17.90V OMEGA = 1948C

 Monday, June 01, 2015, 17:59

After almost an hour at 870A, the temperature went up from 1948C to 1980C; however temperature around the target container/legs are >2000C.  The voltage on the power supply also went up slightly. 

There is a film coated on the window port and that could affect the temp reading.

To be safe, I lowered the TGHT to 830A/17.38V, temp at 1930C. 

Will keep at 830A for 4 hours and cool down this evening. 

Recommend: Using Ta-heat shields for sintering next time.

 Monday, June 01, 2015, 22:55

TGHT at 830A for almost 5 hours.  

TEMP has gone up to 1994C.  Voltage has also gone up to 19V.  

Cooling down at 2A/min for TGHT and 1A/min for TBHT. 

John Wong wrote:

Laura Lambert wrote:  Friday, May 29, 2015, 11:21 Total number of foils: 425 discs Total mass of materials [incl graphite foils]: 44.41g Total length packed: 12.3cm Container has no heat shields. No endcaps inserted to allow outgassing. Currently being pumped down.  Friday, May 29, 2015, 14:13 HS water valves opened, no leaks detected. IGP1 = 5.4e-6 Torr. Tapping up manually. Friday, May 29, 2015, 16:48 Tapped up manually to 20A. IGP1 = 5.9e-6 Torr. Initiating auto-ramp at 0.2A/min for the TGHT and 0.1A/min for the TBHT. Max setpoints set to 580A and 230A for the TGHT and TBHT respectively. Good Vacuum = 3.0e-5 Torr. Bad Vacuum = 4.0e-5 Torr.  Monday, June 01, 2015, 09:17 IGP1 = 3.8e-6 Torr. TGHT = 478A. TBHT reached max setpoint of 230A. Increasing ramping rate to 0.5A/min.  Monday, June 01, 2015, 13:15 Checked window for temperature readings, good visibility, no coating on window.  IGP1 = 9.1e-6 Torr. TGHT reached max setpoint of 580A 30min ago. Stepping up manually to a target temperature of 2000C...  Monday, June 01, 2015, 16:25 IGP1 = 6.5e-6 Torr. TGHT = 870A, 17.90V OMEGA = 1948C    Monday, June 01, 2015, 17:59 After almost an hour at 870A, the temperature went up from 1948C to 1980C; however temperature around the target container/legs are >2000C.  The voltage on the power supply also went up slightly.  There is a film coated on the window port and that could affect the temp reading. To be safe, I lowered the TGHT to 830A/17.38V, temp at 1930C.  Will keep at 830A for 4 hours and cool down this evening.  Recommend: Using Ta-heat shields for sintering next time.  Monday, June 01, 2015, 22:55 TGHT at 830A for almost 5 hours.   TEMP has gone up to 1994C.  Voltage has also gone up to 19V.   Cooling down at 2A/min for TGHT and 1A/min for TBHT.

 Tuesday, June 02, 2015, 12:37

Chamber was vented and the target was inspected. 

Some stressed marks on the target container can be observed.

The container is also slightly curved but otherwise it's fine. 

The materials packed length has expended outward so 3 discs were removed in order to insert the end caps. 

The packed length is now 16cm.

Two extra graphite foils were inserted on both ends, and previously coated/sintered TaC-end caps are inserted and expended. 

Rn foil is inserted & Std solutions are added. 

Ready for test-stand.

Link to photos for more details:

https://www.dropbox.com/sh/0cra7viqs9ro8q3/AADEGk8goGI4c-uzRQSGwWmxa?dl=0

John Wong wrote:

John Wong wrote: Laura Lambert wrote:  Friday, May 29, 2015, 11:21 Total number of foils: 425 discs Total mass of materials [incl graphite foils]: 44.41g Total length packed: 12.3cm Container has no heat shields. No endcaps inserted to allow outgassing. Currently being pumped down.  Friday, May 29, 2015, 14:13 HS water valves opened, no leaks detected. IGP1 = 5.4e-6 Torr. Tapping up manually. Friday, May 29, 2015, 16:48 Tapped up manually to 20A. IGP1 = 5.9e-6 Torr. Initiating auto-ramp at 0.2A/min for the TGHT and 0.1A/min for the TBHT. Max setpoints set to 580A and 230A for the TGHT and TBHT respectively. Good Vacuum = 3.0e-5 Torr. Bad Vacuum = 4.0e-5 Torr.  Monday, June 01, 2015, 09:17 IGP1 = 3.8e-6 Torr. TGHT = 478A. TBHT reached max setpoint of 230A. Increasing ramping rate to 0.5A/min.  Monday, June 01, 2015, 13:15 Checked window for temperature readings, good visibility, no coating on window.  IGP1 = 9.1e-6 Torr. TGHT reached max setpoint of 580A 30min ago. Stepping up manually to a target temperature of 2000C...  Monday, June 01, 2015, 16:25 IGP1 = 6.5e-6 Torr. TGHT = 870A, 17.90V OMEGA = 1948C    Monday, June 01, 2015, 17:59 After almost an hour at 870A, the temperature went up from 1948C to 1980C; however temperature around the target container/legs are >2000C.  The voltage on the power supply also went up slightly.  There is a film coated on the window port and that could affect the temp reading. To be safe, I lowered the TGHT to 830A/17.38V, temp at 1930C.  Will keep at 830A for 4 hours and cool down this evening.  Recommend: Using Ta-heat shields for sintering next time.  Monday, June 01, 2015, 22:55 TGHT at 830A for almost 5 hours.   TEMP has gone up to 1994C.  Voltage has also gone up to 19V.   Cooling down at 2A/min for TGHT and 1A/min for TBHT.     Tuesday, June 02, 2015, 12:37 Chamber was vented and the target was inspected.  Some stressed marks on the target container can be observed. The container is also slightly curved but otherwise it's fine.  The materials packed length has expended outward so 3 discs were removed in order to insert the end caps.  The packed length is now 16cm. Two extra graphite foils were inserted on both ends, and previously coated/sintered TaC-end caps are inserted and expended.  Rn foil is inserted & Std solutions are added.  Ready for test-stand. Link to photos for more details: https://www.dropbox.com/sh/0cra7viqs9ro8q3/AADEGk8goGI4c-uzRQSGwWmxa?dl=0

 see attachment for data recorded during ZrC conditioning 

 Thursday, June 25, 2015, 16:14

Total number of foils: 422 discs

Total mass of materials [incl graphite foils]: 

Total length packed: 12.0cm

Container has one Ta heat shield.

No endcaps inserted to allow outgassing

Two TaC coated Ta wires formed into a spring inserted either end to avoid ZrC expansion of materials.

Currently being pumped down.

 Friday, June 26, 2015, 11:44

HS water valves opened.

No leaks detected.

Initiating ramp up.

 Friday, June 26, 2015, 14:44

EVAP2 was tapped up manually to 50A.

Vacuum tripped evap off.

Tapping back up manually now...

 Friday, June 26, 2015, 15:53

Tapped up manually to 45A for both TGHT and TBHT

IGP1 = 4.8e-5 Torr

Will initiate auto-ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively once vacuum settled down and stable.

Max setpoints set to 520A and 230A for the TGHT and TBHT respectively.

Good Vacuum = 3.0e-5 Torr. Bad Vacuum = 4.0e-5 Torr.

Laura Lambert wrote:

Thursday, June 25, 2015, 16:14 Total number of foils: 422 discs Total mass of materials [incl graphite foils]:  Total length packed: 13.2cm Container has one Ta heat shield. No endcaps inserted to allow outgassing Two TaC coated Ta wires formed into a spring inserted either end to avoid ZrC expansion of materials. Currently being pumped down.  Friday, June 26, 2015, 11:44 HS water valves opened. No leaks detected. Initiating ramp up.  Friday, June 26, 2015, 14:44 EVAP2 was tapped up manually to 50A. Vacuum tripped evap off. Tapping back up manually now...  Friday, June 26, 2015, 15:53 Tapped up manually to 45A for both TGHT and TBHT IGP1 = 4.8e-5 Torr Will initiate auto-ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively once vacuum settled down and stable. Max setpoints set to 520A and 230A for the TGHT and TBHT respectively. Good Vacuum = 3.0e-5 Torr. Bad Vacuum = 4.0e-5 Torr.

 Monday, June 29, 2015, 06:57

TGHT has been at 520A/9.80V, DV 5.80V for 7 hours, temperature measured at 1800C.  Vac is coming down to 9.18e-6 Torr.  However, TGHT voltage is slightly going up over the 7 hours of heating, See screenshot attachment. (Can't make further comments until target is inspected.)

Initiated cooling down at 2A/min for TGHT and 1A/min for TBHT.

Chamber can be vented later today.

 Monday, June 29, 2015, 14:58

Target has been inspected.

Slightly crystallization on the outer tube of the container can be observed. 

Overall, the container looks a lot better than before. 

Rn foiled inserted. Salt added - Ready for test-stand

Monday, March 18, 2019, 15:51

Total number of foils: 555

Total mass of material including graphite foils: 478 grams

Total length packed 14.2 cm

container has 3 Ta heat shields.

No endcaps inserted to facilitate outgassing

Two TaC coated Ta wire springs inserted at either end to allow for ZrC expansion.

5 extra foils tucked beneath each spring for QC; total mass (10 discs) =1.0160 g

Desired temp = 1900 C, Auto ramping TGHT at  0.1 A/min to reach 280A A (Omega slope set = 0.990, approx 1400 C, Elog#427),  TGHT will be tapped up accordingly to reach desired temperature. 

TBHT will be set fixed at 230A (max). TBHT at 0.1 A/min to reach 230A.

Good vac at 3.00-5 Torr

Bad vac at 5.0e-5 Torr.

Currently being pumped down.

 Tuesday, March 19, 2019, 08:57

Current pressure IGP1 = 5.24e-07 Torr

Manually tapping to 40A on TBHT and TGHT

At 20 A IGP1 pressure trending up.  Will leave at 20A until trending down.

Pressure @ 20 A set, peaked ~1.8e-06 Torr after 1 hour

Tuesday, March 19, 2019, 10:32

Tapping manually to 50 A on TBHT and TGHT while monitoring IGP1 pressure

Tapped to 25 A and IGP1 pressure trending up.  Will allow to stabilize.

Tuesday, March 19, 2019, 11:34

Pressure stabilized at ~3.25e-06 Torr

Tapped up to 30 A on both TGHT and TBHT

Pressure stabilized at ~6.6e-06

Tapped up to 34A on both TGHT and TBHT

Pressure stabilized at ~1.2e-05 Will allow to drop before proceeding

 Tuesday, March 19, 2019, 13:43

Tapped up to 40A waiting for pressure to stabilize

Pressure shot up ~8.5e-05, therefore tapped down TGHT to 35A (At 35A TGHT current value fluctuates, probably better to ramp up to 36A)

Will let pressure drop before proceeding with TGHT heating

Ramped TGHT to 36A, IGP1 pressure still trending down and current measurements stable.

 Starting autoramp at 0.3A/min for both TGHT and TBHT until 280A and 230A respectively

Initial TGHT Current: 33.6A, 0.05V

Initial TBHT Current: 38.6A, 0.48V

IGP1 = 4.9e-05 Torr

Wednesday, March 20, 2019, 09:41

 TGHT has only ramped to 45.7 A, 0.085V

TBHT has only ramped to 50.2A, 0.62V

IGPI pressure ~4.0 e-5 Torr

Stopping ramp and monitoring pressure to see if it drops appropriate levels.

Wednesday, March 20, 2019, 14:10  

IGP1 pressure = 7.6e-06 Torr

TGHT 47.7Z, 0.16V

TBHT 50.1A, 0.63V

Autoramp at 0.1A/min both TGHT and TBHT to 280A and 230A respectively.

 Thursday, March 21, 2019, 08:12

IGP1 = 3.1e-05 Torr

TGHT = 51.4 A, 0.18V

TBHT=61.9A, 0.87V

Stopped autoramp

Manually ramping TGHT and TBHT while monitoring pressure

 Rampted up TGHT to 54A (reading 65 A), 0.5V and TBHT to 68A, 0.9V

Allowing pressure to stabilize

Manually tapped TGHT to 80A, .81V

Manually tapped TBHT to 90A, 1.3V

IGP1 = .0002 Torr

Will leave over night to allow pressure to drop

Friday, March 22, 2019, 08:17

IGP1 = 6.6e-06

TGHT = 88.8A, 0.81V

TBHT = 90.1A, 1.3V

Will manually tap ~100A on both TBHT and TGHT

Friday, March 22, 2019, 12:18

IGP1 = 1.28e-05 Torr

TGHT = 100.9A, 1.0V

TBHT = 101.2A, 1.5V

will allow pressure to drop slightly the autoramp at 0.1A/min for both TGHT and TBHT until 280A and 230A respectively

Friday, March 22, 2019, 14:51

IGP1= 7.4 e-06 Torr

TGHT = 100.8A, 1.0V

TBHT= 101.5A, 1.5V

Started autoramp at 0.1A/min for both TGHT and TBHT until 280A and 230A respectively

Tuesday, March 26, 2019, 08:18

IGP1 oscillated around ramping trip point 3.0e-05 while current slowly ramped to 280A (reached sometime during the night).

IGP1= 7.8e-06 Torr

TGHT= 283.4A, 4.2V

TBHT= 233.1A, 4.1V

Will continue ramp TGHT @0.2A/min up to 400A  (Omega slope set = 0.990, approx 1800 C, Elog#427)

Wednesday, March 27, 2019, 09:39

Target has been at 400A, OMEGA ~1400C since ~7pm of previous evening

TGHT = 400.2A, 6.45V

TBHT= 233.1A, 4.16V

IGP1= 3.1e-07 Torr

Autoramp TGHT to440A @0.2A/min

 Stopped autoramp at TGHT = 427.4 A and 7.00V, OMEGA= 1492 C

Wednesday, March 27, 2019, 14:14

Restarted TGHT autoramp @.2A/min up to 440A

Friday, March 29, 2019, 12:06

Changed OMEGA slope to 1.09 after checking with the analog pyrometer

IGP1 = 1.65e-07 Torr

TGHT = 441.3A, 7.5V

TBHT= 233.0A, 4.2V

Tapping TGHT to 450A @ ~1A/min while monitoring pressure

TGHT remained at 451A, 7.8 V  and  TBHT at 233.2A, 4.2 V,  for 10.5 hours while OMEGA Temperature ~1810 C.

Ramp-down was initiated with IGP1 = 1.7e-07 Torr

Ramp rate = 2A/min for TGHT and 1/min for TBHT

 Monday, April 01, 2019, 08:53

TGHT = 0A, 0.05V

TBHT= 0.01A, 0V

IGP1= 4.05e-08 Torr

Unloading Target

Target Final weight = 473 g

% Mass of ZrC+C+organics lost = 14.20 % compared to 13.95% theoretical organics content.

Final weight of 10 discs = 0.9250 g

% mass lost on this discs = 13.66%

The tube was slightly bent along the short axis

The discs expanded but more towards one side (possibly due to discrepancy in spring strength).

 One protective graphite disc added to each end

One end cap on each end

Tuesday, July 30, 2019, 15:33

ZrC backup Target 12.6 cm disc length, 465 g total weight (no springs and no analysis discs).

Total weight= 470 g.

20 Analysis discs weighing 2.368 g (10 at each end).

Two springs (one at each end).

OMEGA slope initially = 0.990  (was changed to 1.09 at higher Temperature as per eLog #434

Target is being pumped down.

Wednesday, July 31, 2019, 09:31

Desired temp = 1900 C, Auto ramping TGHT at  0.1 A/min to reach 400A then  TGHT will be tapped up accordingly to reach desired temperature. (eLog 434)

TBHT will be set fixed at 230A (max). TBHT at 0.1 A/min to reach 230A.

Note: Initially both TGHT and TBHT will be ramped up at 0.3A/min up to 30A each.

IGP1= 1.35e-06 Torr

Good vac at 3.00-5 Torr

Bad vac at 5.0e-5 Torr.

Wednesday, July 31, 2019, 12:02

At 30A pressure was increasing a bit fast, therefore, the ramp was changed to increments of .1A every 120s (.05A/min). 

Thursday, August 01, 2019, 08:42

TGHT = 54.7

TBHT = 54.3

IGP1 = 3.86e-5 Torr

Will changer heat ramp to .1A/min by changing wait interval to 60s

Tuesday, August 06, 2019, 07:14

OMEGA = 1212 C

TGHT = 344.7 A, 5.79 V

TBHT = 233 A, 4.17 V

IGP1 = 1.05 e-06 Torr

Autoramping to 400A at increments of 0.1A/min

Tuesday, August 06, 2019, 09:50

OMEGA = 1233 C

TGHT = 360 A, 6.05 V

TBHT = 233 A, 4.18 V

IGP1 = 1.21 e-06 Torr

increasing autoramp increments to .5A/min

Tuesday, August 06, 2019, 12:27

OMEGA = 1356 C

TGHT = 400.6 A, 6.92 V

TBHT = 233.8 A, 4.20 V

IGP1 = 1.95 e-06 Torr

Autoramping to 430 A on TGHT at 0.5 A/min

Tuesday, August 06, 2019, 14:02

OMEGA = 1447 C

TGHT= 430.9 A, 7.66V

TBHT = 233.2A, 4.2 V

IGP1= 2.01e-06 Torr

Autoramping to 440 A on TGHT at 0.5 A/min

Wednesday, August 07, 2019, 09:10

OMEGA = 1548

TGHT = 441.56 A, 8.2 V

TBHT = 233.3 A, 4.2 V

IGP1 = 6.21e-07 Torr

Manually ramping up to 1900C @ 1A/min

Wednesday, August 07, 2019, 09:43

Changed OMEGA slope to 1.09 as per eLog #434

OMEGA reads 1773 C @ TGHT 451A, 8.4V

IGP1 = 7.02 e-07

Wednesday, August 07, 2019, 10:56

OMEGA = 1903 C

TGHT = 483.5 A, 9.2V

TBHT = 233.3 A, 4.3V

IGP1 = 1.7 e-06 Torr trending down

Wednesday, August 07, 2019, 11:40

OMEGA = 1914 C

TGHT = 483.5 A, 9.3V

TBHT = 233.3 A, 4.3V

IGP1 = 1.5 e-06 Torr trending down

Decrease TGHT current to 480.4 A

Wednesday, August 07, 2019, 13:04

OMEGA = 1918 C

TGHT = 480.3 A, 9.4V

TBHT = 233.3 A, 4.3V

IGP1 = 1.28e-06 Torr

Decrease TGHT current to 474.5 A

Wednesday, August 07, 2019, 13:26

OMEGA = 1904 C

TGHT = 474.8 A, 9.3V

TBHT = 233.3 A, 4.3V

IGP1 = 1.11e-06 Torr

Wednesday, August 07, 2019, 13:47

OMEGA = 1912 C

TGHT = 474.8 A, 9.3V

TBHT = 233.3 A, 4.3V

IGP1 = 1.10e-06 Torr

Decrease TGHT to 471.8 A

OMEGA temperature went down to 1904 C

Wednesday, August 07, 2019, 14:26

OMEGA = 1911 C

TGHT = 471.8 A, 9.3V

TBHT = 233.3 A, 4.3V

IGP1 = 1.00e-06 Torr

Decrease TGHT to 469.0 A

OMEGA temperature down to 1904C

Wednesday, August 07, 2019, 15:45

OMEGA = 1912 C

TGHT = 468.8.8 A, 9.2V

TBHT = 233.3 A, 4.3V

IGP1 = 9.2e-07 Torr

Decrease TGHT to 466.0 A

OMEGA temperature down to 1903C

Wednesday, August 07, 2019, 22:09

OMEGA = 1924 C

TGHT = 466.8. A, 9.3V

TBHT = 233.3 A, 4.3V

IGP1 = 7.6e-07 Torr

Cooling at 2A/min TGHT to 456.0 A, 9.0 V and 1A/min TBHT to 230.1 A, 4.2 V

OMEGA = 1900 C

Will allow Pressure to stabilize

 Thursday, August 08, 2019, 06:54

OMEGA = 1919 C

TGHT = 456.9 A, 9.1V

TBHT = 230.3 A, 4.2 V

IGP1 =5.7e-07 Torr

Cooling at 2A/min TGHT and 1A/min TBHT

Thursday, August 08, 2019, 13:30

Target removed from Evap2.  Awaiting inspection by John.

Darwin Ortiz Rosales wrote:

Tuesday, July 30, 2019, 15:33 ZrC backup Target 12.6 cm disc length, 465 g total weight (no springs and no analysis discs). Total weight= 470 g. 20 Analysis discs weighing 2.368 g (10 at each end). Two springs (one at each end). OMEGA slope initially = 0.990  (was changed to 1.09 at higher Temperature as per eLog #434 Target is being pumped down. Wednesday, July 31, 2019, 09:31 Desired temp = 1900 C, Auto ramping TGHT at  0.1 A/min to reach 400A then  TGHT will be tapped up accordingly to reach desired temperature. (eLog 434) TBHT will be set fixed at 230A (max). TBHT at 0.1 A/min to reach 230A. Note: Initially both TGHT and TBHT will be ramped up at 0.3A/min up to 30A each. IGP1= 1.35e-06 Torr Good vac at 3.00-5 Torr Bad vac at 5.0e-5 Torr. Wednesday, July 31, 2019, 12:02 At 30A pressure was increasing a bit fast, therefore, the ramp was changed to increments of .1A every 120s (.05A/min).  Thursday, August 01, 2019, 08:42 TGHT = 54.7 TBHT = 54.3 IGP1 = 3.86e-5 Torr Will changer heat ramp to .1A/min by changing wait interval to 60s Tuesday, August 06, 2019, 07:14 OMEGA = 1212 C TGHT = 344.7 A, 5.79 V TBHT = 233 A, 4.17 V IGP1 = 1.05 e-06 Torr Autoramping to 400A at increments of 0.1A/min Tuesday, August 06, 2019, 09:50 OMEGA = 1233 C TGHT = 360 A, 6.05 V TBHT = 233 A, 4.18 V IGP1 = 1.21 e-06 Torr increasing autoramp increments to .5A/min Tuesday, August 06, 2019, 12:27 OMEGA = 1356 C TGHT = 400.6 A, 6.92 V TBHT = 233.8 A, 4.20 V IGP1 = 1.95 e-06 Torr Autoramping to 430 A on TGHT at 0.5 A/min Tuesday, August 06, 2019, 14:02 OMEGA = 1447 C TGHT= 430.9 A, 7.66V TBHT = 233.2A, 4.2 V IGP1= 2.01e-06 Torr Autoramping to 440 A on TGHT at 0.5 A/min Wednesday, August 07, 2019, 09:10 OMEGA = 1548 TGHT = 441.56 A, 8.2 V TBHT = 233.3 A, 4.2 V IGP1 = 6.21e-07 Torr Manually ramping up to 1900C @ 1A/min Wednesday, August 07, 2019, 09:43 Changed OMEGA slope to 1.09 as per eLog #434 OMEGA reads 1773 C @ TGHT 451A, 8.4V IGP1 = 7.02 e-07 Wednesday, August 07, 2019, 10:56 OMEGA = 1903 C TGHT = 483.5 A, 9.2V TBHT = 233.3 A, 4.3V IGP1 = 1.7 e-06 Torr trending down Wednesday, August 07, 2019, 11:40 OMEGA = 1914 C TGHT = 483.5 A, 9.3V TBHT = 233.3 A, 4.3V IGP1 = 1.5 e-06 Torr trending down Decrease TGHT current to 480.4 A Wednesday, August 07, 2019, 13:04 OMEGA = 1918 C TGHT = 480.3 A, 9.4V TBHT = 233.3 A, 4.3V IGP1 = 1.28e-06 Torr Decrease TGHT current to 474.5 A Wednesday, August 07, 2019, 13:26 OMEGA = 1904 C TGHT = 474.8 A, 9.3V TBHT = 233.3 A, 4.3V IGP1 = 1.11e-06 Torr Wednesday, August 07, 2019, 13:47 OMEGA = 1912 C TGHT = 474.8 A, 9.3V TBHT = 233.3 A, 4.3V IGP1 = 1.10e-06 Torr Decrease TGHT to 471.8 A OMEGA temperature went down to 1904 C Wednesday, August 07, 2019, 14:26 OMEGA = 1911 C TGHT = 471.8 A, 9.3V TBHT = 233.3 A, 4.3V IGP1 = 1.00e-06 Torr Decrease TGHT to 469.0 A OMEGA temperature down to 1904C Wednesday, August 07, 2019, 15:45 OMEGA = 1912 C TGHT = 468.8.8 A, 9.2V TBHT = 233.3 A, 4.3V IGP1 = 9.2e-07 Torr Decrease TGHT to 466.0 A OMEGA temperature down to 1903C   Wednesday, August 07, 2019, 22:09 OMEGA = 1924 C TGHT = 466.8. A, 9.3V TBHT = 233.3 A, 4.3V IGP1 = 7.6e-07 Torr Cooling at 2A/min TGHT to 456.0 A, 9.0 V and 1A/min TBHT to 230.1 A, 4.2 V OMEGA = 1900 C Will allow Pressure to stabilize    Thursday, August 08, 2019, 06:54 OMEGA = 1919 C TGHT = 456.9 A, 9.1V TBHT = 230.3 A, 4.2 V IGP1 =5.7e-07 Torr Cooling at 2A/min TGHT and 1A/min TBHT Thursday, August 08, 2019, 13:30 Target removed from Evap2.  Awaiting inspection by John.

 Monday, August 12, 2019, 15:45

Visual inspection on the target was performed today.  See attachment for details.

Target container is slightly bent, and some visible crystallization on the container surface.  

The discs are nicely packed with only a slight expansion in length was measured.

No clogging inside the container nor the ionizer tube. 

Some sintered discs samples were collected and SEM will be perform later. 

Friday, July 24, 2020, 15:00

Ta tube cotaining 497 ZrC discs wrapped with Ta heat-shields (3 layers)

Desired temperature= 1800C (expected TGHT 410 A), TBHT will be set fixed at 230A (max).

good vacuum = 3.00 e-05 Torr

bad vacuum = 5.00 e-05 Torr

Evap 2 was left to pump down over night.

Saturday, July 25, 2020, 08:57

IGP1= 8.7 e-07 Torr

Start ramp at 0.25 A/min to 20 A on TGHT 

Saturday, July 25, 2020, 10:07

IGP1= 2.7e -06 Torr

Set ramp target to 30 A 

Wednesday, July 29, 2020, 13:11 

OMEGA reading 1700 C at 430 A during the night.  It was kept at this temperature for 3.5 hours.  The OMEGA slope was not changed from 0.990

when IGP1 = 1.2 e-06 Torr and stable, cooling was started at -3A/min at 9 am on this day.

IGP1= 2.2 e-07 Torr now at time of dismounting

Saturday, November 23, 2024, 11:08

 No milling ZrC material sintering inside graphite cartridge

baseline standard discs included for comparison. 

4 Ta foils wrapped around  container

one spring at the back end to retain the graphite cartridge

One Ta cap with perforations at the front for T readings

initial heating at 2A/min to 50A, followed by heating at 1A/min to 90 A

Initial IGP1= 1.0e-6 Torr

OMEGA slope =0.990

Good and bad vacuum =5.0e-5 Torr and 5e-4 torr

Saturday, November 23, 2024, 11:20

autoramp start at 2A/min to 50A on tght

Saturday, November 23, 2024, 20:11

allowed pressure to drop to 3.3e-6 Torr after degassing. 

Started ramp to 90A at 1A/min

Saturday, November 23, 2024, 23:46

started ramping at 1.5A/120s or 0.75A/min to 400A

Sunday, November 24, 2024, 07:55

Reached 1900 C at 410 A setpoint and 402 A on RD

Pressure did not increase after bumping up to 410 setpoint so will keep at this current until 11 am (four hours near 1900 C in total)

Sunday, November 24, 2024, 10:58

Final IGP1 at start of rampdown = 2.9e-6 Torr

Ramping down at -2A/min

Tuesday, October 16, 2012, 14:12

Target is filled with 360 discs of TiC (with 1 mole of graphite) backed on C-grv foil.  

No Ta heat-shields wrapped around the container.

One regular end-cap is inserted and expanded.  The other end is inserted with a D-cap for out-gassing.

Re ionizer foil is inserted.

TGHT will be ramped up to 580A, TBHT to 230A; ramping rate at 0.2A/min.

Chamber is currently being pumped down...

 Tuesday, October 16, 2012, 16:11

HS water valve is opened.  No leaks is detected.

Vacuum is coming down steadily.  IGP1 currently at 1.7e-5 Torr.

 Wednesday, October 17, 2012, 11:41

The chamber was pumped down overnight.  IGP1 reads at 5.8e-7 Torr.

Both TGHT & TBHT were stepped up to 30A. P/S OK! 

Initiated auto-ramping...

Monday, October 22, 2012, 10:58

TGHT and TBHT have reached to 580A & 230A, respectively (see attachment#1).

IGP1 currently at 6.27e-6 Torr.  BP@20mTorr.

Currents will remain at max for another 3 hours. 

Local temperature measured at 1500C (container surface), 1300C (center block)

 Monday, October 22, 2012, 17:27

Auto cooling initiated.

 Tuesday, October 23, 2012, 17:54

TGHT & TBHT are at 0A.  P/S & pumps off. 

The chamber will be vented, and the target will be taken out for inspections.

 Friday, March 21, 2014, 16:09

Target container is loaded with 360 Discs of TiC.  

Target length = 11.7cm.  

Total green mass = 40.945g 

Container is wrapped with 3 Ta-heat shields, and have been pumped down in the chamber. 

For the sintering process: 

TGHT ramp up to 820A, and TGHT to 300A at 0.1A/min. 

Friday, March 21, 2014, 16:15

TGHT/TBHT were manually stepped up to 40A.  

Vac stabilizes at 1.7e-6 Torr.  

Initiate auto-ramping... 

John Wong wrote:

Friday, March 21, 2014, 16:09 Target container is loaded with 360 Discs of TiC.   Target length = 11.7cm.   Total green mass = 40.945g  Container is wrapped with 3 Ta-heat shields, and have been pumped down in the chamber.  For the sintering process:  TGHT ramp up to 820A, and TGHT to 300A at 0.1A/min.  Friday, March 21, 2014, 16:15 TGHT/TBHT were manually stepped up to 40A.   Vac stabilizes at 1.7e-6 Torr.   Initiate auto-ramping...

 Wednesday, March 26, 2014, 11:05

TBHT reached max desired current of 300A

IGP1 = 1.4e-6 Torr

TGHT = 543A

Increasing TGHT auto-ramp to 2.0A/min

Laura Lambert wrote:

John Wong wrote:  Friday, March 21, 2014, 16:09 Target container is loaded with 360 Discs of TiC.   Target length = 11.7cm.   Total green mass = 40.945g  Container is wrapped with 3 Ta-heat shields, and have been pumped down in the chamber.  For the sintering process:  TGHT ramp up to 820A, and TGHT to 300A at 0.1A/min.  Friday, March 21, 2014, 16:15 TGHT/TBHT were manually stepped up to 40A.   Vac stabilizes at 1.7e-6 Torr.   Initiate auto-ramping...     Wednesday, March 26, 2014, 11:05 TBHT reached max desired current of 300A IGP1 = 1.4e-6 Torr TGHT = 543A Increasing TGHT auto-ramp to 2.0A/min

 Wednesday, March 26, 2014, 18:18

TGHT has reached to 820A\13.4V and target has been heated at that current for 4.5 hours.

Vac is coming down to 1.1e-6 Torr.

See link for RGA results: https://www.dropbox.com/sh/08dcxskux21aqap/1SF_dTJB4l

Cooling down in process at 2A/min for TGHT and 1A/min for TBHT.

 Thursday, March 27, 2014, 11:14

Target is cooled down.  TGHT/TBHT have reached to 0A. 

All pumps off; chamber will be vented soon. 

 Friday, March 28, 2014, 15:00

Target has been assembled.  Heat shield WO#39956-10

Thursday, August 25, 2022, 10:06

Target container is loaded with 379 Discs of TiC for Target and 5 extra discs for analysis on left end

Target length = 12.5

3 Ta foil heatshields and on TaC coated Ta spring on right side

Total weight including heatshields and spring = 1551.4 g   Final total weight = 1545.5 g

Final power should be ~10988 Watt

TGHT ramp up to 820A, and TGHT to 300A at 0.1A/min.

IGP1= 7.7e-7 Torr

Good vacuum =3.0e-05 Torr

Bad vacuum = 5e-04 Torr

Initial TGHT and TBHT autoramped @1A/min to 50A

TBHT mas 230A

TGHT max depends on final power

Thursday, August 25, 2022, 11:17 

Start autoramp at 1A/min to 80A on both TGHT and TBHT

Thursday, August 25, 2022, 11:54 

leaving at 80A until pressure stops rising

Thursday, August 25, 2022, 22:29

left to autoramp to 230A TBHT and 750 A TGHT since approximately 2:00 pm

Will leave ramping @1A/min to 750 A on TGHT

TBHT currently at 230A

 Friday, August 26, 2022, 07:27

TGHT = 850A, 9.3V

Started autoramp to 850A at 1A/min for TGHT

TBHT held at 230A

OMEGA = 1584C

Friday, August 26, 2022, 09:34

Target running at ~820A, 13.1 V since 9

Cooling to start between 1:15 to 1:30 pm

OMEGA reads 1668 C at top current

current reading oscillates between 812A and 828A and 13.1V  to 13.2V.

Monday, August 29, 2022, 12:21

Cooling at -2A/min for TGHT and -1A/min TBHT started on time on Friday August 26th.

Target remained under vacuum after cooling, over the weekend.

Target removed this morning and looks good. 5 discs removed for analysis