Friday, October 17, 2014, 11:47

Target container was previously coated with TaC spray and sintered.

It's is wrapped with 3 layers of Ta-heat shield, including the center block.

The target consists of 255 discs of UCx with 10.5cm in length.

A regular TaC coated endcap is inserted right, wrt the ionizer tube pointing down, so the left is open with a removable half-cap to allow out-gassing.

The chamber was pumped down overnight.

TGHT will be ramped up to 520A - keep heating the current for 4-5 hours.

Parameter setup: 5.0e-5 good vac, 6.0e-5 bad vac.

Auto ramp at 0.1A/min.

 Friday, October 17, 2014, 13:25

IG1 = 2.6e-6 Torr

Manually stepped up to 35A

Waited ~1hr15

IG1 = 4.2e-6 Torr

Initiating auto-ramp.

 Tuesday, June 30, 2015, 13:28

Target container was previously coated with TaC spray and sintered.

It's is wrapped with 3 layers of Ta-heat shield, including the center block.

The target consists of 221 discs of UCx with 7.3cm in length.

A regular TaC coated endcap is inserted left, wrt the ionizer tube pointing down, so the right is open - discs are held on with Ta wire spring.

The chamber is currently pumping down.

TGHT will be ramped up to 520A at 0.1A/min

Parameter setup: 5.0e-5 good vac, 6.0e-5 bad vac.

 Tuesday, June 30, 2015, 14:43

IG1 = 1.8e-5 Torr.

Tapped up manually to 30A.

Vacuum stable; IG1 = 1.2e-5 Torr.

Initiating auto-ramp.

 Thursday, July 02, 2015, 08:41

EVAP1 was tripped off due to backflow preventer test this morning.

IG1 - 4.2e-6 Torr.

Tapping back-up manually before re-initiating auto-ramp.

 Thursday, July 02, 2015, 11:49

Tapped up manually to 85A, 0.65V

IG1 = 3.6e-6 Torr.

Initiating auto-ramp.

 Friday, July 03, 2015, 14:47

All water valves look good, flow is good.

WV turned back on, TGHT turned back on. 

Tapped back up manually to 20A.

IG1 = 2.3e-6 Torr

Initiating auto-ramp at 0.1A/min with a max setpoint of 150A over the weekend.

Will continue to ramp up monday.

Approved by Peter Kunz.

Laura Lambert wrote:

Tuesday, June 30, 2015, 13:28 Target container was previously coated with TaC spray and sintered. It's is wrapped with 3 layers of Ta-heat shield, including the center block. The target consists of 221 discs of UCx with 7.3cm in length. A regular TaC coated endcap is inserted left, wrt the ionizer tube pointing down, so the right is open - discs are held on with Ta wire spring. The chamber is currently pumping down. TGHT will be ramped up to 520A at 0.1A/min Parameter setup: 5.0e-5 good vac, 6.0e-5 bad vac.  Tuesday, June 30, 2015, 14:43 IG1 = 1.8e-5 Torr. Tapped up manually to 30A. Vacuum stable; IG1 = 1.2e-5 Torr. Initiating auto-ramp.  Thursday, July 02, 2015, 08:41 EVAP1 was tripped off due to backflow preventer test this morning. IG1 - 4.2e-6 Torr. Tapping back-up manually before re-initiating auto-ramp.  Thursday, July 02, 2015, 11:49 Tapped up manually to 85A, 0.65V IG1 = 3.6e-6 Torr. Initiating auto-ramp.

 Thursday, July 02, 2015, 12:58

NOTE:  Before venting the EVAP1 chamber, the Ar line must disconnect from Peter's sampling chamber (inside the fumehood) and connect back to the EVAP. 

John Wong wrote:

Laura Lambert wrote:  Tuesday, June 30, 2015, 13:28 Target container was previously coated with TaC spray and sintered. It's is wrapped with 3 layers of Ta-heat shield, including the center block. The target consists of 221 discs of UCx with 7.3cm in length. A regular TaC coated endcap is inserted left, wrt the ionizer tube pointing down, so the right is open - discs are held on with Ta wire spring. The chamber is currently pumping down. TGHT will be ramped up to 520A at 0.1A/min Parameter setup: 5.0e-5 good vac, 6.0e-5 bad vac.  Tuesday, June 30, 2015, 14:43 IG1 = 1.8e-5 Torr. Tapped up manually to 30A. Vacuum stable; IG1 = 1.2e-5 Torr. Initiating auto-ramp.  Thursday, July 02, 2015, 08:41 EVAP1 was tripped off due to backflow preventer test this morning. IG1 - 4.2e-6 Torr. Tapping back-up manually before re-initiating auto-ramp.  Thursday, July 02, 2015, 11:49 Tapped up manually to 85A, 0.65V IG1 = 3.6e-6 Torr. Initiating auto-ramp.    Thursday, July 02, 2015, 12:58 NOTE:  Before venting the EVAP1 chamber, the Ar line must disconnect from Peter's sampling chamber (inside the fumehood) and connect back to the EVAP.

 Friday, July 03, 2015, 13:42

water valve tripped off at ~1pm, which subsequently tripped off the TGHT [see photo]

currently trying to figure out what caused this to occur before re-starting....

 Friday, July 03, 2015, 14:47

All water valves look good, flow is good.

WV turned back on, TGHT turned back on. 

Tapped back up manually to 20A.

IG1 = 2.3e-6 Torr

Initiating auto-ramp at 0.1A/min with a max setpoint of 150A over the weekend.

Will continue to ramp up monday.

Approved by Peter Kunz.

 Monday, July 06, 2015, 09:29

TGHT reached 150A 1.5hrs ago.

Vacuum stable.

IG1 = 2.7e-5 Torr.

Re-starting auto-ramp at 0.1A/min with a max setpoint of 520A.

 Thursday, July 30, 2015, 17:10

The mixture of UO2/C was prepared on July 13, 2015.  See screen shot for more info. 

The material is loaded into a target boat and wrapped with 3 layers of Ta-heat shield. 

 Chamber is currently being pumped down

Target boat will be ramped up to 520A at the rate of 0.1A/min

Vacuum limit stop at 5.0e-5 Torr, backing off at 6.0e-5 Torr.

 Friday, July 31, 2015, 14:33

Chamber has been pumped down overnight, currently at 3.3e-6 Torr.

Manually stepping up to 35A.

Set auto ramping TGHT to 200A at 0.1A/min for over the long weekend.  This current should be safe to just burn off the organic binder but not to start the carbonization process. 

Thursday, October 15, 2015, 15:52

Target container previously sintered with TaC in Evap#2 - Target current at 440A, temp measured at 1900C.  A few tests on the temp measured were done (see Evap#2 elog #251 & 252). 
Note:  This is the new design container with a small back block.

Container is loaded with 245 discs of UC2; measured disc length 7.5 cm

A regular TaC coated endcap is inserted left, wrt the ionizer tube pointing down, so the right is open - discs are held on with Ta wire spring.

3 layers of Ta-heat shield is used. 

Target heater will be ramped up to 440A (according to the achieved temperature from Evap#2). 

Ramping rate at 0.1A/min.

Monitor closely on the vacuum around 400A to see if the carbonization process is complete. 

Chamber is currently being pumped down. 

 Friday, October 16, 2015, 10:33

Chamber has pumped down to 2e-6 Torr. 

Stepping up TGHT to 70A/0.23V. 

 Friday, October 16, 2015, 14:55

TGHT stepped up to 70A, pressure went to max 5.7e-5 Torr and it's coming down.

Initated autoramping.  (good vac at 5e-5 Torr, bad at 6.0e-5 Torr)

 Thursday, October 22, 2015, 12:26

TGHT has reached 440A/4.403V and stablized for about 5 hours. 

Pressure started coming down at around 370A which indicated the ending of the carbonization process. 

Currently vacuum is at 5.6e-6 torr. 

Initiated cooling down process at 2A/min.

 Thursday, February 18, 2016, 15:34

Target container was previously coated with TaC spray and sintered.

Container is wrapped with 3 layers of Ta-heat shield, including the center block - same method as for sintering TaC coating [new wrapping method-see elog112 eva2].

The target consists of 244 discs of UCx with 7.8cm in length.

A regular TaC coated endcap is inserted left, wrt the ionizer tube pointing down, so the right is open

The chamber is currently pumping down.

TGHT will be ramped up to 520A at 0.1A/min

Parameter setup: 5.0e-5 good vac, 6.0e-5 bad vac.

 Friday, February 19, 2016, 08:28

IG1 = 4.7e-6 Torr

Tapped up manually to 35A.

Waited ~1hr, vacuum stable

IG1 = 3.8e-6 Torr.

Initiating auto-ramp.

Laura Lambert wrote:

Thursday, February 18, 2016, 15:34 Target container was previously coated with TaC spray and sintered. Container is wrapped with 3 layers of Ta-heat shield, including the center block - same method as for sintering TaC coating [new wrapping method-see elog112 eva2]. The target consists of 244 discs of UCx with 7.8cm in length. A regular TaC coated endcap is inserted left, wrt the ionizer tube pointing down, so the right is open The chamber is currently pumping down. TGHT will be ramped up to 520A at 0.1A/min Parameter setup: 5.0e-5 good vac, 6.0e-5 bad vac.  Friday, February 19, 2016, 08:28 IG1 = 4.7e-6 Torr Tapped up manually to 35A. Waited ~1hr, vacuum stable IG1 = 3.8e-6 Torr. Initiating auto-ramp.

 Friday, February 26, 2016, 10:26

Target has been heated at 520A for 10 hrs.

Vacuum at 5.3e-6 Torr. 

Initiated cool down at 1A/min. 

Remember to vent with Ar. 

Monday, September 12, 2016, 17:30

A bunch of end caps (12?) and a long Ta-wire in spring sharp  were coated with TaC coating and wrapped in a small sheet of graphite foil. 

Container is then wrapped with a sheet of Ta heat shield.

These caps and wires will be sintered in Evap 1, so they may be prompted to contamination from the uranium processes. 

I have no choice but to use Evap1 to do this work since we are falling behind with the schedule.  

In the future, please have all the materials (targets, end caps, binder, etc) well prepared. 

I do not know what is the required current to sinter the caps since there is no temp measurement.  So, the best is to go with how the container was sintered, 580A. 

Monday, September 12, 2016, 17:36

Chamber has been pumped down to mid 10-6 Torr. 

Auto ramp to 580A at 2A/min.

 Monday, November 07, 2016, 13:29

UO2/C green was prepared Nov 3rd, 2016.

This is the first cast made with the new batch of UO2 [but from the same purchase as the last batch]

The cast peeled off the glass nicely Nov 4th, 2016 and finished drying over the weekend.

Some materials were stuck on the WC jar wall and balls, consistent with every time.

Initial UO2 powder used = 50.16g (Inventory R-01032A, UO2 + bottle = 1078.15g before use)

Graphite powder used = 10.03g

Green cast dried UO2/C + organic mass = 60.91g 

The green was rolled up and wrapped in a piece of graphite sheet.

The Ta-target boat was wrapped with 3-layers of heat shield and installed in evap1 today.

Chamber is currently pumping down, IG1 = 2.4e-5 Torr.

Target boat will be ramped up to 520A at the rate of 0.1A/min.

Vacuum limit stop at 5.0e-5 Torr, backing off at 6.0e-5 Torr.

 Tuesday, November 08, 2016, 07:43

IG1 = 2.4e-6 Torr

Tapped up to 35A, 0.50V

Waited ~50min, vacuum stable.

IG1 = 1.3e-5 Torr

Initiating auto-ramp

Laura Lambert wrote:

Monday, November 07, 2016, 13:29 UO2/C green was prepared Nov 3rd, 2016. This is the first cast made with the new batch of UO2 [but from the same purchase as the last batch] The cast peeled off the glass nicely Nov 4th, 2016 and finished drying over the weekend. Some materials were stuck on the WC jar wall and balls, consistent with every time. Initial UO2 powder used = 50.16g (Inventory R-01032A, UO2 + bottle = 1078.15g before use) Graphite powder used = 10.03g Green cast dried UO2/C + organic mass = 61.91g  The green was rolled up and wrapped in a piece of graphite sheet. The Ta-target boat was wrapped with 3-layers of heat shield and installed in evap1 today. Chamber is currently pumping down, IG1 = 2.4e-5 Torr. Target boat will be ramped up to 520A at the rate of 0.1A/min. Vacuum limit stop at 5.0e-5 Torr, backing off at 6.0e-5 Torr.  Tuesday, November 08, 2016, 07:43 IG1 = 2.4e-6 Torr Tapped up to 35A, 0.50V Waited ~50min, vacuum stable. IG1 = 1.3e-5 Torr Initiating auto-ramp

 Tuesday, November 15, 2016, 09:59

TGHT reached to 520A/5.12V; however the pressure was still remained high at the limit 5.0e-5 Torr which indicating that the carbonization process isn't complete yet.

Increase TGHT to 520A at a ramping rate of 0.1A/min.

 Tuesday, May 23, 2017, 14:42

UO2/C green was prepared May 16th, 2017.

The cast peeled off the glass nicely May 17th, 2017.

Initial UO2 powder used = 50.25g (Inventory R-01032A, UO2 + bottle = 876.80g before use)

Graphite powder used = 10.32g

Green cast dried UO2/C + organic mass = 61.70g 

The green was rolled up and wrapped in a piece of graphite sheet.

The Ta-target boat was wrapped with 1 long layer of heat shield and installed in evap1 today.

Chamber pumped down today.

Target boat will be ramped up to 520A at the rate of 0.1A/min.

Vacuum limit stop at 5.0e-5 Torr, backing off at 6.0e-5 Torr.

IG1 = 4.80e-6 Torr

Tapped up to 30A, 0.45V

Waited ~1hr, vacuum stable.

IG1 = 8.3e-6 Torr

Initiating auto-ramp

 Wednesday, May 24, 2017, 09:26

IG1 = 5.5e-5 Torr

TGHT = 64A, 0.72V

Vacuum currently yo-yo-ing.

Changing vacuum limits to attempt to speed up process.

Vacuum limit stop at 1.0e-4 Torr, backing off at 5.0e-4 Torr.

Once vacuum settles and vacuum starts to drop will adjust limits again accordingly.

 Wednesday, May 24, 2017, 11:17

IG1 = 1.2e-4 Torr

TGHT = 69A, 0.74V

TGHT direct readout = 66A, 0.73V

Thermometer attached to TP = 41.0C

Room temp = 24.0C

Wednesday, May 24, 2017, 13:16 

Vacuum going well.

Stable yo-yo-ing at current vacuum limit.

TP = 41.5C, RT = 23.9C

IG1 = 1.2e-4 Torr

TGHT = 71A, 0.77V

Increasing vacuum limit stop to 2.0e-4 Torr.

Thursday, May 25, 2017, 13:03

Vacuum has stabilized.

TGHT = 188A, 1.85V

IG1 = 2.2e-5 Torr.

Adjusting vacuum limits so when 2nd phase starts, vacuum does not spike.

Vacuum limit stop at 5.0e-5 Torr, backing off at 1.0e-4 Torr.

Laura Lambert wrote:

Laura Lambert wrote:  Tuesday, May 23, 2017, 14:42 UO2/C green was prepared May 16th, 2017. The cast peeled off the glass nicely May 17th, 2017. Initial UO2 powder used = 50.25g (Inventory R-01032A, UO2 + bottle = 876.80g before use) Graphite powder used = 10.32g Green cast dried UO2/C + organic mass = 61.70g  The green was rolled up and wrapped in a piece of graphite sheet. The Ta-target boat was wrapped with 1 long layer of heat shield and installed in evap1 today. Chamber pumped down today. Target boat will be ramped up to 520A at the rate of 0.1A/min. Vacuum limit stop at 5.0e-5 Torr, backing off at 6.0e-5 Torr. IG1 = 4.80e-6 Torr Tapped up to 30A, 0.45V Waited ~1hr, vacuum stable. IG1 = 8.3e-6 Torr Initiating auto-ramp  Wednesday, May 24, 2017, 09:26 IG1 = 5.5e-5 Torr TGHT = 64A, 0.72V Vacuum currently yo-yo-ing. Changing vacuum limits to attempt to speed up process. Vacuum limit stop at 1.0e-4 Torr, backing off at 5.0e-4 Torr. Once vacuum settles and vacuum starts to drop will adjust limits again accordingly.  Wednesday, May 24, 2017, 11:17 IG1 = 1.2e-4 Torr TGHT = 69A, 0.74V TGHT direct readout = 66A, 0.73V Thermometer attached to TP = 41.0C Room temp = 24.0C Wednesday, May 24, 2017, 13:16  Vacuum going well. Stable yo-yo-ing at current vacuum limit. TP = 41.5C, RT = 23.9C IG1 = 1.2e-4 Torr TGHT = 71A, 0.77V Increasing vacuum limit stop to 2.0e-4 Torr. Thursday, May 25, 2017, 13:03 Vacuum has stabilized. TGHT = 188A, 1.85V IG1 = 2.2e-5 Torr. Adjusting vacuum limits so when 2nd phase starts, vacuum does not spike. Vacuum limit stop at 5.0e-5 Torr, backing off at 1.0e-4 Torr.    Friday, May 26, 2017, 13:40 Everything tripped off this morning at around 4:30am This was not due to the vacuum spiking as one would expect. No power bumps according to  ISAC controls. Looking back on elogs  [see elog i.d. 145] evap1 had also tripped off during the last round of carbonizing UO2, however last time everything tripped off ~60A. For last trip off the water valve remained open and on. This time  WV1 showed yellow in the TGHT epics box, off under WV epics box, but black [open] in the WV epics box diagram [see screenshot for better understanding]. Water valves are closed - confirmed in person - water wheels not turning. Trip-off occured ~275A. Vacuum was stable at trip-off point; IG1 ~6e-6 Torr  Reason: currently unknown.

 Friday, May 26, 2017, 15:43

Starting pumping down again this afternoon while trying to understand trip-off - no progress on that end.

IG1 = 4.9e-6 Torr

Tapped up to 40A, 0.24V

Vacuum spiked to 2e-5 Torr

Backed off to 35A, 0.20V

Showing lower voltage output than the last round that had tripped off...but ramping is so early on/ low current, hard to tell...

Vacuum stable.

IG1 = 5.4e-6 Torr

Target boat will be ramped up to 275A [trip-off point] at the rate of 0.1A/min.

Vacuum limit stop at 5.0e-5 Torr, backing off at 6.0e-5 Torr.

TP = 37.9C, RT = 25.2C

 Wednesday, July 12, 2017, 17:06

Target container was previously coated with TaC and sintered.

Container is wrapped with 3 layers of Ta-heat shield, including the center block

The target consists of 400 discs of UCx with 13.60cm in length [8 packs of 5 + 360 single discs/ 2.6cm on left side, 2.8cm on right side wrt ionizer into page].

Discs in target are arranged as follows: 1pack / 60singles / 1pack / 60singles / 1pack / 60singles / 2packs / 60singles / 1pack / 60singles / 1pack / 60singles / 1pack

A regular TaC coated endcap is inserted left, wrt the ionizer tube pointing down.

The right side is open with a TaC coated spring to help hold materials in.

The chamber is currently pumping down.

TGHT will be ramped up to 450A at 0.1A/min [same current used to reach 1900C in evap2 when sintering TaC coating - elog373 evap2]

Parameter setup: 5.0e-5 good vac, 6.0e-5 bad vac.

Thursday, July 13, 2017, 12:49

Tapped up manually to 35A.

Waited ~2hrs, vacuum stable: IG1 = 2.64e-6 Torr

Initiating auto-ramp.

Laura Lambert wrote:

Laura Lambert wrote: Laura Lambert wrote:  Wednesday, July 12, 2017, 17:06 Target container was previously coated with TaC and sintered. Container is wrapped with 3 layers of Ta-heat shield, including the center block The target consists of 400 discs of UCx with 13.60cm in length [8 packs of 5 + 360 single discs/ 2.6cm on left side, 2.8cm on right side wrt ionizer into page]. Discs in target are arranged as follows: 1pack / 60singles / 1pack / 60singles / 1pack / 60singles / 2packs / 60singles / 1pack / 60singles / 1pack / 60singles / 1pack A regular TaC coated endcap is inserted left, wrt the ionizer tube pointing down. The right side is open with a TaC coated spring to help hold materials in. The chamber is currently pumping down. TGHT will be ramped up to 450A at 0.1A/min [same current used to reach 1900C in evap2 when sintering TaC coating - elog373 evap2] Parameter setup: 5.0e-5 good vac, 6.0e-5 bad vac. Thursday, July 13, 2017, 12:49 Tapped up manually to 35A. Waited ~2hrs, vacuum stable: IG1 = 2.64e-6 Torr Initiating auto-ramp.    Thursday, July 13, 2017, 14:48 Update: auto-ramp not started. With recent updates to evap1 epics, not everything was uploaded correctly. TGHT auto-ramp system not working: parameter boxes have white outline indicating locked. No parameters can be inputed and therefore unable to start auto-ramp.  Friday, July 14, 2017, 15:56 Problems still not fixed. Have tapped up manually to 50A, 0.59V Vacuum stable; IG1 = 5.26e-6 Torr. Will remain at setpoints over weekend before continuing to ramp up manually...  Monday, July 17, 2017, 15:10 New problems: Paddle wheels for evap2 need replacing asap [see elog evap2 i.d.378] In order to replace, supply/ return need to be turned off and a full purge; therefore, evap1 must be off otherwise it will trip off from no water. Evap2 needs to be fixed asap and cannot wait for this process to be complete. Evap1 had been tapped up manually to 60A. Tapping down manually to 0A so one can start the paddle wheel replacement work tomorrow.  Tuesday, July 18, 2017, 15:31 Paddle wheels for evap2 replaced and up and running again. IG1 = 1.2e-6 Torr. Starting to tap back-up manually...    Wednesday, July 19, 2017, 14:12 TGHT auto-ramp fixed. Since TBHT isn't hooked up yet, epics thinks TBHT has tripped off. Currently during auto-ramp, every time steps up: states TBHT tripped off. This is not the case but not a big deal as we will soon have TBHT hooked up and this won't be an issue. Also it only states it, doesn't stop auto-ramp and therefore technically works fine/ will go with this for now... Note: Might be a few spikes on striptool from past hour when IOC was rebooted.

 Wednesday, July 19, 2017, 14:16

Tapped up manually to 30A yesterday.

Continued manual tap up today and reached 60A.

Initiated auto-ramp.

IG1 = 4.4e-6 Torr

 Wednesday, January 10, 2018, 14:44

Circles from cast 1 were used, the same as the last round of 1stepUCx [see elog i.d. 164]

A 14mm punch was used to punch out circles from the cast.

35 circles were packed into a graphite sample container.

35 x UO2/C circles = 5.75 g

Graphite container = 5.38 g

Graphite container is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3-layers of heat shield and installed in Evap1.

Chamber currently pumping down.

Marla Cervantes wrote:

Wednesday, January 10, 2018, 14:44 Circles from cast 1 were used, the same as the last round of 1stepUCx [see elog i.d. 164] A 14mm punch was used to punch out circles from the cast. 35 circles were packed into a graphite sample container. 35 x UO2/C circles = 5.75 g Graphite container = 5.38 g Graphite container is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3-layers of heat shield and installed in Evap1. Chamber currently pumping down.

 Friday, January 12, 2018, 07:43

IGP1 = 0.0266 Torr

TGHT = 520A, 5.92V

Voltage has been climbing consistently since it has reached it's max setpoint, gone up ~0.8V in ~18hrs

Carbonization complete.

Initiating auto-cool at 2.0A/min

Will update later with more information on this process.

 Friday, January 12, 2018, 09:47

Turned the turbo pump back on, to ensure safe cooling.

 Friday, January 19, 2018, 12:29

Circles from cast 1 were used, the same as the last round of 1stepUCx [see elog i.d. 164]

A 14mm punch was used to punch out circles from the cast.

35 circles were packed into a graphite sample container.

35 x UO2/C circles = 5.69 g

Graphite container = 6.84 g

Graphite container is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3-layers of heat shield and installed in Evap1.

Chamber currently pumping down.

 Monday, January 29, 2018, 09:26

35 circles of 14 mm diameter were packed into a graphite sample container.

35 x UO2/C circles = 4.94 g

Graphite container = 5.03 g

Graphite tube is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3 new Ta foils for heat shielding and the boat was installed in Evap1.

Chamber currently pumping down.

 Wednesday, March 28, 2018, 11:35

D-shaped discs were cut from cast 2, the same as the last sample of 1stepUCx [see elog i.d. 197]

A 13mm punch was used to punch out discs from pre-cut strips using the old method.

The target consists of 195 discs with 8.1cm in length - all single discs, no packs.

195 x UO2/C discs = 19.79g

Graphite insert is placed inside a target boat with both endcaps on.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3-layers of heat shield and installed in evap1 yesterday afternoon.

Chamber pumped down overnight.

 Wednesday, March 28, 2018, 13:33

IGP1 = 4.03e-7 Torr

Tapped up TGHT manually to 80A, 0.83V - waited 50min, vacuum started to drop/stabilize.

Continued to tap up manually to 430A, 4.22V

Started out slow with a rate of ~10A/5min, and slowly increased to a rate of ~10A/min as vacuum stabilized, slowing down again when reaching carbonization outgassing.

Auto ramp at 0.2A/min from 430A-520A.

Thursday, March 29, 2018, 10:04

Reached 520A around 2am.

TGHT = 520A, 5.13V

IGP1 = 1.74e-6 Torr

Initiated auto-cool this morning at a rate of 1.0A/min.