Laura Lambert wrote:

Thursday, August 08, 2013, 15:19 NiO target materials loaded into the container yesterday. Total discs = 530, (5 discs/pack) length [after loaded] = 9.0cm Target container is wrapped with Ta-heat shields, and will be removed after sintering process. No end caps were inserted. The chamber has been pumped down and currently IG1 = 3.8x10-06 Torr. The HS cooling water was turned on and no leaks were detected. TGHT and TBHT have been stepped up to 50A. Auto-ramping setting: 0.2A/min for TGHT max = 250A, TBHT max = 230A. Good vacuum = 3.00e-05 Torr Bad vacuum = 4.00e-05 Torr **See attachment #1 for pictures of target pre-sintering

 Thursday, August 08, 2013, 17:26

Pressure is stabilizing at ~2.2e-5 Torr.  TGHT/TBHT at 50A.

Initiated auto-ramping... 

Sunday, August 11, 2013, 21:30  

TGHT/TBHT have reached to 250A/230A.  Target have been heated over the weekend.  

Cooling down initiated; 2A/min.  

The chamber wil be vented in air tomorrow. 

 Monday, August 12, 2013, 18:01

The sinterring process is complete. 

The target is ready to be removed from the evaporator, and the endcaps will be inserted.

Tuesday, September 01, 2015, 17:16

Target container contains 533 discs of SiC with packed length of 17cm. 

Mass of 533 discs SiC(green)  = 57.8979g

Total mass SiC(green) + target container = 1455g

Container is wrapped with 3 heatshields; no end caps are inserted yet.

Sintering temp at 1800C - TGHT will be set accordingly.  TBHT max at 230A. 

Chamber is currently being pumped down. 

John Wong wrote:

Tuesday, September 01, 2015, 17:16 Target container contains 533 discs of SiC with packed length of 17cm.  Mass of 533 discs SiC(green)  = 57.8979g Total mass SiC(green) + target container = 1455g Container is wrapped with 3 heatshields; no end caps are inserted yet. Sintering temp at 1800C - TGHT will be set accordingly.  TBHT max at 230A.  Chamber is currently being pumped down.

 Wednesday, September 02, 2015, 09:11

HS water valves opened, no leaks detected.

IGP1 = 1.15e-6 Torr

Tapped up manually to 40A.

Waited ~1hr40 for vacuum to stabilize.

IGP1 = 3.6e-6 Torr.

Max setpoints set to TGHT = 630A and TBHT = 230A, ~1400C

Initiating auto ramp at a rate of 0.2A/min and 0.1A/min for the TGHT and TBHT respectively.

Once max setpoints achieved, will tap up manually until window port becomes coated [as previously observed]

Once window port becomes coated will leave at set temp for ~4hrs to continue with outgassing, then cool down, clean window and ramp back up.

If LS port still clean, will continue to ramp up to final desired temperature of 1800C.

 Wednesday, September 02, 2015, 14:23

IGP1 = 4.0e-5 Torr.

Vacuum too high, stopped auto-ramp and tapped down manually.

Dropped TGHT down from 80A to 50A

Dropped TBHT down from 55A to 50A

Wednesday, September 02, 2015, 15:29

Vacuum down to IGP1 = 1.2e-5 Torr.

Re-initiating auto-ramp...

 Tuesday, September 08, 2015, 10:04

IGP1 = 4.5e-7 Torr.

TGHT = 630A, 9.6V

TBHT = 230A, 3.2V

DV = 0.22V

OMEGA RS = 1476C

OMEGA LS = 1450C

see attached photo for screenshot.

will tap up manually with a visual on both window ports...

Laura Lambert wrote:

John Wong wrote: Tuesday, September 01, 2015, 17:16 Target container contains 533 discs of SiC with packed length of 17cm.  Mass of 533 discs SiC(green)  = 57.8979g Total mass SiC(green) + target container = 1455g Container is wrapped with 3 heatshields; no end caps are inserted yet. Sintering temp at 1800C - TGHT will be set accordingly.  TBHT max at 230A.  Chamber is currently being pumped down.     Wednesday, September 02, 2015, 09:11 HS water valves opened, no leaks detected. IGP1 = 1.15e-6 Torr Tapped up manually to 40A. Waited ~1hr40 for vacuum to stabilize. IGP1 = 3.6e-6 Torr. Max setpoints set to TGHT = 630A and TBHT = 230A, ~1400C Initiating auto ramp at a rate of 0.2A/min and 0.1A/min for the TGHT and TBHT respectively. Once max setpoints achieved, will tap up manually until window port becomes coated [as previously observed] Once window port becomes coated will leave at set temp for ~4hrs to continue with outgassing, then cool down, clean window and ramp back up. If LS port still clean, will continue to ramp up to final desired temperature of 1800C.  Wednesday, September 02, 2015, 14:23 IGP1 = 4.0e-5 Torr. Vacuum too high, stopped auto-ramp and tapped down manually. Dropped TGHT down from 80A to 50A Dropped TBHT down from 55A to 50A Wednesday, September 02, 2015, 15:29 Vacuum down to IGP1 = 1.2e-5 Torr. Re-initiating auto-ramp...  Tuesday, September 08, 2015, 10:04 IGP1 = 4.5e-7 Torr. TGHT = 630A, 9.6V TBHT = 230A, 3.2V DV = 0.22V OMEGA RS = 1476C OMEGA LS = 1450C see attached photo for screenshot. will tap up manually with a visual on both window ports...

 Tuesday, September 08, 2015, 15:44

TGHT has stepped up to 820A.  Coating on both windows is becoming obvious and it's interfering the temp readers; however, the left window (see attachment, which is further away from the target) is lightly coated than the right.  See attachment for The Temp (and Power) vs current plots.

Target will remained heated at the current and will be cooled down later today. 

The target will be re-conditioned up to 820A and temp and mass will be re-measured.

Plans:

The chamber will be vented tomorrow and the target will be taken out to weigh for mass change. 

The chamber windows will need to be clean.

A piece of Ta foil will be cover in front of the ionizer to trap any loss material (if any).

 Tuesday, September 08, 2015, 17:37

TGHT was at 800A for 2 hours before ramping up 820A for another 2 hours heating.  More coating on the right window is observed and temp reading came down to 1340C.  The left window remains the same and temp reads at 1646C.  

Ramping TGHT/TBHT to 0A at 2A/min and 1A/min, respectively.  

 Wednesday, September 09, 2015, 12:27

Result after the sintering process:

No yellow crystal formed (compared to previously observed SiC targets that heated up above 1900C). 

Total green mass = 57.90g 

mass of graphite foil = 0.035g x 533 discs = 18.7g 

mass of green SiC = 39.30g 

Target container with SiC before sintered = 1455g 

Target container after sintered = 1450g 

mass loss ~ 5.0g ~ 13% organic mass, as expected!  

The target will undergo the re-condition stage, and the temperature will be measured from 600A to 820A. 

John Wong wrote:

Laura Lambert wrote: John Wong wrote: Tuesday, September 01, 2015, 17:16 Target container contains 533 discs of SiC with packed length of 17cm.  Mass of 533 discs SiC(green)  = 57.8979g Total mass SiC(green) + target container = 1455g Container is wrapped with 3 heatshields; no end caps are inserted yet. Sintering temp at 1800C - TGHT will be set accordingly.  TBHT max at 230A.  Chamber is currently being pumped down.     Wednesday, September 02, 2015, 09:11 HS water valves opened, no leaks detected. IGP1 = 1.15e-6 Torr Tapped up manually to 40A. Waited ~1hr40 for vacuum to stabilize. IGP1 = 3.6e-6 Torr. Max setpoints set to TGHT = 630A and TBHT = 230A, ~1400C Initiating auto ramp at a rate of 0.2A/min and 0.1A/min for the TGHT and TBHT respectively. Once max setpoints achieved, will tap up manually until window port becomes coated [as previously observed] Once window port becomes coated will leave at set temp for ~4hrs to continue with outgassing, then cool down, clean window and ramp back up. If LS port still clean, will continue to ramp up to final desired temperature of 1800C.  Wednesday, September 02, 2015, 14:23 IGP1 = 4.0e-5 Torr. Vacuum too high, stopped auto-ramp and tapped down manually. Dropped TGHT down from 80A to 50A Dropped TBHT down from 55A to 50A Wednesday, September 02, 2015, 15:29 Vacuum down to IGP1 = 1.2e-5 Torr. Re-initiating auto-ramp...  Tuesday, September 08, 2015, 10:04 IGP1 = 4.5e-7 Torr. TGHT = 630A, 9.6V TBHT = 230A, 3.2V DV = 0.22V OMEGA RS = 1476C OMEGA LS = 1450C see attached photo for screenshot. will tap up manually with a visual on both window ports...    Tuesday, September 08, 2015, 15:44 TGHT has stepped up to 820A.  Coating on both windows is becoming obvious and it's interfering the temp readers; however, the left window (see attachment, which is further away from the target) is lightly coated than the right.  See attachment for The Temp (and Power) vs current plots. Target will remained heated at the current and will be cooled down later today.    The target will be re-conditioned up to 820A and temp and mass will be re-measured. Plans: The chamber will be vented tomorrow and the target will be taken out to weigh for mass change.  The chamber windows will need to be clean. A piece of Ta foil will be cover in front of the ionizer to trap any loss material (if any).  Tuesday, September 08, 2015, 17:37 TGHT was at 800A for 2 hours before ramping up 820A for another 2 hours heating.  More coating on the right window is observed and temp reading came down to 1340C.  The left window remains the same and temp reads at 1646C.   Ramping TGHT/TBHT to 0A at 2A/min and 1A/min, respectively.    Wednesday, September 09, 2015, 12:27 Result after the sintering process: No yellow crystal formed (compared to previously observed SiC targets that heated up above 1900C).  Total green mass = 57.90g  mass of graphite foil = 0.035g x 533 discs = 18.7g  mass of green SiC = 39.30g  Target container with SiC before sintered = 1455g  Target container after sintered = 1450g  mass loss ~ 5.0g ~ 13% organic mass, as expected!   The target will undergo the re-condition stage, and the temperature will be measured from 600A to 820A.

 Wednesday, September 09, 2015, 17:39

Both end-caps are inserted onto the targets.  The total mass (Target, Sintered SiC, end caps, 4x 19"round graphite foils) = 1453g.

Target is wrapped with 3 layers of heat shields.  

The extraction electrode is wrapped with Ta-foil (see attachment).  This is to trap any lose particle, if any.  

Chamber is currently being pumped down, currently at 1.2e-5 Torr.  

John Wong wrote:

John Wong wrote: Laura Lambert wrote: John Wong wrote: Tuesday, September 01, 2015, 17:16 Target container contains 533 discs of SiC with packed length of 17cm.  Mass of 533 discs SiC(green)  = 57.8979g Total mass SiC(green) + target container = 1455g Container is wrapped with 3 heatshields; no end caps are inserted yet. Sintering temp at 1800C - TGHT will be set accordingly.  TBHT max at 230A.  Chamber is currently being pumped down.     Wednesday, September 02, 2015, 09:11 HS water valves opened, no leaks detected. IGP1 = 1.15e-6 Torr Tapped up manually to 40A. Waited ~1hr40 for vacuum to stabilize. IGP1 = 3.6e-6 Torr. Max setpoints set to TGHT = 630A and TBHT = 230A, ~1400C Initiating auto ramp at a rate of 0.2A/min and 0.1A/min for the TGHT and TBHT respectively. Once max setpoints achieved, will tap up manually until window port becomes coated [as previously observed] Once window port becomes coated will leave at set temp for ~4hrs to continue with outgassing, then cool down, clean window and ramp back up. If LS port still clean, will continue to ramp up to final desired temperature of 1800C.  Wednesday, September 02, 2015, 14:23 IGP1 = 4.0e-5 Torr. Vacuum too high, stopped auto-ramp and tapped down manually. Dropped TGHT down from 80A to 50A Dropped TBHT down from 55A to 50A Wednesday, September 02, 2015, 15:29 Vacuum down to IGP1 = 1.2e-5 Torr. Re-initiating auto-ramp...  Tuesday, September 08, 2015, 10:04 IGP1 = 4.5e-7 Torr. TGHT = 630A, 9.6V TBHT = 230A, 3.2V DV = 0.22V OMEGA RS = 1476C OMEGA LS = 1450C see attached photo for screenshot. will tap up manually with a visual on both window ports...    Tuesday, September 08, 2015, 15:44 TGHT has stepped up to 820A.  Coating on both windows is becoming obvious and it's interfering the temp readers; however, the left window (see attachment, which is further away from the target) is lightly coated than the right.  See attachment for The Temp (and Power) vs current plots. Target will remained heated at the current and will be cooled down later today.    The target will be re-conditioned up to 820A and temp and mass will be re-measured. Plans: The chamber will be vented tomorrow and the target will be taken out to weigh for mass change.  The chamber windows will need to be clean. A piece of Ta foil will be cover in front of the ionizer to trap any loss material (if any).  Tuesday, September 08, 2015, 17:37 TGHT was at 800A for 2 hours before ramping up 820A for another 2 hours heating.  More coating on the right window is observed and temp reading came down to 1340C.  The left window remains the same and temp reads at 1646C.   Ramping TGHT/TBHT to 0A at 2A/min and 1A/min, respectively.    Wednesday, September 09, 2015, 12:27 Result after the sintering process: No yellow crystal formed (compared to previously observed SiC targets that heated up above 1900C).  Total green mass = 57.90g  mass of graphite foil = 0.035g x 533 discs = 18.7g  mass of green SiC = 39.30g  Target container with SiC before sintered = 1455g  Target container after sintered = 1450g  mass loss ~ 5.0g ~ 13% organic mass, as expected!   The target will undergo the re-condition stage, and the temperature will be measured from 600A to 820A.     Wednesday, September 09, 2015, 17:39 Both end-caps are inserted onto the targets.  The total mass (Target, Sintered SiC, end caps, 4x 19"round graphite foils) = 1453g. Target is wrapped with 3 layers of heat shields.   The extraction electrode is wrapped with Ta-foil (see attachment).  This is to trap any lose particle, if any.   Chamber is currently being pumped down, currently at 1.2e-5 Torr.

 Thursday, September 10, 2015, 09:55

HS water valves opened this morning, no leaks detected.

TGHT and TBHT tapped up manually to 35A.

IGP1 = 4.4e-7 Torr, vacuum stable.

Initiating auto-ramp at 1.0A/min and 0.5A/min for the TGHT and TBHT respectively with final setpoints of 600A and 230A.

Laura Lambert wrote:

John Wong wrote: John Wong wrote: Laura Lambert wrote: John Wong wrote: Tuesday, September 01, 2015, 17:16 Target container contains 533 discs of SiC with packed length of 17cm.  Mass of 533 discs SiC(green)  = 57.8979g Total mass SiC(green) + target container = 1455g Container is wrapped with 3 heatshields; no end caps are inserted yet. Sintering temp at 1800C - TGHT will be set accordingly.  TBHT max at 230A.  Chamber is currently being pumped down.     Wednesday, September 02, 2015, 09:11 HS water valves opened, no leaks detected. IGP1 = 1.15e-6 Torr Tapped up manually to 40A. Waited ~1hr40 for vacuum to stabilize. IGP1 = 3.6e-6 Torr. Max setpoints set to TGHT = 630A and TBHT = 230A, ~1400C Initiating auto ramp at a rate of 0.2A/min and 0.1A/min for the TGHT and TBHT respectively. Once max setpoints achieved, will tap up manually until window port becomes coated [as previously observed] Once window port becomes coated will leave at set temp for ~4hrs to continue with outgassing, then cool down, clean window and ramp back up. If LS port still clean, will continue to ramp up to final desired temperature of 1800C.  Wednesday, September 02, 2015, 14:23 IGP1 = 4.0e-5 Torr. Vacuum too high, stopped auto-ramp and tapped down manually. Dropped TGHT down from 80A to 50A Dropped TBHT down from 55A to 50A Wednesday, September 02, 2015, 15:29 Vacuum down to IGP1 = 1.2e-5 Torr. Re-initiating auto-ramp...  Tuesday, September 08, 2015, 10:04 IGP1 = 4.5e-7 Torr. TGHT = 630A, 9.6V TBHT = 230A, 3.2V DV = 0.22V OMEGA RS = 1476C OMEGA LS = 1450C see attached photo for screenshot. will tap up manually with a visual on both window ports...    Tuesday, September 08, 2015, 15:44 TGHT has stepped up to 820A.  Coating on both windows is becoming obvious and it's interfering the temp readers; however, the left window (see attachment, which is further away from the target) is lightly coated than the right.  See attachment for The Temp (and Power) vs current plots. Target will remained heated at the current and will be cooled down later today.    The target will be re-conditioned up to 820A and temp and mass will be re-measured. Plans: The chamber will be vented tomorrow and the target will be taken out to weigh for mass change.  The chamber windows will need to be clean. A piece of Ta foil will be cover in front of the ionizer to trap any loss material (if any).  Tuesday, September 08, 2015, 17:37 TGHT was at 800A for 2 hours before ramping up 820A for another 2 hours heating.  More coating on the right window is observed and temp reading came down to 1340C.  The left window remains the same and temp reads at 1646C.   Ramping TGHT/TBHT to 0A at 2A/min and 1A/min, respectively.    Wednesday, September 09, 2015, 12:27 Result after the sintering process: No yellow crystal formed (compared to previously observed SiC targets that heated up above 1900C).  Total green mass = 57.90g  mass of graphite foil = 0.035g x 533 discs = 18.7g  mass of green SiC = 39.30g  Target container with SiC before sintered = 1455g  Target container after sintered = 1450g  mass loss ~ 5.0g ~ 13% organic mass, as expected!   The target will undergo the re-condition stage, and the temperature will be measured from 600A to 820A.     Wednesday, September 09, 2015, 17:39 Both end-caps are inserted onto the targets.  The total mass (Target, Sintered SiC, end caps, 4x 19"round graphite foils) = 1453g. Target is wrapped with 3 layers of heat shields.   The extraction electrode is wrapped with Ta-foil (see attachment).  This is to trap any lose particle, if any.   Chamber is currently being pumped down, currently at 1.2e-5 Torr.      Thursday, September 10, 2015, 09:55 HS water valves opened this morning, no leaks detected. TGHT and TBHT tapped up manually to 35A. IGP1 = 4.4e-7 Torr, vacuum stable. Initiating auto-ramp at 1.0A/min and 0.5A/min for the TGHT and TBHT respectively with final setpoints of 600A and 230A.

Thursday, September 10, 2015, 12:05  

Changed TGHT to 2A/min and TGHT remains at 1A/min.  Vacuum is table at 1.0e-6 Torr. 

Friday, September 11, 2015, 11:34  

TGHT was at 600A for almost 20 hours.  Vac at 5.2 e-7 Torr.   L-temp at 1490C, R-temp at 1685 (odd?).   Using pyrometer to measure - Right end does seem brighter than the L end.  

Continue to ramp up TGHT.  Date is collected, will be posted later.  

 Friday, September 11, 2015, 11:53

L/R-temp measurements just don't seem normal.  

Ramped up to 220A- temp reads L = 1522C, R = 1722C.  

Ramping down TBHT doesn't change the temp.  

Will cool TGHT/TBHT to 0A at 2A/min & 1A/min, respectively.  

Will vent the chamber on Monday and inspect for any wrong.

 Monday, September 14, 2015, 12:13

The target has taken out for inspection.  No visible damage/problem was observed.  The Ta-foil for loss particle capture only showed some heat marking but no material was trapped. 

Target was weighted, no mass loss was observed.

Try expending the end caps to get a good thermal conductivity and will re-conditiong again.  

 Tuesday, September 15, 2015, 12:31

The end caps have been expended. 

New Ta foils are used for the heat shields.  The foils are cut in 3 1/4" x 12" and wrapped around the target.  (see attachment).  This is to see if the heat is evenly distributed.  

Both omega optical lens are aligned properly.  

Target is installed but the chamber is NOT yet being pumped down.  Awaiting for the fume hood work in B2 level to be complete before the evaporator can be started. 

 Wednesday, September 16, 2015, 17:57

The work in the B2 level is done; the nuclear ventilation for the evaporators is now operational. 

Chamber is currently being pumped down.

 Thursday, September 17, 2015, 12:19

Chamber has been pump down overnight and pressure is currently at 5.8e-7 Torr.

HS valves are opened and no leaks are detected.

Ramping up TGHT/TBHT to 600A at 2A/min and 230A at 1A/min, respectively.

 Thursday, September 17, 2015, 17:58

TGHT has reached to 600A/9.14V.  Both the L and R temperatures are measured at 1710C and 1760C, respectively.  At 600A, the temperature now is about 300C higher compared to that during the sintering process. 

The difference in the temperature could be from Ta surface vs SiC surface.  (But the 2-color IR temp reader shouldn't matter what color it's measuring?!! I don't know!)

Note: 

Both temperature readings are fairly close.  Could this be improved from the new Ta-foils?  Possible!

It is still unclear what is the absolute temperature.  A more systematic student needs to be done. 

Using a thermocouple couple to measurement the endcaps at 600A and compared with the Omage reader may help to understand more. 

After discussing with Friedhelm, it is decided to stay the target at 600A for the conditioning process. 

 Friday, September 18, 2015, 09:10

Target has been heated at 600A at stable temperature at 1716C (LS) and 1769C (RS), see attachment. 

 Friday, September 18, 2015, 11:45

Initiated cooling down at 2A/min for TGHT, and 1A/min TBHT. 

Currently vac at 5.48e-7 Torr.

 Thursday, September 24, 2015, 11:31

Target was inspected after the 2nd conditioning, up to 1700C at 600A for overnight. 

No solid particle was observed that might have extracted from the ionizer tube.  

The heat shields have been removed and the target is ready for assembly. 

 Friday, December 16, 2016, 14:08

Target consists of 470 discs.

Total packed length 3.4cm [exactly 7.8cm space on both sides]

Total mass 45.9091g [Incl foils + Ta wire on 6 packs]

Target consists of 350 single discs and 6x20 packs of Ta discs

Discs in target are arranged as follows: 1pack / 75singles / 1pack / 100singles / 2packs / 100singles / 1pack / 75singles / 1pack

3x Ta Heat shields.

LP-FEBIAD container with large center block.

No endcaps inserted, no Rh foil inserted.

Chamber currently pumping down.

TBHT will be ramped up to 230A at 1.0A/min.

TGHT will be ramped up to 350A at 2.0A/min.

Final desired temperature = 1900C

 Friday, December 16, 2016, 14:32

 Monday, December 19, 2016, 11:52

Tapped up manually to ~1900C [see attached excel for details on data collected - interesting temperature fluctuations]

 Will remain at max setpoints for min 4hrs then auto-cool

 Monday, December 19, 2016, 15:20

Target has remained at max setpoints for just over 4hrs

TGHT = 520A, 8.67V

OMEGA = 1820C

IGP1 = 5.2e-7 Torr

Initiating auto-cool at 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.

 Tuesday, December 20, 2016, 11:52

Vented in air and opened up this morning.

Looks like the windows was coated in evap2, unsure if this was missed and coated before conditioning target or if this is from materials coming out during conditioning process...

Target looks good.

Endcaps inserted but not expanded.

 Wednesday, November 29, 2017, 16:17

LP-FEBIAD loaded into evap2 today and currently pumping down.

Temperature measurements of the ionizer will be done by Fernando for ARIEL development.

Ta foil covering side holes on heat shield so no temp measurements can be done using OMEGA on side ports of evaporator as per request of Fernando

No Ta heat shields on container.

Final desired temperature of ionizer = 2000C

 Thursday, November 30, 2017, 09:51

HS water valves opened, no leaks detected.

IGP1 = 2.1e-7 Torr

IGP2 = 1.7e-7 Torr

Tapped up to TGHT = 350A, 5.83V; TBHT = 230A, 3.31V

IGP1 = 6.3e-7 Torr

IGP2 = 3.7e-7 Torr

Will check temp measurements in lab after lunch before proceeding...

 Friday, December 01, 2017, 11:04

Temperature measurements done.

Initiated auto-cool this morning.

TGHT cooling at 2.0A/min and TBHT at 1.0A/min.

Monday, December 04, 2017, 11:04

Removed from evap2 this morning.

 Wednesday, December 13, 2017, 10:36

LP-FEBIAD loaded into evap2 this morning and pumped down.

Temperature measurements of the ionizer will be done by Fernando for ARIEL development.

Ta foil covering side holes on heat shield so no temp measurements can be done using OMEGA on side ports of evaporator as per request of Fernando

No Ta heat shields on container.

HS water valves opened, no leaks detected.

IGP1 = 2.3e-6 Torr

IGP2 = 1.7e-6 Torr

Tapped up to TGHT = 50A, 0.30V; TBHT = 50A, 0.59V

IGP1 = 1.8e-6 Torr

IGP2 = 1.4e-6 Torr

Initiating auto ramp for TGHT at 2.0A/min up to 350A and TBHT at 1.0A/min up to 210A

 Wednesday, December 13, 2017, 14:53

IGP1 = 7.6e-7 Torr

IGP2 = 6.4e-7 Torr

TGHT = 350A, 5.85V

TBHT = 210A, 3.02V

TGHT and TBHT will be adjusted accordingly for temperature measurements...

Thursday, December 14, 2017, 09:16 

IGP1 = 2.1e-7 Torr

IGP2 = 1.7e-7 Torr

TGHT = 385A, 6.80V

TBHT = 210A, 3.01V

Tapped up to TGHT = 400A, 7.11V

Stopped for temperature measurements.

Tapped up to TGHT = 450A, 8.20V

 Friday, December 15, 2017, 09:50

IGP1 = 1.2e-7 Torr

IGP2 = 9.6e-8 Torr

TGHT = 350A, 5.82V

TBHT = 210A, 2.94V

Initiating auto-ramp to TGHT = 650A

Monday, December 18, 2017, 10:43

Temperature measurements done.

Initiated auto-cool.

TGHT cooling at 2.0A/min and TBHT at 1.0A/min.

 Tuesday, December 19, 2017, 11:40

Vented in air and removed from evap2 today.

Monday, February 19, 2018, 13:39

LP-FEBIAD loaded into evap2 this morning and pumped down.

Temperature measurements of the ionizer will be done by Fernando for ARIEL development.

Ta foil covering side holes on heat shield so no temp measurements can be done using OMEGA on side ports of evaporator as per request of Fernando

No Ta heat shields on container.

HS water valves opened, no leaks detected.

IGP1 = 2.75e-6 Torr

IGP2 = 1.42e-6 Torr

Tapped up to TGHT = 50A, 0.53V; TBHT = 50A, 0.56V

IGP1 = 2.64e-6 Torr

IGP2 = 1.35e-6 Torr

Initiating auto ramp for TGHT at 2.0A/min up to 350A and TBHT at 1.0A/min up to 210A

 Tuesday, February 20, 2018, 09:15

IGP1 = 6.9e-7 Torr

IGP2 = 3.8e-7 Torr

TGHT = 350A, 5.98V

TBHT = 210A, 3.02V

TGHT and TBHT will be adjusted accordingly for temperature measurements...

 Tuesday, February 27, 2018, 14:55

Temperature measurements done.

Initiated auto-cool.

TGHT cooling at 2.0A/min and TBHT at 1.0A/min.

 Wednesday, February 28, 2018, 10:39

Tuesday, December 19, 2017, 11:40

Vented in air and removed from evap2 today.

 Friday, March 09, 2018, 11:03

LP-FEBIAD loaded into evap2 and pumped down.

Temperature measurements of the ionizer will be done by Fernando for ARIEL development.

Ta foil covering side holes on heat shield so no temp measurements can be done using OMEGA on side ports of evaporator as per request of Fernando

No Ta heat shields on container.

HS water valves opened, no leaks detected.

Tapped up to TGHT = 50 A, 0.54 V; TBHT = 50 A, 0.45 V

IGP1 = 1.8e-6 Torr

IGP2 = 1.4e-6 Torr

Initiating auto ramp for TGHT at 2.0A/min up to 310A and TBHT at 1.0A/min up to 210A

Monday, March 12, 2018, 10:16 

IGP1 = 8.8e-8 Torr

IGP2 = 6.6e-8 Torr

TGHT = 310A, 5.06V

TBHT = 210A, 2.98 V

TGHT and TBHT will be adjusted accordingly for temperature measurements

Tuesday, March 13, 2018, 16:00 

Temperature measurements done.

Initiated auto-cool.

TGHT cooling at 2.0A/min and TBHT at 1.0A/min.

Wednesday, March 14, 2018, 16:03

Removed from evap2.

 Wednesday, November 19, 2014, 15:10

currently pumping down

 Wednesday, November 19, 2014, 15:28

container is wrapped with 3 x Ta-heat shield

leak check done

Starting voltage = -0.017mV

TGHT = 0A, 0V

TBHT = 0A, 0V

IGP1 = 1.7e-6 Torr

 Wednesday, November 19, 2014, 16:33

Tapped TGHT up manually to 100A

DV [direct voltage] = 0.33V

TGHT = 109A

TBHT = 0A

IGP1 = 1.3e-6 Torr

Initiating auto-ramp of TGHT to 400A at 2A/min

 Thursday, November 20, 2014, 09:49

DV = 3.47V

OMEGA = 1645C

TGHT = 401A, 6.49V

TBHT = 0

IGP1 = 4.5e-7Torr

TGHT finished auto-ramping ~19:00 last night

initiating manual tap up to 2000 celsius or 580A [whichever is higher] and recording activity

 Friday, November 21, 2014, 12:50

TGHT was ramped up to 580A yesterday and left overnight.

In the picture attached one can see the TGHT current has remained constant at 578A [red = TGHT current, green = TGHT voltage]

The vacuum has slowly gone down as expected.

However, the DV, TGHT voltage and temperature have deviated. They have dipped up and down several times throughout the night. The first deviation was observed ~3.5hours after it reached its target of 580A.

DV reached 6.02V [when TGHT initially hit 580A] and increased to 6.27V after 3.5hrs and is currently sitting at 5.94V

OMEGA reached 2111C [when TGHT initially hit 580A] and increased to 2154C after 3.5 hrs and is currently sitting at 2094C

TGHT voltage reached 10.4V [when TGHT initially hit 580A] and increased to 10.6V after 3.5hrs and is currently sitting at 10.3V

 Friday, November 21, 2014, 17:59

EVAP2 sat at max setting: TGHT = 580A and TBHT = 230A for ~4hours

Initiating auto-cool TGHT 2A/min, TBHT 1A/min

 Monday, November 24, 2014, 14:28

Vented and opened this morning.

No notable changes on target container.

[See attachments for more detailed information of results]

 Tuesday, January 31, 2017, 13:43

Container coated with TaC using new method: Ends taped off,  with liquid poured in and swirled around entire container, then poured back out - 'flushing technique'

Container is wrapped with 3 x Ta heat shields, not incl center block.

Loaded into EVAP2 and currently pumping down.

Tuesday, January 31, 2017, 16:02 

IGP1 = 3.9e-6 Torr.

HS water valves opened.

No leaks detected.

Tapped up manually to 35A.

Vacuum stable.

Initiated auto ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively.

Final setpoints for TGHT = 450A and TBHT = 230A, with final desired temp of 1900C

OMEGA slope = 0.98

 Wednesday, February 01, 2017, 10:01

IGP1 = 5.7e-7 Torr.

TGHT = 254A, 3.0V

TBHT = 142A, 1.8V

Increasing ramping rate to 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.

 Wednesday, February 01, 2017, 11:48

IGP1 = 1.7e-6 Torr.

TGHT = 450A, 6.27V

TBHT = 230A, 3.14V

OMEGA = 1176C

Increasing max setpoint of TGHT = 600A

 Wednesday, February 01, 2017, 13:09

IGP1 = 3.7e-6 Torr.

TGHT = 600A, 9.0V

TBHT = 230A, 3.18V

OMEGA = 1480C

Increasing max setpoint of TGHT = 700A

 Wednesday, February 01, 2017, 14:08

IGP1 = 3.8e-6 Torr.

TGHT = 700A, 10.96V

TBHT = 230A, 3.2V

OMEGA = 1705C

Increasing max setpoint of TGHT = 750A

 Wednesday, February 01, 2017, 15:02

IGP1 = 5.1e-6 Torr.

TGHT = 750A, 11.87V

TBHT = 230A, 3.2V

OMEGA = 1808C

Increasing max setpoint of TGHT = 800A

 Wednesday, February 01, 2017, 15:30

IGP1 = 6.6e-6 Torr.

TGHT = 800A, 12.86V

TBHT = 230A, 3.2V

OMEGA = 1903C

Will remain at max setpoints overnight.

 Thursday, February 02, 2017, 09:16

Remained at max setpoints for ~18hrs.

IGP1 = 9.5e-7 Torr.

OMEGA =1914C

TGHT = 800A, 12.83V

TBHT = 230A, 3.22V

Initiating auto-cool at 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.

 Friday, February 03, 2017, 14:24

Vented in air and opened up this morning

Coating looks good.

See photos attached.

 Thursday, April 27, 2017, 14:01

Target container contains 470 discs of SiC 

Target packed length = 16cm. 

Mass of SiC(green)  = 52.13g

Discs in target are arranged as follows: 5singles / 1pack / 65singles / 1pack / 75singles / 1pack / 75singles / 2packs / 75singles / 1pack / 75singles / 1pack / 55singles / 1pack / 5singles

Container is wrapped with 1x heatshield around each side of cooling fins; no end caps are inserted yet - coated spring inserted both sides to hold discs in place.

Sintering temp = 1800C

Chamber is currently being pumped down. 

Friday, April 28, 2017, 13:06

HS water valves turned on this morning, no leaks detected.

Tapped up manually to 40A

Waited ~3hrs , vacuum stable.

IGP1 = 4.13e-6 Torr

Initiating auto-ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively.

TGHT max = 400A.  TBHT max at 230A. 

Slope on OMEGA = 1.08 [see elog i.d. # 326 for reasoning behind OMEGA slope choice]

 Tuesday, May 02, 2017, 09:24

IGP1 = 2.34e-6 Torr

TBHT = 230A, 3.15V

TGHT = 298A, 3.96V

OMEGA = 1030C

Vacuum stable, increasing ramping rate up to 0.5A/min

 Tuesday, May 02, 2017, 13:20

IGP1 = 1.3e-5 Torr

TGHT = 400A, 5.6V

OMEGA = 1175C

Increasing max setpoint to 500A

Laura Lambert wrote:

Thursday, April 27, 2017, 14:01 Target container contains 470 discs of SiC  Target packed length = 16cm.  Mass of SiC(green)  = 52.13g Discs in target are arranged as follows: 5singles / 1pack / 65singles / 1pack / 75singles / 1pack / 75singles / 2packs / 75singles / 1pack / 75singles / 1pack / 55singles / 1pack / 5singles Container is wrapped with 1x heatshield around each side of cooling fins; no end caps are inserted yet - coated spring inserted both sides to hold discs in place. Sintering temp = 1800C Chamber is currently being pumped down.  Friday, April 28, 2017, 13:06 HS water valves turned on this morning, no leaks detected. Tapped up manually to 40A Waited ~3hrs , vacuum stable. IGP1 = 4.13e-6 Torr Initiating auto-ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively. TGHT max = 400A.  TBHT max at 230A.  Slope on OMEGA = 1.08 [see elog i.d. # 326 for reasoning behind OMEGA slope choice]  Tuesday, May 02, 2017, 09:24 IGP1 = 2.34e-6 Torr TBHT = 230A, 3.15V TGHT = 298A, 3.96V OMEGA = 1030C Vacuum stable, increasing ramping rate up to 0.5A/min  Tuesday, May 02, 2017, 13:20 IGP1 = 1.3e-5 Torr TGHT = 400A, 5.6V OMEGA = 1175C Increasing max setpoint to 500A

  Wednesday, May 03, 2017, 13:33

TGHT had remained at 500A for 16hrs, vacuum had initially come down nicely.

Vacuum was starting to creep up when i came in this morning before 8am,  IGP1 was at 1.2e-5 Torr

TGHT = 500A, 7.77V

OMEGA = 1440C

Around 8:30 vacuum started to spike, so the TGHT was tapped down rapidly to 450A

Tapping the TGHT down made no difference to the vacuum.

By the time 450A was hit, it was too late and the spike in vacuum caused the evaporator to trip off.

Turbo pump in epics showed on, turbo pump showed on according to TP direct controls.

Everything was shut off and the venting tapped, this made it obvious the turbo pump was already off as there was no ramping down noises from the turbo pump.

TP control box turned off then on again, at this point the controls showed a 'fail' message.

Turns out the turbo pump control box was fried and that's what had caused the turbo pump to fail with no notice in epics causing the vacuum to spontaneously spike.

Waiting on a new one from vacuum group...

See photos attached of striptool screenshots.

 Wednesday, May 03, 2017, 15:03

New TP control boxed installed.

Turbo pump turned on, everything pumped down.

Vacuum good, IGP1 = 6.92e-7 Torr.

IGP2 still not working, won't turn on via epics.

Tried unplugging and plugging back in...still appears red with 'fail' message...

Laura Lambert wrote:

Laura Lambert wrote:  Thursday, April 27, 2017, 14:01 Target container contains 470 discs of SiC  Target packed length = 16cm.  Mass of SiC(green)  = 52.13g Discs in target are arranged as follows: 5singles / 1pack / 65singles / 1pack / 75singles / 1pack / 75singles / 2packs / 75singles / 1pack / 75singles / 1pack / 55singles / 1pack / 5singles Container is wrapped with 1x heatshield around each side of cooling fins; no end caps are inserted yet - coated spring inserted both sides to hold discs in place. Sintering temp = 1800C Chamber is currently being pumped down.  Friday, April 28, 2017, 13:06 HS water valves turned on this morning, no leaks detected. Tapped up manually to 40A Waited ~3hrs , vacuum stable. IGP1 = 4.13e-6 Torr Initiating auto-ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively. TGHT max = 400A.  TBHT max at 230A.  Slope on OMEGA = 1.08 [see elog i.d. # 326 for reasoning behind OMEGA slope choice]  Tuesday, May 02, 2017, 09:24 IGP1 = 2.34e-6 Torr TBHT = 230A, 3.15V TGHT = 298A, 3.96V OMEGA = 1030C Vacuum stable, increasing ramping rate up to 0.5A/min  Tuesday, May 02, 2017, 13:20 IGP1 = 1.3e-5 Torr TGHT = 400A, 5.6V OMEGA = 1175C Increasing max setpoint to 500A     Wednesday, May 03, 2017, 13:33 TGHT had remained at 500A for 16hrs, vacuum had initially come down nicely. Vacuum was starting to creep up when i came in this morning before 8am,  IGP1 was at 1.2e-5 Torr TGHT = 500A, 7.77V OMEGA = 1440C Around 8:30 vacuum started to spike, so the TGHT was tapped down rapidly to 450A Tapping the TGHT down made no difference to the vacuum. By the time 450A was hit, it was too late and the spike in vacuum caused the evaporator to trip off. Turbo pump in epics showed on, turbo pump showed on according to TP direct controls. Everything was shut off and the venting tapped, this made it obvious the turbo pump was already off as there was no ramping down noises from the turbo pump. TP control box turned off then on again, at this point the controls showed a 'fail' message. Turns out the turbo pump control box was fried and that's what had caused the turbo pump to fail with no notice in epics causing the vacuum to spontaneously spike. Waiting on a new one from vacuum group... See photos attached of striptool screenshots.  Wednesday, May 03, 2017, 15:03 New TP control boxed installed. Turbo pump turned on, everything pumped down. Vacuum good, IGP1 = 6.92e-7 Torr. IGP2 still not working, won't turn on via epics. Tried unplugging and plugging back in...still appears red with 'fail' message...

 Wednesday, May 03, 2017, 16:07

Unplugging and plugging back in seemed to work now that evap2 under vacuum

IGP2 works again.

Will look into replacement ion gauge...

Laura Lambert wrote:

Laura Lambert wrote: Laura Lambert wrote:  Thursday, April 27, 2017, 14:01 Target container contains 470 discs of SiC  Target packed length = 16cm.  Mass of SiC(green)  = 52.13g Discs in target are arranged as follows: 5singles / 1pack / 65singles / 1pack / 75singles / 1pack / 75singles / 2packs / 75singles / 1pack / 75singles / 1pack / 55singles / 1pack / 5singles Container is wrapped with 1x heatshield around each side of cooling fins; no end caps are inserted yet - coated spring inserted both sides to hold discs in place. Sintering temp = 1800C Chamber is currently being pumped down.  Friday, April 28, 2017, 13:06 HS water valves turned on this morning, no leaks detected. Tapped up manually to 40A Waited ~3hrs , vacuum stable. IGP1 = 4.13e-6 Torr Initiating auto-ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively. TGHT max = 400A.  TBHT max at 230A.  Slope on OMEGA = 1.08 [see elog i.d. # 326 for reasoning behind OMEGA slope choice]  Tuesday, May 02, 2017, 09:24 IGP1 = 2.34e-6 Torr TBHT = 230A, 3.15V TGHT = 298A, 3.96V OMEGA = 1030C Vacuum stable, increasing ramping rate up to 0.5A/min  Tuesday, May 02, 2017, 13:20 IGP1 = 1.3e-5 Torr TGHT = 400A, 5.6V OMEGA = 1175C Increasing max setpoint to 500A     Wednesday, May 03, 2017, 13:33 TGHT had remained at 500A for 16hrs, vacuum had initially come down nicely. Vacuum was starting to creep up when i came in this morning before 8am,  IGP1 was at 1.2e-5 Torr TGHT = 500A, 7.77V OMEGA = 1440C Around 8:30 vacuum started to spike, so the TGHT was tapped down rapidly to 450A Tapping the TGHT down made no difference to the vacuum. By the time 450A was hit, it was too late and the spike in vacuum caused the evaporator to trip off. Turbo pump in epics showed on, turbo pump showed on according to TP direct controls. Everything was shut off and the venting tapped, this made it obvious the turbo pump was already off as there was no ramping down noises from the turbo pump. TP control box turned off then on again, at this point the controls showed a 'fail' message. Turns out the turbo pump control box was fried and that's what had caused the turbo pump to fail with no notice in epics causing the vacuum to spontaneously spike. Waiting on a new one from vacuum group... See photos attached of striptool screenshots.  Wednesday, May 03, 2017, 15:03 New TP control boxed installed. Turbo pump turned on, everything pumped down. Vacuum good, IGP1 = 6.92e-7 Torr. IGP2 still not working, won't turn on via epics. Tried unplugging and plugging back in...still appears red with 'fail' message...    Wednesday, May 03, 2017, 16:07 Unplugging and plugging back in seemed to work now that evap2 under vacuum IGP2 works again. Will look into replacement ion gauge...

 Wednesday, May 03, 2017, 16:09

HS water valves opened, no leaks detected.

Tapped up manually to 40A.

Vacuum stable.

IGP1 = 3.6e-7 Torr

Initiated auto-ramp at 1.0A/min and 0.5A/min to 300A and 230A for the TGHT and TBHT respectively.

 Thursday, May 04, 2017, 08:41

Reached 300A, 230A 10hrs ago.

IGP1 = 1.5e-7 Torr

OMEGA = 1070C

Increasing max setpoint to 500A at a rate of 0.5A/min for TGHT

 Thursday, May 04, 2017, 14:58

Back up to max setpoint that was reached before evap2 tripped off.

TGHT = 500A, 7.65V

IGP1 = 9.3e-7 Torr

OMEGA = 1450C

Increasing max setpoint to 550A, ramping up at a lower rate of 0.2A/min since this will be done overnight.

 Friday, May 05, 2017, 08:53

TGHT = 550A, 8.64V

IGP1 = 2.8e-7 Torr

OMEGA = 1560C

Increasing max setpoint to 600A at a ramping rate of 0.5A/min

 Friday, May 05, 2017, 11:09

TGHT = 600A, 9.58V

IGP1 = 7.3e-7 Torr

OMEGA = 1670C

Increasing max setpoint to 625A at a ramping rate of 0.5A/min

 Friday, May 05, 2017, 12:05

TGHT = 625A, 10.05V

IGP1 = 9.9e-7 Torr

OMEGA = 1710C

Increasing max setpoint to 650A at a ramping rate of 0.5A/min

 Friday, May 05, 2017, 13:13

TGHT = 650A, 10.57V

IGP1 = 1.1e-6 Torr

OMEGA  = 1740C

Mikron through left side windown on outside bottom left edge on container = 1750C

Tapping up manually to 1800C

 Friday, May 05, 2017, 13:42

Adjusted slope to 1.09 so same spot on leg using MIKRON = OMEGA

TGHT = 680A, 11.08V

IGP1 = 1.6e-6 Torr

OMEGA = 1795C

MIKRON = 1795C

Plotting a temperature curve, the predicted required current to reach 1800C was 670A using a slope of 1.08

Currently sitting 10A above predicted required current.

After several minutes, temperature dropped a few degrees to 1790C

Window remains clear and uncoated.

Tapped up to TGHT = 685A, 11.2V

OMEGA = 1795C

Will remain at this setpoint over the weekend.

 Monday, May 08, 2017, 08:59

TGHT = 685A, 11.08V

TBHT = 230A, 3.24V

IGP1 = 1.98e-7 Torr

OMEGA has lowered to 1342C

Evap2 sat at max setpoints over the wknd.

Will check window port before cooling...

*UPDATE ON TRIP-OFF*

A closer look into the details using archives [see photos attached]:

TP tripped off TBHT and TGHT at ~8e-5Torr

Anything in the evaporator requires ~1hr to cool before turning things off.

In this scenario, the target was @ ~1440C. so ~30min post TP trip, the target may still be at ~1000C.

Anything above 0.02Torr could be close enough to atmopheric pressure that this would be cooling too fast and could lead to breaking the target/ cracking the Ta metal.

As one can see in the screenshots attached, the vacuum lingered around 0.005Torr for ~2hrs before anything was done.

This provided enough time for the target to cool before it was introduced to atmospheric pressure when the BV was closed when trying to figure out the problem.

In summary, the target 'should' be OK...will inspect target further when removed from the evaporator.

 Tuesday, May 09, 2017, 09:16

TGHT = 685A, 11.04V

TGHT power supply = 686A, 11.31V

TBHT = 230A, 3.24V

TBHT power supply = 236A, 3.32V

IGP1 = 1.6e-7 Torr

IGP1 direct readout = 2.3e-7 mbar

IGP2 = 6.8e-8 Torr

IGP2 direct readout = 8.46e-8 Torr

Evap2 reached max setpoint friday afternoon.

Window clearly coated - see attached photo.

Initiating auto cool at 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.

 Wednesday, May 10, 2017, 09:18

Vented in air and opened up this morning.

Inspected container carefully for any cracks/ marks due to TP tripping off at 1450C

Target looks good! 

One sample disc removed for SEM.

When removing disc for sample, the SiC came off the graphite backing and just SiC flake came out - see photo

Photos attached showing inside container with no Si crystal formation/ good clear path all the way through target and sample removed for tests

Laura Lambert wrote:

Laura Lambert wrote: Laura Lambert wrote: Laura Lambert wrote:  Thursday, April 27, 2017, 14:01 Target container contains 470 discs of SiC  Target packed length = 16cm.  Mass of SiC(green)  = 52.13g Discs in target are arranged as follows: 5singles / 1pack / 65singles / 1pack / 75singles / 1pack / 75singles / 2packs / 75singles / 1pack / 75singles / 1pack / 55singles / 1pack / 5singles Container is wrapped with 1x heatshield around each side of cooling fins; no end caps are inserted yet - coated spring inserted both sides to hold discs in place. Sintering temp = 1800C Chamber is currently being pumped down.  Friday, April 28, 2017, 13:06 HS water valves turned on this morning, no leaks detected. Tapped up manually to 40A Waited ~3hrs , vacuum stable. IGP1 = 4.13e-6 Torr Initiating auto-ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively. TGHT max = 400A.  TBHT max at 230A.  Slope on OMEGA = 1.08 [see elog i.d. # 326 for reasoning behind OMEGA slope choice]  Tuesday, May 02, 2017, 09:24 IGP1 = 2.34e-6 Torr TBHT = 230A, 3.15V TGHT = 298A, 3.96V OMEGA = 1030C Vacuum stable, increasing ramping rate up to 0.5A/min  Tuesday, May 02, 2017, 13:20 IGP1 = 1.3e-5 Torr TGHT = 400A, 5.6V OMEGA = 1175C Increasing max setpoint to 500A     Wednesday, May 03, 2017, 13:33 TGHT had remained at 500A for 16hrs, vacuum had initially come down nicely. Vacuum was starting to creep up when i came in this morning before 8am,  IGP1 was at 1.2e-5 Torr TGHT = 500A, 7.77V OMEGA = 1440C Around 8:30 vacuum started to spike, so the TGHT was tapped down rapidly to 450A Tapping the TGHT down made no difference to the vacuum. By the time 450A was hit, it was too late and the spike in vacuum caused the evaporator to trip off. Turbo pump in epics showed on, turbo pump showed on according to TP direct controls. Everything was shut off and the venting tapped, this made it obvious the turbo pump was already off as there was no ramping down noises from the turbo pump. TP control box turned off then on again, at this point the controls showed a 'fail' message. Turns out the turbo pump control box was fried and that's what had caused the turbo pump to fail with no notice in epics causing the vacuum to spontaneously spike. Waiting on a new one from vacuum group... See photos attached of striptool screenshots.  Wednesday, May 03, 2017, 15:03 New TP control boxed installed. Turbo pump turned on, everything pumped down. Vacuum good, IGP1 = 6.92e-7 Torr. IGP2 still not working, won't turn on via epics. Tried unplugging and plugging back in...still appears red with 'fail' message...    Wednesday, May 03, 2017, 16:07 Unplugging and plugging back in seemed to work now that evap2 under vacuum IGP2 works again. Will look into replacement ion gauge...    Wednesday, May 03, 2017, 16:09 HS water valves opened, no leaks detected. Tapped up manually to 40A. Vacuum stable. IGP1 = 3.6e-7 Torr Initiated auto-ramp at 1.0A/min and 0.5A/min to 300A and 230A for the TGHT and TBHT respectively.  Thursday, May 04, 2017, 08:41 Reached 300A, 230A 10hrs ago. IGP1 = 1.5e-7 Torr OMEGA = 1070C Increasing max setpoint to 500A at a rate of 0.5A/min for TGHT  Thursday, May 04, 2017, 14:58 Back up to max setpoint that was reached before evap2 tripped off. TGHT = 500A, 7.65V IGP1 = 9.3e-7 Torr OMEGA = 1450C Increasing max setpoint to 550A, ramping up at a lower rate of 0.2A/min since this will be done overnight.  Friday, May 05, 2017, 08:53 TGHT = 550A, 8.64V IGP1 = 2.8e-7 Torr OMEGA = 1560C Increasing max setpoint to 600A at a ramping rate of 0.5A/min  Friday, May 05, 2017, 11:09 TGHT = 600A, 9.58V IGP1 = 7.3e-7 Torr OMEGA = 1670C Increasing max setpoint to 625A at a ramping rate of 0.5A/min  Friday, May 05, 2017, 12:05 TGHT = 625A, 10.05V IGP1 = 9.9e-7 Torr OMEGA = 1710C Increasing max setpoint to 650A at a ramping rate of 0.5A/min  Friday, May 05, 2017, 13:13 TGHT = 650A, 10.57V IGP1 = 1.1e-6 Torr OMEGA  = 1740C Mikron through left side windown on outside bottom left edge on container = 1750C Tapping up manually to 1800C  Friday, May 05, 2017, 13:42 Adjusted slope to 1.09 so same spot on leg using MIKRON = OMEGA TGHT = 680A, 11.08V IGP1 = 1.6e-6 Torr OMEGA = 1795C MIKRON = 1795C Plotting a temperature curve, the predicted required current to reach 1800C was 670A using a slope of 1.08 Currently sitting 10A above predicted required current. After several minutes, temperature dropped a few degrees to 1790C Window remains clear and uncoated. Tapped up to TGHT = 685A, 11.2V OMEGA = 1795C Will remain at this setpoint over the weekend.  Monday, May 08, 2017, 08:59 TGHT = 685A, 11.08V TBHT = 230A, 3.24V IGP1 = 1.98e-7 Torr OMEGA has lowered to 1342C Evap2 sat at max setpoints over the wknd. Will check window port before cooling...   *UPDATE ON TRIP-OFF* A closer look into the details using archives [see photos attached]: TP tripped off TBHT and TGHT at ~8e-5Torr Anything in the evaporator requires ~1hr to cool before turning things off. In this scenario, the target was @ ~1440C. so ~30min post TP trip, the target may still be at ~1000C. Anything above 0.02Torr could be close enough to atmopheric pressure that this would be cooling too fast and could lead to breaking the target/ cracking the Ta metal. As one can see in the screenshots attached, the vacuum lingered around 0.005Torr for ~2hrs before anything was done. This provided enough time for the target to cool before it was introduced to atmospheric pressure when the BV was closed when trying to figure out the problem. In summary, the target 'should' be OK...will inspect target further when removed from the evaporator.  Tuesday, May 09, 2017, 09:16 TGHT = 685A, 11.04V TGHT power supply = 686A, 11.31V TBHT = 230A, 3.24V TBHT power supply = 236A, 3.32V IGP1 = 1.6e-7 Torr IGP1 direct readout = 2.3e-7 mbar IGP2 = 6.8e-8 Torr IGP2 direct readout = 8.46e-8 Torr Evap2 reached max setpoint friday afternoon. Window clearly coated - see attached photo. Initiating auto cool at 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.  Wednesday, May 10, 2017, 09:18 Vented in air and opened up this morning. Inspected container carefully for any cracks/ marks due to TP tripping off at 1450C Target looks good!  One sample disc removed for SEM. When removing disc for sample, the SiC came off the graphite backing and just SiC flake came out - see photo Photos attached showing inside container with no Si crystal formation/ good clear path all the way through target and sample removed for tests

 Wednesday, October 31, 2018, 19:35

Container is coated with TaC and wrapped with Ta heat-shield (3 layers)

Desired temp = 1900 C (expected TGHT ~445A/7.5V), TBHT will be set fixed at 230A (max).

Chamber is currently being pumped down

 Thursday, November 01, 2018, 10:31

Pressure at IGP1 9.44e-7 Torr. 

Tapped up TGHT and TBHT manually to 40 A

Thursday, November 01, 2018, 12:32

Waited ~1 hr for vacuum to stabilize.

IGP1 = 1.42e-6 Torr

Good vac at 3.00-5 Torr

Bad vac at 5.0e-5 Torr.

Initiating auto ramp for TGHT @ 1 A/min to a max setpoint of 350 A

Initiating auto ramp for TBHT @ 0.5 A/min to a max setpoint of 230 A

Once max setpoints achieved, will tap up manually to final desired temperature of 1900 C

 Tapped manually to 445 A, Temperature 1896 C.

Friday, November 02, 2018, 07:35

TGHT 7.86 V 445.6 A

TBHT 3.22 V 233.3 A

IGP1 1e-6 Torr

Ramping down TGHT and TBHT to 0 A @ 2 A/min.  

Friday, November 02, 2018, 17:28

Monday, October 29, 2018, 12:39

Venting EVAP2, TaC coat sintering completed.