John Wong wrote:

Laura Lambert wrote: John Wong wrote: Laura Lambert wrote:  Thursday, September 15, 2016, 16:23 Target container contains 487 discs of SiC  Target packed length = 16cm.  Mass of SiC(green)  = 58.8795g Container is wrapped with 1x heatshield around each side of cooling fins; no end caps are inserted yet - coated spring inserted both sides to hold discs in place. Sintering temp = 1800C Chamber is currently being pumped down.   Friday, September 16, 2016, 10:50 Tapped up manually to 50A Waited ~1hr , vacuum stable. IGP1 = 1.24e-5 Torr Initiating auto-ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively. TGHT max = 500A.  TBHT max at 230A.  Slope on OMEGA = 1.15  Monday, September 19, 2016, 10:53 OMEGA = 1230C TGHT = 360A, 4.75V TBHT = 204A, 2.68V IGP1 = 5.3e-6 Torr Increasing ramping rate to 1.0A/min and 0.5A/min for the TGHT and TBHT respectively.  Monday, September 19, 2016, 11:57 OMEGA = ~1300C TBHT = 230A, 3.16V TGHT = 409A, 5.55V Lowering ramping rate to 0.2A/min while vaccum high IGP1 = 3.05e-5 Torr  Monday, September 19, 2016, 13:22 OMEGA = 1350C TGHT = 425A, 5.82V IGP1 = 1.97e-5 Torr Stepping ramping rate back up to 1.0A/min    Monday, September 19, 2016, 18:24 Measuring the temperature on the SiC is difficult due to the changing in emissivity as the temperature goes up.  So, I will use the MIKRON to measure the temperature on the Ta surface near the end of the tube and OMEGA for measuring the inside.   Using the analogue pyrometer, the temperature on the Ta surface at the end of the tube was measured at around ~1450C; this temperature match the temperature on the Mikron at slope 0.98 (as usual).  To match it with OMEGA, I changed the slope to 1.04 since this measurement is taking readings on the  inside of the tube and on the SiC material.    Note:  The measurements are NOT the absolute temperature.  These are relative temperature measurements  which give some guideline where the target current should be at for the sintering process.  Please plot the temp vs current as the TGHT is being ramped up.  At some point, the windows will get coated and the measurement is no longer reliable.   The plot will be used to give an estimation of the current for 1800C.        Tuesday, September 20, 2016, 15:18 there was a temperature fluctuation resulting in the MIKRON no longer matching the readout on the OMEGA this prompted another change in the slope on the OMEGA to 1.08 TGHT was then tapped up manually to 600A/ 1800C will remain at this max setpoint for a few days before ramping down see attachment for raw data  Wednesday, September 21, 2016, 11:34 temperatures dropped a small amount overnight. tapped up manually to 625A/ 1810C still no coating on window. see attachment for updated raw data    Thursday, September 22, 2016, 12:07 Temperature reader on OMEGA dropped slightly to 1785C overnight.  The temperature on the leg remained at 1800C (MIKRON).  No coating on windows.   Increased TGHT to 635A/10.12V (local 10.40V).  OMEGA reads 1800C, MIKRON ~1817C.   Continue to monitor… (see dropbox for captured photos)

 Monday, September 26, 2016, 13:24

Temperature decreased over weekend.

MIKRON dropped from ~1800C to ~1670C, OMEGA on right side remained ~1800C

Comparing screen shots of temperature readings and camera looking at target from left side, changes can be seen:

-darker area on top edge of target tube, above inside tube, grows larger when temperature drops - indicating 'cooler area' has grown

-initially darker area covers top above target materials on tube, when drops to ~1670C darker area extends down sides of target tube and reaches past target material area

See attached picture showing these details

Target has remained at this max setpoint for ~4-5 days

Windows remain un-coated.

Current and voltage readings remain un-changed.

Initiating auto-cool at 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.

 Wednesday, September 28, 2016, 17:05

Vented in air, target taken out today.

Target looks good!

A small amount of material was removed from the windows in evap2, very thin layer of coating.

Will update tomorrow with photos

Endcaps inserted.