Friday, January 31, 2014, 11:28

Target container is coated with TaC.

The container is wrapped with 3 x Ta heat-shield.

Chamber was pumped down to 1.9e-7 Torr.

HS water valves were opened, no leak detected.

TGHT and TBHT were stepped up to 35A. Waited ~20min, current stabilized and vacuum starting to drop.

TGHT will be ramped up to 580A at 0.2A/min, max voltage = 11.05V.

TBHT will be ramped up to 230A at 0.2A/min, max volatge = 5V.

Initiating auto-ramping: Good Vac = 3.0e-5 Torr, Bad Vac = 4.0e-5 Torr.

 Monday, February 03, 2014, 10:21

TGHT reached 580A pver the weekend.

TBHT sitting at 1.4A, checked archive: never went over 1.6A. Aborted auto-ramp, re-starting auto ramp process for TBHT.

IGP1 = 1.6e-7 Torr.

 Monday, February 03, 2014, 15:23

TBHT running smoothly, must have been and electrical problem.

TBHT currently at 85A, vacuum has not changed, increasing TBHT auto-ramp to 2.0A/min

 Tuesday, February 04, 2014, 10:10

TBHT reached 230A yesterday pm. Measured temp this morning at 1800C.

Initiated TGHT/TBHT auto-cooling at 2.0A/min.

 Wednesday, February 05, 2014, 11:33

Chamber cooled down overnight, vented and opened up this morning.

Smooth run! Container fully sintered.

 Thursday, April 09, 2015, 09:33

Target container is coated with TaC and wrapped with 3-Ta heat shields, not incl center block.

TGHT and TBHT will be ramped up to 820A and 230A, respectively.

Chamber pumped down overnight.

IGP1 = 5.2e-7 Torr.

HS cooling water valves opened; no leaks detected.

TGHT max voltage = 18V, TBHT max voltage = 5V

Stepping TGHT and TBHT up to 35A...

 Thursday, April 09, 2015, 10:07

Waited ~20min, vacuum stable.

IGP1 = 5.3e-7 Torr.

Good vac = 3e-5 Torr. Bad vac = 4e-5 Torr.

Auto-ramp initiated at 0.2A/min.

 Monday, April 13, 2015, 09:06

Reached max setpoints sunday morning [see attached photo for striptool].

Internal temperature measured with OMEGA  = 1965C

IGP1 = 4.4e-7 Torr,

Initiating auto cool for TGHT and TBHT at 2.0A/min and 1.0A/min respectively.

 Tuesday, April 14, 2015, 14:12

Vented in air and opened up this morning.

Fully sintered.

 Tuesday, June 17, 2014, 13:11

Target container is coated with TaC.

Container is wrapped with 3x Ta-heat shields.

Currently being pumped down.

For sintering process:

TGHT and TBHT will be ramped up to 820A and 300A respectively at 0.1A/min

 Tuesday, June 17, 2014, 14:22

HS water cooling valves opened, no leaks detected.

IGP1 @1.8e-6 Torr

TGHT max = 820A/ 17V

TBHT max = 300A/ 5V

Stepped up manually to 40A, waited ~20min, vacuum stable.

Initiating auto-ramp @ 1.0A/min

 Wednesday, June 18, 2014, 11:24

TGHT and TBHT reached their respective 820A and 300A last night.

Internal temp measured from side of EVAP2 with mikron = 1830C

IGP1 = 7.6e-7 Torr

Initiating auto-cool down process at 2.0A/min and 1.0A/min for TGHT and TBHT respectively

vented and opened this morning.

smooth run

 Wednesday, September 07, 2016, 14:45

Container was previously coated with TaC solution and wrapped with 1-full length layer of Ta- heat shield around the fins.  

Chamber is being pumped down.  Vac at 5.6e-7 Torr before HS water valves were open; no leaks were detected. 

Sintering Temperature 1900C (Omega slope @ 0.98); expected TGHT ~765A/11.90V, TGHT max at 230A.

 Thursday, September 08, 2016, 18:14

At about 1600C, it was observed that the coating inside the tube seems to chip off (see attachment 1).

TGHT was ramped up to 745A/11.85V and TBHT to 230A/3.25V.  Temperature measured on OMEGA/Mikron = 1914C/1881C; both instruments slopes set at 0.98.

Will remain at this TGHT current over night

Vac at 3.0e-6 Torr and coming down.

Friday, September 09, 2016, 11:01 

Target has been heated at the stable temperature at 1914C (for OMEGA) and 1881C (for Mikron) with current at 745A/11.94V (see attachment 2) for almost 19 hours. 

No fluctuation in p/s current or temperature was observed.  The ramping up process is captured and can be view from the link below:

https://www.dropbox.com/sh/9lgtin54o17ds6j/AABn1-XjvK44mm74TjqTAmvta?dl=0

Pressure at 1.07e-6 Torr. 

Cooling down TGHT at 2A/min and TBHT at 1A/min. 

Continue to capture the cooling down process. 

 Friday, September 09, 2016, 15:17

 While the target container was cooling down, the chip-like particle began obvious (see attachment 3).  

Will inspect the container.. TGHT currently at 260A.

 Tuesday, August 25, 2015, 11:50

Container coated with TaC using new method: Ends tapped off,  with liquid poured in and swirled around entire container, then poured back out - 'flushing technique'

Container is wrapped with 3 x Ta heat shields, not incl center block.

Loaded into EVAP2 and currently pumping down.

 Tuesday, August 25, 2015, 13:52

IGP1 = 2.2e-6 Torr.

HS water valves opened.

No leaks detected.

Tapped up manually to 35A.

Vacuum stable.

Initiated auto ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively.

Final setpoints for TGHT = 720A and TBHT = 230A, with final desired temp of 1800C

 Wednesday, August 26, 2015, 09:56

IGP1 = 8.8e-7 Torr.

TGHT = 260A, 3.0V

TBHT = 145A, 1.8V

Increasing ramping rate to 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.

 Wednesday, August 26, 2015, 14:15

IGP1 = 3.5e-6 Torr.

TGHT = 720A, 11.3V

TBHT = 230A, 3.2V

DV = 5.48V

OMEGA RS [right side-old port] = 1745C

OMEGA LS [left side-new port] = 1880C

Tapping up manually to achieve 1800C on OMEGA RS

 Wednesday, August 26, 2015, 14:44

IGP1 = 3.7e-6 Torr.

TGHT = 748A, 11.9V

DV = 5.78V

OMEGA RS = 1803C

OMEGA LS = 1935C

Thursday, August 27, 2015, 07:31

 Remained at max setpoints for ~17hrs.

IGP1 = 1.3e-6 Torr.

DV = 5.79V

OMEGA RS = 1862 [this reading may not be correct due to the laser being moved at max setpoint - this temperature reading may be taken from a different location then the last reading]

OMEGA LS = 1955

Initiating auto-cool at 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.

Laura Lambert wrote:

Tuesday, August 25, 2015, 11:50 Container coated with TaC using new method: Ends tapped off,  with liquid poured in and swirled around entire container, then poured back out - 'flushing technique' Container is wrapped with 3 x Ta heat shields, not incl center block. Loaded into EVAP2 and currently pumping down.  Tuesday, August 25, 2015, 13:52 IGP1 = 2.2e-6 Torr. HS water valves opened. No leaks detected. Tapped up manually to 35A. Vacuum stable. Initiated auto ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively. Final setpoints for TGHT = 720A and TBHT = 230A, with final desired temp of 1800C  Wednesday, August 26, 2015, 09:56 IGP1 = 8.8e-7 Torr. TGHT = 260A, 3.0V TBHT = 145A, 1.8V Increasing ramping rate to 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.  Wednesday, August 26, 2015, 14:15 IGP1 = 3.5e-6 Torr. TGHT = 720A, 11.3V TBHT = 230A, 3.2V DV = 5.48V OMEGA RS [right side-old port] = 1745C OMEGA LS [left side-new port] = 1880C Tapping up manually to achieve 1800C on OMEGA RS  Wednesday, August 26, 2015, 14:44 IGP1 = 3.7e-6 Torr. TGHT = 748A, 11.9V DV = 5.78V OMEGA RS = 1803C OMEGA LS = 1935C Thursday, August 27, 2015, 07:31  Remained at max setpoints for ~17hrs. IGP1 = 1.3e-6 Torr. DV = 5.79V OMEGA RS = 1862 [this reading may not be correct due to the laser being moved at max setpoint - this temperature reading may be taken from a different location then the last reading] OMEGA LS = 1955 Initiating auto-cool at 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.

 Thursday, August 27, 2015, 16:34

Target is removed from the evaporator and inspected.  

The "flushing technique" has a much better result.  The inner coated surface is sintered well.  

John Wong wrote:

Wednesday, January 15, 2014, 17:30 Target container is coated with TaC.  No Ta-heat shields are used. TGHT will be ramped up to 580A at 0.2A/min.  TBHT will be ramped up to 230A at 0.2A/min.    Chamber is currently being pumped.  Tomorrow, the HS water valve can be opened to test for leaks.   Notes:  If everything is fine, TGHT/TBHT can be stepped up to 30A-50A.  Watch for the vacuum; once it's stable the auto ramping program can be initiated.   Once TGHT/TBHT reached above 200A, the ramping rate for TGHT can be increased up to 2A/min.  (This step is to speed up the process; however it's not mandatory)

 Thursday, January 16, 2014, 11:35

Chamber was pumped down overnight to 10-7 Torr. HS water valve was opened and no leak in vacuum was observed.

TGHT and TBHT were stepped up to 35A. Waited ~30min, current stabilized and vacuum starting to drop.

Initiating auto-ramping: Good Vac = 2.0e-5 Torr, Bad Vac = 3.0e-5 Torr.

Laura Lambert wrote:

John Wong wrote:  Wednesday, January 15, 2014, 17:30 Target container is coated with TaC.  No Ta-heat shields are used. TGHT will be ramped up to 580A at 0.2A/min.  TBHT will be ramped up to 230A at 0.2A/min.    Chamber is currently being pumped.  Tomorrow, the HS water valve can be opened to test for leaks.   Notes:  If everything is fine, TGHT/TBHT can be stepped up to 30A-50A.  Watch for the vacuum; once it's stable the auto ramping program can be initiated.   Once TGHT/TBHT reached above 200A, the ramping rate for TGHT can be increased up to 2A/min.  (This step is to speed up the process; however it's not mandatory)     Thursday, January 16, 2014, 11:35 Chamber was pumped down overnight to 10-7 Torr. HS water valve was opened and no leak in vacuum was observed. TGHT and TBHT were stepped up to 35A. Waited ~30min, current stabilized and vacuum starting to drop. Initiating auto-ramping: Good Vac = 2.0e-5 Torr, Bad Vac = 3.0e-5 Torr.

 Friday, January 17, 2014, 09:28

TGHT/TBHT @ 300/200A.  TBHT voltage is limited at 3A.  

TGHT ramping rate increased to 2A/min.  Pressure @ 4.5e-7 Torr.  

Laura Lambert wrote:

John Wong wrote: Laura Lambert wrote: John Wong wrote:  Wednesday, January 15, 2014, 17:30 Target container is coated with TaC.  No Ta-heat shields are used. TGHT will be ramped up to 580A at 0.2A/min.  TBHT will be ramped up to 230A at 0.2A/min.    Chamber is currently being pumped.  Tomorrow, the HS water valve can be opened to test for leaks.   Notes:  If everything is fine, TGHT/TBHT can be stepped up to 30A-50A.  Watch for the vacuum; once it's stable the auto ramping program can be initiated.   Once TGHT/TBHT reached above 200A, the ramping rate for TGHT can be increased up to 2A/min.  (This step is to speed up the process; however it's not mandatory)     Thursday, January 16, 2014, 11:35 Chamber was pumped down overnight to 10-7 Torr. HS water valve was opened and no leak in vacuum was observed. TGHT and TBHT were stepped up to 35A. Waited ~30min, current stabilized and vacuum starting to drop. Initiating auto-ramping: Good Vac = 2.0e-5 Torr, Bad Vac = 3.0e-5 Torr.    Friday, January 17, 2014, 09:28 TGHT/TBHT @ 300/200A.  TBHT voltage is limited at 3A.   TGHT ramping rate increased to 2A/min.  Pressure @ 4.5e-7 Torr.      Friday, January 17, 2014, 10:14 TBHT stopped at 200A with voltage limit sitting at 3V. Aborted auto-ramp, changed the voltage limit to 5V and increased ramping rate to 2A/min. Re-started auto-ramp. IGP1 @ 5.0e-7 Torr

 Friday, January 17, 2014, 12:45

TGHT voltage limiting at 9.9V, and  current stayed at 560A.  Increased the TGHT voltage to 10.5V and continued ramping the heater up.

TGHT/TBHT stabilized at 580A (~10V) and 230A(3.6V). 

Pressure at 1.03e-6 Torr and coming down... 

Target will be heated until 5pm (4hrs) before cooling down at the ramping rate of 2A/min. 

Chamber will be vented in air, next week.

 Friday, January 17, 2014, 16:51

Auto-cooling initiated at 2A/min.

Vac @ 5.3e-7 Torr.

John Wong wrote:

Laura Lambert wrote: John Wong wrote: Laura Lambert wrote: John Wong wrote:  Wednesday, January 15, 2014, 17:30 Target container is coated with TaC.  No Ta-heat shields are used. TGHT will be ramped up to 580A at 0.2A/min.  TBHT will be ramped up to 230A at 0.2A/min.    Chamber is currently being pumped.  Tomorrow, the HS water valve can be opened to test for leaks.   Notes:  If everything is fine, TGHT/TBHT can be stepped up to 30A-50A.  Watch for the vacuum; once it's stable the auto ramping program can be initiated.   Once TGHT/TBHT reached above 200A, the ramping rate for TGHT can be increased up to 2A/min.  (This step is to speed up the process; however it's not mandatory)     Thursday, January 16, 2014, 11:35 Chamber was pumped down overnight to 10-7 Torr. HS water valve was opened and no leak in vacuum was observed. TGHT and TBHT were stepped up to 35A. Waited ~30min, current stabilized and vacuum starting to drop. Initiating auto-ramping: Good Vac = 2.0e-5 Torr, Bad Vac = 3.0e-5 Torr.    Friday, January 17, 2014, 09:28 TGHT/TBHT @ 300/200A.  TBHT voltage is limited at 3A.   TGHT ramping rate increased to 2A/min.  Pressure @ 4.5e-7 Torr.      Friday, January 17, 2014, 10:14 TBHT stopped at 200A with voltage limit sitting at 3V. Aborted auto-ramp, changed the voltage limit to 5V and increased ramping rate to 2A/min. Re-started auto-ramp. IGP1 @ 5.0e-7 Torr  Friday, January 17, 2014, 12:45 TGHT voltage limiting at 9.9V, and  current stayed at 560A.  Increased the TGHT voltage to 10.5V and continued ramping the heater up. TGHT/TBHT stabilized at 850A (~10V) and 230A(3.6V).  Pressure at 1.03e-6 Torr and coming down...  Target will be heated until 5pm (4hrs) before cooling down at the ramping rate of 2A/min.  Chamber will be vented in air, next week.  Friday, January 17, 2014, 16:51 Auto-cooling initiated at 2A/min. Vac @ 5.3e-7 Torr.

 Wednesday, January 15, 2014, 17:30

Target container is coated with TaC.  No Ta-heat shields are used.

TGHT will be ramped up to 580A at 0.2A/min. 

TBHT will be ramped up to 230A at 0.2A/min.  

 Chamber is currently being pumped.  Tomorrow, the HS water valve can be opened to test for leaks.  

Notes: 

If everything is fine, TGHT/TBHT can be stepped up to 30A-50A.  Watch for the vacuum; once it's stable the auto ramping program can be initiated.  

Once TGHT/TBHT reached above 200A, the ramping rate for TGHT can be increased up to 2A/min.  (This step is to speed up the process; however it's not mandatory) 

John Wong wrote:

Laura Lambert wrote: John Wong wrote:  Wednesday, January 15, 2014, 17:30 Target container is coated with TaC.  No Ta-heat shields are used. TGHT will be ramped up to 580A at 0.2A/min.  TBHT will be ramped up to 230A at 0.2A/min.    Chamber is currently being pumped.  Tomorrow, the HS water valve can be opened to test for leaks.   Notes:  If everything is fine, TGHT/TBHT can be stepped up to 30A-50A.  Watch for the vacuum; once it's stable the auto ramping program can be initiated.   Once TGHT/TBHT reached above 200A, the ramping rate for TGHT can be increased up to 2A/min.  (This step is to speed up the process; however it's not mandatory)     Thursday, January 16, 2014, 11:35 Chamber was pumped down overnight to 10-7 Torr. HS water valve was opened and no leak in vacuum was observed. TGHT and TBHT were stepped up to 35A. Waited ~30min, current stabilized and vacuum starting to drop. Initiating auto-ramping: Good Vac = 2.0e-5 Torr, Bad Vac = 3.0e-5 Torr.    Friday, January 17, 2014, 09:28 TGHT/TBHT @ 300/200A.  TBHT voltage is limited at 3A.   TGHT ramping rate increased to 2A/min.  Pressure @ 4.5e-7 Torr.

 Friday, January 17, 2014, 10:14

TBHT stopped at 200A with voltage limit sitting at 3V.

Aborted auto-ramp, changed the voltage limit to 5V and increased ramping rate to 2A/min. Re-started auto-ramp.

IGP1 @ 5.0e-7 Torr

 Monday, June 29, 2015, 16:17

Target container is coated with TaC. No Ta-heat shields are used.

TGHT will be ramped up to 580A at 0.2A/min.

TBHT will be ramped up to 230A at 01A/min.

Chamber is currently being pumped down.

Laura Lambert wrote:

Monday, June 29, 2015, 16:17 Target container is coated with TaC. No Ta-heat shields are used. TGHT will be ramped up to 580A at 0.2A/min. TBHT will be ramped up to 230A at 01A/min. Chamber is currently being pumped down.

 Monday, June 29, 2015, 23:37

Opened the HS valves around 5pm.  Small leaks or just a vibration in the pipe line caused a rise in vacuum.  Leak rate is small, so allow the chamber to continue to pump down over night.

Sintering process can begin tomorrow if vacuum is allowed.

John Wong wrote:

Laura Lambert wrote:  Monday, June 29, 2015, 16:17 Target container is coated with TaC. No Ta-heat shields are used. TGHT will be ramped up to 580A at 0.2A/min. TBHT will be ramped up to 230A at 01A/min. Chamber is currently being pumped down.    Monday, June 29, 2015, 23:37 Opened the HS valves around 5pm.  Small leaks or just a vibration in the pipe line caused a rise in vacuum.  Leak rate is small, so allow the chamber to continue to pump down over night. Sintering process can begin tomorrow if vacuum is allowed.

 Tuesday, June 30, 2015, 08:22

IGP1 = 3.6e-7 Torr.

Tapped up manually to 40A.

Vacuum looks good.

IGP1 = 6.9e-7 Torr.

Inititating auto-ramp...

 Thursday, July 02, 2015, 09:56

IGP1 = 8.9e-7 Torr.

OMEGA = 1728C

TGHT and TBHT = 580A and 230A respectively.

Tapping up manually to 1800C.

 Thursday, July 02, 2015, 11:02

TGHT = 615A, 10.9V

OMEGA = 1800C

IGP1 = 1.1e-6 Torr.

Will continue to heat for 4hrs.

 Thursday, July 02, 2015, 15:43

Target container remained at 1800C for 4hrs50min.

Initiating auto-cool for TGHT = 2A/min and TBHT = 1A/min.

 Friday, July 03, 2015, 08:24

Vented in air and opened up this morning.

Edge of container on both ends not fully sintered [see photos]

Laura Lambert wrote:

John Wong wrote: Laura Lambert wrote:  Monday, June 29, 2015, 16:17 Target container is coated with TaC. No Ta-heat shields are used. TGHT will be ramped up to 580A at 0.2A/min. TBHT will be ramped up to 230A at 01A/min. Chamber is currently being pumped down.    Monday, June 29, 2015, 23:37 Opened the HS valves around 5pm.  Small leaks or just a vibration in the pipe line caused a rise in vacuum.  Leak rate is small, so allow the chamber to continue to pump down over night. Sintering process can begin tomorrow if vacuum is allowed.    Tuesday, June 30, 2015, 08:22 IGP1 = 3.6e-7 Torr. Tapped up manually to 40A. Vacuum looks good. IGP1 = 6.9e-7 Torr. Inititating auto-ramp...  Thursday, July 02, 2015, 09:56 IGP1 = 8.9e-7 Torr. OMEGA = 1728C TGHT and TBHT = 580A and 230A respectively. Tapping up manually to 1800C.  Thursday, July 02, 2015, 11:02 TGHT = 615A, 10.9V OMEGA = 1800C IGP1 = 1.1e-6 Torr. Will continue to heat for 4hrs.  Thursday, July 02, 2015, 15:43 Target container remained at 1800C for 4hrs50min. Initiating auto-cool for TGHT = 2A/min and TBHT = 1A/min.  Friday, July 03, 2015, 08:24 Vented in air and opened up this morning. Edge of container on both ends not fully sintered [see photos]

 Monday, July 06, 2015, 11:54

Inner tube surface isn't homogeneously sintered with TaC (see attachment).  

A second coating may help.  

For the re-sintering process, the target container will be wrapped with 6.2cm Ta (width) foil as a layer for heat shield on each side of the tube,  excluding the centre block - just like the same process was done last time, see e-log ID#217.  

The Ta-foil and the target tube will be spaced with Ta wire coiled around it.  

TGHT can be ramped up about 520A/9.1V to achieve 1900C.  Heating time for 3-4 hours until vacuum comes down to low 10-6 Torr. 

John Wong wrote:

Laura Lambert wrote: John Wong wrote: Laura Lambert wrote:  Monday, June 29, 2015, 16:17 Target container is coated with TaC. No Ta-heat shields are used. TGHT will be ramped up to 580A at 0.2A/min. TBHT will be ramped up to 230A at 01A/min. Chamber is currently being pumped down.    Monday, June 29, 2015, 23:37 Opened the HS valves around 5pm.  Small leaks or just a vibration in the pipe line caused a rise in vacuum.  Leak rate is small, so allow the chamber to continue to pump down over night. Sintering process can begin tomorrow if vacuum is allowed.    Tuesday, June 30, 2015, 08:22 IGP1 = 3.6e-7 Torr. Tapped up manually to 40A. Vacuum looks good. IGP1 = 6.9e-7 Torr. Inititating auto-ramp...  Thursday, July 02, 2015, 09:56 IGP1 = 8.9e-7 Torr. OMEGA = 1728C TGHT and TBHT = 580A and 230A respectively. Tapping up manually to 1800C.  Thursday, July 02, 2015, 11:02 TGHT = 615A, 10.9V OMEGA = 1800C IGP1 = 1.1e-6 Torr. Will continue to heat for 4hrs.  Thursday, July 02, 2015, 15:43 Target container remained at 1800C for 4hrs50min. Initiating auto-cool for TGHT = 2A/min and TBHT = 1A/min.  Friday, July 03, 2015, 08:24 Vented in air and opened up this morning. Edge of container on both ends not fully sintered [see photos]    Monday, July 06, 2015, 11:54 Inner tube surface isn't homogeneously sintered with TaC (see attachment).   A second coating may help.   For the re-sintering process, the target container will be wrapped with 6.2cm Ta (width) foil as a layer for heat shield on each side of the tube,  excluding the centre block - just like the same process was done last time, see e-log ID#217.   The Ta-foil and the target tube will be spaced with Ta wire coiled around it.   TGHT can be ramped up about 520A/9.1V to achieve 1900C.  Heating time for 3-4 hours until vacuum comes down to low 10-6 Torr.

 Monday, July 06, 2015, 16:28

Container has been re-coated with TaC.

Target container is wrapped with a single 15.5cm x 8.5cm Ta foil heat shield on each side of the center block, spaced with Ta wire coil.

Chamber is currently being pumped down.

 Tuesday, July 07, 2015, 09:36

HS water valves were opened this morning, no leaks detected.

IGP1 = 6e-7 Torr.

Tapped up manually to 30A.

Waited ~1hr.

Vacuum stable, IGP1 = 1.9e-6 Torr.

Initiating auto-ramp at 0.2A/min and 0.1A/min for TGHT and TBHT respectively.

 Target container reached max setpoints of 520A/230A and 1950C ~6hrs ago.

IGP1 = 7.6e-7 Torr.

Initiating auto-cool at 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.

 Friday, July 10, 2015, 11:16

Vented in air and removed from evap2.

Again, edges not fully sintered [see photos]

Inside of container looks better, fully coated.

Wednesday, July 23, 2014, 15:07

Target container is coated with TaC.  No Ta-heat shields are used.

TGHT will be ramped up to 580A at 0.2A/min.

TBHT will be ramped up to 230A at 0.2A/min.

Chamber is currently being pumped down

 Wednesday, July 23, 2014, 17:40

Vacuum came down to mid 10-6 Torr.

Stepped up TGHT and TBHT to 30A - IG1 @ 1.4e-5 Torr.

Initiated auto-ramping.

 Thursday, July 24, 2014, 17:19

TGHT and TBHT have reached to 100A, and vacuum is coming down to 1.4e-6 Torr.

Increase ramping rate, TGHT to 1A/min, TBHT 0.5A/min.

 Friday, July 25, 2014, 11:26

Target container temperature reaches ~1550C at 580A on TGHT and 230A TBHT, and it has been heated for ~10 hrs.

Auto-cooling initiated at 2A/min.

John Wong wrote:

Wednesday, July 23, 2014, 15:07 Target container is coated with TaC.  No Ta-heat shields are used. TGHT will be ramped up to 580A at 0.2A/min. TBHT will be ramped up to 230A at 0.2A/min. Chamber is currently being pumped down  Wednesday, July 23, 2014, 17:40 Vacuum came down to mid 10-6 Torr. Stepped up TGHT and TBHT to 30A - IG1 @ 1.4e-5 Torr. Initiated auto-ramping.  Thursday, July 24, 2014, 17:19 TGHT and TBHT have reached to 100A, and vacuum is coming down to 1.4e-6 Torr. Increase ramping rate, TGHT to 1A/min, TBHT 0.5A/min.  Friday, July 25, 2014, 11:26 Target container temperature reaches ~1550C at 580A on TGHT and 230A TBHT, and it has been heated for ~10 hrs. Auto-cooling initiated at 2A/min.

 Monday, July 28, 2014, 10:50

vented in air and opened this morning. successful run

Tuesday, July 17, 2012, 15:45

Target boat is filled with TaC coated regular- and D-endcaps. 

The boat is wrapped with a Ta heat-shield. 

Chamber is being pumped down, currently at 5e-6 Torr.

Tuesday, July 17, 2012, 15:58

Heat-shield cooling water valve opened; no leaks detected.

Initiated TGHT auto-ramping at 0.5A/min, set TGHT max at 580A.

 Wednesday, July 18, 2012, 10:44

Yesterday evening, the target heater tripped off a few times due to high vacuum excursion.  The TGHT ramping rate was low to 0.2A/min.  The current was ramped up sturdily to 500A this morning.  

Wednesday, July 18, 2012, 10:46

Increased ramping rate to 2A/min.  Vacuum currently at 2.2e-6 Torr.

 Wednesday, July 18, 2012, 16:18

TGHt has reached to 580A and stayed for about 5 hrs. 

Cooling down in process...  2A/min for TGHT --> 0A.

 Thursday, July 19, 2012, 10:31

TGHT reached to 0A. 

Evaporator is off. 

Venting chamber...