John Wong wrote:

Laura Lambert wrote: Tuesday, August 18, 2015, 15:53 Target consists of 505 discs. Total packed length 3.4cm. Total mass 75.2772g. Re foil inserted. 3x Ta Heat shields. No endcaps inserted. Chamber currently pumping down. TBHT will be ramped up to 230A at 1.0A/min. TGHT will be ramped up to 1800C, auto ramp to 600A at 2.0A/min [estimated final value of 720A according to elog ID 184] *Note: Turbo Pump is on low speed  Wednesday, August 19, 2015, 10:15 IGP1 = 8.3e-7 Torr. Tapped up manually to 35A. Initiating auto-ramp. Wednesday, August 19, 2015, 15:55   IGP1 = 3.3e-6 Torr. TBHT reached max setpoint of 230A TGHT reached max setpoint of 600A OMEGA = 1554C Increasing final setpoint of TGHT to 700A and re-initiating auto-ramp.    Wednesday, August 19, 2015, 17:13 TGHT reached to 700A/10.5V, direct voltage at 5.2V, and temp measured at both ends at 1755C.  Vac is coming down from 4.2e-6 Torr.  Stepping up TGHT to reach 1800C Wednesday, August 19, 2015, 17:22 Increased TGHT to 722A/11.3V (direct voltage at 5.48V) to reach 1800C (consistant with the heating curve as for the previous HPTa target, elog 184) Will continue to condition the target at this temperature for overnight.  Cooling down can be initiated tomorrow morning at 2A/min --- Please measure the target temperature from the new window port before cooling it down.

 Thursday, August 20, 2015, 08:27

OMEGA = 1830C

Internal temperature using Mikron taken from the second 'new' view port: Hottest point on target leg = 2250C; hottest point on target material discs inside container = 1830C.

IGP1 = 1.5e-6 Torr.

EVAP2 has been sitting at max setpoints for ~15hours.

Initiated auto-cool at 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.

 Tuesday, August 25, 2015, 11:50

Container coated with TaC using new method: Ends tapped off,  with liquid poured in and swirled around entire container, then poured back out - 'flushing technique'

Container is wrapped with 3 x Ta heat shields, not incl center block.

Loaded into EVAP2 and currently pumping down.

 Tuesday, August 25, 2015, 13:52

IGP1 = 2.2e-6 Torr.

HS water valves opened.

No leaks detected.

Tapped up manually to 35A.

Vacuum stable.

Initiated auto ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively.

Final setpoints for TGHT = 720A and TBHT = 230A, with final desired temp of 1800C

 Wednesday, August 26, 2015, 09:56

IGP1 = 8.8e-7 Torr.

TGHT = 260A, 3.0V

TBHT = 145A, 1.8V

Increasing ramping rate to 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.

 Wednesday, August 26, 2015, 14:15

IGP1 = 3.5e-6 Torr.

TGHT = 720A, 11.3V

TBHT = 230A, 3.2V

DV = 5.48V

OMEGA RS [right side-old port] = 1745C

OMEGA LS [left side-new port] = 1880C

Tapping up manually to achieve 1800C on OMEGA RS

 Wednesday, August 26, 2015, 14:44

IGP1 = 3.7e-6 Torr.

TGHT = 748A, 11.9V

DV = 5.78V

OMEGA RS = 1803C

OMEGA LS = 1935C

Thursday, August 27, 2015, 07:31

 Remained at max setpoints for ~17hrs.

IGP1 = 1.3e-6 Torr.

DV = 5.79V

OMEGA RS = 1862 [this reading may not be correct due to the laser being moved at max setpoint - this temperature reading may be taken from a different location then the last reading]

OMEGA LS = 1955

Initiating auto-cool at 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.

Tuesday, September 01, 2015, 17:16

Target container contains 533 discs of SiC with packed length of 17cm. 

Mass of 533 discs SiC(green)  = 57.8979g

Total mass SiC(green) + target container = 1455g

Container is wrapped with 3 heatshields; no end caps are inserted yet.

Sintering temp at 1800C - TGHT will be set accordingly.  TBHT max at 230A. 

Chamber is currently being pumped down. 

John Wong wrote:

Tuesday, September 01, 2015, 17:16 Target container contains 533 discs of SiC with packed length of 17cm.  Mass of 533 discs SiC(green)  = 57.8979g Total mass SiC(green) + target container = 1455g Container is wrapped with 3 heatshields; no end caps are inserted yet. Sintering temp at 1800C - TGHT will be set accordingly.  TBHT max at 230A.  Chamber is currently being pumped down.

 Wednesday, September 02, 2015, 09:11

HS water valves opened, no leaks detected.

IGP1 = 1.15e-6 Torr

Tapped up manually to 40A.

Waited ~1hr40 for vacuum to stabilize.

IGP1 = 3.6e-6 Torr.

Max setpoints set to TGHT = 630A and TBHT = 230A, ~1400C

Initiating auto ramp at a rate of 0.2A/min and 0.1A/min for the TGHT and TBHT respectively.

Once max setpoints achieved, will tap up manually until window port becomes coated [as previously observed]

Once window port becomes coated will leave at set temp for ~4hrs to continue with outgassing, then cool down, clean window and ramp back up.

If LS port still clean, will continue to ramp up to final desired temperature of 1800C.

 Wednesday, September 02, 2015, 14:23

IGP1 = 4.0e-5 Torr.

Vacuum too high, stopped auto-ramp and tapped down manually.

Dropped TGHT down from 80A to 50A

Dropped TBHT down from 55A to 50A

Wednesday, September 02, 2015, 15:29

Vacuum down to IGP1 = 1.2e-5 Torr.

Re-initiating auto-ramp...

 Tuesday, September 08, 2015, 10:04

IGP1 = 4.5e-7 Torr.

TGHT = 630A, 9.6V

TBHT = 230A, 3.2V

DV = 0.22V

OMEGA RS = 1476C

OMEGA LS = 1450C

see attached photo for screenshot.

will tap up manually with a visual on both window ports...

Laura Lambert wrote:

John Wong wrote: Tuesday, September 01, 2015, 17:16 Target container contains 533 discs of SiC with packed length of 17cm.  Mass of 533 discs SiC(green)  = 57.8979g Total mass SiC(green) + target container = 1455g Container is wrapped with 3 heatshields; no end caps are inserted yet. Sintering temp at 1800C - TGHT will be set accordingly.  TBHT max at 230A.  Chamber is currently being pumped down.     Wednesday, September 02, 2015, 09:11 HS water valves opened, no leaks detected. IGP1 = 1.15e-6 Torr Tapped up manually to 40A. Waited ~1hr40 for vacuum to stabilize. IGP1 = 3.6e-6 Torr. Max setpoints set to TGHT = 630A and TBHT = 230A, ~1400C Initiating auto ramp at a rate of 0.2A/min and 0.1A/min for the TGHT and TBHT respectively. Once max setpoints achieved, will tap up manually until window port becomes coated [as previously observed] Once window port becomes coated will leave at set temp for ~4hrs to continue with outgassing, then cool down, clean window and ramp back up. If LS port still clean, will continue to ramp up to final desired temperature of 1800C.  Wednesday, September 02, 2015, 14:23 IGP1 = 4.0e-5 Torr. Vacuum too high, stopped auto-ramp and tapped down manually. Dropped TGHT down from 80A to 50A Dropped TBHT down from 55A to 50A Wednesday, September 02, 2015, 15:29 Vacuum down to IGP1 = 1.2e-5 Torr. Re-initiating auto-ramp...  Tuesday, September 08, 2015, 10:04 IGP1 = 4.5e-7 Torr. TGHT = 630A, 9.6V TBHT = 230A, 3.2V DV = 0.22V OMEGA RS = 1476C OMEGA LS = 1450C see attached photo for screenshot. will tap up manually with a visual on both window ports...

 Tuesday, September 08, 2015, 15:44

TGHT has stepped up to 820A.  Coating on both windows is becoming obvious and it's interfering the temp readers; however, the left window (see attachment, which is further away from the target) is lightly coated than the right.  See attachment for The Temp (and Power) vs current plots.

Target will remained heated at the current and will be cooled down later today. 

The target will be re-conditioned up to 820A and temp and mass will be re-measured.

Plans:

The chamber will be vented tomorrow and the target will be taken out to weigh for mass change. 

The chamber windows will need to be clean.

A piece of Ta foil will be cover in front of the ionizer to trap any loss material (if any).

 Tuesday, September 08, 2015, 17:37

TGHT was at 800A for 2 hours before ramping up 820A for another 2 hours heating.  More coating on the right window is observed and temp reading came down to 1340C.  The left window remains the same and temp reads at 1646C.  

Ramping TGHT/TBHT to 0A at 2A/min and 1A/min, respectively.  

 Wednesday, September 09, 2015, 12:27

Result after the sintering process:

No yellow crystal formed (compared to previously observed SiC targets that heated up above 1900C). 

Total green mass = 57.90g 

mass of graphite foil = 0.035g x 533 discs = 18.7g 

mass of green SiC = 39.30g 

Target container with SiC before sintered = 1455g 

Target container after sintered = 1450g 

mass loss ~ 5.0g ~ 13% organic mass, as expected!  

The target will undergo the re-condition stage, and the temperature will be measured from 600A to 820A. 

John Wong wrote:

Laura Lambert wrote: John Wong wrote: Tuesday, September 01, 2015, 17:16 Target container contains 533 discs of SiC with packed length of 17cm.  Mass of 533 discs SiC(green)  = 57.8979g Total mass SiC(green) + target container = 1455g Container is wrapped with 3 heatshields; no end caps are inserted yet. Sintering temp at 1800C - TGHT will be set accordingly.  TBHT max at 230A.  Chamber is currently being pumped down.     Wednesday, September 02, 2015, 09:11 HS water valves opened, no leaks detected. IGP1 = 1.15e-6 Torr Tapped up manually to 40A. Waited ~1hr40 for vacuum to stabilize. IGP1 = 3.6e-6 Torr. Max setpoints set to TGHT = 630A and TBHT = 230A, ~1400C Initiating auto ramp at a rate of 0.2A/min and 0.1A/min for the TGHT and TBHT respectively. Once max setpoints achieved, will tap up manually until window port becomes coated [as previously observed] Once window port becomes coated will leave at set temp for ~4hrs to continue with outgassing, then cool down, clean window and ramp back up. If LS port still clean, will continue to ramp up to final desired temperature of 1800C.  Wednesday, September 02, 2015, 14:23 IGP1 = 4.0e-5 Torr. Vacuum too high, stopped auto-ramp and tapped down manually. Dropped TGHT down from 80A to 50A Dropped TBHT down from 55A to 50A Wednesday, September 02, 2015, 15:29 Vacuum down to IGP1 = 1.2e-5 Torr. Re-initiating auto-ramp...  Tuesday, September 08, 2015, 10:04 IGP1 = 4.5e-7 Torr. TGHT = 630A, 9.6V TBHT = 230A, 3.2V DV = 0.22V OMEGA RS = 1476C OMEGA LS = 1450C see attached photo for screenshot. will tap up manually with a visual on both window ports...    Tuesday, September 08, 2015, 15:44 TGHT has stepped up to 820A.  Coating on both windows is becoming obvious and it's interfering the temp readers; however, the left window (see attachment, which is further away from the target) is lightly coated than the right.  See attachment for The Temp (and Power) vs current plots. Target will remained heated at the current and will be cooled down later today.    The target will be re-conditioned up to 820A and temp and mass will be re-measured. Plans: The chamber will be vented tomorrow and the target will be taken out to weigh for mass change.  The chamber windows will need to be clean. A piece of Ta foil will be cover in front of the ionizer to trap any loss material (if any).  Tuesday, September 08, 2015, 17:37 TGHT was at 800A for 2 hours before ramping up 820A for another 2 hours heating.  More coating on the right window is observed and temp reading came down to 1340C.  The left window remains the same and temp reads at 1646C.   Ramping TGHT/TBHT to 0A at 2A/min and 1A/min, respectively.    Wednesday, September 09, 2015, 12:27 Result after the sintering process: No yellow crystal formed (compared to previously observed SiC targets that heated up above 1900C).  Total green mass = 57.90g  mass of graphite foil = 0.035g x 533 discs = 18.7g  mass of green SiC = 39.30g  Target container with SiC before sintered = 1455g  Target container after sintered = 1450g  mass loss ~ 5.0g ~ 13% organic mass, as expected!   The target will undergo the re-condition stage, and the temperature will be measured from 600A to 820A.

 Wednesday, September 09, 2015, 17:39

Both end-caps are inserted onto the targets.  The total mass (Target, Sintered SiC, end caps, 4x 19"round graphite foils) = 1453g.

Target is wrapped with 3 layers of heat shields.  

The extraction electrode is wrapped with Ta-foil (see attachment).  This is to trap any lose particle, if any.  

Chamber is currently being pumped down, currently at 1.2e-5 Torr.  

John Wong wrote:

John Wong wrote: Laura Lambert wrote: John Wong wrote: Tuesday, September 01, 2015, 17:16 Target container contains 533 discs of SiC with packed length of 17cm.  Mass of 533 discs SiC(green)  = 57.8979g Total mass SiC(green) + target container = 1455g Container is wrapped with 3 heatshields; no end caps are inserted yet. Sintering temp at 1800C - TGHT will be set accordingly.  TBHT max at 230A.  Chamber is currently being pumped down.     Wednesday, September 02, 2015, 09:11 HS water valves opened, no leaks detected. IGP1 = 1.15e-6 Torr Tapped up manually to 40A. Waited ~1hr40 for vacuum to stabilize. IGP1 = 3.6e-6 Torr. Max setpoints set to TGHT = 630A and TBHT = 230A, ~1400C Initiating auto ramp at a rate of 0.2A/min and 0.1A/min for the TGHT and TBHT respectively. Once max setpoints achieved, will tap up manually until window port becomes coated [as previously observed] Once window port becomes coated will leave at set temp for ~4hrs to continue with outgassing, then cool down, clean window and ramp back up. If LS port still clean, will continue to ramp up to final desired temperature of 1800C.  Wednesday, September 02, 2015, 14:23 IGP1 = 4.0e-5 Torr. Vacuum too high, stopped auto-ramp and tapped down manually. Dropped TGHT down from 80A to 50A Dropped TBHT down from 55A to 50A Wednesday, September 02, 2015, 15:29 Vacuum down to IGP1 = 1.2e-5 Torr. Re-initiating auto-ramp...  Tuesday, September 08, 2015, 10:04 IGP1 = 4.5e-7 Torr. TGHT = 630A, 9.6V TBHT = 230A, 3.2V DV = 0.22V OMEGA RS = 1476C OMEGA LS = 1450C see attached photo for screenshot. will tap up manually with a visual on both window ports...    Tuesday, September 08, 2015, 15:44 TGHT has stepped up to 820A.  Coating on both windows is becoming obvious and it's interfering the temp readers; however, the left window (see attachment, which is further away from the target) is lightly coated than the right.  See attachment for The Temp (and Power) vs current plots. Target will remained heated at the current and will be cooled down later today.    The target will be re-conditioned up to 820A and temp and mass will be re-measured. Plans: The chamber will be vented tomorrow and the target will be taken out to weigh for mass change.  The chamber windows will need to be clean. A piece of Ta foil will be cover in front of the ionizer to trap any loss material (if any).  Tuesday, September 08, 2015, 17:37 TGHT was at 800A for 2 hours before ramping up 820A for another 2 hours heating.  More coating on the right window is observed and temp reading came down to 1340C.  The left window remains the same and temp reads at 1646C.   Ramping TGHT/TBHT to 0A at 2A/min and 1A/min, respectively.    Wednesday, September 09, 2015, 12:27 Result after the sintering process: No yellow crystal formed (compared to previously observed SiC targets that heated up above 1900C).  Total green mass = 57.90g  mass of graphite foil = 0.035g x 533 discs = 18.7g  mass of green SiC = 39.30g  Target container with SiC before sintered = 1455g  Target container after sintered = 1450g  mass loss ~ 5.0g ~ 13% organic mass, as expected!   The target will undergo the re-condition stage, and the temperature will be measured from 600A to 820A.     Wednesday, September 09, 2015, 17:39 Both end-caps are inserted onto the targets.  The total mass (Target, Sintered SiC, end caps, 4x 19"round graphite foils) = 1453g. Target is wrapped with 3 layers of heat shields.   The extraction electrode is wrapped with Ta-foil (see attachment).  This is to trap any lose particle, if any.   Chamber is currently being pumped down, currently at 1.2e-5 Torr.

 Thursday, September 10, 2015, 09:55

HS water valves opened this morning, no leaks detected.

TGHT and TBHT tapped up manually to 35A.

IGP1 = 4.4e-7 Torr, vacuum stable.

Initiating auto-ramp at 1.0A/min and 0.5A/min for the TGHT and TBHT respectively with final setpoints of 600A and 230A.

Thursday, September 24, 2015, 08:39

IGP1 = 6.5e-7Torr

HS water valves opened, no leaks detected.

Tapped up manually to 35A.

Waited ~20min.

Vacuum stable, IGP1 = 1.5e-6 Torr.

Initiated auto-ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively with final setpoints of 250A and 230A.

Final temp of 1200C on auto-ramp in order to initiate temperature measurements starting at ~1200C.

Thursday, September 24, 2015, 10:24  

IGP1 = 8.7e-7 Torr

TGHT = 44A, TBHT = 38A

Increasing auto-ramp to 0.5A/min and 0.2A/min for the TGHT and TBHT respectively.

 Thursday, September 24, 2015, 12:03

Vacuum spiking rapidly.

Stopped auto-ramp, tapped TGHT and TBHT down manually, allowing vacuum to stabilize.

IGP1 = 3.5e-6 Torr.

Re-initiating auto-ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively.

John Wong wrote:

Laura Lambert wrote: Thursday, September 24, 2015, 08:39 IGP1 = 6.5e-7Torr HS water valves opened, no leaks detected. Tapped up manually to 35A. Waited ~20min. Vacuum stable, IGP1 = 1.5e-6 Torr. Initiated auto-ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively with final setpoints of 250A and 230A. Final temp of 1200C on auto-ramp in order to initiate temperature measurements starting at ~1200C. Thursday, September 24, 2015, 10:24   IGP1 = 8.7e-7 Torr TGHT = 44A, TBHT = 38A Increasing auto-ramp to 0.5A/min and 0.2A/min for the TGHT and TBHT respectively.      Thursday, September 24, 2015, 12:04  A few notes about the target container:The Ta-foil is cut in a full length of the target container, and that also covers up the back block, and the container is wrapped with 3 sheets (see attachment)  The inner tube is coated with TaC, using the "flushing technique" - the coating looks much better; will see how it turns out after the sintering process The target will be heated up to 1900C .  Due to the new wrapping of the Ta-heat shield, the heat distribution may be different.  So the target heater will be ramped up to achieve the desired temperature.   Thursday, September 24, 2015, 18:45   TGHT reached to 250A3.6V, TGHT at 230A and stayed for 1.5 hours.  Temp-L = 1280C, Temp-R = 1360C.   Auto-ramp TGHT to 500A at 1A/min and heat at that current for overnight.  Will take temp reading tomorrow.   Thursday, September 24, 2015, 23:08   TGHT has reached to 500A/8.57V.  Temp-L = 1895C, Temp-R = 2073C. (Not sure why the temperature is real, will need to investigate more to get an absolute temp) Just to be safe… Ramping down TGHT to 425A (according to e-log id 216, Temp-R reached to 1800C with TGHT at 425A/6.84V, but no temp measured for the left at that time) Will check again later. Friday, September 25, 2015, 11:52   The target has been heated at 420A for ~12hours; temp measured ~1900C, slightly higher than the previous target container (W.O#40860-1); the Ta-wraping could affect the heat distribution.   The temperature is also confirmed by using the 2-C digital pyrometer.  The tube inner surface is measured about 1900C, and the ionizer tube is about 2400C.  (see attachment #2). Initiating auto-cooling at 2A/min for TGHT and 1A/min for TBHT. The target will be inspected next Monday  Wednesday, September 30, 2015, 16:01 The target container is fully sintered (see attachment#3)  It is still in the discussion where this container will be used online for the UCx.  Nevertheless, the target contain is ready and it looks pretty good.

 Tuesday, October 06, 2015, 15:09

After further discussion, we are going to reheat this container to 420A.  The temperature will be measured with the thermocouple - probe inside the centre of the tube - and the 2C-IR for comparison. 

This test is to ensure that the container is actually heated to 1900C before the UCx material can be loaded

The chamber has been pumped down to 1.92e-6 Torr.  Heat shield valve is open and no leaks are detected. 

Ramping up TBHT to 230A max and TGHT to achieve ~1900C

 Wednesday, October 07, 2015, 11:12

Yesterday...

TBHT ramped up to 230A and TGHT was at 160A before taking temperature readings. 

TGHT from 160A to 423A, IR2C temp reading increases linearly from 1138C to 1900C, whereas the thermocouple readouts are not quite linear, 1040C to 1748C (see attachment)

After 18 hours, both temp reader dropped about 45C. 

Increased TGHT to 440C, IR2C & thermocouple currently read 1912C & 1762C, respectively. 

 Wednesday, October 07, 2015, 12:28

Lowered TBHT to 200A and TGHT remained at 440A.  IR2C = 1900C, TypeC = 1745C.  Not much affect from TBHT. 

Will increase TBHT back to 230A, then start ramping down TGHT and taking temp readings. 

 Wednesday, October 07, 2015, 17:49

Stepped down TGHT to 160A and TBHT stayed at 230A.  Cooling down temp is generated.  See attachment. 

Notice the overall temp during cooling is lower than that during heating. 

TGHT and TBHT will be ramped down to 0A. 

Chamber will be vented tomorrow. 

More details later...

John Wong wrote:

John Wong wrote: Laura Lambert wrote: Thursday, September 24, 2015, 08:39 IGP1 = 6.5e-7Torr HS water valves opened, no leaks detected. Tapped up manually to 35A. Waited ~20min. Vacuum stable, IGP1 = 1.5e-6 Torr. Initiated auto-ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively with final setpoints of 250A and 230A. Final temp of 1200C on auto-ramp in order to initiate temperature measurements starting at ~1200C. Thursday, September 24, 2015, 10:24   IGP1 = 8.7e-7 Torr TGHT = 44A, TBHT = 38A Increasing auto-ramp to 0.5A/min and 0.2A/min for the TGHT and TBHT respectively.      Thursday, September 24, 2015, 12:04  A few notes about the target container:The Ta-foil is cut in a full length of the target container, and that also covers up the back block, and the container is wrapped with 3 sheets (see attachment)  The inner tube is coated with TaC, using the "flushing technique" - the coating looks much better; will see how it turns out after the sintering process The target will be heated up to 1900C .  Due to the new wrapping of the Ta-heat shield, the heat distribution may be different.  So the target heater will be ramped up to achieve the desired temperature.   Thursday, September 24, 2015, 18:45   TGHT reached to 250A3.6V, TGHT at 230A and stayed for 1.5 hours.  Temp-L = 1280C, Temp-R = 1360C.   Auto-ramp TGHT to 500A at 1A/min and heat at that current for overnight.  Will take temp reading tomorrow.   Thursday, September 24, 2015, 23:08   TGHT has reached to 500A/8.57V.  Temp-L = 1895C, Temp-R = 2073C. (Not sure why the temperature is real, will need to investigate more to get an absolute temp) Just to be safe… Ramping down TGHT to 425A (according to e-log id 216, Temp-R reached to 1800C with TGHT at 425A/6.84V, but no temp measured for the left at that time) Will check again later. Friday, September 25, 2015, 11:52   The target has been heated at 420A for ~12hours; temp measured ~1900C, slightly higher than the previous target container (W.O#40860-1); the Ta-wraping could affect the heat distribution.   The temperature is also confirmed by using the 2-C digital pyrometer.  The tube inner surface is measured about 1900C, and the ionizer tube is about 2400C.  (see attachment #2). Initiating auto-cooling at 2A/min for TGHT and 1A/min for TBHT. The target will be inspected next Monday  Wednesday, September 30, 2015, 16:01 The target container is fully sintered (see attachment#3)  It is still in the discussion where this container will be used online for the UCx.  Nevertheless, the target contain is ready and it looks pretty good.     Tuesday, October 06, 2015, 15:09 After further discussion, we are going to reheat this container to 420A.  The temperature will be measured with the thermocouple - probe inside the centre of the tube - and the 2C-IR for comparison.  This test is to ensure that the container is actually heated to 1900C before the UCx material can be loaded The chamber has been pumped down to 1.92e-6 Torr.  Heat shield valve is open and no leaks are detected.  Ramping up TBHT to 230A max and TGHT to achieve ~1900C  Wednesday, October 07, 2015, 11:12 Yesterday... TBHT ramped up to 230A and TGHT was at 160A before taking temperature readings.  TGHT from 160A to 423A, IR2C temp reading increases linearly from 1138C to 1900C, whereas the thermocouple readouts are not quite linear, 1040C to 1748C (see attachment) After 18 hours, both temp reader dropped about 45C.  Increased TGHT to 440C, IR2C & thermocouple currently read 1912C & 1762C, respectively.   Wednesday, October 07, 2015, 12:28 Lowered TBHT to 200A and TGHT remained at 440A.  IR2C = 1900C, TypeC = 1745C.  Not much affect from TBHT.  Will increase TBHT back to 230A, then start ramping down TGHT and taking temp readings.   Wednesday, October 07, 2015, 17:49 Stepped down TGHT to 160A and TBHT stayed at 230A.  Cooling down temp is generated.  See attachment.  Notice the overall temp during cooling is lower than that during heating.  TGHT and TBHT will be ramped down to 0A.  Chamber will be vented tomorrow.  More details later...

Thursday, October 08, 2015, 12:01  

Test 2: To heat the target container back to ~440A and measure the temperature with the type C thermocouple (inside the tube, away from the centre block) and compared the temp reading with the 2C-IR.   

Chamber is currently being pump down, vac at 9e-6 Torr.  

Will ramp up TGHT to 160A and TBHT to 230A at 2A/min.

 Thursday, October 08, 2015, 17:01

TGHT is now at 440A, TBHT is constant at 230A - IR2C is reading the same as before, 1910C, but Type C is reading lower at 1770C.  (see attachment)

Will keep the current at 440A overnight. 

 Friday, October 09, 2015, 10:06

TGHT has stayed at 440A, TBHT at 230A for ~18hours.  R-temp dropped slightly from 1910C to 1890C and typeC dropped from 1770 to 1756; otherwise the measurements are reproducible. 

After the group discussion, the online heating curve will be re-calculated based on the temp reading from the IR2C curve. 

Next, the target container will be filled with UCx material and the conditioning current for Evap#1 will only go up to 440A (or at least the required current to reach the end of the re-carbonization step). 

So pay attention to the current when heating the target up in EVAP#1.

Initiate cooling at 2A/min for TGHT and 1A/min TBHT

 Friday, October 09, 2015, 11:35

A note about the voltage that may explain the change in the temperature: 

See attachment #2: 

Left plot = Test #1:

Initially TGHT ramped up to 423A and temp measured at 1900C.  Notice, about an hour later, there was a sudden drop in the voltage, and from thereon, the temp was measured at 1860C.  About 18 hours later, TGHT was increased to 440A to achieve 1910C.  

Right plot = Test #2 
Ramped up TGHT to 440A, temp measured 1910C.  At that constant current over the 6 hours period, the voltage slowly increased, and the temperature slightly dropped to 1895C.  

 Wednesday, October 21, 2015, 17:35

This container is prepared for a backup UCx target (otherwise it will be used for development purposes).

The container is coated with TaC; one layer of Ta-heat shield is used. 

TGHT will be ramped up to reach 1900C (previous container had TGHT ramped up to 440A).  

TBHT will be ramped up to max 230A.  

Chamber is currently being pumped down.  

Heating can begin once the vacuum is good, currently at 4.8e-5 Torr. 

 Friday, October 23, 2015, 16:15

TGHT reached to 500A and temp measured at 1940C.  More about the temp plot can be found in the dropbox.

Initiated cooling down at 2A/min. 

Target will be inspected next Monday.

John Wong wrote:

Wednesday, October 21, 2015, 17:35 This container is prepared for a backup UCx target (otherwise it will be used for development purposes). The container is coated with TaC; one layer of Ta-heat shield is used.  TGHT will be ramped up to reach 1900C (previous container had TGHT ramped up to 440A).   TBHT will be ramped up to max 230A.   Chamber is currently being pumped down.   Heating can begin once the vacuum is good, currently at 4.8e-5 Torr.

 Thursday, October 22, 2015, 11:36

HS water valves opened, no leaks detected.

Tapped up manually to 35A.

Vacuum stabilized, initiated auto-ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively.

Final setpoints TGHT = 300A, TBHT = 230A

IGP1 = 1.0e-6 Torr; TGHT = 45.18A, 0.17V; TBHT = 38.4A, 0.41V

Laura Lambert wrote:

John Wong wrote:  Wednesday, October 21, 2015, 17:35 This container is prepared for a backup UCx target (otherwise it will be used for development purposes). The container is coated with TaC; one layer of Ta-heat shield is used.  TGHT will be ramped up to reach 1900C (previous container had TGHT ramped up to 440A).   TBHT will be ramped up to max 230A.   Chamber is currently being pumped down.   Heating can begin once the vacuum is good, currently at 4.8e-5 Torr.     Thursday, October 22, 2015, 11:36 HS water valves opened, no leaks detected. Tapped up manually to 35A. Vacuum stabilized, initiated auto-ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively. Final setpoints TGHT = 300A, TBHT = 230A IGP1 = 1.0e-6 Torr; TGHT = 45.18A, 0.17V; TBHT = 38.4A, 0.41V

 Thursday, October 22, 2015, 17:09

Pressure coming down to 1.5e-6 Torr. 

Increased ramping rate to 2A/min for both TGHT and TBHT.

 Thursday, November 05, 2015, 16:19

Springs coated with TaC and loaded into container for sintering.

3x Ta heat shield.

EVAP2 currently pumping down.

 Friday, November 06, 2015, 08:39

Opened HS water valves, no leaks detected.

Tapped up manually to 35A.

IGP1 = 5.5e-7 Torr.

 Friday, November 06, 2015, 10:08

IGP1 = 5.8e-7 Torr.

Vacuum stable.

Initiating auto-ramp at 0.2A/min and 0.1A/min with final setpoints of 450A and 230A for the TGHT and TBHT respectively.

See photos attached to view how springs were coated and loaded into container.

 Monday, November 09, 2015, 09:07

TGHT reached 450A, 7.2V ~8pm sat, nov 7th.

OMEGA = 1775C

IGP1 = 3.2e-7 Torr.

Tapping up manually to 1900C.

Laura Lambert wrote:

Thursday, November 05, 2015, 16:19 Springs coated with TaC and loaded into container for sintering. 3x Ta heat shield. EVAP2 currently pumping down.  Friday, November 06, 2015, 08:39 Opened HS water valves, no leaks detected. Tapped up manually to 35A. IGP1 = 5.5e-7 Torr.  Friday, November 06, 2015, 10:08 IGP1 = 5.8e-7 Torr. Vacuum stable. Initiating auto-ramp at 0.2A/min and 0.1A/min with final setpoints of 450A and 230A for the TGHT and TBHT respectively. See photos attached to view how springs were coated and loaded into container.  Monday, November 09, 2015, 09:07 TGHT reached 450A, 7.2V ~8pm sat, nov 7th. OMEGA = 1775C IGP1 = 3.2e-7 Torr. Tapping up manually to 1900C.

 Monday, November 09, 2015, 12:30

Checked the temp on the inner surface (not at the spring) of the container was around 2050C at 500A. 

The TaC coated spring is reading at 1900C; that's what the OMEGA is reading with the setting for 2-colors and slope at 0.98.

Lower TGHT to 450A/ 7.12V.

By comparing the data from the previous temp curve (OMEGA slope at 0.98) with no material inside the container,  the voltage and current plot is aligned with the curve.

Changed OMEGA setting slope to 1.04.  Current temp is reading at 1917C at 450A.

For 2-Color setting, the emissivity should be negligible.  That makes me believe that different materials has different slope setting for the temp reading.  

One thing to note is that, the sintering temp of TaC is around 1900-2000C.  It was clear that the container was fully sintered with TGHT at 450A.

Will need to gather more data with different material to understand the slope setting better. 

Try: 

SiC at 1700C, slope at 1.04

ZrC at 1900C, slope at 104

Ta at 1900C, slope at 0.98.

Compare the data...

 Data from thermocouple attached. Raw data and Excel sheet with plot.

Temperature measurements in progress this week for Ta HP-SIS.

See attachment for the current settings and rampings of the TGHT/TBHT  for the temperature measurements taken on  Jan. 9-10, 2016 .

Note: TBHT PS tripped off on Jan. 9, 2016 (see first page of the attached file) and couldn't turn it ON again over the week-end.

 Tuesday, February 16, 2016, 14:19

coated with TaC yesterday and let dry overnight.

wrapped with one long Ta heat shield - wrapped around tube 3x, with Ta wire to offset Ta foil away from container

loaded into evap2 and currently pumping down.

 Wednesday, February 17, 2016, 10:51

HS water valves opened, no leaks detected.

Tapped up manually to 35A.

Waited ~20min, vacuum stable.

IGP1 = 5.9e-7 Torr.

Initiating auto-ramp at 0.2A/min to a final setpoint of 400A.

Final desired temperature = 1900C

 Thursday, February 18, 2016, 09:16

IGP1 = 6.6e-7 Torr.

TGHT = 303A, 4.3V

OMEGA = 1311C

Increasing ramping rate to 1.0A/min.

Laura Lambert wrote:

Tuesday, February 16, 2016, 14:19 coated with TaC yesterday and let dry overnight. wrapped with one long Ta heat shield - wrapped around tube 3x, with Ta wire to offset Ta foil away from container loaded into evap2 and currently pumping down.  Wednesday, February 17, 2016, 10:51 HS water valves opened, no leaks detected. Tapped up manually to 35A. Waited ~20min, vacuum stable. IGP1 = 5.9e-7 Torr. Initiating auto-ramp at 0.2A/min to a final setpoint of 400A. Final desired temperature = 1900C  Thursday, February 18, 2016, 09:16 IGP1 = 6.6e-7 Torr. TGHT = 303A, 4.3V OMEGA = 1311C Increasing ramping rate to 1.0A/min.

 Thursday, February 18, 2016, 13:10

TGHT reached to 450A, temp at 1800C.  Stepped up TGHT 490A, temp measured at ~1900C. 

Started Ta#47 heating at Evap2 using the autoramp program. The TGHT current is setup to go to 300A (for now) and the TBHT to 230A (final value).