  Evaporator_2, Page 20 of 35  Not logged in ELOG logo
IDdown Date Author Target Material Target Oven W.O# Source Status Subject
  308   Monday, June 27, 2016, 11:08 Laura LambertEmpty41790-3LP-SISDonesintering TaC coating on UCx#17 container

 Monday, June 27, 2016, 11:07

Container coated with TaC using 'flushing technique'.

Wrapped with 3 x Ta heat shields, incl center block - new method of each layer being one long single Ta foil covering entire container incl center block

Currently pumping down in evap2


 Monday, June 27, 2016, 13:23

HS water valves opened

Tapped up manually to 35A

Waited ~1hr, vacuum stable

IGP1 = 1.8e-6 Torr

Initiating auto ramp for TGHT @ 0.2A/min to a max setpoint of 400A

Initiating auto ramp for TBHT @ 0.1A/min to a max setpoint of 230A

Once max setpoints achieved, will tap up manually to final desired temperature of 1900C


 Wednesday, June 29, 2016, 11:33

IGP1 = 1.9e-7

TGHT = 400A, 6.0V

TBHT = 223A, 3.9V

OMEGA = 1885C

Remained at these settings for ~13hrs

Increased TBHT max voltage to 4.3V to achieve 230A

TBHT = 230A, 4.1V

OMEGA = 1890C

Tapped up to TGHT = 405A, 6.17V to achieve 1900C...OMEGA reached 1915C

Lowered TGHT to = 403A, 6.12V

OMEGA = 1905C

Measured ~1870C with the mikron, same window the OMEGA measurements are taken out of.

IGP1 = 2.1e-7


 Thursday, June 30, 2016, 08:44

TGHT = 403A, 6.07V

OMEGA = 1886C

Tapped back up to 1900C

TGHT = 410A, 6.22V

OMEGA = 1911C


Thursday, June 30, 2016, 16:01

OMEGA = 1911C

Container has remained at ~1900C for ~1.5 days

Initiating auto-cool at 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.


 Monday, July 04, 2016, 09:59

Vented in air and opened up this morning.

Container looks good.

Confirmed coating fully sintered with J.Wong.

Photos attached.


 

Attachment 1: LP-SIS_post_sintering_TaC(3).jpg
LP-SIS_post_sintering_TaC(3).jpg
Attachment 2: LP-SIS_post_sintering_TaC(4).jpg
LP-SIS_post_sintering_TaC(4).jpg
  307   Thursday, June 16, 2016, 11:01 Laura LambertSiC41369-4HP-SISDoneConditioning SiC#33 - 1st beta SiC target!

 Thursday, June 16, 2016, 10:59

Previously sintered over weekend [see elog i.d 306]

Target container contains 450 discs of SiC [4 x 5 packs + 430 single discs]

Target packed length = 16cm. 

Mass of 533 discs SiC(green)  = 53.8758g

Container is wrapped with 3 heatshields; no end caps are inserted yet - coated spring inserted both sides to hold discs in place.

Conditioning temp = 1800C.

TGHT max = 710A according to sintering data.  TBHT max = 230A. 

Chamber is currently being pumped down. 


 Thursday, June 16, 2016, 15:43

Target was not removed from evap2 after sintering, vented and cleaned windows only.

HS water valves already open.

Stepped up manually to 70A, vacuum stable.

Initiated auto-ramp at 1.0A/min for the TGHT and 0.5A/min for the TBHT with max setpoints of 600A and 230A respectively.

TGHT = 118A, 0.9V

TBHT = 90A, 1.1V

IGP1 = 7.3e-7 Torr


 Friday, June 17, 2016, 12:14

TGHT has been tapped up manually to reach max desired temperature of 1800C

TGHT = 690A, 10.85V

TBHT = 230A, 3.88V

IGP1 = 4.9e-7 Torr

This is a lower current than the current required to reach 1800C during the sintering process.

For sintering, the max current was determined via extrapolation of trendline from raw data due to interference of coating on window and unable to take reliable readings from OMEGA.

For this conditioning process ~1800C is reached on the OMEGA since the window is still ~un-coated.

Will remain at 690A, ~1800C for several days to maximize conditioning process.

See attachment for raw data.


 Monday, June 20, 2016, 09:01

At the end of the day on friday 17th, OMEGA read ~1750C - no change in the current or voltage, vacuum was stable, this was the max setpoints used to reach 1800C.

This morning OMEGA = 2040C

TGHT = 690A, 10.95V

vacuum stable at IGP1 = 1.8e-7 Torr.

Slightly more noticeable coating on window port, looks like a thin ink layer, still relatively thin coating [ see attached image]

Also attached is archive from over wknd to show vacuum stable, current unchanged and voltage negligibly changed [only gone up by ~0.1V]


 Friday, June 24, 2016, 13:52

Container has remained at max setpoints for 7 days.

Initiating auto-cool for TGHT @ 2.0A/min and for TBHT @ 1.0A/min.

Will vent chamber and remove from evap2 to pass off for assembly monday morning.

See attachment for updated excel on temperature readings for the conditioning process.


 Monday, June 27, 2016, 08:28

vented in air and removed this morning.

target looks good!

all discs remained nicely alligned.

discs expanded outwards ~1cm, pushed back in to keep target length at 16cm

no visible yellow crystals like previous SiC targets 

endcaps inserted and expanded.

Rh foil inserted.

Ta heat shield foils removed, fins look good.

see photos attached for pictures of target - post conditioning.

coating on window very hard to remove. looked like a light sharpy pen coating on window. ended up scratching off with acetone and screw driver. couldn't remove all of it...

Attachment 1: current_vs_voltage_vs_temp.xlsx
Attachment 2: Tapping_up_from_600A_to_1800C_for_conditioning.JPG
Tapping_up_from_600A_to_1800C_for_conditioning.JPG
Attachment 3: Conditioning_window_port_at_2040C_mon_20th.jpg
Conditioning_window_port_at_2040C_mon_20th.jpg
Attachment 4: archive_of_conditioning_over_wknd.JPG
archive_of_conditioning_over_wknd.JPG
Attachment 5: current_vs_voltage_vs_temp.xlsx
Attachment 6: Evernote_Camera_Roll_20160627_10.jpg
Evernote_Camera_Roll_20160627_10.jpg
Attachment 7: Evernote_Camera_Roll_20160627_102.jpg
Evernote_Camera_Roll_20160627_102.jpg
Attachment 8: Evernote_Camera_Roll_20160627_1023.jpg
Evernote_Camera_Roll_20160627_1023.jpg
Attachment 9: Evernote_Camera_Roll_20160627_10233.jpg
Evernote_Camera_Roll_20160627_10233.jpg
  306   Thursday, June 16, 2016, 10:58 Laura LambertSiC41369-4HP-SISDoneSintering SiC#33 - 1st beta-SiC target!

John Wong wrote:

Laura Lambert wrote:

John Wong wrote:

 

Laura Lambert wrote:

 Thursday, June 09, 2016, 15:39

First target using beta-SiC material!

Target container contains 450 discs of SiC [4 x 5 packs + 430 single discs]

Target packed length = 16cm. 

Mass of 533 discs SiC(green)  = 53.8758g

Container is wrapped with 3 heatshields; no end caps are inserted yet - coated spring inserted both sides to hold discs in place.

Sintering temp = 1800C, TGHT will be set accordingly.  TBHT max at 230A. 

Chamber is currently being pumped down. 


Friday, June 10, 2016, 13:24

HS water valves opened, no leaks detected.

Tapping up manually to 70A...

Auto ramp will be set for TGHT = 0.2A/min to a final setpoint of 520A

Auto-ramp for TBHT = 0.1A/min to a final setpoint of 230A.


 

 

 Friday, June 10, 2016, 16:27

TGHT stepped up to 70A/0.55V.  TGHT at 50A/0.62V. 

Pressure stabilized at 5.5e-5 Torr.

Initiated auto ramping.  TGHT at 0.2A/min --> 520A.  TBHT at 0.1A/min --> 230A.


 

 Monday, June 13, 2016, 09:51

TGHT = 425A, 5.65V

TBHT = 225A, 3.7V

IGP1 = 8.7e-6 Torr.

Increasing ramping rate to 1.0A/min...


 Monday, June 13, 2016, 15:56

Tapped up manually from 520A to 1800C

Extrapolated data on graph to determine correct current required to reach desired max temperature.

Will remain at 1800C for ~48hrs

See attachements for excel sheet and screenshot of striptool.


 

 Wednesday, June 15, 2016, 17:54

TGHT at 710A, 11.35V.  TBHT at 230A/3.86V. 

Omega reading droppd to 1130C due to coating on windows. 

Ionizer tube was measured (center) at around 1900C

Cooling down at 2A/min for TGHT, 1A/min for TBHT. 

Samples will be collected prior to cleaning the windows.

NEXT:  Conditioning.


 

Thursday, June 16, 2016, 09:29

vented in air and opened up this morning.

took some samples to be tested.


 

  305   Wednesday, June 15, 2016, 17:58 John WongSiC41369-4HP-SISIn progressSintering SiC#33 - 1st beta-SiC target!

Laura Lambert wrote:

John Wong wrote:

 

Laura Lambert wrote:

 Thursday, June 09, 2016, 15:39

First target using beta-SiC material!

Target container contains 450 discs of SiC [4 x 5 packs + 430 single discs]

Target packed length = 16cm. 

Mass of 533 discs SiC(green)  = 53.8758g

Container is wrapped with 3 heatshields; no end caps are inserted yet - coated spring inserted both sides to hold discs in place.

Sintering temp = 1800C, TGHT will be set accordingly.  TBHT max at 230A. 

Chamber is currently being pumped down. 


Friday, June 10, 2016, 13:24

HS water valves opened, no leaks detected.

Tapping up manually to 70A...

Auto ramp will be set for TGHT = 0.2A/min to a final setpoint of 520A

Auto-ramp for TBHT = 0.1A/min to a final setpoint of 230A.


 

 

 Friday, June 10, 2016, 16:27

TGHT stepped up to 70A/0.55V.  TGHT at 50A/0.62V. 

Pressure stabilized at 5.5e-5 Torr.

Initiated auto ramping.  TGHT at 0.2A/min --> 520A.  TBHT at 0.1A/min --> 230A.


 

 Monday, June 13, 2016, 09:51

TGHT = 425A, 5.65V

TBHT = 225A, 3.7V

IGP1 = 8.7e-6 Torr.

Increasing ramping rate to 1.0A/min...


 Monday, June 13, 2016, 15:56

Tapped up manually from 520A to 1800C

Extrapolated data on graph to determine correct current required to reach desired max temperature.

Will remain at 1800C for ~48hrs

See attachements for excel sheet and screenshot of striptool.


 

 Wednesday, June 15, 2016, 17:54

TGHT at 710A, 11.35V.  TBHT at 230A/3.86V. 

Omega reading droppd to 1130C due to coating on windows. 

Ionizer tube was measured (center) at around 1900C

Cooling down at 2A/min for TGHT, 1A/min for TBHT. 

Samples will be collected prior to cleaning the windows.

NEXT:  Conditioning.


 

  304   Monday, June 13, 2016, 09:53 Laura LambertSiC41369-4HP-SISIn progressSintering SiC#33 - 1st beta-SiC target!

John Wong wrote:

 

Laura Lambert wrote:

 Thursday, June 09, 2016, 15:39

First target using beta-SiC material!

Target container contains 450 discs of SiC [4 x 5 packs + 430 single discs]

Target packed length = 16cm. 

Mass of 533 discs SiC(green)  = 53.8758g

Container is wrapped with 3 heatshields; no end caps are inserted yet - coated spring inserted both sides to hold discs in place.

Sintering temp = 1800C, TGHT will be set accordingly.  TBHT max at 230A. 

Chamber is currently being pumped down. 


Friday, June 10, 2016, 13:24

HS water valves opened, no leaks detected.

Tapping up manually to 70A...

Auto ramp will be set for TGHT = 0.2A/min to a final setpoint of 520A

Auto-ramp for TBHT = 0.1A/min to a final setpoint of 230A.


 

 

 Friday, June 10, 2016, 16:27

TGHT stepped up to 70A/0.55V.  TGHT at 50A/0.62V. 

Pressure stabilized at 5.5e-5 Torr.

Initiated auto ramping.  TGHT at 0.2A/min --> 520A.  TBHT at 0.1A/min --> 230A.


 

 Monday, June 13, 2016, 09:51

TGHT = 425A, 5.65V

TBHT = 225A, 3.7V

IGP1 = 8.7e-6 Torr.

Increasing ramping rate to 1.0A/min...


 Monday, June 13, 2016, 15:56

Tapped up manually from 520A to 1800C

Extrapolated data on graph to determine correct current required to reach desired max temperature.

Will remain at 1800C for ~48hrs

See attachements for excel sheet and screenshot of striptool.


 

Attachment 1: current_vs_voltage_vs_temp.xlsx
Attachment 2: Tapping_up_from_520A_to_1800C.JPG
Tapping_up_from_520A_to_1800C.JPG
  303   Friday, June 10, 2016, 16:30 John WongSiC41369-4HP-SISIn progressSintering SiC#33 - 1st beta-SiC target!

 

Laura Lambert wrote:

 Thursday, June 09, 2016, 15:39

First target using beta-SiC material!

Target container contains 450 discs of SiC [4 x 5 packs + 430 single discs]

Target packed length = 16cm. 

Mass of 533 discs SiC(green)  = 53.8758g

Container is wrapped with 3 heatshields; no end caps are inserted yet - coated spring inserted both sides to hold discs in place.

Sintering temp = 1800C, TGHT will be set accordingly.  TBHT max at 230A. 

Chamber is currently being pumped down. 


Friday, June 10, 2016, 13:24

HS water valves opened, no leaks detected.

Tapping up manually to 70A...

Auto ramp will be set for TGHT = 0.2A/min to a final setpoint of 520A

Auto-ramp for TBHT = 0.1A/min to a final setpoint of 230A.


 

 

 Friday, June 10, 2016, 16:27

TGHT stepped up to 70A/0.55V.  TGHT at 50A/0.62V. 

Pressure stabilized at 5.5e-5 Torr.

Initiated auto ramping.  TGHT at 0.2A/min --> 520A.  TBHT at 0.1A/min --> 230A.


 

  302   Thursday, June 09, 2016, 15:48 Laura LambertSiC41369-4HP-SISIn progressSintering SiC#33 - 1st beta-SiC target!

 Thursday, June 09, 2016, 15:39

First target using beta-SiC material!

Target container contains 450 discs of SiC [4 x 5 packs + 430 single discs]

Target packed length = 16cm. 

Mass of 533 discs SiC(green)  = 53.8758g

Container is wrapped with 3 heatshields; no end caps are inserted yet - coated spring inserted both sides to hold discs in place.

Sintering temp = 1800C, TGHT will be set accordingly.  TBHT max at 230A. 

Chamber is currently being pumped down. 


Friday, June 10, 2016, 13:24

HS water valves opened, no leaks detected.

Tapping up manually to 70A...

Auto ramp will be set for TGHT = 0.2A/min to a final setpoint of 520A

Auto-ramp for TBHT = 0.1A/min to a final setpoint of 230A.


 

 

Attachment 1: target_with_end-coils.jpg
target_with_end-coils.jpg
  301   Tuesday, May 31, 2016, 11:10 John WongEmpty41369-4HP-SISDonesintering TaC coating on SiC#33 container

Laura Lambert wrote:

 Wednesday, May 25, 2016, 11:37

Container coated with TaC using 'flushing technique' [cleaned ionizer tube with acetone, so no coating inside ionizer tube]

Wrapped with 2 x Ta heat shields - one full height of Ta foil wrapped around cooling fins twice

Currently pumping down in evap2


 Thursday, May 26, 2016, 09:28

Tapped up manually to 40A

IGP1 = 6.6e-7 Torr

Initiating auto-ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively.

Final setpoints for TGHT = 650A and TBHT = 230A

Once max setpoints reached will continue to tap up manually while monitoring temperature to 1900C


 

 Tuesday, May 31, 2016, 11:09

TGHT at 615A/9.08V, temp = 1610C.  Vacuum at 1.8e-7 Torr. 

Tapping up TGHT to reach 1900C


 Tuesday, May 31, 2016, 12:04

TGHT at 765A/11.90V.  Temp at 1900C.  Pressure is coming down from 8.7e-7Torr. 

Will keep at this temperature for a day.


 Wednesday, June 01, 2016, 15:22

Temperature has been stable at 1900C.  Pressure is coming down from 3.4e-7 Torr. 

Cooling down TGHT and TBHT at 2A/min and 1A/min, respectively.


 Friday, June 03, 2016, 12:10

TGHT/TBHT at 0A.  Target can be remained under vacuum until Monday.


 Monday, June 06, 2016, 16:54

Target container was inspected; it looks good


 

  300   Wednesday, May 25, 2016, 11:40 Laura LambertEmpty41369-4HP-SISIn progresssintering TaC coating on SiC#33 container

 Wednesday, May 25, 2016, 11:37

Container coated with TaC using 'flushing technique' [cleaned ionizer tube with acetone, so no coating inside ionizer tube]

Wrapped with 2 x Ta heat shields - one full height of Ta foil wrapped around cooling fins twice

Currently pumping down in evap2


 Thursday, May 26, 2016, 09:28

Tapped up manually to 40A

IGP1 = 6.6e-7 Torr

Initiating auto-ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively.

Final setpoints for TGHT = 650A and TBHT = 230A

Once max setpoints reached will continue to tap up manually while monitoring temperature to 1900C


 

  299   Tuesday, May 24, 2016, 11:18 John WongSiC TARGET BOATIn progressHeat-treatment: Beta-SiC (1um) target discs

Laura Lambert wrote:

John Wong wrote:

The purpose of this experiment is to determined the limiting operating temperature for Beta-SiC.  To do so, samples will be heated in sequence to observe any volatile Si coated on the window.  The coating is observed above 1400C for the conventional SiC (mixuture of alpha and beta) and this coating leads to HV shorting problem. 


Thursday, May 19, 2016, 14:26

Beta-SiC (size ~1um) slurry was prepared and casted on a graphite foil. 

Discs are cut into D-shape

Average thickness (including graphite foil) = 0.349mm

Graphite foil = 0.13mm

Actual SiC thickness = 0.219mm (close to normal SiC thickness)

Samples are loaded into a target boat.

Total discs = 120

Total mass = 14.3507g


Thursday, May 19, 2016, 14:32

Omega slope set to = 1.04

Heat-treatment #1: 1400C


 Thursday, May 19, 2016, 17:04

TGHT ramping up to 250A at 0.5A/min


 

 Friday, May 20, 2016, 08:53

IGP1 = 9.2e-6 Torr.

Increasing ramping rate to 1.0A/min up to 250A


 Friday, May 20, 2016, 09:17

IGP1 = 2.1e-5 Torr

TGHT = 215A, 3.1V

OMEGA = 1035C

Stopping auto-ramp and tapping up manually...


 Friday, May 20, 2016, 12:26

OMEGA slope changed to 1.04

OMEGA reached ~1430C and kept there for ~1hr.

no change. no coating on window observed

tapped up manually to OMEGA =1500C

TGHT = 350A, 5.8V


 Friday, May 20, 2016, 14:17

Not much change to window.

Might be beginning of light dusting, hard to tell.

Will be better observed after longer period of time at 1500C

Will remain at 1500C over weekend.


 

 Tuesday, May 24, 2016, 11:15

Sample has been heated over the long weekend.  Temp dropped to 1400C.  TGHT at 350A/5.78V.  Vac at 1.5e-7 Torr.

It is hard to tell if there is any coating on the window.  Will increase temperature to 1800C


 Tuesday, May 24, 2016, 11:43

Temp at 1620C. TGHT at 440A/7.7V. 

At this temperature, the coating would have been seen for the conventional SiC target material.  But, no much of change on the window since the TGHT was tapped up from 1400C.

Continue to increase TGHT to reach 1800C


 Tuesday, May 24, 2016, 11:58

Temp at 1680C/TGHT 470A/8.4C - a very light film on the window was observed.  Not sure if this film was left from previous processes; it is just that the target container is getting very bright and hard to see.


 Tuesday, May 24, 2016, 12:15

TGHT at 510A/9.16V - Observed coating on window.  Omega got interfered, therefore temp is unknown.  But it was read at ~1720C before the window was getting coated and temp started to dropped.

Will leave at this stage for now...


 Tuesday, May 24, 2016, 16:57

Window is fully coated.  Based on the heating curve, at 500A, the temp should be at ~1900C (wrapped with a layer of heat shield).  Temperature reader dropped to1340C due to the coating interference. 

Cooling down TGHT at 2A/min. And will exam the materials tomorrow... 


 

  298   Friday, May 20, 2016, 08:54 Laura LambertSiC TARGET BOATIn progressHeat-treatment: Beta-SiC (1um) target discs

John Wong wrote:

The purpose of this experiment is to determined the limiting operating temperature for Beta-SiC.  To do so, samples will be heated in sequence to observe any volatile Si coated on the window.  The coating is observed above 1400C for the conventional SiC (mixuture of alpha and beta) and this coating leads to HV shorting problem. 


Thursday, May 19, 2016, 14:26

Beta-SiC (size ~1um) slurry was prepared and casted on a graphite foil. 

Discs are cut into D-shape

Average thickness (including graphite foil) = 0.349mm

Graphite foil = 0.13mm

Actual SiC thickness = 0.219mm (close to normal SiC thickness)

Samples are loaded into a target boat.

Total discs = 120

Total mass = 14.3507g


Thursday, May 19, 2016, 14:32

Omega slope set to = 1.04

Heat-treatment #1: 1400C


 Thursday, May 19, 2016, 17:04

TGHT ramping up to 250A at 0.5A/min


 

 Friday, May 20, 2016, 08:53

IGP1 = 9.2e-6 Torr.

Increasing ramping rate to 1.0A/min up to 250A


 Friday, May 20, 2016, 09:17

IGP1 = 2.1e-5 Torr

TGHT = 215A, 3.1V

OMEGA = 1035C

Stopping auto-ramp and tapping up manually...


 Friday, May 20, 2016, 12:26

OMEGA slope changed to 1.04

OMEGA reached ~1430C and kept there for ~1hr.

no change. no coating on window observed

tapped up manually to OMEGA =1500C

TGHT = 350A, 5.8V


 Friday, May 20, 2016, 14:17

Not much change to window.

Might be beginning of light dusting, hard to tell.

Will be better observed after longer period of time at 1500C

Will remain at 1500C over weekend.


 

  297   Thursday, May 19, 2016, 14:38 John WongSiC TARGET BOATIn progressHeat-treatment: Beta-SiC (1um) target discs

The purpose of this experiment is to determined the limiting operating temperature for Beta-SiC.  To do so, samples will be heated in sequence to observe any volatile Si coated on the window.  The coating is observed above 1400C for the conventional SiC (mixuture of alpha and beta) and this coating leads to HV shorting problem. 


Thursday, May 19, 2016, 14:26

Beta-SiC (size ~1um) slurry was prepared and casted on a graphite foil. 

Discs are cut into D-shape

Average thickness (including graphite foil) = 0.349mm

Graphite foil = 0.13mm

Actual SiC thickness = 0.219mm (close to normal SiC thickness)

Samples are loaded into a target boat.

Total discs = 120

Total mass = 14.3507g


Thursday, May 19, 2016, 14:32

Omega slope set to = 1.04

Heat-treatment #1: 1400C


 Thursday, May 19, 2016, 17:04

TGHT ramping up to 250A at 0.5A/min


 

  296   Wednesday, May 11, 2016, 17:24 John Wongnp-SiC TARGET BOATDoneTemperature Treament of Nanofiber SiC/PAN

Wednesday, May 11, 2016, 17:15

Nanofiber SiC (~50nm grain size)/PAN was prepared at UBC. 

SiC 0.50g, DMF 9.0g, PAN 1.0g, tiny bit of SDS.

The fiber mat was stabilized in air at 250C and then cut into discs, initial mass = 0.1072g

Discs were then bounded with PVA on 9 pieces of rounded graphite foil  (green mass gained to 0.6031g)

The stack of naofiber SiC/PAN was loaded on to Ta boated (coated) and wrapped with Ta heat shield. 

Chamber is currently being pumped down.


 Friday, May 13, 2016, 15:00

TGHT at 390A/6.966V.  Temp measured at 1615C. 

Will keep at that temperature for a few days.


 Monday, May 16, 2016, 15:44

Sample has been heated at ~1600C for 4 days.  TGHT at 400A/7.02V. 

Cooling down at 2A/min


 Tuesday, May 17, 2016, 11:18

Chamber vented.  Inspecting samples.


 

  295   Tuesday, May 10, 2016, 11:57 Laura Lambert 40282-3TARGET BOATDoneConditioning Nb samples for Tobias

John Wong wrote:

Laura Lambert wrote:

 Wednesday, May 04, 2016, 13:28

Target boat has a layer of niobium foil on the bottom of the boat.

A niobium foil has been made with slots to hold samples [similar to when sintering endcaps] *See attached photos

Larger niobium samples are placed in the slots, holding in place, to avoid warping; smaller niobium sample sitting inside the boat by itself.

Smaller sample closest to OMEGA IR reading [right side]

Boat is wrapped with 1 large layer of Ta foil, wrapped around the boat 3x, careful to avoid touching samples.

Loaded into evap2 yesterday.

Vacuum pump bearings gone - pump replaced this morning by vacuum group.

Pumping down now...


 Friday, May 06, 2016, 13:36

HS water valves opened, no leaks detected.

Tapped up manually to 35A.

IGP1 = 2.4e-7 Torr

Setting auto-ramp rate at 0.2A/min to 250A over the weekend.

Will tap up manually monday to final desired temperature of 1400C.


 Monday, May 09, 2016, 09:38

OMEGA = 1128C

IGP1 = 1.3e-7 Torr

TGHT = 250A, 3.7V

Tapping up manually to 1400C...


 Monday, May 09, 2016, 14:05

Evap2 has reached ~1405C

TGHT = 341A, 5.34V

IGP1 = 1.9e-7 Torr

Will remain at max setpoints for min 4hrs then initiate cool down.


 

 Monday, May 09, 2016, 18:18

TGHT at 341A/5.34V for over 4 hours.  Vac stables at 1.78e-7 Torr.

Cooling down at 2A/min


 

 Tuesday, May 10, 2016, 08:45

Vented in air and opened up this morning.

Samples look good!


 

  294   Monday, May 09, 2016, 18:19 John Wong 40282-3TARGET BOATIn progressConditioning Nb samples for Tobias

Laura Lambert wrote:

 Wednesday, May 04, 2016, 13:28

Target boat has a layer of niobium foil on the bottom of the boat.

A niobium foil has been made with slots to hold samples [similar to when sintering endcaps] *See attached photos

Larger niobium samples are placed in the slots, holding in place, to avoid warping; smaller niobium sample sitting inside the boat by itself.

Smaller sample closest to OMEGA IR reading [right side]

Boat is wrapped with 1 large layer of Ta foil, wrapped around the boat 3x, careful to avoid touching samples.

Loaded into evap2 yesterday.

Vacuum pump bearings gone - pump replaced this morning by vacuum group.

Pumping down now...


 Friday, May 06, 2016, 13:36

HS water valves opened, no leaks detected.

Tapped up manually to 35A.

IGP1 = 2.4e-7 Torr

Setting auto-ramp rate at 0.2A/min to 250A over the weekend.

Will tap up manually monday to final desired temperature of 1400C.


 Monday, May 09, 2016, 09:38

OMEGA = 1128C

IGP1 = 1.3e-7 Torr

TGHT = 250A, 3.7V

Tapping up manually to 1400C...


 Monday, May 09, 2016, 14:05

Evap2 has reached ~1405C

TGHT = 341A, 5.34V

IGP1 = 1.9e-7 Torr

Will remain at max setpoints for min 4hrs then initiate cool down.


 

 Monday, May 09, 2016, 18:18

TGHT at 341A/5.34V for over 4 hours.  Vac stables at 1.78e-7 Torr.

Cooling down at 2A/min


 

  293   Wednesday, May 04, 2016, 13:45 Laura Lambert 40282-3TARGET BOATIn progressConditioning Nb samples for Tobias

 Wednesday, May 04, 2016, 13:28

Target boat has a layer of niobium foil on the bottom of the boat.

A niobium foil has been made with slots to hold samples [similar to when sintering endcaps] *See attached photos

Larger niobium samples are placed in the slots, holding in place, to avoid warping; smaller niobium sample sitting inside the boat by itself.

Smaller sample closest to OMEGA IR reading [right side]

Boat is wrapped with 1 large layer of Ta foil, wrapped around the boat 3x, careful to avoid touching samples.

Loaded into evap2 yesterday.

Vacuum pump bearings gone - pump replaced this morning by vacuum group.

Pumping down now...


 Friday, May 06, 2016, 13:36

HS water valves opened, no leaks detected.

Tapped up manually to 35A.

IGP1 = 2.4e-7 Torr

Setting auto-ramp rate at 0.2A/min to 250A over the weekend.

Will tap up manually monday to final desired temperature of 1400C.


 Monday, May 09, 2016, 09:38

OMEGA = 1128C

IGP1 = 1.3e-7 Torr

TGHT = 250A, 3.7V

Tapping up manually to 1400C...


 Monday, May 09, 2016, 14:05

Evap2 has reached ~1405C

TGHT = 341A, 5.34V

IGP1 = 1.9e-7 Torr

Will remain at max setpoints for min 4hrs then initiate cool down.


 

Attachment 1: Nb_samples_in_boat_(2).jpg
Nb_samples_in_boat_(2).jpg
  292   Tuesday, May 03, 2016, 14:44 Laura Lambert    VACUUM PUMP REPLACEMENT

 Tuesday, May 03, 2016, 14:29

Turned vacuum pump on this morning, sounded awful: loud grinding bad noises.

Called vacuum group, will replace pump tomorrow morning.

Sounds like materials coming out from all the out-gassing during sintering processes has ruined the bearings.


 

  291   Tuesday, April 26, 2016, 13:50 Laura LambertEmpty40860-2LP-IG-LISDonesintering TaC coating on UCx#16 container

Tuesday, April 26, 2016, 13:32

Container coated with TaC using 'flushing technique'.

Wrapped with 3 x Ta heat shields, incl center block - new method of each layer being one long single Ta foil covering entire container incl center block

Currently pumping down in evap2


 Wednesday, April 27, 2016, 10:25

IGP1 = 2.6e-7 Torr.

HS water valves opened, no leaks detected.

Tapped up manually to 35A.

Waited ~35min

Vacuum stable, IGP1 = 6.7e-7 Torr

Initiated auto-ramp at 0.2A/min for the TGHT with a final setpoint of 400A

Final desired temperature = 1900C


 Thursday, April 28, 2016, 14:41

Previously TBHT not on when sintering IGLIS container [since no ionizer tube] - John decided will turn on for this round

Tapped up TBHT manually to 140A, 1.69V

IGP1 = 4.5e-7 Torr

OMEGA = 1635C

TGHT = 382A, 5.8V

Initiating auto-ramp of TBHT at 0.1A/min with a final setpoint of 230A.


Friday, April 29, 2016, 08:40

IGP1 = 2.22-7 Torr

TGHT = 400A, 6.1V

TBHT = 233A, 2.9V

OMEGA = 1719C

Tapping up manually to OMEGA = 1900C


Friday, April 29, 2016, 15:22

IGP1 = 3.0e-7 Torr

TGHT = 460A, 7.52V

TBHT =230A, 2.93V

OMEGA = 1904C

Target container has remained at max temperature setpoint of 1900C for 4.5hrs.

Initiating auto cool for TGHT and TBHT at 2.0A/min and 1.0A/min respectively.


 Monday, May 02, 2016, 08:35

Vented in air and opened up this morning.

Container looks good.

See attached photos.


 

Attachment 1: TaC_coating_sintered1.jpg
TaC_coating_sintered1.jpg
Attachment 2: TaC_coating_sintered2.jpg
TaC_coating_sintered2.jpg
Attachment 3: TaC_coating_sintered3.jpg
TaC_coating_sintered3.jpg
  290   Tuesday, April 19, 2016, 09:28 Anders MjosTa41790-1LP-SISDoneTa#47 LP-SIS (with new center block) conditioning

John Wong wrote:

Aurelia Laxdal wrote:

Aurelia Laxdal wrote:

Aurelia Laxdal wrote:

Aurelia Laxdal wrote:

Anders Mjos wrote:

Laura Lambert wrote:

Aurelia Laxdal wrote:

Started Ta#47 heating at Evap2 using the autoramp program. The TGHT current is setup to go to 300A (for now) and the TBHT to 230A (final value).

 Monday, March 14, 2016, 09:20

One thermocouple was not welded on correctly and is not working. 

Cooling evap2 back down, to remove target and re-weld thermocouple.

Once thermocouple replaced, will ramp back up and continue with tests/ conditioning of target.


 

 Monday, March 14, 2016, 13:12: Stopped turbo pump

 After EVAP2 was vented the thermocouple problem was fixed: it was the wire at on connector inside the box not making proper contact. The lid of the heat shield was also replaced since the one initially mounted had no holes, so one couldn't see the center block. Restarted pumping down at 4:30pm. Just started again the autoramp program: TGHT set to 300A (for the time being) and TBHT to 230A. Temperature measurements will resume tomorrow morning.

 Raised the TGHT at 620A. The TBHT was already set at 230A. The temperature is at 1902 deg C. As per John's instructions the target will condition at these setpoints over the week-end.

Today, lowered the TGHT from 620A (at 1894 deg C) to 300A.  TBHT is still at 230A.

 Cooling down the target.

 

Thursday, March 24, 2016, 11:29 

Target was removed from the Evaporator.  

The thermocouples broke off.  

Need to insert Re foil prior to installing


 

 

 Tuesday, April 19, 2016, 09:28: Uploaded thermoucouple data.

Attachment 1: 2016-03-11_Evaporator_2.4ch
°C	Date Time	T1 - C	T2 - C	T3 - C	T4 - C	
1	2016/03/11 14:25:25	21.1	24.7	 	 	
2	2016/03/11 14:25:55	25.0	24.8	 	 	
3	2016/03/11 14:26:25	21.6	- - -	 	 	
4	2016/03/11 14:26:55	21.0	- - -	 	 	
5	2016/03/11 14:27:25	21.3	- - -	 	 	
6	2016/03/11 14:27:55	21.1	- - -	 	 	
7	2016/03/11 14:28:25	21.1	- - -	 	 	
8	2016/03/11 14:28:55	21.0	- - -	 	 	
9	2016/03/11 14:29:25	21.1	- - -	 	 	
10	2016/03/11 14:29:55	21.1	- - -	 	 	
11	2016/03/11 14:30:25	21.1	- - -	 	 	
12	2016/03/11 14:30:55	21.1	- - -	 	 	
13	2016/03/11 14:31:25	21.1	- - -	 	 	
14	2016/03/11 14:31:55	21.1	- - -	 	 	
15	2016/03/11 14:32:25	21.1	- - -	 	 	
16	2016/03/11 14:32:55	21.1	- - -	 	 	
17	2016/03/11 14:33:25	20.0	- - -	 	 	
18	2016/03/11 14:33:55	20.2	- - -	 	 	
19	2016/03/11 14:34:25	20.8	- - -	 	 	
20	2016/03/11 14:34:55	20.8	- - -	 	 	
21	2016/03/11 14:35:25	21.1	- - -	 	 	
22	2016/03/11 14:35:55	19.7	- - -	 	 	
23	2016/03/11 14:36:25	20.8	- - -	 	 	
24	2016/03/11 14:36:55	20.7	- - -	 	 	
25	2016/03/11 14:37:25	21.3	- - -	 	 	
26	2016/03/11 14:37:55	21.1	- - -	 	 	
27	2016/03/11 14:38:25	21.2	- - -	 	 	
28	2016/03/11 14:38:55	20.2	- - -	 	 	
29	2016/03/11 14:39:25	20.7	- - -	 	 	
30	2016/03/11 14:39:55	20.8	- - -	 	 	
31	2016/03/11 14:40:25	21.3	- - -	 	 	
32	2016/03/11 14:40:55	19.7	- - -	 	 	
33	2016/03/11 14:41:25	20.8	- - -	 	 	
34	2016/03/11 14:41:55	20.8	- - -	 	 	
35	2016/03/11 14:42:25	20.8	- - -	 	 	
36	2016/03/11 14:42:55	20.8	- - -	 	 	
37	2016/03/11 14:43:25	20.8	- - -	 	 	
38	2016/03/11 14:43:55	20.8	- - -	 	 	
39	2016/03/11 14:44:25	20.8	- - -	 	 	
40	2016/03/11 14:44:55	20.2	- - -	 	 	
41	2016/03/11 14:45:25	20.8	- - -	 	 	
42	2016/03/11 14:45:55	21.3	- - -	 	 	
43	2016/03/11 14:46:25	20.8	- - -	 	 	
44	2016/03/11 14:46:55	20.4	- - -	 	 	
45	2016/03/11 14:47:25	20.8	- - -	 	 	
46	2016/03/11 14:47:55	20.8	- - -	 	 	
47	2016/03/11 14:48:25	20.8	- - -	 	 	
48	2016/03/11 14:48:55	20.3	- - -	 	 	
49	2016/03/11 14:49:25	20.4	- - -	 	 	
50	2016/03/11 14:49:55	19.9	- - -	 	 	
51	2016/03/11 14:50:25	20.4	- - -	 	 	
52	2016/03/11 14:50:55	20.8	- - -	 	 	
53	2016/03/11 14:51:25	20.5	- - -	 	 	
54	2016/03/11 14:51:55	20.4	- - -	 	 	
55	2016/03/11 14:52:25	20.5	- - -	 	 	
56	2016/03/11 14:52:55	20.4	- - -	 	 	
57	2016/03/11 14:53:25	20.8	- - -	 	 	
58	2016/03/11 14:53:55	20.8	- - -	 	 	
59	2016/03/11 14:54:25	20.3	- - -	 	 	
60	2016/03/11 14:54:55	19.8	- - -	 	 	
61	2016/03/11 14:55:25	20.3	- - -	 	 	
62	2016/03/11 14:55:55	20.4	- - -	 	 	
63	2016/03/11 14:56:25	21.3	- - -	 	 	
64	2016/03/11 14:56:55	21.3	- - -	 	 	
65	2016/03/11 14:57:25	20.5	- - -	 	 	
66	2016/03/11 14:57:55	21.3	- - -	 	 	
67	2016/03/11 14:58:25	21.3	- - -	 	 	
68	2016/03/11 14:58:55	20.4	- - -	 	 	
69	2016/03/11 14:59:25	20.0	- - -	 	 	
70	2016/03/11 14:59:55	20.4	- - -	 	 	
71	2016/03/11 15:00:25	19.8	- - -	 	 	
72	2016/03/11 15:00:55	19.8	- - -	 	 	
73	2016/03/11 15:01:25	19.8	- - -	 	 	
74	2016/03/11 15:01:55	20.4	- - -	 	 	
75	2016/03/11 15:02:25	20.4	- - -	 	 	
76	2016/03/11 15:02:55	20.3	- - -	 	 	
77	2016/03/11 15:03:25	21.2	- - -	 	 	
78	2016/03/11 15:03:55	20.0	- - -	 	 	
79	2016/03/11 15:04:25	21.0	- - -	 	 	
80	2016/03/11 15:04:55	20.5	- - -	 	 	
81	2016/03/11 15:05:25	20.0	- - -	 	 	
82	2016/03/11 15:05:55	20.5	- - -	 	 	
83	2016/03/11 15:06:25	20.5	- - -	 	 	
84	2016/03/11 15:06:55	21.4	- - -	 	 	
85	2016/03/11 15:07:25	21.4	- - -	 	 	
86	2016/03/11 15:07:55	20.5	- - -	 	 	
87	2016/03/11 15:08:25	20.5	- - -	 	 	
88	2016/03/11 15:08:55	20.5	- - -	 	 	
89	2016/03/11 15:09:25	21.4	- - -	 	 	
90	2016/03/11 15:09:55	20.5	- - -	 	 	
91	2016/03/11 15:10:25	21.0	- - -	 	 	
92	2016/03/11 15:10:55	21.0	- - -	 	 	
93	2016/03/11 15:11:25	20.0	- - -	 	 	
94	2016/03/11 15:11:55	21.0	- - -	 	 	
95	2016/03/11 15:12:25	21.0	- - -	 	 	
96	2016/03/11 15:12:55	20.5	- - -	 	 	
97	2016/03/11 15:13:25	21.0	- - -	 	 	
98	2016/03/11 15:13:55	20.5	- - -	 	 	
99	2016/03/11 15:14:25	20.5	- - -	 	 	
100	2016/03/11 15:14:55	20.5	- - -	 	 	
101	2016/03/11 15:15:25	20.0	- - -	 	 	
102	2016/03/11 15:15:55	21.0	- - -	 	 	
103	2016/03/11 15:16:25	21.0	- - -	 	 	
104	2016/03/11 15:16:55	19.9	- - -	 	 	
105	2016/03/11 15:17:25	21.0	- - -	 	 	
106	2016/03/11 15:17:55	21.4	- - -	 	 	
107	2016/03/11 15:18:25	20.8	- - -	 	 	
108	2016/03/11 15:18:55	20.5	- - -	 	 	
109	2016/03/11 15:19:25	21.0	- - -	 	 	
110	2016/03/11 15:19:55	20.0	- - -	 	 	
111	2016/03/11 15:20:25	19.9	- - -	 	 	
112	2016/03/11 15:20:55	21.4	- - -	 	 	
113	2016/03/11 15:21:25	20.8	- - -	 	 	
114	2016/03/11 15:21:55	20.8	- - -	 	 	
115	2016/03/11 15:22:25	20.8	- - -	 	 	
116	2016/03/11 15:22:55	20.3	- - -	 	 	
117	2016/03/11 15:23:25	21.3	- - -	 	 	
118	2016/03/11 15:23:55	20.8	- - -	 	 	
119	2016/03/11 15:24:25	20.8	- - -	 	 	
120	2016/03/11 15:24:55	20.4	- - -	 	 	
121	2016/03/11 15:25:25	21.0	- - -	 	 	
122	2016/03/11 15:25:55	20.5	- - -	 	 	
123	2016/03/11 15:26:25	20.4	- - -	 	 	
124	2016/03/11 15:26:55	20.8	- - -	 	 	
125	2016/03/11 15:27:25	21.3	- - -	 	 	
126	2016/03/11 15:27:55	21.3	- - -	 	 	
127	2016/03/11 15:28:25	20.8	- - -	 	 	
128	2016/03/11 15:28:55	21.3	- - -	 	 	
129	2016/03/11 15:29:25	21.3	- - -	 	 	
130	2016/03/11 15:29:55	20.7	- - -	 	 	
131	2016/03/11 15:30:25	21.3	- - -	 	 	
132	2016/03/11 15:30:55	21.3	- - -	 	 	
133	2016/03/11 15:31:25	20.8	- - -	 	 	
134	2016/03/11 15:31:55	20.7	- - -	 	 	
135	2016/03/11 15:32:25	21.3	- - -	 	 	
136	2016/03/11 15:32:55	21.3	- - -	 	 	
137	2016/03/11 15:33:25	20.8	- - -	 	 	
138	2016/03/11 15:33:55	20.8	- - -	 	 	
139	2016/03/11 15:34:25	20.8	- - -	 	 	
140	2016/03/11 15:34:55	19.9	- - -	 	 	
141	2016/03/11 15:35:25	21.3	- - -	 	 	
142	2016/03/11 15:35:55	20.8	- - -	 	 	
143	2016/03/11 15:36:25	20.8	- - -	 	 	
144	2016/03/11 15:36:55	21.3	- - -	 	 	
145	2016/03/11 15:37:25	20.4	- - -	 	 	
146	2016/03/11 15:37:55	20.2	- - -	 	 	
147	2016/03/11 15:38:25	21.3	- - -	 	 	
148	2016/03/11 15:38:55	20.7	- - -	 	 	
149	2016/03/11 15:39:25	20.8	- - -	 	 	
150	2016/03/11 15:39:55	20.8	- - -	 	 	
151	2016/03/11 15:40:25	20.7	- - -	 	 	
152	2016/03/11 15:40:55	20.3	- - -	 	 	
153	2016/03/11 15:41:25	20.8	- - -	 	 	
154	2016/03/11 15:41:55	19.8	- - -	 	 	
155	2016/03/11 15:42:25	19.7	- - -	 	 	
156	2016/03/11 15:42:55	21.2	- - -	 	 	
157	2016/03/11 15:43:25	20.7	- - -	 	 	
158	2016/03/11 15:43:55	20.2	- - -	 	 	
159	2016/03/11 15:44:25	20.8	- - -	 	 	
160	2016/03/11 15:44:55	20.7	- - -	 	 	
161	2016/03/11 15:45:25	20.8	- - -	 	 	
162	2016/03/11 15:45:55	21.3	- - -	 	 	
163	2016/03/11 15:46:25	20.8	- - -	 	 	
164	2016/03/11 15:46:55	20.2	- - -	 	 	
165	2016/03/11 15:47:25	21.3	- - -	 	 	
166	2016/03/11 15:47:55	20.8	- - -	 	 	
167	2016/03/11 15:48:25	21.3	- - -	 	 	
168	2016/03/11 15:48:55	21.3	- - -	 	 	
169	2016/03/11 15:49:25	21.3	- - -	 	 	
170	2016/03/11 15:49:55	20.8	- - -	 	 	
171	2016/03/11 15:50:25	19.8	- - -	 	 	
172	2016/03/11 15:50:55	20.8	- - -	 	 	
173	2016/03/11 15:51:25	21.3	- - -	 	 	
174	2016/03/11 15:51:55	19.7	- - -	 	 	
175	2016/03/11 15:52:25	20.8	- - -	 	 	
176	2016/03/11 15:52:55	20.8	- - -	 	 	
177	2016/03/11 15:53:25	20.4	- - -	 	 	
178	2016/03/11 15:53:55	20.8	- - -	 	 	
179	2016/03/11 15:54:25	21.3	- - -	 	 	
180	2016/03/11 15:54:55	21.3	- - -	 	 	
181	2016/03/11 15:55:25	20.8	- - -	 	 	
182	2016/03/11 15:55:55	20.8	- - -	 	 	
183	2016/03/11 15:56:25	20.4	- - -	 	 	
184	2016/03/11 15:56:55	19.8	- - -	 	 	
185	2016/03/11 15:57:25	21.3	- - -	 	 	
186	2016/03/11 15:57:55	21.3	- - -	 	 	
187	2016/03/11 15:58:25	21.3	- - -	 	 	
188	2016/03/11 15:58:55	20.4	- - -	 	 	
189	2016/03/11 15:59:25	21.3	- - -	 	 	
190	2016/03/11 15:59:55	20.8	- - -	 	 	
191	2016/03/11 16:00:25	20.8	- - -	 	 	
192	2016/03/11 16:00:55	19.7	- - -	 	 	
193	2016/03/11 16:01:25	20.3	- - -	 	 	
194	2016/03/11 16:01:55	21.3	- - -	 	 	
195	2016/03/11 16:02:25	20.8	- - -	 	 	
196	2016/03/11 16:02:55	21.3	- - -	 	 	
197	2016/03/11 16:03:25	21.3	- - -	 	 	
198	2016/03/11 16:03:55	20.8	- - -	 	 	
199	2016/03/11 16:04:25	20.2	- - -	 	 	
200	2016/03/11 16:04:55	21.3	- - -	 	 	
201	2016/03/11 16:05:25	20.2	- - -	 	 	
202	2016/03/11 16:05:55	20.2	- - -	 	 	
203	2016/03/11 16:06:25	20.3	- - -	 	 	
204	2016/03/11 16:06:55	20.2	- - -	 	 	
205	2016/03/11 16:07:25	19.7	- - -	 	 	
206	2016/03/11 16:07:55	21.3	- - -	 	 	
207	2016/03/11 16:08:25	19.7	- - -	 	 	
208	2016/03/11 16:08:55	21.3	- - -	 	 	
209	2016/03/11 16:09:25	20.8	- - -	 	 	
210	2016/03/11 16:09:55	20.8	- - -	 	 	
211	2016/03/11 16:10:25	20.8	- - -	 	 	
212	2016/03/11 16:10:55	21.3	- - -	 	 	
213	2016/03/11 16:11:25	21.3	- - -	 	 	
214	2016/03/11 16:11:55	21.3	- - -	 	 	
215	2016/03/11 16:12:25	20.8	- - -	 	 	
216	2016/03/11 16:12:55	20.8	- - -	 	 	
217	2016/03/11 16:13:25	20.1	- - -	 	 	
218	2016/03/11 16:13:55	20.2	- - -	 	 	
219	2016/03/11 16:14:25	21.3	- - -	 	 	
220	2016/03/11 16:14:55	21.3	- - -	 	 	
221	2016/03/11 16:15:25	20.8	- - -	 	 	
222	2016/03/11 16:15:55	20.8	- - -	 	 	
223	2016/03/11 16:16:25	20.3	- - -	 	 	
224	2016/03/11 16:16:55	21.1	- - -	 	 	
225	2016/03/11 16:17:25	20.8	- - -	 	 	
226	2016/03/11 16:17:55	20.3	- - -	 	 	
227	2016/03/11 16:18:25	20.3	- - -	 	 	
228	2016/03/11 16:18:55	20.6	- - -	 	 	
229	2016/03/11 16:19:25	19.8	- - -	 	 	
230	2016/03/11 16:19:55	20.2	- - -	 	 	
231	2016/03/11 16:20:25	20.8	- - -	 	 	
232	2016/03/11 16:20:55	20.6	- - -	 	 	
233	2016/03/11 16:21:25	21.3	- - -	 	 	
234	2016/03/11 16:21:55	20.6	- - -	 	 	
235	2016/03/11 16:22:25	20.8	- - -	 	 	
236	2016/03/11 16:22:55	20.8	- - -	 	 	
237	2016/03/11 16:23:25	21.1	- - -	 	 	
238	2016/03/11 16:23:55	20.8	- - -	 	 	
239	2016/03/11 16:24:25	20.4	- - -	 	 	
240	2016/03/11 16:24:55	20.2	- - -	 	 	
241	2016/03/11 16:25:25	21.3	- - -	 	 	
242	2016/03/11 16:25:55	20.8	- - -	 	 	
243	2016/03/11 16:26:25	20.4	- - -	 	 	
244	2016/03/11 16:26:55	20.8	- - -	 	 	
245	2016/03/11 16:27:25	19.8	- - -	 	 	
246	2016/03/11 16:27:55	19.9	- - -	 	 	
247	2016/03/11 16:28:25	20.2	- - -	 	 	
248	2016/03/11 16:28:55	20.8	- - -	 	 	
249	2016/03/11 16:29:25	20.8	- - -	 	 	
250	2016/03/11 16:29:55	21.3	- - -	 	 	
251	2016/03/11 16:30:25	21.1	- - -	 	 	
252	2016/03/11 16:30:55	20.8	- - -	 	 	
253	2016/03/11 16:31:25	21.3	- - -	 	 	
254	2016/03/11 16:31:55	21.3	- - -	 	 	
255	2016/03/11 16:32:25	21.3	- - -	 	 	
256	2016/03/11 16:32:55	20.8	- - -	 	 	
257	2016/03/11 16:33:25	21.1	- - -	 	 	
258	2016/03/11 16:33:55	20.8	- - -	 	 	
259	2016/03/11 16:34:25	20.3	- - -	 	 	
260	2016/03/11 16:34:55	21.2	- - -	 	 	
261	2016/03/11 16:35:25	20.8	- - -	 	 	
262	2016/03/11 16:35:55	20.8	- - -	 	 	
263	2016/03/11 16:36:25	20.8	- - -	 	 	
264	2016/03/11 16:36:55	21.3	- - -	 	 	
265	2016/03/11 16:37:25	21.3	- - -	 	 	
266	2016/03/11 16:37:55	21.3	- - -	 	 	
267	2016/03/11 16:38:25	21.3	- - -	 	 	
268	2016/03/11 16:38:55	19.8	- - -	 	 	
269	2016/03/11 16:39:25	20.2	- - -	 	 	
270	2016/03/11 16:39:55	20.8	- - -	 	 	
271	2016/03/11 16:40:25	20.8	- - -	 	 	
272	2016/03/11 16:40:55	20.8	- - -	 	 	
273	2016/03/11 16:41:25	20.8	- - -	 	 	
274	2016/03/11 16:41:55	20.8	- - -	 	 	
275	2016/03/11 16:42:25	21.3	- - -	 	 	
276	2016/03/11 16:42:55	21.3	- - -	 	 	
277	2016/03/11 16:43:25	20.7	- - -	 	 	
278	2016/03/11 16:43:55	20.2	- - -	 	 	
279	2016/03/11 16:44:25	20.3	- - -	 	 	
280	2016/03/11 16:44:55	20.4	- - -	 	 	
281	2016/03/11 16:45:25	20.2	- - -	 	 	
282	2016/03/11 16:45:55	20.2	- - -	 	 	
283	2016/03/11 16:46:25	21.3	- - -	 	 	
284	2016/03/11 16:46:55	20.8	- - -	 	 	
285	2016/03/11 16:47:25	20.8	- - -	 	 	
286	2016/03/11 16:47:55	20.8	- - -	 	 	
287	2016/03/11 16:48:25	20.7	- - -	 	 	
288	2016/03/11 16:48:55	20.8	- - -	 	 	
289	2016/03/11 16:49:25	19.9	- - -	 	 	
290	2016/03/11 16:49:55	20.2	- - -	 	 	
291	2016/03/11 16:50:25	21.3	- - -	 	 	
292	2016/03/11 16:50:55	21.3	- - -	 	 	
293	2016/03/11 16:51:25	20.5	- - -	 	 	
294	2016/03/11 16:51:55	21.3	- - -	 	 	
295	2016/03/11 16:52:25	21.3	- - -	 	 	
296	2016/03/11 16:52:55	21.3	- - -	 	 	
297	2016/03/11 16:53:25	20.8	- - -	 	 	
298	2016/03/11 16:53:55	20.5	- - -	 	 	
299	2016/03/11 16:54:25	20.5	- - -	 	 	
... 53646 more lines ...
Attachment 2: 2016-03-11_Evaporator_2.xlsx
  289   Thursday, April 07, 2016, 15:23 John WongSiC TARGET BOATDoneE-spun SiC/PAN thermal treatment

Thursday, April 07, 2016, 15:18

E-spun SiC/PAN fiber mats were produced at UBC.

12%PAN solution; 50% SiC to weight of PAN.

Materials used:

1.2g PAN, 8.8g DMF, 0.6g SiC, SDS ~0.1% to SiC

Fiber mats were heat treated at 250C in air.  Then cut into 18" discs and loaded into Ta target boat with heatshield wrapped. 

3 temperature treatments will carry out: 1200C, 1400C and 1600C

Chamber is being pumped down


 Friday, April 08, 2016, 10:02

TGHT at 285A, Temp at ~1200C.  Will remain at this temp for a few hours before cooling down. 

Some samples will be taken out for analysis. 

Next week, temperature treatment will continue at 1400C


 Friday, April 08, 2016, 14:26

Samples have been heated at 1200C for just over 4 hours.

Initiated auto-cooling at 2A/min


 Tuesday, April 12, 2016, 17:51

Heat treatment #2 - 1400C. 

Initial mass after 1200C = 0.0312g


 Monday, April 18, 2016, 12:55

Samples was heated at 1400C (TGHT maintained at ~370A) for 4 days (see attachment 1).

Chamber is vented; samples will be inspected.


 Tuesday, April 19, 2016, 17:49

Results

Sample mass after 1200C = 0.0312g

Sample mass after 1400C = 0.0294g

~5.78% mass  loss. 


Tuesday, April 19, 2016, 17:57

Heat Treatment#3: 1600C

sample mass before heating = 0.0238g (this sample is taken from the batch after it was heated at 1400C)

Chamber is being pumped.


 Thursday, April 21, 2016, 11:07

TGHT stepped up to 330A, temp measured at 1422C.


 Thursday, April 21, 2016, 12:05

TGHT at 415A/7.16V; temp at 1610C


 Thursday, April 21, 2016, 17:49

Temp dropped to 1590.  Increased TGHT to 425A; temp reads 1602A.


 Friday, April 22, 2016, 10:57

Voltage increased to 7.33V, TGHT stepped down to 418A, temp maintained at 1610A.


 Monday, April 25, 2016, 12:08

Sample was heat treated for almost 4 days.  Temperature dropped to 1578C, TGHT at 418/7.26V.  (see attachment #2)

Ramping down TGHT 2A/min.


 Monday, April 25, 2016, 16:00

Result:

Mass after 1600C = 0.0104g, 5.63% mass loss. 

Will do XRD/EDX


 

Attachment 1: SiC_PAN_1400c.PNG
SiC_PAN_1400c.PNG
Attachment 2: archiver.PNG
archiver.PNG