Tuesday, April 03, 2012, 08:54

Yesterday, a new target boat was sprayed with TaC coating and let dried.

The boat was then installed in the Evap#2 chamber and pumped down to 10-6 Torr before the target heater was turned on.  NOTE: Target boat is not wrapped with Ta-heat shield. 

TGHT auto ramping was initiated at 2.0A/min and max setpoint to 700A.  The voltage was set at 3V; therefore, the current only ramped up to 250A over night.

--> Increased the TGHT voltage to 15A, and continue ramping the TGHT to 700A.  Currently vac at low 2.3e-7 Torr. 

 Tuesday, April 03, 2012, 09:12

The vac is at low 10e-7 as the TGHT is ramping up.  Changing ramping rate from 2A/min to 5A/min. 

Tuesday, April 03, 2012, 12:00  

TGHT reached to 700A. Measured temp @ 1280C. 

Tapped up TGHT to:

800A.  Measured temp @ 1400C. 

850A (local 843A/15.60V). Measured temp @ 1450C.  

900A (local 893A/16.88V).  Measured temp @ 1500C

 Tuesday, April 03, 2012, 14:35:

Try autoramping TGHT to 1000A but voltage has gone up close to the max limit (20V).  TGHT could only go up to ~970A (see attachment 1: TGHT_maxcurrent.jpg).  The heater remained at that current for ~1hr but auto cooling was initiated - at 10A/min.

 Monday, March 04, 2013, 17:39

This is the 2nd modified target container for RFQ LPSIS.  The container will be heated up to 650A TGHT and 150A on TBHT.  No Ta-heat shield is being used.  

Heating rate at 1A/min for both TGHT & TBHT.  Once the target is at the currents, TBHT will be further ramped up to 300A.  

Temperatures are being measured by two thermocouples (one on RFQ component and the other on the Cu heat-shield).  

Gases are being analyzed using the RGA. 

Tuesday, September 17, 2013, 11:14

Target boat contains 5 Nb discs.  3 discs are wraps with 0.001" thin of Nb foil (99.8% pure), and 2 are wraps with 0.001" Ta foil (see attachment#1)

Chamber has been pumped down over night.  Pressure is currently at 9.8e-7 Torr. 

Heating instructions:

Samples will be heated up to 800C.  TGHT will be ramped up accordingly. (Two thermocouples are wielded on the target container.)

Once at the desired temperature; the samples will be heat for 4 hours before cooling down.

 Tuesday, September 17, 2013, 14:37

Target temperature has reached to 800C at around 13:00 (see attachment#2)

TGHT @ 230A/3.07V (local 233A/3.25V). 

IG @ 1.06e-6 Torr. 

The heater will be ramped down at ~17:00 at 2A/min.

 Tuesday, September 17, 2013, 17:36

Target temp: T1 = 805C, T2=797.6C

IG @ 9.4e-7 Torr.

Cooling down initiated. 

 Wednesday, September 18, 2013, 11:34

TGHT at 0A.  Temp at 22C. 

IG @ 5.8e-7 Torr.

Venting chamber.

John Wong wrote:

Tuesday, September 17, 2013, 11:14 Target boat contains 5 Nb discs.  3 discs are wraps with 0.001" thin of Nb foil (99.8% pure), and 2 are wraps with 0.001" Ta foil (see attachment#1) Chamber has been pumped down over night.  Pressure is currently at 9.8e-7 Torr.  Heating instructions: Samples will be heated up to 800C.  TGHT will be ramped up accordingly. (Two thermocouples are wielded on the target container.) Once at the desired temperature; the samples will be heat for 4 hours before cooling down.  Tuesday, September 17, 2013, 14:37 Target temperature has reached to 800C at around 13:00 (see attachment#2) TGHT @ 230A/3.07V (local 233A/3.25V).  IG @ 1.06e-6 Torr.  The heater will be ramped down at ~17:00 at 2A/min.  Tuesday, September 17, 2013, 17:36 Target temp: T1 = 805C, T2=797.6C IG @ 9.4e-7 Torr. Cooling down initiated.   Wednesday, September 18, 2013, 11:34 TGHT at 0A.  Temp at 22C.  IG @ 5.8e-7 Torr. Venting chamber.

 Thursday, September 19, 2013, 11:41

Target boat contains batch#2 Nb samples (see attachment #1)

Chamber has been pumped down over night.  

IG @ 5.5e-07 Torr. 

CG1B @ 0.033 T

CG1A @ 0.127 T

There is a leak in the backing line.  BV1 was bypassed in order to turn on the turbo pump. (Will investigate the leaks after the processes are done)  

*See attached picture to view samples

Laura Lambert wrote:

John Wong wrote: Tuesday, September 17, 2013, 11:14 Target boat contains 5 Nb discs.  3 discs are wraps with 0.001" thin of Nb foil (99.8% pure), and 2 are wraps with 0.001" Ta foil (see attachment#1) Chamber has been pumped down over night.  Pressure is currently at 9.8e-7 Torr.  Heating instructions: Samples will be heated up to 800C.  TGHT will be ramped up accordingly. (Two thermocouples are wielded on the target container.) Once at the desired temperature; the samples will be heat for 4 hours before cooling down.  Tuesday, September 17, 2013, 14:37 Target temperature has reached to 800C at around 13:00 (see attachment#2) TGHT @ 230A/3.07V (local 233A/3.25V).  IG @ 1.06e-6 Torr.  The heater will be ramped down at ~17:00 at 2A/min.  Tuesday, September 17, 2013, 17:36 Target temp: T1 = 805C, T2=797.6C IG @ 9.4e-7 Torr. Cooling down initiated.   Wednesday, September 18, 2013, 11:34 TGHT at 0A.  Temp at 22C.  IG @ 5.8e-7 Torr. Venting chamber.    Thursday, September 19, 2013, 11:41 Target boat contains batch#2 Nb samples (see attachment #1) Chamber has been pumped down over night.   IG @ 5.5e-07 Torr.  CG1B @ 0.033 T CG1A @ 0.127 T There is a leak in the backing line.  BV1 was bypassed in order to turn on the turbo pump. (Will investigate the leaks after the processes are done)   *See attached picture to view samples

Thursday, September 19, 2013, 17:01  

TGHT reached to 800A.  Temp at 795.9C for 4 hours.  Vac at 5.8e-7 Torr.

Cooling down initiated.  ramping rate at 2A/min. 

John Wong wrote:

Tuesday, September 17, 2013, 11:14 Target boat contains 5 Nb discs.  3 discs are wraps with 0.001" thin of Nb foil (99.8% pure), and 2 are wraps with 0.001" Ta foil (see attachment#1) Chamber has been pumped down over night.  Pressure is currently at 9.8e-7 Torr.  Heating instructions: Samples will be heated up to 800C.  TGHT will be ramped up accordingly. (Two thermocouples are wielded on the target container.) Once at the desired temperature; the samples will be heat for 4 hours before cooling down.  Tuesday, September 17, 2013, 14:37 Target temperature has reached to 800C at around 13:00 (see attachment#2) TGHT @ 230A/3.07V (local 233A/3.25V).  IG @ 1.06e-6 Torr.  The heater will be ramped down at ~17:00 at 2A/min.  Tuesday, September 17, 2013, 17:36 Target temp: T1 = 805C, T2=797.6C IG @ 9.4e-7 Torr. Cooling down initiated.   Wednesday, September 18, 2013, 11:34 TGHT at 0A.  Temp at 22C.  IG @ 5.8e-7 Torr. Venting chamber.

 Friday, September 20, 2013, 14:56

Target contains batch#3 sample wrapped with Nb foil. 

Chamber has been pumped down to 1.03e-6 Torr. 

Samples will be heated up to 1200C for 4 hours.  

 Friday, September 20, 2013, 16:54

TGHT at 450A, temp stabilizes at 1238C.

Will cool down at 20:30 tonight.

Friday, September 20, 2013, 20:40  

Samples has been heated for 4 hours at 1235C.  

Cooling down initiated. 

 Monday, September 23, 2013, 14:40

Chamber was vented.

Batch#3 process completed.

John Wong wrote:

John Wong wrote: Tuesday, September 17, 2013, 11:14 Target boat contains 5 Nb discs.  3 discs are wraps with 0.001" thin of Nb foil (99.8% pure), and 2 are wraps with 0.001" Ta foil (see attachment#1) Chamber has been pumped down over night.  Pressure is currently at 9.8e-7 Torr.  Heating instructions: Samples will be heated up to 800C.  TGHT will be ramped up accordingly. (Two thermocouples are wielded on the target container.) Once at the desired temperature; the samples will be heat for 4 hours before cooling down.  Tuesday, September 17, 2013, 14:37 Target temperature has reached to 800C at around 13:00 (see attachment#2) TGHT @ 230A/3.07V (local 233A/3.25V).  IG @ 1.06e-6 Torr.  The heater will be ramped down at ~17:00 at 2A/min.  Tuesday, September 17, 2013, 17:36 Target temp: T1 = 805C, T2=797.6C IG @ 9.4e-7 Torr. Cooling down initiated.   Wednesday, September 18, 2013, 11:34 TGHT at 0A.  Temp at 22C.  IG @ 5.8e-7 Torr. Venting chamber.    Friday, September 20, 2013, 14:56 Target contains batch#3 sample wrapped with Nb foil.  Chamber has been pumped down to 1.03e-6 Torr.  Samples will be heated up to 1200C for 4 hours.    Friday, September 20, 2013, 16:54 TGHT at 450A, temp stabilizes at 1238C. Will cool down at 20:30 tonight. Friday, September 20, 2013, 20:40   Samples has been heated for 4 hours at 1235C.   Cooling down initiated.   Monday, September 23, 2013, 14:40 Chamber was vented. Batch#3 process completed.

 Monday, September 23, 2013, 16:14

Batch#4.  Target container contains 2 Nb stables (a bullet type and a disc).  

Samples are wrapped with "dimpled" Nb foil to prevent diffusion bonding. 

Chamber has been pumped down to 8.3e-7 Torr, CG1B @ 30mT, CG1A @ 118mT. 

Samples will be heated up to 1400C for 4 hours. 

Monday, September 23, 2013, 17:46

TGHT at 620A. Temp at 1400C. Current pressure @ 2.5e-6 Torr. 

Tuesday, September 24, 2013, 16:45

Sample#4 was heated up to 1400C and after about 3hrs, the target container started to break.

See the link below for more details:

https://www.dropbox.com/s/9mhpkz66u6yqldm/Nb_1400C.mp4

 Monday, January 20, 2014, 16:32

A new target boat was sprayed with TaC coating and let dry this morning.

The target boat is NOT wrapped with Ta-heat shield.

The boat was installed in Evap#2, chamber is currently being pumped down overnight.

Laura Lambert wrote:

Monday, January 20, 2014, 16:32 A new target boat was sprayed with TaC coating and let dry this morning. The target boat is NOT wrapped with Ta-heat shield. The boat was installed in Evap#2, chamber is currently being pumped down overnight.

 Tuesday, January 21, 2014, 11:10

Chamber was pumped down to ~2e-7 Torr. HS cooling water valves were opened, no leaks detected.

TGHT was stepped up to 35A, voltage max set at 13V. TBHT currently @ 0A.

Waited ~20min, current stabilized, vacuum started to drop, auto-ramp initiated at 2.0A/min and max setpoint to 700A.

Good vacuum: 3.00e-5 Torr, Bad vacuum 4.00e-5 Torr.

Laura Lambert wrote:

Laura Lambert wrote:  Monday, January 20, 2014, 16:32 A new target boat was sprayed with TaC coating and let dry this morning. The target boat is NOT wrapped with Ta-heat shield. The boat was installed in Evap#2, chamber is currently being pumped down overnight.    Tuesday, January 21, 2014, 11:10 Chamber was pumped down to ~2e-7 Torr. HS cooling water valves were opened, no leaks detected. TGHT was stepped up to 35A, voltage max set at 13V. TBHT currently @ 0A. Waited ~20min, current stabilized, vacuum started to drop, auto-ramp initiated at 2.0A/min and max setpoint to 700A. Good vacuum: 3.00e-5 Torr, Bad vacuum 4.00e-5 Torr.

 Tuesday, January 21, 2014, 11:51

Vacuum was grumpy and was well on it's way to tripping off [reached 5e-5 Torr], auto ramping was stopped at ~95A and quickly stepped down to 90A to avoid tripping it off.

Allowed vacuum to settle back down to 2.3e-6 Torr. Auto ramping changed to 0.2A/min and re-started.

 close-call!

Laura Lambert wrote:

Laura Lambert wrote: Laura Lambert wrote:  Monday, January 20, 2014, 16:32 A new target boat was sprayed with TaC coating and let dry this morning. The target boat is NOT wrapped with Ta-heat shield. The boat was installed in Evap#2, chamber is currently being pumped down overnight.    Tuesday, January 21, 2014, 11:10 Chamber was pumped down to ~2e-7 Torr. HS cooling water valves were opened, no leaks detected. TGHT was stepped up to 35A, voltage max set at 13V. TBHT currently @ 0A. Waited ~20min, current stabilized, vacuum started to drop, auto-ramp initiated at 2.0A/min and max setpoint to 700A. Good vacuum: 3.00e-5 Torr, Bad vacuum 4.00e-5 Torr.    Tuesday, January 21, 2014, 11:51 Vacuum was grumpy and was well on it's way to tripping off [reached 5e-5 Torr], auto ramping was stopped at ~95A and quickly stepped down to 90A to avoid tripping it off. Allowed vacuum to settle back down to 2.3e-6 Torr. Auto ramping changed to 0.2A/min and re-started.  close-call!

 Wednesday, January 22, 2014, 09:46

TGHT has been slowly ramping up overnight at a rate of 0.2A/min.

IGP1 = 2.9e-7 Torr, TGHT = 342A; stepping ramping rate up to 2.0A/min.

Laura Lambert wrote:

Laura Lambert wrote: Laura Lambert wrote: Laura Lambert wrote:  Monday, January 20, 2014, 16:32 A new target boat was sprayed with TaC coating and let dry this morning. The target boat is NOT wrapped with Ta-heat shield. The boat was installed in Evap#2, chamber is currently being pumped down overnight.    Tuesday, January 21, 2014, 11:10 Chamber was pumped down to ~2e-7 Torr. HS cooling water valves were opened, no leaks detected. TGHT was stepped up to 35A, voltage max set at 13V. TBHT currently @ 0A. Waited ~20min, current stabilized, vacuum started to drop, auto-ramp initiated at 2.0A/min and max setpoint to 700A. Good vacuum: 3.00e-5 Torr, Bad vacuum 4.00e-5 Torr.    Tuesday, January 21, 2014, 11:51 Vacuum was grumpy and was well on it's way to tripping off [reached 5e-5 Torr], auto ramping was stopped at ~95A and quickly stepped down to 90A to avoid tripping it off. Allowed vacuum to settle back down to 2.3e-6 Torr. Auto ramping changed to 0.2A/min and re-started.  close-call!    Wednesday, January 22, 2014, 09:46 TGHT has been slowly ramping up overnight at a rate of 0.2A/min. IGP1 = 2.9e-7 Torr, TGHT = 342A; stepping ramping rate up to 2.0A/min.

 Wednesday, January 22, 2014, 13:43

TGHT is sitting at 693A, IGP1 = 1.3e-6 Torr.

Stepping up TGHT voltage up to 14V from 13.05V to reach the max current of 700A.

Laura Lambert wrote:

Laura Lambert wrote: Laura Lambert wrote: Laura Lambert wrote: Laura Lambert wrote:  Monday, January 20, 2014, 16:32 A new target boat was sprayed with TaC coating and let dry this morning. The target boat is NOT wrapped with Ta-heat shield. The boat was installed in Evap#2, chamber is currently being pumped down overnight.    Tuesday, January 21, 2014, 11:10 Chamber was pumped down to ~2e-7 Torr. HS cooling water valves were opened, no leaks detected. TGHT was stepped up to 35A, voltage max set at 13V. TBHT currently @ 0A. Waited ~20min, current stabilized, vacuum started to drop, auto-ramp initiated at 2.0A/min and max setpoint to 700A. Good vacuum: 3.00e-5 Torr, Bad vacuum 4.00e-5 Torr.    Tuesday, January 21, 2014, 11:51 Vacuum was grumpy and was well on it's way to tripping off [reached 5e-5 Torr], auto ramping was stopped at ~95A and quickly stepped down to 90A to avoid tripping it off. Allowed vacuum to settle back down to 2.3e-6 Torr. Auto ramping changed to 0.2A/min and re-started.  close-call!    Wednesday, January 22, 2014, 09:46 TGHT has been slowly ramping up overnight at a rate of 0.2A/min. IGP1 = 2.9e-7 Torr, TGHT = 342A; stepping ramping rate up to 2.0A/min.    Wednesday, January 22, 2014, 13:43 TGHT is sitting at 693A, IGP1 = 1.3e-6 Torr. Stepping up TGHT voltage up to 14V from 13.05V to reach the max current of 700A.

 Wednesday, January 22, 2014, 15:09

TGHT reached to 700A/12.83V.  Local temperature on the boat surface was measured at ~1500C.

Note: This is the "old" design boat.  The new design boat was able to heat up to 900A/16.88 - the temperature was measured at about 1500C.  (see elog: https://elog.triumf.ca/TIS/Evaporator_2/15)

Target will be heated for a few hours and will be cooled down later tonight.

The chamber will be vented tomorrow and the boat will be inspected.

Tuesday June 16, 2015

An Extraction Insulator ITD0381 made from a different grade of AiN was installed in Evaporator 2 for testing purposes. The sub assembly included the SIS Restraint Housing ITD0389, New Extraction Insulator ITD0381, Repeller Electrode ITD0377, Extraction Electrode ITD0374 with fingerstock mounted.

The standoff insulator ITD0400 was found to be swelled up and broken. It was replaced with and glazed alumina insulator.

The tube heater Insulator ITD0342 - central support helicoil was repaired.

 Tuesday, May 03, 2016, 14:29

Turned vacuum pump on this morning, sounded awful: loud grinding bad noises.

Called vacuum group, will replace pump tomorrow morning.

Sounds like materials coming out from all the out-gassing during sintering processes has ruined the bearings.

 Tuesday, September 12, 2017, 12:00:

The coated back window was changed to a shuttered window.

On star-point flange bolt interfered with the shutter, however it was removed, shortened, and re-installed.

The installation is complete. Awaiting roughing pump to leak check.

 Tuesday, September 11, 2018, 10:45:

TGHT: 53.4 A   TBHT: 57.75

Actual

TGHT: 60.0A  TBHT: 59.0A

Uploaded the rest to Word doc. Screenshots included.

 Tuesday, April 16, 2019, 13:38: Replaced the bottom insert on the heat shield. 

Used small amount of isopropyl alcohol to wipe the inside if the HS out. 

 Tuesday, May 21, 2019, 14:33: Install flexible line evap 2 HS.

Gradually open waterlines under vacuum after period of no use.

Wednesday, May 20, 2020, 07:17: Vacuum @ 1.13e-06T

Wednesday, May 20, 2020, 07:19: Hot lab cooling water return opened. Vacuum @ 1.13e-06T.

Wednesday, May 20, 2020, 07:22: Hot lab cooling water supply opened. Vacuum @ 1.11e-06T.

Wednesday, May 20, 2020, 07:29: Vacuum remains stable @ 1.11e-06T.