Monday, January 29, 2018, 09:26

35 circles of 14 mm diameter were packed into a graphite sample container.

35 x UO2/C circles = 4.94 g

Graphite container = 5.03 g

Graphite tube is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3 new Ta foils for heat shielding and the boat was installed in Evap1.

Chamber currently pumping down.

Marla Cervantes wrote:

Monday, January 29, 2018, 09:26 35 circles of 14 mm diameter were packed into a graphite sample container. 35 x UO2/C circles = 4.94 g Graphite container = 5.03 g Graphite tube is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3 new Ta foils for heat shielding and the boat was installed in Evap1. Chamber currently pumping down.

 Monday, January 29, 2018, 11:06

A power outage around 10 am tripped off EVAP1.

Marla Cervantes wrote:

Marla Cervantes wrote:  Monday, January 29, 2018, 09:26 35 circles of 14 mm diameter were packed into a graphite sample container. 35 x UO2/C circles = 4.94 g Graphite container = 5.03 g Graphite tube is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3 new Ta foils for heat shielding and the boat was installed in Evap1. Chamber currently pumping down.    Monday, January 29, 2018, 11:06 A power outage around 10 am tripped off EVAP1.

 Monday, January 29, 2018, 14:22

Water flow turned on.

Chamber set to pumping down. 

Marla Cervantes wrote:

Marla Cervantes wrote: Marla Cervantes wrote:  Monday, January 29, 2018, 09:26 35 circles of 14 mm diameter were packed into a graphite sample container. 35 x UO2/C circles = 4.94 g Graphite container = 5.03 g Graphite tube is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3 new Ta foils for heat shielding and the boat was installed in Evap1. Chamber currently pumping down.    Monday, January 29, 2018, 11:06 A power outage around 10 am tripped off EVAP1.  Monday, January 29, 2018, 14:22 Water flow turned on. Chamber set to pumping down.

 Tuesday, January 30, 2018, 16:06

Initial IGP1 = 9.4x10e-7 Torr

Tapped up entire process manually to 520A in 32 min

TGHT = 520 A, 5.45 V

Vacuum coming down indicating carbonization process complete 

Will remain at max setpoint for 4 hrs to ensure full carbonization before cooling down.

 Tuesday, January 30, 2018, 18:40

 Initiating auto-cool at 2.0 A/min 

 Wednesday, January 31, 2018, 14:00

 Monday, January 15, 2018, 13:37

35 circles of 14 mm diameter were packed into a graphite sample container.

35 x UO2/C circles = 5.58 g

Graphite container = 5.22 g

Graphite tube is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3 new Ta foils for heat shielding and the boat was installed in Evap1.

Chamber currently pumping down.

Tuesday, January 16, 2018, 13:41 

Initial IGP1 = 9x10e-7 Torr

Tapped up entire process manually to 520A in 1.5 hrs

TGHT = 525 A, 5.64 V

Vacuum coming down nicely indicating carbonization process complete 

Will remain at max setpoint overnight to ensure full carbonization before cooling down.

Wednesday, January 17, 2018, 10:30

Initiating auto-cool at 2.0A/min 

Wednesday, January 17, 2018, 4:30

 Wednesday, January 10, 2018, 14:44

Circles from cast 1 were used, the same as the last round of 1stepUCx [see elog i.d. 164]

A 14mm punch was used to punch out circles from the cast.

35 circles were packed into a graphite sample container.

35 x UO2/C circles = 5.75 g

Graphite container = 5.38 g

Graphite container is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3-layers of heat shield and installed in Evap1.

Chamber currently pumping down.

 Thursday, November 23, 2017, 13:34

Circles from cast 1 were used, the same as the last round of 1stepUCx [see elog i.d. 164]

A 14mm punch was used to punch out circles from the cast.

35 circles were packed into a graphite sample container.

35 x UO2/C circles = 5.75 g

Graphite container = 5.38 g

Graphite container is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3-layers of heat shield and installed in Evap1.

Chamber currently pumping down.

 Friday, November 24, 2017, 12:48

IGP1=1.3e-6 Torr

TGHT = 520A, 4.98V 

Vacuum went down indicating carbonization.

Will remain at max setpoint for the weekend.

 Monday, November 27, 2017, 09:58

IG1 = 2.6e-6 Torr

TGHT = 520A, 5.1V

Carbonization complete in 3 hrs and 30 min.

Initiating auto-cool at 2.0A/min

 Wednesday, November 27, 2017, 13:10

 IEVAP was vented in argon and sample removed/transferred to glove box on Friday.

 Monday, March 12, 2018, 9:13

35 circles from cast#2 of 14 mm diameter were packed into a graphite sample container.

35 x UO2/C circles = 5.21 g

Graphite container = 6.85 g

Graphite tube is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3 Ta foils for heat shielding and the boat was installed in Evap1.

Chamber currently pumping down.

 Monday, March 12, 2018, 13:57

Initial IGP1 = 4.79e-7 Torr

Tapped up entire process manually to 520A in 30 min

TGHT = 520 A, 5.32 V

Vacuum coming down indicating carbonization process complete.  

Will remain at max setpoint for 1 hrs to ensure full carbonization before cooling down.

 Monday, March 12, 2018, 14:57 

Cooling down rate used 3 A/10s.

 Tuesday, March 13, 2018, 18:22

Vented with Ar and removed from EVAP1

 Tuesday, February 13, 2018, 11:39

35 circles of 14 mm diameter were packed into a graphite sample container.

35 x UO2/C circles = 5.74 g

Graphite container = 5.20 g

Graphite tube is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3 used Ta foils for heat shielding and the boat was installed in Evap1.

Chamber currently pumping down.

 Tuesday, February 13, 2018, 15:30

Initial IGP1 = 2.73x10e-6 Torr

Tapped up entire process manually to 520 A in 30 min

TGHT = 520 A, 5.41 V

Vacuum coming down nicely indicating carbonization process complete.

Current trip off after 5 min of being at 520 A.

 Wednesday, February 14, 2018, 15:32

EVAP1 vented with Argon and the target was removed.

Target was transferred to glove box.

Ta boat and graphite container look unbroken.

Marla Cervantes wrote:

Tuesday, February 13, 2018, 11:39 35 circles of 14 mm diameter were packed into a graphite sample container. 35 x UO2/C circles = 5.74 g Graphite container = 5.20 g Graphite tube is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3 used Ta foils for heat shielding and the boat was installed in Evap1. Chamber currently pumping down.  Tuesday, February 13, 2018, 15:30 Initial IGP1 = 2.73x10e-6 Torr Tapped up entire process manually to 520 A in 30 min TGHT = 520 A, 5.41 V Vacuum coming down nicely indicating carbonization process complete. Current trip off after 5 min of being at 520 A.  Wednesday, February 14, 2018, 15:32 EVAP1 vented with Argon and the target was removed. Target was transferred to glove box. Ta boat and graphite container look unbroken.

 Friday, March 02, 2018, 16:31

A test was performed in EVAP1 (see log ID 194):

- A Ta boat without Ta shielding was submitted to 520 A and it remained at that current point overnight.

-No trip off

Marla Cervantes wrote:

Marla Cervantes wrote:  Tuesday, February 13, 2018, 11:39 35 circles of 14 mm diameter were packed into a graphite sample container. 35 x UO2/C circles = 5.74 g Graphite container = 5.20 g Graphite tube is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3 used Ta foils for heat shielding and the boat was installed in Evap1. Chamber currently pumping down.  Tuesday, February 13, 2018, 15:30 Initial IGP1 = 2.73x10e-6 Torr Tapped up entire process manually to 520 A in 30 min TGHT = 520 A, 5.41 V Vacuum coming down nicely indicating carbonization process complete. Current trip off after 5 min of being at 520 A.  Wednesday, February 14, 2018, 15:32 EVAP1 vented with Argon and the target was removed. Target was transferred to glove box. Ta boat and graphite container look unbroken.  Friday, March 02, 2018, 16:31 A test was performed in EVAP1 (see log ID 194): - A Ta boat without Ta shielding was submitted to 520 A and it remained at that current point overnight. -No trip off

 Thursday, February 08, 2018, 14:50

35 circles from cast#2 of 14 mm diameter were packed into a graphite sample container.

35 x UO2/C circles = 4.76 g

Graphite container = 5.3 g

Graphite tube is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3 new Ta foils for heat shielding and the boat was installed in Evap1.

Chamber currently pumping down.

 Friday, February 09, 2018, 10:40

Initial IGP1 = 4.54e-7 Torr

Tapped up entire process manually to 520A in 25 min

TGHT = 520 A, 5.49 V

Vacuum coming down indicating carbonization process complete.  

Current suddenly tripped off from 520 A to 0 A.

There was not a power outage.

There was good vacuum.

Water cooling did not trip off 

Marla Cervantes wrote:

Thursday, February 08, 2018, 14:50 35 circles from cast#2 of 14 mm diameter were packed into a graphite sample container. 35 x UO2/C circles = 4.76 g Graphite container = 5.3 g Graphite tube is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3 new Ta foils for heat shielding and the boat was installed in Evap1. Chamber currently pumping down.  Friday, February 09, 2018, 10:40 Initial IGP1 = 4.54e-7 Torr Tapped up entire process manually to 520A in 25 min TGHT = 520 A, 5.49 V Vacuum coming down indicating carbonization process complete.   Current suddenly tripped off from 520 A to 0 A. There was not a power outage. There was good vacuum. Water cooling did not trip off

 Friday, February 09, 2018, 16:49

The power supply was tested and its working normally.

Apparently a glitch on EPICS caused the tripped off.

Marla Cervantes wrote:

Marla Cervantes wrote:  Thursday, February 08, 2018, 14:50 35 circles from cast#2 of 14 mm diameter were packed into a graphite sample container. 35 x UO2/C circles = 4.76 g Graphite container = 5.3 g Graphite tube is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3 new Ta foils for heat shielding and the boat was installed in Evap1. Chamber currently pumping down.  Friday, February 09, 2018, 10:40 Initial IGP1 = 4.54e-7 Torr Tapped up entire process manually to 520A in 25 min TGHT = 520 A, 5.49 V Vacuum coming down indicating carbonization process complete.   Current suddenly tripped off from 520 A to 0 A. There was not a power outage. There was good vacuum. Water cooling did not trip off     Friday, February 09, 2018, 16:49 The power supply was tested and its working normally. Apparently a glitch on EPICS caused the tripped off.

 Friday, February 09, 2018, 17:00

Target remained in EVAP1 for 2 hours at 0 A to ensure cooling.

EVAP1 was vented with Ar and the target was removed from EVAP1.

Graphite container seems unbroken.

Ta boat looks unbroken.

Laura Lambert wrote:

Marla Cervantes wrote:  Wednesday, January 10, 2018, 14:44 Circles from cast 1 were used, the same as the last round of 1stepUCx [see elog i.d. 164] A 14mm punch was used to punch out circles from the cast. 35 circles were packed into a graphite sample container. 35 x UO2/C circles = 5.75 g Graphite container = 5.38 g Graphite container is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3-layers of heat shield and installed in Evap1. Chamber currently pumping down.  Friday, January 12, 2018, 07:43 IGP1 = 0.0266 Torr TGHT = 520A, 5.92V Voltage has been climbing consistently since it has reached it's max setpoint, gone up ~0.8V in ~18hrs Carbonization complete. Initiating auto-cool at 2.0A/min Will update later with more information on this process.  Friday, January 12, 2018, 09:47 Turned the turbo pump back on, to ensure safe cooling.

 Monday, January 15, 2018, 10:00

Vented with Argon and removed from evap1

NB: The initial mass of the UO2/C discs was 5.9 g

       The final mass of the UCx discs was 4.614 g

 Friday, June 15, 2018, 16:39

35 circles of 14 mm diameter of cast #3 were packed into a graphite sample container.

35 x UO₂/C circles = 4.07 g

Graphite container mass = 5.3 g

Graphite tube is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3 used Ta foils for heat shielding and the boat was installed in Evap1.

Chamber currently pumping down.

 Saturday, June 16, 2018, 15:00

Tapped to 80A at 10A/10s with 20 s waiting period each 10 A

Waited 5 min for vacuum to stabilize.

Tapped to 90 A at 10A/10s with 20 s waiting period each 10 A

Waited 14 min for vacuum to stabilize

Tapped to 100 A at 10A/10s with 20 s waiting period each 10 A

Tapped to 520 A at 20A/20s with 20 s waiting period each 20 A

 Tuesday, June 19, 2018, 15:51 

 The material will be in the evap for a week

Wednesday, June 27, 2018, 09:53 

 The IEVAP  was vented with Ar and the UCx was trasnferred to the glove box.

 Tuesday, June 12, 2018, 18:20

35 circles of 14 mm diameter of cast #4 were packed into a graphite sample container.

30 x UO₂/C circles = 4.07 g

Graphite container mass = 5.3 g

Graphite tube is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3 used Ta foils for heat shielding and the boat was installed in Evap1.

Chamber currently pumping down.

Wednesday, June 13, 2018, 10:29 

Initial IGP1 = 6.43e-7 Torr

Tapped to 80A at 10A/10s with 20 s waiting period each 10 A

Waited 5 min for vacuum to stabilize.

Tapped to 90 A at 10A/10s with 20 s waiting period each 10 A

Waited 5 min to tap to 100 A 

Waited 14 min for vacuum to stabilize

Tapped to 400 A at 25A/30s with 30 s waiting period each 25 A

Tapped to 520 A at 20A/30s with 30 s waiting period each 20 A

Max pressure ~0.06 Torr 

Marla Cervantes wrote:

Tuesday, June 12, 2018, 18:20 35 circles of 14 mm diameter of cast #4 were packed into a graphite sample container. 30 x UO2/C circles = 4.07 g Graphite container mass = 5.3 g Graphite tube is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3 used Ta foils for heat shielding and the boat was installed in Evap1. Chamber currently pumping down. Wednesday, June 13, 2018, 10:29  Initial IGP1 = 6.43e-7 Torr Tapped to 80A at 10A/10s with 20 s waiting period each 10 A Waited 5 min for vacuum to stabilize. Tapped to 90 A at 10A/10s with 20 s waiting period each 10 A Waited 5 min to tap to 100 A  Waited 14 min for vacuum to stabilize Tapped to 400 A at 25A/30s with 30 s waiting period each 25 A Tapped to 520 A at 20A/30s with 30 s waiting period each 20 A Max pressure ~0.06 Torr

 Wednesday, June 13, 2018, 11:08

Pressure was dropping indicating full carbothermal reduction but the current tripped off to 0 A.

Marla Cervantes wrote:

Marla Cervantes wrote:  Tuesday, June 12, 2018, 18:20 35 circles of 14 mm diameter of cast #4 were packed into a graphite sample container. 30 x UO2/C circles = 4.07 g Graphite container mass = 5.3 g Graphite tube is placed inside a target boat. Boat previously coated with TaC and sintered. Ta-target boat is wrapped with 3 used Ta foils for heat shielding and the boat was installed in Evap1. Chamber currently pumping down. Wednesday, June 13, 2018, 10:29  Initial IGP1 = 6.43e-7 Torr Tapped to 80A at 10A/10s with 20 s waiting period each 10 A Waited 5 min for vacuum to stabilize. Tapped to 90 A at 10A/10s with 20 s waiting period each 10 A Waited 5 min to tap to 100 A  Waited 14 min for vacuum to stabilize Tapped to 400 A at 25A/30s with 30 s waiting period each 25 A Tapped to 520 A at 20A/30s with 30 s waiting period each 20 A Max pressure ~0.06 Torr   Wednesday, June 13, 2018, 11:08 Pressure was dropping indicating full carbothermal reduction but the current tripped off to 0 A.

 Wednesday, June 13, 2018, 12:23

The problem was reported to controls group

After 1 hour at 0 A, the autoramp was set to 4 A/min up to 520 A

The current and voltage are increasing accordingly.

The material will stay 4 hours at max point.

Thursday, June 14, 2018, 09:14 

After 4 hours the auto ramp was set to -1A/min to 0 A

Thursday, June 14, 2018, 14:47 

The IEVAP  was vented with Ar and the UCx was trasnferred to the glove box.

 Friday, May 18, 2018, 18:32

35 circles of 14 mm diameter of cast #3 were packed into a graphite sample container.

40 x UO2/C circles = 4.58 g

Graphite container mass = 6.95 g

Graphite tube is placed inside a target boat.

Boat previously coated with TaC and sintered.

Ta-target boat is wrapped with 3 used Ta foils for heat shielding and the boat was installed in Evap1.

Chamber currently pumping down.

Saturday, May 19, 2018, 07:30 

Initial IGP1 = 6.27e-7 Torr

 Tapped to 80A at 10A/10s with 20 s waiting period each 10 A

 Waited 4 min for vacuum to stabilize.

 Tapped to 100 A at 10A/10s with 20 s waiting period each 10 A

 Waited 12 min for vacuum

Tapped to 400 A at 25A/30s with 30 s waiting period each 25 A

Tapped to 520 A at 20A/30s with 30 s waiting period each 20 A

Pressure dropping indicates carbonization complete.

Current tripped off, vacuum was ok, water cooling was ok.

Saturday, May 19, 2018, 10:00 

Current was returned to 520 A manually

Tapped to 100 A at 10A/10s with 20 s waiting period each 10 A 

Tapped to 400 A at 25A/30s with 30 s waiting period each 25 A

Tapped to 520 A at 20A/30s with 30 s waiting period each 20 A

The discs will stay at max current for 4 hrs

 Saturday, May 19, 2018, 18:31

Vented with Argon and removed form evaporator 1