John Wong wrote:

Aurelia Laxdal wrote: Aurelia Laxdal wrote: Aurelia Laxdal wrote: Aurelia Laxdal wrote: Anders Mjos wrote: Laura Lambert wrote: Aurelia Laxdal wrote: Started Ta#47 heating at Evap2 using the autoramp program. The TGHT current is setup to go to 300A (for now) and the TBHT to 230A (final value).  Monday, March 14, 2016, 09:20 One thermocouple was not welded on correctly and is not working.  Cooling evap2 back down, to remove target and re-weld thermocouple. Once thermocouple replaced, will ramp back up and continue with tests/ conditioning of target.    Monday, March 14, 2016, 13:12: Stopped turbo pump  After EVAP2 was vented the thermocouple problem was fixed: it was the wire at on connector inside the box not making proper contact. The lid of the heat shield was also replaced since the one initially mounted had no holes, so one couldn't see the center block. Restarted pumping down at 4:30pm. Just started again the autoramp program: TGHT set to 300A (for the time being) and TBHT to 230A. Temperature measurements will resume tomorrow morning.  Raised the TGHT at 620A. The TBHT was already set at 230A. The temperature is at 1902 deg C. As per John's instructions the target will condition at these setpoints over the week-end. Today, lowered the TGHT from 620A (at 1894 deg C) to 300A.  TBHT is still at 230A.  Cooling down the target.   Thursday, March 24, 2016, 11:29  Target was removed from the Evaporator.   The thermocouples broke off.   Need to insert Re foil prior to installing

 Tuesday, April 19, 2016, 09:28: Uploaded thermoucouple data.

 Tuesday, July 26, 2016, 16:50

loaded into evap2

pumped down, HS water valves opened, no leaks detected.

tapped up manually to 35A

vacuum stable = 3.8e-6 Torr

Initiating auto-ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively.

Final setpoints at 230A for the TBHT and 600A for the TGHT.

Final desired temperature = 1800C

 Wednesday, July 27, 2016, 09:20

IGP1 = 6.3e-7 Torr, vacuum stable.

TGHT = 232A, 2.7V

TBHT = 131A, 1.76V

Increasing ramping rate to 1.0A/min and 0.5A/min for the TGHT and TBHT respectively.

 Wednesday, July 27, 2016, 15:46

TGHT = 600A, 8.87V

TBHT = 230A, 3.7V

IGP1 = 1.37e-6 Torr

OMEGA = 1640C

Increased max TGHT voltage to 12V

Tapped up manually to OMEGA = 1810C

TGHT = 675A, 10.21V

IGP1 = 2.2e-6 Torr

Will remain at max setpoints for the rest of the week and cool down over weekend.

 Thursday, July 28, 2016, 08:34

TGHT = 675A, 10.41V

OMEGA = 1833C

Tapped down to 660A, 10.09V

OMEGA = 1805C

 Friday, July 29, 2016, 13:57

OMEGA = 1814C

TGHT = 660A, 10.16V

TBHT = 230A, 3.72V

IGP1 = 3.43e-7 Torr

evap2 has remained at max setpoints for ~42hrs

conditioning complete.

Initiating auto-cool at 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.

 Tuesday, August 02, 2016, 13:39

vented in air and removed from evap2 this morning.

target looks good!

 Wednesday, December 16, 2015, 10:09

Target consists of 505 discs.

Total packed length 3.4cm.

*same parameters at Ta#46*

Total mass of target materials 53.9381g [4 packs of 20 with Ta wire + 425 single discs].

3 x Ta Heat shields.

No Re foil inserted.

No endcaps inserted.

Chamber pumped down overnight.

IGP1 = 5.1e-7 Torr.

Tapped up manually to 35A.

IGP1 = 5.2e-7 Torr.

Vacuum stable, initiating auto-ramp.

TBHT will be ramped up to 230A at 1.0A/min.

TGHT will be ramped up to 1800C, auto ramp to 600A at 2.0A/min [estimated final value of 720A according to elog ID 239]

 Wednesday, December 16, 2015, 15:08

TBHT reached max setpoint of 230A, 3.3V

TGHT = 600A, 8.9V

IGP1 = 1.1e-6 Torr.

OMEGA = 1543C

Increasing final setpoint of TGHT to 700A and re-initiating auto-ramp.

 Wednesday, December 16, 2015, 16:02

TGHT = 700A, 10.6V

IGP1 = 2.1e-6 Torr.

OMEGA = 1740C

Tapping up manually to 1800C.

 Wednesday, December 16, 2015, 16:28

TGHT = 730A, 11.2V

Vacuum is coming down from IGP1 = 2.6e-6 Torr.

OMEGA = 1800C

Will condition the target at 1800C overnight and ramp down in the morning.

 Thursday, December 17, 2015, 09:31

OMEGA = 1802C on right side

Temp on leg of left side = 2150C, the hottest point - measured with the Mikron pyrometer.

 Friday, December 18, 2015, 08:53

Evap2 remained at 1800C for ~26.5hrs

Auto-ramped down to TGHT = 300A and TBHT = 90A at a rate of 2.0A/min and 1.0A/min respectively.

Conditioning complete.

TGHT will be ramped up later today for emissivity measurements.

 Monday, January 04, 2016, 11:21

the following was performed by aurelia.

emissivity measurements were taken late december.

evap2 was cooled down and left under vacuum over the xmas break.

currently ramping back up for more emissivity measurements.

 Friday, January 08, 2016, 10:47

Aurelia done measurements.

vented and opened this morning.

Temperature measurements in progress this week for Ta HP-SIS.

See attachment for the current settings and rampings of the TGHT/TBHT  for the temperature measurements taken on  Jan. 9-10, 2016 .

Note: TBHT PS tripped off on Jan. 9, 2016 (see first page of the attached file) and couldn't turn it ON again over the week-end.

Aurelia Laxdal wrote:

Temperature measurements in progress this week for Ta HP-SIS.

 Friday, January 08, 2016, 10:49

Rh foil added.

endcaps inserted and expanded.

total length of target with end caps = 3.45cm

spot weld one thermocouple onto center block and one thermocouple onto target leg [left side wrt ionizer tube into page].

 see elog id# 268 for more info regarding measurements taken and state of TBHT power supply...

 Wednesday, May 25, 2016, 11:37

Container coated with TaC using 'flushing technique' [cleaned ionizer tube with acetone, so no coating inside ionizer tube]

Wrapped with 2 x Ta heat shields - one full height of Ta foil wrapped around cooling fins twice

Currently pumping down in evap2

 Thursday, May 26, 2016, 09:28

Tapped up manually to 40A

IGP1 = 6.6e-7 Torr

Initiating auto-ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively.

Final setpoints for TGHT = 650A and TBHT = 230A

Once max setpoints reached will continue to tap up manually while monitoring temperature to 1900C

Laura Lambert wrote:

Wednesday, May 25, 2016, 11:37 Container coated with TaC using 'flushing technique' [cleaned ionizer tube with acetone, so no coating inside ionizer tube] Wrapped with 2 x Ta heat shields - one full height of Ta foil wrapped around cooling fins twice Currently pumping down in evap2  Thursday, May 26, 2016, 09:28 Tapped up manually to 40A IGP1 = 6.6e-7 Torr Initiating auto-ramp at 0.2A/min and 0.1A/min for the TGHT and TBHT respectively. Final setpoints for TGHT = 650A and TBHT = 230A Once max setpoints reached will continue to tap up manually while monitoring temperature to 1900C

 Tuesday, May 31, 2016, 11:09

TGHT at 615A/9.08V, temp = 1610C.  Vacuum at 1.8e-7 Torr. 

Tapping up TGHT to reach 1900C

 Tuesday, May 31, 2016, 12:04

TGHT at 765A/11.90V.  Temp at 1900C.  Pressure is coming down from 8.7e-7Torr. 

Will keep at this temperature for a day.

 Wednesday, June 01, 2016, 15:22

Temperature has been stable at 1900C.  Pressure is coming down from 3.4e-7 Torr. 

Cooling down TGHT and TBHT at 2A/min and 1A/min, respectively.

 Friday, June 03, 2016, 12:10

TGHT/TBHT at 0A.  Target can be remained under vacuum until Monday.

 Monday, June 06, 2016, 16:54

Target container was inspected; it looks good

 Thursday, June 09, 2016, 15:39

First target using beta-SiC material!

Target container contains 450 discs of SiC [4 x 5 packs + 430 single discs]

Target packed length = 16cm. 

Mass of 533 discs SiC(green)  = 53.8758g

Container is wrapped with 3 heatshields; no end caps are inserted yet - coated spring inserted both sides to hold discs in place.

Sintering temp = 1800C, TGHT will be set accordingly.  TBHT max at 230A. 

Chamber is currently being pumped down. 

Friday, June 10, 2016, 13:24

HS water valves opened, no leaks detected.

Tapping up manually to 70A...

Auto ramp will be set for TGHT = 0.2A/min to a final setpoint of 520A

Auto-ramp for TBHT = 0.1A/min to a final setpoint of 230A.

 Friday, June 10, 2016, 16:27

TGHT stepped up to 70A/0.55V.  TGHT at 50A/0.62V. 

Pressure stabilized at 5.5e-5 Torr.

Initiated auto ramping.  TGHT at 0.2A/min --> 520A.  TBHT at 0.1A/min --> 230A.

John Wong wrote:

Laura Lambert wrote:  Thursday, June 09, 2016, 15:39 First target using beta-SiC material! Target container contains 450 discs of SiC [4 x 5 packs + 430 single discs] Target packed length = 16cm.  Mass of 533 discs SiC(green)  = 53.8758g Container is wrapped with 3 heatshields; no end caps are inserted yet - coated spring inserted both sides to hold discs in place. Sintering temp = 1800C, TGHT will be set accordingly.  TBHT max at 230A.  Chamber is currently being pumped down.  Friday, June 10, 2016, 13:24 HS water valves opened, no leaks detected. Tapping up manually to 70A... Auto ramp will be set for TGHT = 0.2A/min to a final setpoint of 520A Auto-ramp for TBHT = 0.1A/min to a final setpoint of 230A.      Friday, June 10, 2016, 16:27 TGHT stepped up to 70A/0.55V.  TGHT at 50A/0.62V.  Pressure stabilized at 5.5e-5 Torr. Initiated auto ramping.  TGHT at 0.2A/min --> 520A.  TBHT at 0.1A/min --> 230A.

 Monday, June 13, 2016, 09:51

TGHT = 425A, 5.65V

TBHT = 225A, 3.7V

IGP1 = 8.7e-6 Torr.

Increasing ramping rate to 1.0A/min...

 Monday, June 13, 2016, 15:56

Tapped up manually from 520A to 1800C

Extrapolated data on graph to determine correct current required to reach desired max temperature.

Will remain at 1800C for ~48hrs

See attachements for excel sheet and screenshot of striptool.

Laura Lambert wrote:

John Wong wrote:   Laura Lambert wrote:  Thursday, June 09, 2016, 15:39 First target using beta-SiC material! Target container contains 450 discs of SiC [4 x 5 packs + 430 single discs] Target packed length = 16cm.  Mass of 533 discs SiC(green)  = 53.8758g Container is wrapped with 3 heatshields; no end caps are inserted yet - coated spring inserted both sides to hold discs in place. Sintering temp = 1800C, TGHT will be set accordingly.  TBHT max at 230A.  Chamber is currently being pumped down.  Friday, June 10, 2016, 13:24 HS water valves opened, no leaks detected. Tapping up manually to 70A... Auto ramp will be set for TGHT = 0.2A/min to a final setpoint of 520A Auto-ramp for TBHT = 0.1A/min to a final setpoint of 230A.      Friday, June 10, 2016, 16:27 TGHT stepped up to 70A/0.55V.  TGHT at 50A/0.62V.  Pressure stabilized at 5.5e-5 Torr. Initiated auto ramping.  TGHT at 0.2A/min --> 520A.  TBHT at 0.1A/min --> 230A.    Monday, June 13, 2016, 09:51 TGHT = 425A, 5.65V TBHT = 225A, 3.7V IGP1 = 8.7e-6 Torr. Increasing ramping rate to 1.0A/min...  Monday, June 13, 2016, 15:56 Tapped up manually from 520A to 1800C Extrapolated data on graph to determine correct current required to reach desired max temperature. Will remain at 1800C for ~48hrs See attachements for excel sheet and screenshot of striptool.

 Wednesday, June 15, 2016, 17:54

TGHT at 710A, 11.35V.  TBHT at 230A/3.86V. 

Omega reading droppd to 1130C due to coating on windows. 

Ionizer tube was measured (center) at around 1900C

Cooling down at 2A/min for TGHT, 1A/min for TBHT. 

Samples will be collected prior to cleaning the windows.

NEXT:  Conditioning.

John Wong wrote:

Laura Lambert wrote: John Wong wrote:   Laura Lambert wrote:  Thursday, June 09, 2016, 15:39 First target using beta-SiC material! Target container contains 450 discs of SiC [4 x 5 packs + 430 single discs] Target packed length = 16cm.  Mass of 533 discs SiC(green)  = 53.8758g Container is wrapped with 3 heatshields; no end caps are inserted yet - coated spring inserted both sides to hold discs in place. Sintering temp = 1800C, TGHT will be set accordingly.  TBHT max at 230A.  Chamber is currently being pumped down.  Friday, June 10, 2016, 13:24 HS water valves opened, no leaks detected. Tapping up manually to 70A... Auto ramp will be set for TGHT = 0.2A/min to a final setpoint of 520A Auto-ramp for TBHT = 0.1A/min to a final setpoint of 230A.      Friday, June 10, 2016, 16:27 TGHT stepped up to 70A/0.55V.  TGHT at 50A/0.62V.  Pressure stabilized at 5.5e-5 Torr. Initiated auto ramping.  TGHT at 0.2A/min --> 520A.  TBHT at 0.1A/min --> 230A.    Monday, June 13, 2016, 09:51 TGHT = 425A, 5.65V TBHT = 225A, 3.7V IGP1 = 8.7e-6 Torr. Increasing ramping rate to 1.0A/min...  Monday, June 13, 2016, 15:56 Tapped up manually from 520A to 1800C Extrapolated data on graph to determine correct current required to reach desired max temperature. Will remain at 1800C for ~48hrs See attachements for excel sheet and screenshot of striptool.    Wednesday, June 15, 2016, 17:54 TGHT at 710A, 11.35V.  TBHT at 230A/3.86V.  Omega reading droppd to 1130C due to coating on windows.  Ionizer tube was measured (center) at around 1900C Cooling down at 2A/min for TGHT, 1A/min for TBHT.  Samples will be collected prior to cleaning the windows. NEXT:  Conditioning.

Thursday, June 16, 2016, 09:29

vented in air and opened up this morning.

took some samples to be tested.

 Thursday, June 16, 2016, 10:59

Previously sintered over weekend [see elog i.d 306]

Target container contains 450 discs of SiC [4 x 5 packs + 430 single discs]

Target packed length = 16cm. 

Mass of 533 discs SiC(green)  = 53.8758g

Container is wrapped with 3 heatshields; no end caps are inserted yet - coated spring inserted both sides to hold discs in place.

Conditioning temp = 1800C.

TGHT max = 710A according to sintering data.  TBHT max = 230A. 

Chamber is currently being pumped down. 

 Thursday, June 16, 2016, 15:43

Target was not removed from evap2 after sintering, vented and cleaned windows only.

HS water valves already open.

Stepped up manually to 70A, vacuum stable.

Initiated auto-ramp at 1.0A/min for the TGHT and 0.5A/min for the TBHT with max setpoints of 600A and 230A respectively.

TGHT = 118A, 0.9V

TBHT = 90A, 1.1V

IGP1 = 7.3e-7 Torr

 Friday, June 17, 2016, 12:14

TGHT has been tapped up manually to reach max desired temperature of 1800C

TGHT = 690A, 10.85V

TBHT = 230A, 3.88V

IGP1 = 4.9e-7 Torr

This is a lower current than the current required to reach 1800C during the sintering process.

For sintering, the max current was determined via extrapolation of trendline from raw data due to interference of coating on window and unable to take reliable readings from OMEGA.

For this conditioning process ~1800C is reached on the OMEGA since the window is still ~un-coated.

Will remain at 690A, ~1800C for several days to maximize conditioning process.

See attachment for raw data.

 Monday, June 20, 2016, 09:01

At the end of the day on friday 17th, OMEGA read ~1750C - no change in the current or voltage, vacuum was stable, this was the max setpoints used to reach 1800C.

This morning OMEGA = 2040C

TGHT = 690A, 10.95V

vacuum stable at IGP1 = 1.8e-7 Torr.

Slightly more noticeable coating on window port, looks like a thin ink layer, still relatively thin coating [ see attached image]

Also attached is archive from over wknd to show vacuum stable, current unchanged and voltage negligibly changed [only gone up by ~0.1V]

 Friday, June 24, 2016, 13:52

Container has remained at max setpoints for 7 days.

Initiating auto-cool for TGHT @ 2.0A/min and for TBHT @ 1.0A/min.

Will vent chamber and remove from evap2 to pass off for assembly monday morning.

See attachment for updated excel on temperature readings for the conditioning process.

 Monday, June 27, 2016, 08:28

vented in air and removed this morning.

target looks good!

all discs remained nicely alligned.

discs expanded outwards ~1cm, pushed back in to keep target length at 16cm

no visible yellow crystals like previous SiC targets 

endcaps inserted and expanded.

Rh foil inserted.

Ta heat shield foils removed, fins look good.

see photos attached for pictures of target - post conditioning.

coating on window very hard to remove. looked like a light sharpy pen coating on window. ended up scratching off with acetone and screw driver. couldn't remove all of it...

 Monday, June 29, 2015, 16:17

Target container is coated with TaC. No Ta-heat shields are used.

TGHT will be ramped up to 580A at 0.2A/min.

TBHT will be ramped up to 230A at 01A/min.

Chamber is currently being pumped down.

Laura Lambert wrote:

Monday, June 29, 2015, 16:17 Target container is coated with TaC. No Ta-heat shields are used. TGHT will be ramped up to 580A at 0.2A/min. TBHT will be ramped up to 230A at 01A/min. Chamber is currently being pumped down.

 Monday, June 29, 2015, 23:37

Opened the HS valves around 5pm.  Small leaks or just a vibration in the pipe line caused a rise in vacuum.  Leak rate is small, so allow the chamber to continue to pump down over night.

Sintering process can begin tomorrow if vacuum is allowed.

John Wong wrote:

Laura Lambert wrote:  Monday, June 29, 2015, 16:17 Target container is coated with TaC. No Ta-heat shields are used. TGHT will be ramped up to 580A at 0.2A/min. TBHT will be ramped up to 230A at 01A/min. Chamber is currently being pumped down.    Monday, June 29, 2015, 23:37 Opened the HS valves around 5pm.  Small leaks or just a vibration in the pipe line caused a rise in vacuum.  Leak rate is small, so allow the chamber to continue to pump down over night. Sintering process can begin tomorrow if vacuum is allowed.

 Tuesday, June 30, 2015, 08:22

IGP1 = 3.6e-7 Torr.

Tapped up manually to 40A.

Vacuum looks good.

IGP1 = 6.9e-7 Torr.

Inititating auto-ramp...

 Thursday, July 02, 2015, 09:56

IGP1 = 8.9e-7 Torr.

OMEGA = 1728C

TGHT and TBHT = 580A and 230A respectively.

Tapping up manually to 1800C.

 Thursday, July 02, 2015, 11:02

TGHT = 615A, 10.9V

OMEGA = 1800C

IGP1 = 1.1e-6 Torr.

Will continue to heat for 4hrs.

 Thursday, July 02, 2015, 15:43

Target container remained at 1800C for 4hrs50min.

Initiating auto-cool for TGHT = 2A/min and TBHT = 1A/min.

 Friday, July 03, 2015, 08:24

Vented in air and opened up this morning.

Edge of container on both ends not fully sintered [see photos]

Laura Lambert wrote:

John Wong wrote: Laura Lambert wrote:  Monday, June 29, 2015, 16:17 Target container is coated with TaC. No Ta-heat shields are used. TGHT will be ramped up to 580A at 0.2A/min. TBHT will be ramped up to 230A at 01A/min. Chamber is currently being pumped down.    Monday, June 29, 2015, 23:37 Opened the HS valves around 5pm.  Small leaks or just a vibration in the pipe line caused a rise in vacuum.  Leak rate is small, so allow the chamber to continue to pump down over night. Sintering process can begin tomorrow if vacuum is allowed.    Tuesday, June 30, 2015, 08:22 IGP1 = 3.6e-7 Torr. Tapped up manually to 40A. Vacuum looks good. IGP1 = 6.9e-7 Torr. Inititating auto-ramp...  Thursday, July 02, 2015, 09:56 IGP1 = 8.9e-7 Torr. OMEGA = 1728C TGHT and TBHT = 580A and 230A respectively. Tapping up manually to 1800C.  Thursday, July 02, 2015, 11:02 TGHT = 615A, 10.9V OMEGA = 1800C IGP1 = 1.1e-6 Torr. Will continue to heat for 4hrs.  Thursday, July 02, 2015, 15:43 Target container remained at 1800C for 4hrs50min. Initiating auto-cool for TGHT = 2A/min and TBHT = 1A/min.  Friday, July 03, 2015, 08:24 Vented in air and opened up this morning. Edge of container on both ends not fully sintered [see photos]

 Monday, July 06, 2015, 11:54

Inner tube surface isn't homogeneously sintered with TaC (see attachment).  

A second coating may help.  

For the re-sintering process, the target container will be wrapped with 6.2cm Ta (width) foil as a layer for heat shield on each side of the tube,  excluding the centre block - just like the same process was done last time, see e-log ID#217.  

The Ta-foil and the target tube will be spaced with Ta wire coiled around it.  

TGHT can be ramped up about 520A/9.1V to achieve 1900C.  Heating time for 3-4 hours until vacuum comes down to low 10-6 Torr. 

John Wong wrote:

Laura Lambert wrote: John Wong wrote: Laura Lambert wrote:  Monday, June 29, 2015, 16:17 Target container is coated with TaC. No Ta-heat shields are used. TGHT will be ramped up to 580A at 0.2A/min. TBHT will be ramped up to 230A at 01A/min. Chamber is currently being pumped down.    Monday, June 29, 2015, 23:37 Opened the HS valves around 5pm.  Small leaks or just a vibration in the pipe line caused a rise in vacuum.  Leak rate is small, so allow the chamber to continue to pump down over night. Sintering process can begin tomorrow if vacuum is allowed.    Tuesday, June 30, 2015, 08:22 IGP1 = 3.6e-7 Torr. Tapped up manually to 40A. Vacuum looks good. IGP1 = 6.9e-7 Torr. Inititating auto-ramp...  Thursday, July 02, 2015, 09:56 IGP1 = 8.9e-7 Torr. OMEGA = 1728C TGHT and TBHT = 580A and 230A respectively. Tapping up manually to 1800C.  Thursday, July 02, 2015, 11:02 TGHT = 615A, 10.9V OMEGA = 1800C IGP1 = 1.1e-6 Torr. Will continue to heat for 4hrs.  Thursday, July 02, 2015, 15:43 Target container remained at 1800C for 4hrs50min. Initiating auto-cool for TGHT = 2A/min and TBHT = 1A/min.  Friday, July 03, 2015, 08:24 Vented in air and opened up this morning. Edge of container on both ends not fully sintered [see photos]    Monday, July 06, 2015, 11:54 Inner tube surface isn't homogeneously sintered with TaC (see attachment).   A second coating may help.   For the re-sintering process, the target container will be wrapped with 6.2cm Ta (width) foil as a layer for heat shield on each side of the tube,  excluding the centre block - just like the same process was done last time, see e-log ID#217.   The Ta-foil and the target tube will be spaced with Ta wire coiled around it.   TGHT can be ramped up about 520A/9.1V to achieve 1900C.  Heating time for 3-4 hours until vacuum comes down to low 10-6 Torr.

 Monday, July 06, 2015, 16:28

Container has been re-coated with TaC.

Target container is wrapped with a single 15.5cm x 8.5cm Ta foil heat shield on each side of the center block, spaced with Ta wire coil.

Chamber is currently being pumped down.

 Tuesday, July 07, 2015, 09:36

HS water valves were opened this morning, no leaks detected.

IGP1 = 6e-7 Torr.

Tapped up manually to 30A.

Waited ~1hr.

Vacuum stable, IGP1 = 1.9e-6 Torr.

Initiating auto-ramp at 0.2A/min and 0.1A/min for TGHT and TBHT respectively.

 Target container reached max setpoints of 520A/230A and 1950C ~6hrs ago.

IGP1 = 7.6e-7 Torr.

Initiating auto-cool at 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.

 Friday, July 10, 2015, 11:16

Vented in air and removed from evap2.

Again, edges not fully sintered [see photos]

Inside of container looks better, fully coated.

Tuesday, September 12, 2023, 09:51

The coated container was wrapped in 3 Ta foil heatshield and left in evap2 over night to attain vacuum.

Target temperature on OMEGA= 1850-1900 C

OMEGA slope:= 0.990

Target time at max temperature = 4 hours

Final Current TBHT= 230 A

Final TGHT current= ~700A (adjustable)

Heating autoramp starged at 1A/min on  TGHT  and TBHT to 120A

Then at 2 A/min  to =400 A TGHT and 230A TBHT

Good vacuum = 5.0 e-04 Torr

Bad vacuum = 5.0E-02 Torr

Initial IGP1= 2.7e-06 Torr

Tuesday, September 12, 2023, 7:00

Started autoramp @1A/min to 120A on both TGHT and TBHT

Tuesday, September 12, 2023, 09:53

Heating ramp set to 230A for both TGHT and TBHT.  Rate at 2A/min for both heaters.

Tuesday, September 12, 2023, 11:21

Continued ramp on TGHT at 2A/min to 335A and now setting to 3A/min (1.5A/30s)

Tuesday, September 12, 2023, 11:47

Continue ramping @3A/min on TGHT

 Tuesday, September 12, 2023, 13:33

Reached 1840 C at TGHT =677A and 10.5V

Will keep for 4 hours

Thursday, December 14, 2023, 09:53

Target left pumping down in Evap2 overnight. 

Initial weight including protective jig = 1474.3 g

Total number of target foils:388 

 10 analysis discs: 5x 220727-2 labelled as A and 5x 231123-2 labelled as B on the right side (front) of container.  Order of discs ABABABABAB.

Total length packed 15.5 cm

container has 3 Ta heat shields including the inner made of three pieces as to cover the center block.

No endcaps inserted to facilitate out-gassing

Ta coated spring at  both ends

ramp to 500A @ 1A/min TGHT and to 230A on TBHT

max approx 700A on TGHT and 230A on TBHT (Omega slope set = 0.990)

Then temperature = 1800C

TBHT will be set fixed at 230 A (max).  TBHT heated manually and automatically to max.

Good vac at 5.00 e -4 Torr

Bad vac at 5.00 e-2 Torr

 IGP1= 9.3e-07 Torr at start of initial ramp.

Thursday, December 14, 2023, 09:56

Started initial ramp up 1A/min on both heaters

Thursday, December 14, 2023, 11:03

Pressure dropping.  Will increase ramp speed to 2A/min on both heaters (1A/30s)

Thursday, December 14, 2023, 11:17

pressure dropping.  Increase ramp to 4A/min (2A/30s)

Will stop and ramping for temperature measurements

Thursday, December 14, 2023, 13:28

Increased ramp to 5A/min (2.5A/30s)

 Will heat to 703A on TGHT and leave for 4 hours