Thursday, October 02, 2014, 11:51

Target container sprayed with TaC, currently drying in fume hood

 Monday, October 06, 2014, 12:11

Target container & back block is wrapped with 3 layers of Ta-heat shield.  The chamber has been pumped down over the weekend. 

Pressure currently at 2.23e-7 Torr. 

HS water valves open; no leaks detected.

TGHT will be ramped up to 580A at 0.2A/min

TBHT will be ramped up to 230A at 0.2A/min.

Laura Lambert wrote:

Thursday, October 02, 2014, 11:51 Target container sprayed with TaC, currently drying in fume hood  Monday, October 06, 2014, 12:11 Target container & back block is wrapped with 3 layers of Ta-heat shield.  The chamber has been pumped down over the weekend.  Pressure currently at 2.23e-7 Torr.  HS water valves open; no leaks detected. TGHT will be ramped up to 580A at 0.2A/min TBHT will be ramped up to 230A at 0.2A/min.

 Monday, October 06, 2014, 12:16

Stepped up both TGHT/TBHT to 35A. 

Tuesday, October 07, 2014, 12:54

TBHT reached to 230A/3.7V and TGHT is still ramping up, currently at 303A/4.5V. Temp measured with Omega-IR2 = 1165C with e'=0.85

Pressure @ 5.2e-7 Torr. 

Increase ramping rate to 2A/min.

 Tuesday, October 07, 2014, 16:21

TGHT is now at 580A and TGHT at 230A.

Temperature is measured with OMEGA-IR2, MIKRON, and analog pyrometer - All the measurements are agreed at 1700C (without the tantalum emissivity correction of 250C)

The OMEGA-IR2 slope has changed to 0.97 for the correction - The real temperature reading from the display is showing 1935C.

Now... attempting to low TBHT to see any temperature change.

 Tuesday, October 07, 2014, 17:01

TGHT @ 580A.

TBHT = 180C, Temp = 1925C

TBHT = 130C, Temp = 1920C

Not much of change in the temperature on the target tube...

Tuesday, October 07, 2014, 17:07

Attempting to increase the temperature to 2000C

TGHT = 600A, Temp = 1955C

TGHT = 620A, Temp = 2000C

Target will continue heating at this temperature overnight... Will continue to monitor.

 Tuesday, October 07, 2014, 20:59

After almost 4 hours of heating at 620A on TGHT, the temperature has dropped to 1980C.  

Pressure is coming down to 1.17e-6 Torr.  

Increased TGHT to 630A to maintain temp @ 2000C

John Wong wrote:

Laura Lambert wrote:  Thursday, October 02, 2014, 11:51 Target container sprayed with TaC, currently drying in fume hood  Monday, October 06, 2014, 12:11 Target container & back block is wrapped with 3 layers of Ta-heat shield.  The chamber has been pumped down over the weekend.  Pressure currently at 2.23e-7 Torr.  HS water valves open; no leaks detected. TGHT will be ramped up to 580A at 0.2A/min TBHT will be ramped up to 230A at 0.2A/min.    Monday, October 06, 2014, 12:16 Stepped up both TGHT/TBHT to 35A.  Tuesday, October 07, 2014, 12:54 TBHT reached to 230A/3.7V and TGHT is still ramping up, currently at 303A/4.5V. Temp measured with Omega-IR2 = 1165C with e'=0.85 Pressure @ 5.2e-7 Torr.  Increase ramping rate to 2A/min.  Tuesday, October 07, 2014, 16:21 TGHT is now at 580A and TGHT at 230A. Temperature is measured with OMEGA-IR2, MIKRON, and analog pyrometer - All the measurements are agreed at 1700C (without the tantalum emissivity correction of 250C) The OMEGA-IR2 slope has changed to 0.97 for the correction - The real temperature reading from the display is showing 1935C. Now... attempting to low TBHT to see any temperature change.  Tuesday, October 07, 2014, 17:01 TGHT @ 580A. TBHT = 180C, Temp = 1925C TBHT = 130C, Temp = 1920C Not much of change in the temperature on the target tube... Tuesday, October 07, 2014, 17:07 Attempting to increase the temperature to 2000C TGHT = 600A, Temp = 1955C TGHT = 620A, Temp = 2000C Target will continue heating at this temperature overnight... Will continue to monitor.  Tuesday, October 07, 2014, 20:59 After almost 4 hours of heating at 620A on TGHT, the temperature has dropped to 1980C.   Pressure is coming down to 1.17e-6 Torr.   Increased TGHT to 630A to maintain temp @ 2000C

 Wednesday, October 08, 2014, 11:46

Temperature readout from omega-IR2C = 2054C

TGHT = 11.14V, 628.0A

TBHT = 2.01V, 129.8A

IGP1 = 8.2e-7Torr

Initiating auto-cool for TGHT @ 2A/min, TBHT @ 1A/min

 Thursday, October 09, 2014, 16:00

vented in air and opened up this morning

target container looks good!

Laura Lambert wrote:

John Wong wrote: Laura Lambert wrote:  Thursday, October 02, 2014, 11:51 Target container sprayed with TaC, currently drying in fume hood  Monday, October 06, 2014, 12:11 Target container & back block is wrapped with 3 layers of Ta-heat shield.  The chamber has been pumped down over the weekend.  Pressure currently at 2.23e-7 Torr.  HS water valves open; no leaks detected. TGHT will be ramped up to 580A at 0.2A/min TBHT will be ramped up to 230A at 0.2A/min.    Monday, October 06, 2014, 12:16 Stepped up both TGHT/TBHT to 35A.  Tuesday, October 07, 2014, 12:54 TBHT reached to 230A/3.7V and TGHT is still ramping up, currently at 303A/4.5V. Temp measured with Omega-IR2 = 1165C with e'=0.85 Pressure @ 5.2e-7 Torr.  Increase ramping rate to 2A/min.  Tuesday, October 07, 2014, 16:21 TGHT is now at 580A and TGHT at 230A. Temperature is measured with OMEGA-IR2, MIKRON, and analog pyrometer - All the measurements are agreed at 1700C (without the tantalum emissivity correction of 250C) The OMEGA-IR2 slope has changed to 0.97 for the correction - The real temperature reading from the display is showing 1935C. Now... attempting to low TBHT to see any temperature change.  Tuesday, October 07, 2014, 17:01 TGHT @ 580A. TBHT = 180C, Temp = 1925C TBHT = 130C, Temp = 1920C Not much of change in the temperature on the target tube... Tuesday, October 07, 2014, 17:07 Attempting to increase the temperature to 2000C TGHT = 600A, Temp = 1955C TGHT = 620A, Temp = 2000C Target will continue heating at this temperature overnight... Will continue to monitor.  Tuesday, October 07, 2014, 20:59 After almost 4 hours of heating at 620A on TGHT, the temperature has dropped to 1980C.   Pressure is coming down to 1.17e-6 Torr.   Increased TGHT to 630A to maintain temp @ 2000C    Wednesday, October 08, 2014, 11:46 Temperature readout from omega-IR2C = 2054C TGHT = 11.14V, 628.0A TBHT = 2.01V, 129.8A IGP1 = 8.2e-7Torr Initiating auto-cool for TGHT @ 2A/min, TBHT @ 1A/min  Thursday, October 09, 2014, 16:00 vented in air and opened up this morning target container looks good!

 Thursday, October 09, 2014, 16:36

Photos for the OMEGA-IR2C temp measurement can be found on this link (see also the subfolder for the heating process):

https://www.dropbox.com/sh/n5sxcepg7e847xw/AACMubuKW1idd49D1Nz_0diNa?dl=0

Monday, November 10, 2014, 13:51

target container was sprayed with TaC on friday and sintered over the weekend.
vented and removed from evap2 this morning, looks good.

this container will be used as a round2 for UCx #11 since the last container broke as it was being assembled.

hopefully all the materials can be recovered and re-used/re-loaded into the new container...

Monday, February 02, 2015, 16:28

Container is coated with TaC.  No Ta foil wrapped around. 

Chamber is being pumped down.

TGHT/TBHT will be ramped up to 580A/230A at 0.2A/min.

John Wong wrote:

Monday, February 02, 2015, 16:28 Container is coated with TaC.  No Ta foil wrapped around.  Chamber is being pumped down. TGHT/TBHT will be ramped up to 580A/230A at 0.2A/min.

 Tuesday, February 03, 2015, 10:28

HS water valves opened; no leaks detected.

IGP1 = 5.9e-7 Torr

 Wednesday, February 04, 2015, 11:10

attempted to initiate manual ramp up of TGHT and TBHT yesterday, but not responding to EPICS

currently sitting under vacuum, waiting on fix...

 Wednesday, February 04, 2015, 14:16

controls fixed.

initiated auto-ramp.

 Thursday, February 05, 2015, 08:56

IGP1 = 4.1e-7 Torr

TGHT = 290A

TBHT = 225A

Increasing auto-ramp to 1.0A/min

 Thursday, February 05, 2015, 13:49

IGP1 = 1.4e-6 Torr

TGHT = 569A

TBHT = 232A

Increasing auto-ramp to 2.0A/min

Laura Lambert wrote:

John Wong wrote: Monday, February 02, 2015, 16:28 Container is coated with TaC.  No Ta foil wrapped around.  Chamber is being pumped down. TGHT/TBHT will be ramped up to 580A/230A at 0.2A/min.      Tuesday, February 03, 2015, 10:28 HS water valves opened; no leaks detected. IGP1 = 5.9e-7 Torr  Wednesday, February 04, 2015, 11:10 attempted to initiate manual ramp up of TGHT and TBHT yesterday, but not responding to EPICS currently sitting under vacuum, waiting on fix...  Wednesday, February 04, 2015, 14:16 controls fixed. initiated auto-ramp.  Thursday, February 05, 2015, 08:56 IGP1 = 4.1e-7 Torr TGHT = 290A TBHT = 225A Increasing auto-ramp to 1.0A/min  Thursday, February 05, 2015, 13:49 IGP1 = 1.4e-6 Torr TGHT = 569A TBHT = 232A Increasing auto-ramp to 2.0A/min

 Thursday, February 05, 2015, 18:02

Auto-cooling TGHT to 400A at 1A/min.  Need to take voltage reading tomorrow. 

John Wong wrote:

Laura Lambert wrote: John Wong wrote: Monday, February 02, 2015, 16:28 Container is coated with TaC.  No Ta foil wrapped around.  Chamber is being pumped down. TGHT/TBHT will be ramped up to 580A/230A at 0.2A/min.      Tuesday, February 03, 2015, 10:28 HS water valves opened; no leaks detected. IGP1 = 5.9e-7 Torr  Wednesday, February 04, 2015, 11:10 attempted to initiate manual ramp up of TGHT and TBHT yesterday, but not responding to EPICS currently sitting under vacuum, waiting on fix...  Wednesday, February 04, 2015, 14:16 controls fixed. initiated auto-ramp.  Thursday, February 05, 2015, 08:56 IGP1 = 4.1e-7 Torr TGHT = 290A TBHT = 225A Increasing auto-ramp to 1.0A/min  Thursday, February 05, 2015, 13:49 IGP1 = 1.4e-6 Torr TGHT = 569A TBHT = 232A Increasing auto-ramp to 2.0A/min    Thursday, February 05, 2015, 18:02 Auto-cooling TGHT to 400A at 1A/min.  Need to take voltage reading tomorrow.

 Tuesday, February 10, 2015, 09:35

Vented and opened this morning.

Container fully sintered.

 Tuesday, February 10, 2015, 14:00

Container loaded into EVAP2 at noon.

no heat shields.

Chamber currently being pumped down.

TGHT/ TBHT will be ramped up to 580A/ 230A, tapped up manually.

 Tuesday, February 10, 2015, 14:39

HS water valves opened, no leaks detected.

Tapping up manually / recording data in excel

 Wednesday, February 11, 2015, 11:24

Reached max set points yesterday early evening.

Tapped down manually this a.m.

Will vent and open this afternoon.

 Wednesday, February 11, 2015, 15:54

Took out this afternoon.

container looks good.

graphite insert removed/ inspected - not much change, slightly lighter in colour.

[see attachments for graphs/ table]

 Wednesday, February 11, 2015, 16:10

Container loaded into EVAP2.

3xTa heat shields.

Chamber currently being pumped down.

TGHT/ TBHT will be ramped up to 580A/ 230A or 1800C tapped up manually.

 Thursday, February 12, 2015, 09:39

HS water valves opened, no leaks detected.
Tapping up manually.

 Thursday, February 12, 2015, 12:07

OMEGA reached 1805C; TGHT = 415A, TBHT = 205A

Will continue to tap up manually to 2000C

 Thursday, February 12, 2015, 15:19

Reached TGHT = 500A, TBHT = 230A, OMEGA = 2035C.

Sat for ~2hrs.

Tapping up a further 25A on the TGHT.

 Thursday, February 12, 2015, 16:05

Tapped up manually to:

OMEGA = 2250C

DV = 5.65V

TGHT = 580A

TBHT = 230A

Friday, February 13, 2015, 10:05

Reached max setpoint last night.

Voltage starting to increase at contant TGHT @ 580A.  Lower TGHT to 525A, temp at 2150C (time 6:30pm) 

Initiating manual cool down.

Friday, February 13, 2015, 15:31

vented and opened up this afternoon.

everything looked good, container not broken! graphite insert looked good! the container was slightly bent, but nothing of significance.

however, the graphite insert bonded to the container so it was not taken out in one piece...

 Thursday, February 19, 2015, 15:19

Target container coated with TaC, loaded in EVAP2.

No Ta heat shields.

Will pump down over the weekend.

 Monday, February 23, 2015, 10:22

IGP1  = 1.75e-7 Torr

TGHT will be ramped up to 580A at 0.2A/min

TBHT will be ramped up to 230A at 0.2A/min

evap2 power supply not responding to epics controls...waiting on fix

 Wednesday, February 25, 2015, 16:05

controls now fixed.

danceioc1 involving evap ioc will be updated tomorrow by controls.

once ioc update complete will ramp up.

 Friday, February 27, 2015, 09:34

ioc update complete yesterday afternoon.

IGP1 = 1.1e-7

initiating ramp up...

Parameter setup: 5.0e-5 good vac, 6.0e-5 bad vac.

 Monday, March 02, 2015, 09:01

IGP1 = 2.5e-7 Torr

TGHT = 578A

TBHT = 232A

OMEGA = 1750C

Increasing to 1800C

 Monday, March 02, 2015, 10:42

Reached 1800C at 10:30

TGHT = 603A

TBHT = 232A

IGP1 = 2.8e-7 Torr

 Monday, March 02, 2015, 14:26

Sat at max set point for 4hrs.

IGP1 = 2.7e-7 Torr.

Initiating auto-cool, TGHT @ 2A/min, TBHT @ 1A/min.

 Tuesday, March 03, 2015, 09:17

vented and opened this a.m.

target container looks good, TaC coating fully sintered.

 Tuesday, May 19, 2015, 13:33

Target container is coated with TaC.  No Ta-heat shields are used.

TGHT will be ramped up to 580A at 0.2A/min.

TBHT will be ramped up to 230A at 0.1A/min.

Chamber is currently being pumped down

 Tuesday, May 19, 2015, 15:04

Opened up HS water, no leaks detected.

Stepped up to 35A.

Waited ~35min, vacuum stable.

IGP1 = 1.7e-6 Torr.

Initiating auto-ramp.

 Wednesday, May 20, 2015, 11:43

IGP1 = 3e-7 Torr.

TGHT = 282A, 3.8V

TBHT = 156A, 2.2V

Increasing ramping rate to 1.0A/min and 0.5A/min for the TGHT and TBHT respectively.

 Thursday, May 21, 2015, 10:42

IGP1 = 2.9e-7

Direct voltage = 5.48V

OMEGA = 1703C.

Initiating auto-cool at 2.0A/min  and 1.0A/min for the TGHT and TBHT.

 Friday, May 22, 2015, 11:41

Vented in air and opened up this morning.

TaC coating fully sintered, looks good! 

 Friday, May 29, 2015, 11:21

Total number of foils: 425 discs

Total mass of materials [incl graphite foils]: 44.41g

Total length packed: 12.3cm

Container has no heat shields.

No endcaps inserted to allow outgassing.

Currently being pumped down.

 Friday, May 29, 2015, 14:13

HS water valves opened, no leaks detected.

IGP1 = 5.4e-6 Torr.

Tapping up manually.

Friday, May 29, 2015, 16:48

Tapped up manually to 20A.

IGP1 = 5.9e-6 Torr.

Initiating auto-ramp at 0.2A/min for the TGHT and 0.1A/min for the TBHT.

Max setpoints set to 580A and 230A for the TGHT and TBHT respectively.

Good Vacuum = 3.0e-5 Torr. Bad Vacuum = 4.0e-5 Torr.

 Monday, June 01, 2015, 09:17

IGP1 = 3.8e-6 Torr.

TGHT = 478A.

TBHT reached max setpoint of 230A.

Increasing ramping rate to 0.5A/min.

 Monday, June 01, 2015, 13:15

Checked window for temperature readings, good visibility, no coating on window. 

IGP1 = 9.1e-6 Torr.

TGHT reached max setpoint of 580A 30min ago.

Stepping up manually to a target temperature of 2000C...

 Monday, June 01, 2015, 16:25

IGP1 = 6.5e-6 Torr.

TGHT = 870A, 17.90V

OMEGA = 1948C

Laura Lambert wrote:

Friday, May 29, 2015, 11:21 Total number of foils: 425 discs Total mass of materials [incl graphite foils]: 44.41g Total length packed: 12.3cm Container has no heat shields. No endcaps inserted to allow outgassing. Currently being pumped down.  Friday, May 29, 2015, 14:13 HS water valves opened, no leaks detected. IGP1 = 5.4e-6 Torr. Tapping up manually. Friday, May 29, 2015, 16:48 Tapped up manually to 20A. IGP1 = 5.9e-6 Torr. Initiating auto-ramp at 0.2A/min for the TGHT and 0.1A/min for the TBHT. Max setpoints set to 580A and 230A for the TGHT and TBHT respectively. Good Vacuum = 3.0e-5 Torr. Bad Vacuum = 4.0e-5 Torr.  Monday, June 01, 2015, 09:17 IGP1 = 3.8e-6 Torr. TGHT = 478A. TBHT reached max setpoint of 230A. Increasing ramping rate to 0.5A/min.  Monday, June 01, 2015, 13:15 Checked window for temperature readings, good visibility, no coating on window.  IGP1 = 9.1e-6 Torr. TGHT reached max setpoint of 580A 30min ago. Stepping up manually to a target temperature of 2000C...  Monday, June 01, 2015, 16:25 IGP1 = 6.5e-6 Torr. TGHT = 870A, 17.90V OMEGA = 1948C

 Monday, June 01, 2015, 17:59

After almost an hour at 870A, the temperature went up from 1948C to 1980C; however temperature around the target container/legs are >2000C.  The voltage on the power supply also went up slightly. 

There is a film coated on the window port and that could affect the temp reading.

To be safe, I lowered the TGHT to 830A/17.38V, temp at 1930C. 

Will keep at 830A for 4 hours and cool down this evening. 

Recommend: Using Ta-heat shields for sintering next time.

 Monday, June 01, 2015, 22:55

TGHT at 830A for almost 5 hours.  

TEMP has gone up to 1994C.  Voltage has also gone up to 19V.  

Cooling down at 2A/min for TGHT and 1A/min for TBHT. 

John Wong wrote:

Laura Lambert wrote:  Friday, May 29, 2015, 11:21 Total number of foils: 425 discs Total mass of materials [incl graphite foils]: 44.41g Total length packed: 12.3cm Container has no heat shields. No endcaps inserted to allow outgassing. Currently being pumped down.  Friday, May 29, 2015, 14:13 HS water valves opened, no leaks detected. IGP1 = 5.4e-6 Torr. Tapping up manually. Friday, May 29, 2015, 16:48 Tapped up manually to 20A. IGP1 = 5.9e-6 Torr. Initiating auto-ramp at 0.2A/min for the TGHT and 0.1A/min for the TBHT. Max setpoints set to 580A and 230A for the TGHT and TBHT respectively. Good Vacuum = 3.0e-5 Torr. Bad Vacuum = 4.0e-5 Torr.  Monday, June 01, 2015, 09:17 IGP1 = 3.8e-6 Torr. TGHT = 478A. TBHT reached max setpoint of 230A. Increasing ramping rate to 0.5A/min.  Monday, June 01, 2015, 13:15 Checked window for temperature readings, good visibility, no coating on window.  IGP1 = 9.1e-6 Torr. TGHT reached max setpoint of 580A 30min ago. Stepping up manually to a target temperature of 2000C...  Monday, June 01, 2015, 16:25 IGP1 = 6.5e-6 Torr. TGHT = 870A, 17.90V OMEGA = 1948C    Monday, June 01, 2015, 17:59 After almost an hour at 870A, the temperature went up from 1948C to 1980C; however temperature around the target container/legs are >2000C.  The voltage on the power supply also went up slightly.  There is a film coated on the window port and that could affect the temp reading. To be safe, I lowered the TGHT to 830A/17.38V, temp at 1930C.  Will keep at 830A for 4 hours and cool down this evening.  Recommend: Using Ta-heat shields for sintering next time.  Monday, June 01, 2015, 22:55 TGHT at 830A for almost 5 hours.   TEMP has gone up to 1994C.  Voltage has also gone up to 19V.   Cooling down at 2A/min for TGHT and 1A/min for TBHT.

 Tuesday, June 02, 2015, 12:37

Chamber was vented and the target was inspected. 

Some stressed marks on the target container can be observed.

The container is also slightly curved but otherwise it's fine. 

The materials packed length has expended outward so 3 discs were removed in order to insert the end caps. 

The packed length is now 16cm.

Two extra graphite foils were inserted on both ends, and previously coated/sintered TaC-end caps are inserted and expended. 

Rn foil is inserted & Std solutions are added. 

Ready for test-stand.

Link to photos for more details:

https://www.dropbox.com/sh/0cra7viqs9ro8q3/AADEGk8goGI4c-uzRQSGwWmxa?dl=0

John Wong wrote:

John Wong wrote: Laura Lambert wrote:  Friday, May 29, 2015, 11:21 Total number of foils: 425 discs Total mass of materials [incl graphite foils]: 44.41g Total length packed: 12.3cm Container has no heat shields. No endcaps inserted to allow outgassing. Currently being pumped down.  Friday, May 29, 2015, 14:13 HS water valves opened, no leaks detected. IGP1 = 5.4e-6 Torr. Tapping up manually. Friday, May 29, 2015, 16:48 Tapped up manually to 20A. IGP1 = 5.9e-6 Torr. Initiating auto-ramp at 0.2A/min for the TGHT and 0.1A/min for the TBHT. Max setpoints set to 580A and 230A for the TGHT and TBHT respectively. Good Vacuum = 3.0e-5 Torr. Bad Vacuum = 4.0e-5 Torr.  Monday, June 01, 2015, 09:17 IGP1 = 3.8e-6 Torr. TGHT = 478A. TBHT reached max setpoint of 230A. Increasing ramping rate to 0.5A/min.  Monday, June 01, 2015, 13:15 Checked window for temperature readings, good visibility, no coating on window.  IGP1 = 9.1e-6 Torr. TGHT reached max setpoint of 580A 30min ago. Stepping up manually to a target temperature of 2000C...  Monday, June 01, 2015, 16:25 IGP1 = 6.5e-6 Torr. TGHT = 870A, 17.90V OMEGA = 1948C    Monday, June 01, 2015, 17:59 After almost an hour at 870A, the temperature went up from 1948C to 1980C; however temperature around the target container/legs are >2000C.  The voltage on the power supply also went up slightly.  There is a film coated on the window port and that could affect the temp reading. To be safe, I lowered the TGHT to 830A/17.38V, temp at 1930C.  Will keep at 830A for 4 hours and cool down this evening.  Recommend: Using Ta-heat shields for sintering next time.  Monday, June 01, 2015, 22:55 TGHT at 830A for almost 5 hours.   TEMP has gone up to 1994C.  Voltage has also gone up to 19V.   Cooling down at 2A/min for TGHT and 1A/min for TBHT.     Tuesday, June 02, 2015, 12:37 Chamber was vented and the target was inspected.  Some stressed marks on the target container can be observed. The container is also slightly curved but otherwise it's fine.  The materials packed length has expended outward so 3 discs were removed in order to insert the end caps.  The packed length is now 16cm. Two extra graphite foils were inserted on both ends, and previously coated/sintered TaC-end caps are inserted and expended.  Rn foil is inserted & Std solutions are added.  Ready for test-stand. Link to photos for more details: https://www.dropbox.com/sh/0cra7viqs9ro8q3/AADEGk8goGI4c-uzRQSGwWmxa?dl=0

 see attachment for data recorded during ZrC conditioning 

 Tuesday, June 09, 2015, 9:16

Target container is coated with TaC. No Ta-heat shields are used.

TGHT will be ramped up to 580A at 0.2A/min.

TBHT will be ramped up to 230A at 01A/min.

Chamber is currently being pumped down.

 Tuesday, June 09, 2015, 15:37

HS water valves were opened. no leaks detected.

Tapped up manually to 35A.

Once vacuum stabilized after ~45min, initiated auto-ramp.

 Wednesday, June 10, 2015, 08:02

IGP1 = 5.3e-7 Torr.

TGHT = 250A and TBHT = 140A.

Increasing auto ramp to 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.

Laura Lambert wrote:

Tuesday, June 09, 2015, 9:16 Target container is coated with TaC. No Ta-heat shields are used. TGHT will be ramped up to 580A at 0.2A/min. TBHT will be ramped up to 230A at 01A/min. Chamber is currently being pumped down.  Tuesday, June 09, 2015, 15:37 HS water valves were opened. no leaks detected. Tapped up manually to 35A. Once vacuum stabilized after ~45min, initiated auto-ramp.  Wednesday, June 10, 2015, 08:02 IGP1 = 5.3e-7 Torr. TGHT = 250A and TBHT = 140A. Increasing auto ramp to 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.

 Wednesday, June 10, 2015, 16:32

TGHT/TBHT are at 580A/230A for almost 6 hours, temp at 1728C.

Vac at 8.5e-7 Torr. 

Cooling down initiated at 1A/min.

Target container should be inspected once the chamber is vented.

John Wong wrote:

Laura Lambert wrote:  Tuesday, June 09, 2015, 9:16 Target container is coated with TaC. No Ta-heat shields are used. TGHT will be ramped up to 580A at 0.2A/min. TBHT will be ramped up to 230A at 01A/min. Chamber is currently being pumped down.  Tuesday, June 09, 2015, 15:37 HS water valves were opened. no leaks detected. Tapped up manually to 35A. Once vacuum stabilized after ~45min, initiated auto-ramp.  Wednesday, June 10, 2015, 08:02 IGP1 = 5.3e-7 Torr. TGHT = 250A and TBHT = 140A. Increasing auto ramp to 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.    Wednesday, June 10, 2015, 16:32 TGHT/TBHT are at 580A/230A for almost 6 hours, temp at 1728C. Vac at 8.5e-7 Torr.  Cooling down initiated at 1A/min. Target container should be inspected once the chamber is vented.

 Thursday, June 11, 2015, 10:55

Vented in air and opened up this morning.

Same as last container sintered in evap2 [IG-LIS for UCx#13] - ends not quite fully sintered and coating not very good.

most likely due to old TaC spray.

See link for photos.

https://www.dropbox.com/sh/75o43x8y2z16e7j/AABc8Z1fTTaTRtJ5_Jr1eacWa?dl=0