Nikita Bernier wrote:

Nikita Bernier wrote:  Tuesday, May 07, 2013, 16:48   5 BeO pellets were made.  Each weights about 1.3 g (including org mass).  A piece of Re foil (0.002" thick) is used as the under layer to protect the reaction between Be(g) and the Ta-boat.  (see Attachments) Another layer of Ta-foil is used as the heat-shield to wrap around the Ta-boat. The chamber was pumped down.  TGHT will be ramped up to 600 A (~1360°C) at 0.2 A/min. The vacuum limit parameter was set for good vacuum at < 3.0e-5 Torr and bad vacuum at > 4.0e0-5 Torr. The pressure, voltage and current will be closely monitored.  If the Ta-boat survives, the TGHT will continue to ramp up to max 800 A (~1580°C).    Monday, May 13, 2013, 12:48   TGHT has been at 600 A for about 13 hours with stable very low vacuum (10^-7). See Attachment #1. Temperature measurement has been lost on Saturday. Last measurement was was above 1350°C, at around 480 A. TGHT was ramped down at 1 A/min. The chamber will be vented later today. The pellets and the thermocouples will be inspected.

 Monday, May 13, 2013, 17:21

The following table shows the characteristics of the pellets after sintering at 600 A for 13 hours.

Sample,   Mass (g),   Thickness (mm),   Density (g/cm3),    Diameter (mm)

1    0.8904 4.875 1.364 13.058

2    0.8991 4.744 1.396 13.148

3    0.8846 4.579 1.482 12.884

4    0.9142 4.981 1.254 13.650

5    0.9022 4.978 1.250 13.586

Avg 0.8981 4.831 1.345 13.265