John Wong wrote:

Laura Lambert wrote:  Tuesday, June 09, 2015, 9:16 Target container is coated with TaC. No Ta-heat shields are used. TGHT will be ramped up to 580A at 0.2A/min. TBHT will be ramped up to 230A at 01A/min. Chamber is currently being pumped down.  Tuesday, June 09, 2015, 15:37 HS water valves were opened. no leaks detected. Tapped up manually to 35A. Once vacuum stabilized after ~45min, initiated auto-ramp.  Wednesday, June 10, 2015, 08:02 IGP1 = 5.3e-7 Torr. TGHT = 250A and TBHT = 140A. Increasing auto ramp to 2.0A/min and 1.0A/min for the TGHT and TBHT respectively.    Wednesday, June 10, 2015, 16:32 TGHT/TBHT are at 580A/230A for almost 6 hours, temp at 1728C. Vac at 8.5e-7 Torr.  Cooling down initiated at 1A/min. Target container should be inspected once the chamber is vented.

 Thursday, June 11, 2015, 10:55

Vented in air and opened up this morning.

Same as last container sintered in evap2 [IG-LIS for UCx#13] - ends not quite fully sintered and coating not very good.

most likely due to old TaC spray.

See link for photos.

https://www.dropbox.com/sh/75o43x8y2z16e7j/AABc8Z1fTTaTRtJ5_Jr1eacWa?dl=0