Marla Cervantes wrote:

Marla Cervantes wrote:  Tuesday, October 30, 2018, 10:12 A new LP-SIS was coated and syntered (e-log 420 Evaporator_2)  The container was loaded with a graphite insert loaded with UCx Graphite insert + UCx mass = 26.927 g A current of 440 A TGHT and 230 A TBHT will be inputed to the contianer IGP1 = 8.72e-7 Torr  The current was tapped manually to 440 A TGHT and 230 A TBHT (see fig. Heating test) Maximum pressure during heating = 1.7e-3 Torr. Target will stay at maximum current for 1 week.  Wednesday, October 31, 2018, 10:09 The current tripped off,  around 5:00 am, the pressure was below 1e-5 Torr (see fig. current-trip_off). On a previous test, we measured the maximum temperature of the power supply = 33.3 C (e-log 227). Power supply overheating doesn't seem to be the problem. EPICS windows are half withe and not answering correctly. Also, TBHT says that IGP1 < 500 mTorr, and its interlock needs reset (see figure EPICS).

 Wednesday, October 31, 2018, 15:20

The problem was reported to controls, it will be also reported to power supply group.

In the meantime, the target will be ramp-up again with the auto ramp at:

TGHT = 20 A/min to 440 A

TBHT = 10 A/min to 230 A 

The pressure before heating is 4.07e-7 Torr

Wednesday, October 31, 2018, 19:24

The maximum pressure during heating was 6.57e-6 Torr.

Current pressure 3.00e-6Torr

Wednesday, November 07, 2018, 18:37

IGP1 = 9.7e-7 Torr

 TGHT = -2 A/min to 0A

TBHT = -1 A/min to 0A 

 Thursday, November 08, 2018, 16:16

EVAP1 was vented with Ar, and target was transferred to glove box.

The mass of the loaded graphite insert changed to 26.854 g

That is a difference of 0.075 g

The tantalum container "cathode" crystalized (see fig)

The rest of the tantalum container did not change.