Laura Lambert wrote:

John Wong wrote: Tuesday, November 15, 2016, 16:48 Three samples were prepared  (see my logbook#1 page 3, preparing for carbonization). One layer of Ta foil was used to wrap around the target boat.  Chamber is currently being pumped down  Wednesday, November 16, 2016, 11:04 Ramping up TGHT at 2A/min, set at 350A. Desired temperature, ~1530C (similar heating condition as raw npSiC heat treatment, elog ID335)  Thursday, November 17, 2016, 10:09 TGHT reached to 350A/5.80V, stayed for over 20 hours.  Temp measured at 1276 C (Mikon) and 1270 (Omega), vac at 6.07e-7 Torr.  Stepping up TGHT to reach the desired temp.    Thursday, November 17, 2016, 11:13 TGHT = 400A, 6.73V IGP1 = 8.2e-7 Torr OMEGA = 1385C MIKRON = 1389C Tapping up manually to 1500C or a max setpoint of 450A Thursday, November 17, 2016, 11:56 TGHT = 450A, 7.85V IGP1 = 1.7e-6 Torr OMEGA = 1502C MIKRON = 1510C  Friday, November 18, 2016, 10:08 IGP1 = 5.3e-7 Torr TGHT = 450A, 7.9V OMEGA = 1510C MIKRON = 1515C Evap2 has remained at max setpoints for 23hrs. Initiating auto-cool at 2.0A/min

 Friday, November 18, 2016, 17:27

The heat treatment of the fiber mats is done. 

Analyzing steps...